Fireproof partition laminate
Technical field
The present invention relates to a kind of fireproof partition laminate.
Background technology
Along with the development of society and improving constantly of people's living standard, all kinds of architecture indoor finishing amount is increasing, and the ornament materials of use is also just towards flame-retarded, difficult burning future development.Because general ornament materials can not meet instructions for use, therefore all kinds of flame-retardant composite fancy vener material is come out one after another, disclosed in prior art, some flame-proof sheet materials mostly are and are coated with fire retardant on solid wood boards, these flame-retardant boards not only need to consume a large amount of timber, and burning things which may cause a fire disaster can not really effectively cut off by it, easily deform or the problem such as surface from mildewing in wet weather.
Summary of the invention
The object of the invention is to overcome weak point of the prior art, providing one can effectively reduce timber utilization rate, and the fireproof partition laminate of good flame retardation effect.
In order to achieve the above object, the present invention adopts following scheme:
A kind of fireproof partition laminate, it is characterized in that described fireproof partition laminate comprises the surface layer and bottom be made up of glass fabric or non-woven fabrics, between described surface layer and bottom, be filled with inorganic mixture, wherein said inorganic mixture comprises following component by weight:
Fireproof partition laminate as above, is characterized in that described inorganic mixture comprises following component by weight:
Fireproof partition laminate as above, is characterized in that the density of described glass fabric is 70g/ ㎡, and the density of described non-woven fabrics is 18g/ ㎡.
Fireproof partition laminate as above, is characterized in that the thickness of fireproof partition laminate is 2 ~ 50mm.
In sum, the present invention relative to its beneficial effect of prior art is:
The function of each component in the present invention: sawdust has the function increasing sheet material toughness; Land plaster has the advantages that to increase hardness; The effect of perlite or vermiculite is the hardness and the fireproof performance that improve product; Magnesian effect adds fast response; Magnesium chloride has gains in strength, solidification, and the effect of fireproof performance; Glutinous rice flour has the effect increasing degree of adhesion, intensity, anti-folding degree; Urea acid resin has the effect of the toughness increasing plate; Oxalic acid has the effect preventing from getting damp; Lime has the effect preventing the accumulation of salt in the surface soil; Copper sulphate has peptizaiton.
Fireproof partition laminate fireproof performance of the present invention is that A1 level does not fire product, burst size of methanal is zero, natural environmental-protective, and intensity is high, resistance to compression degree, anti-folding degree, toughness is suitable with solid wood, can replace solid wood board, smokelessly nontoxic, insect protected, moistureproof and waterproof, effectively can reduce the use of timber.
Detailed description of the invention
Below in conjunction with detailed description of the invention, the present invention is described further:
Embodiment 1
Fireproof partition laminate of the present invention, the surface layer that the glass fabric that to comprise by density be 70g/ ㎡ is formed and bottom, between described surface layer and bottom, be filled with inorganic mixture, wherein said inorganic mixture comprises following component:
The method manufacturing fireproof partition laminate of the present invention comprises the following steps:
A, according to gauge thickness, adjustment mold machine tool size; Wherein the thickness of fireproof partition laminate can be 2 ~ 50mm, and in the present embodiment, the thickness of fireproof partition laminate chooses 2mm, so the size of adjustment mold machine tool is to corresponding position;
B, bottom described mold machine tool first layer overlay glass fabric; In proportion said components mixing and stirring is mixed with inorganic mixture, pours the inorganic mixture prepared into above-mentioned mold machine tool; Repave last layer glass fabric;
C, make reverse mould heat treatment to above-mentioned mold machine tool, shape for being taken out by the laminate in mold machine tool after 4 ~ 6 hours and carry out drying in automatic drier, temperature is 90 ~ 120 DEG C, and drying time is 15 ~ 24 hours, obtains fireproof partition laminate.
Embodiment 2
Fireproof partition laminate of the present invention, the surface layer that the non-woven fabrics that to comprise by density be 18g/ ㎡ is formed and bottom, between described surface layer and bottom, be filled with inorganic mixture, wherein said inorganic mixture comprises following component:
The method manufacturing fireproof partition laminate of the present invention comprises the following steps:
A, according to gauge thickness, adjustment mold machine tool size; Wherein the thickness of fireproof partition laminate can be 2 ~ 50mm, and in the present embodiment, the thickness of fireproof partition laminate chooses 5mm, so the size of adjustment mold machine tool is to corresponding position;
B, bottom described mold machine tool first layer overlay non-woven fabrics; In proportion said components mixing and stirring is mixed with inorganic mixture, pours the inorganic mixture prepared into above-mentioned mold machine tool; Repave last layer non-woven fabrics;
C, make reverse mould heat treatment to above-mentioned mold machine tool, shape for being taken out by the laminate in mold machine tool after 4 ~ 6 hours and carry out drying in drying cellar for storing things, temperature is 70 ~ 90 DEG C, and drying time is 15 ~ 24 hours, obtains fireproof partition laminate.
Embodiment 3
Fireproof partition laminate of the present invention, the surface layer that the glass fabric that to comprise by density be 70g/ ㎡ is formed and the bottom that the non-woven fabrics being 18g/ ㎡ by density is formed, between described surface layer and bottom, be filled with inorganic mixture, wherein said inorganic mixture comprises following component:
The method manufacturing fireproof partition laminate of the present invention comprises the following steps:
A, according to gauge thickness, adjustment mold machine tool size; Wherein the thickness of fireproof partition laminate can be 2 ~ 50mm, and in the present embodiment, the thickness of fireproof partition laminate chooses 10mm, so the size of adjustment mold machine tool is to corresponding position;
B, bottom described mold machine tool first layer overlay non-woven fabrics; In proportion said components mixing and stirring is mixed with inorganic mixture, pours the inorganic mixture prepared into above-mentioned mold machine tool; Repave last layer glass fabric;
C, make reverse mould heat treatment to above-mentioned mold machine tool, shape for being taken out by the laminate in mold machine tool after 4 ~ 6 hours and carry out drying in automatic drier, temperature is 90 ~ 120 DEG C, and drying time is 15 ~ 24 hours, obtains fireproof partition laminate.
Embodiment 4
Fireproof partition laminate of the present invention, the surface layer that the glass fabric that to comprise by density be 70g/ ㎡ is formed and bottom, between described surface layer and bottom, be filled with inorganic mixture, wherein said inorganic mixture comprises following component:
The method manufacturing fireproof partition laminate of the present invention comprises the following steps:
A, according to gauge thickness, adjustment mold machine tool size; Wherein the thickness of fireproof partition laminate can be 2 ~ 50mm, and in the present embodiment, the thickness of fireproof partition laminate chooses 15mm, so the size of adjustment mold machine tool is to corresponding position;
B, bottom described mold machine tool first layer overlay glass fabric; In proportion said components mixing and stirring is mixed with inorganic mixture, pours the inorganic mixture prepared into above-mentioned mold machine tool; Repave last layer glass fabric;
C, make reverse mould heat treatment to above-mentioned mold machine tool, shape for being taken out by the laminate in mold machine tool after 4 ~ 6 hours and carry out drying in automatic drier, temperature is 90 ~ 120 DEG C, and drying time is 15 ~ 24 hours, obtains fireproof partition laminate.
Embodiment 5
Fireproof partition laminate of the present invention, the surface layer that the non-woven fabrics that to comprise by density be 18g/ ㎡ is formed and bottom, between described surface layer and bottom, be filled with inorganic mixture, wherein said inorganic mixture comprises following component:
The method manufacturing fireproof partition laminate of the present invention comprises the following steps:
A, according to gauge thickness, adjustment mold machine tool size; Wherein the thickness of fireproof partition laminate can be 2 ~ 50mm, and in the present embodiment, the thickness of fireproof partition laminate chooses 20mm, so the size of adjustment mold machine tool is to corresponding position;
B, bottom described mold machine tool first layer overlay non-woven fabrics; In proportion said components mixing and stirring is mixed with inorganic mixture, pours the inorganic mixture prepared into above-mentioned mold machine tool; Repave last layer non-woven fabrics;
C, make reverse mould heat treatment to above-mentioned mold machine tool, shape for being taken out by the laminate in mold machine tool after 4 ~ 6 hours and carry out drying in drying cellar for storing things, temperature is 70 ~ 90 DEG C, and drying time is 15 ~ 24 hours, obtains fireproof partition laminate.
Embodiment 6
Fireproof partition laminate of the present invention, the surface layer that the glass fabric that to comprise by density be 70g/ ㎡ is formed and the bottom that the non-woven fabrics being 18g/ ㎡ by density is formed, between described surface layer and bottom, be filled with inorganic mixture, wherein said inorganic mixture comprises following component:
The method manufacturing fireproof partition laminate of the present invention comprises the following steps:
A, according to gauge thickness, adjustment mold machine tool size; Wherein the thickness of fireproof partition laminate can be 2 ~ 50mm, and in the present embodiment, the thickness of fireproof partition laminate chooses 25mm, so the size of adjustment mold machine tool is to corresponding position;
B, bottom described mold machine tool first layer overlay non-woven fabrics; In proportion said components mixing and stirring is mixed with inorganic mixture, pours the inorganic mixture prepared into above-mentioned mold machine tool; Repave last layer glass fabric;
C, make reverse mould heat treatment to above-mentioned mold machine tool, shape for being taken out by the laminate in mold machine tool after 4 ~ 6 hours and carry out drying in automatic drier, temperature is 90 ~ 120 DEG C, and drying time is 15 ~ 24 hours, obtains fireproof partition laminate.
Embodiment 7
Fireproof partition laminate of the present invention, the surface layer that the glass fabric that to comprise by density be 70g/ ㎡ is formed and bottom, between described surface layer and bottom, be filled with inorganic mixture, wherein said inorganic mixture comprises following component:
The method manufacturing fireproof partition laminate of the present invention comprises the following steps:
A, according to gauge thickness, adjustment mold machine tool size; Wherein the thickness of fireproof partition laminate can be 2 ~ 50mm, and in the present embodiment, the thickness of fireproof partition laminate chooses 30mm, so the size of adjustment mold machine tool is to corresponding position;
B, bottom described mold machine tool first layer overlay glass fabric; In proportion said components mixing and stirring is mixed with inorganic mixture, pours the inorganic mixture prepared into above-mentioned mold machine tool; Repave last layer glass fabric;
C, make reverse mould heat treatment to above-mentioned mold machine tool, shape for being taken out by the laminate in mold machine tool after 4 ~ 6 hours and carry out drying in automatic drier, temperature is 90 ~ 120 DEG C, and drying time is 15 ~ 24 hours, obtains fireproof partition laminate.
Embodiment 8
Fireproof partition laminate of the present invention, the surface layer that the glass fabric that to comprise by density be 70g/ ㎡ is formed and bottom, between described surface layer and bottom, be filled with inorganic mixture, wherein said inorganic mixture comprises following component:
The method manufacturing fireproof partition laminate of the present invention comprises the following steps:
A, according to gauge thickness, adjustment mold machine tool size; Wherein the thickness of fireproof partition laminate can be 2 ~ 50mm, and in the present embodiment, the thickness of fireproof partition laminate chooses 35mm, so the size of adjustment mold machine tool is to corresponding position;
B, bottom described mold machine tool first layer overlay glass fabric; In proportion said components mixing and stirring is mixed with inorganic mixture, pours the inorganic mixture prepared into above-mentioned mold machine tool; Repave last layer glass fabric;
C, make reverse mould heat treatment to above-mentioned mold machine tool, shape for being taken out by the laminate in mold machine tool after 4 ~ 6 hours and carry out drying in drying cellar for storing things, temperature is 70 ~ 90 DEG C, and drying time is 15 ~ 24 hours, obtains fireproof partition laminate.。
Embodiment 9
Fireproof partition laminate of the present invention, the surface layer that the glass fabric that to comprise by density be 70g/ ㎡ is formed and bottom, between described surface layer and bottom, be filled with inorganic mixture, wherein said inorganic mixture comprises following component:
The method manufacturing fireproof partition laminate of the present invention comprises the following steps:
A, according to gauge thickness, adjustment mold machine tool size; Wherein the thickness of fireproof partition laminate can be 2 ~ 50mm, and in the present embodiment, the thickness of fireproof partition laminate chooses 40mm, so the size of adjustment mold machine tool is to corresponding position;
B, bottom described mold machine tool first layer overlay glass fabric; In proportion said components mixing and stirring is mixed with inorganic mixture, pours the inorganic mixture prepared into above-mentioned mold machine tool; Repave last layer glass fabric;
C, make reverse mould heat treatment to above-mentioned mold machine tool, shape for being taken out by the laminate in mold machine tool after 4 ~ 6 hours and carry out drying in automatic drier, temperature is 90 ~ 120 DEG C, and drying time is 15 ~ 24 hours, obtains fireproof partition laminate.
Embodiment 10
Fireproof partition laminate of the present invention, the surface layer that the glass fabric that to comprise by density be 70g/ ㎡ is formed and bottom, between described surface layer and bottom, be filled with inorganic mixture, wherein said inorganic mixture comprises following component:
The method manufacturing fireproof partition laminate of the present invention comprises the following steps:
A, according to gauge thickness, adjustment mold machine tool size; Wherein the thickness of fireproof partition laminate can be 2 ~ 50mm, and in the present embodiment, the thickness of fireproof partition laminate chooses 50mm, so the size of adjustment mold machine tool is to corresponding 50mm position;
B, bottom described mold machine tool first layer overlay glass fabric; In proportion said components mixing and stirring is mixed with inorganic mixture, pours the inorganic mixture prepared into above-mentioned mold machine tool; Repave last layer glass fabric;
C, make reverse mould heat treatment to above-mentioned mold machine tool, shape for being taken out by the laminate in mold machine tool after 4 ~ 6 hours and carry out drying in automatic drier, temperature is 90 ~ 120 DEG C, and drying time is 15 ~ 24 hours, obtains fireproof partition laminate.
Embodiment 11
Fireproof partition laminate of the present invention, the surface layer that the glass fabric that to comprise by density be 70g/ ㎡ is formed and bottom, between described surface layer and bottom, be filled with inorganic mixture, wherein said inorganic mixture comprises following component:
The method manufacturing fireproof partition laminate of the present invention comprises the following steps:
A, according to gauge thickness, adjustment mold machine tool size; Wherein the thickness of fireproof partition laminate can be 2 ~ 50mm, and in the present embodiment, the thickness of fireproof partition laminate chooses 50mm, so the size of adjustment mold machine tool is to corresponding 50mm position;
B, bottom described mold machine tool first layer overlay glass fabric; In proportion said components mixing and stirring is mixed with inorganic mixture, pours the inorganic mixture prepared into above-mentioned mold machine tool; Repave last layer glass fabric;
C, make reverse mould heat treatment to above-mentioned mold machine tool, shape for being taken out by the laminate in mold machine tool after 4 ~ 6 hours and carry out drying in automatic drier, temperature is 90 ~ 120 DEG C, and drying time is 15 ~ 24 hours, obtains fireproof partition laminate.
Embodiment 12
Fireproof partition laminate of the present invention, the surface layer that the glass fabric that to comprise by density be 70g/ ㎡ is formed and bottom, between described surface layer and bottom, be filled with inorganic mixture, wherein said inorganic mixture comprises following component:
The method manufacturing fireproof partition laminate of the present invention comprises the following steps:
A, according to gauge thickness, adjustment mold machine tool size; Wherein the thickness of fireproof partition laminate can be 2 ~ 50mm, and in the present embodiment, the thickness of fireproof partition laminate chooses 50mm, so the size of adjustment mold machine tool is to corresponding 50mm position;
B, bottom described mold machine tool first layer overlay glass fabric; In proportion said components mixing and stirring is mixed with inorganic mixture, pours the inorganic mixture prepared into above-mentioned mold machine tool; Repave last layer glass fabric;
C, make reverse mould heat treatment to above-mentioned mold machine tool, shape for being taken out by the laminate in mold machine tool after 4 ~ 6 hours and carry out drying in automatic drier, temperature is 90 ~ 120 DEG C, and drying time is 15 ~ 24 hours, obtains fireproof partition laminate.
Embodiment 13
Fireproof partition laminate of the present invention, the surface layer that the glass fabric that to comprise by density be 70g/ ㎡ is formed and bottom, be filled with inorganic mixture between described surface layer and bottom, and wherein described by weight inorganic mixture comprises following component:
The method manufacturing fireproof partition laminate of the present invention comprises the following steps:
A, according to gauge thickness, adjustment mold machine tool size; Wherein the thickness of fireproof partition laminate can be 2 ~ 50mm, and in the present embodiment, the thickness of fireproof partition laminate chooses 50mm, so the size of adjustment mold machine tool is to corresponding 50mm position;
B, bottom described mold machine tool first layer overlay glass fabric; In proportion said components mixing and stirring is mixed with inorganic mixture, pours the inorganic mixture prepared into above-mentioned mold machine tool; Repave last layer glass fabric;
C, make reverse mould heat treatment to above-mentioned mold machine tool, shape for being taken out by the laminate in mold machine tool after 4 ~ 6 hours and carry out drying in automatic drier, temperature is 90 ~ 120 DEG C, and drying time is 15 ~ 24 hours, obtains fireproof partition laminate.
Fireproof partition laminate in the present invention 1 to 13 is through GB8624-2006 " constructional materials and product burns grading performance " inspection, and combustibility meets the regulation requirement of A1 level, and combustibility reaches A1 level; Rupture strength is 1.909 ~ 2.362Mpa; Compressive resistance is 65.213 ~ 72.564Mpa; Bending resistance degree 1.5 ~ 1.7mm; 96 hours are soaked without quality problems with 40% acid-base solution.The fire protection flame retarding wood flooring adopting fireproof partition laminate of the present invention to manufacture is through GB20286-2006 " public place fire-retardant product and assembly combustibility require and mark " inspection, and combustibility reaches Br1-s, tl level, and smoke toxicity reaches accurate safe ZA lower than tl level
3level.