CN105239744B - Fireproof partition laminate - Google Patents

Fireproof partition laminate Download PDF

Info

Publication number
CN105239744B
CN105239744B CN201510548142.6A CN201510548142A CN105239744B CN 105239744 B CN105239744 B CN 105239744B CN 201510548142 A CN201510548142 A CN 201510548142A CN 105239744 B CN105239744 B CN 105239744B
Authority
CN
China
Prior art keywords
fireproof partition
machine tool
mold machine
laminate
layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201510548142.6A
Other languages
Chinese (zh)
Other versions
CN105239744A (en
Inventor
黄冠兴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Gu Junxiong
Original Assignee
Zhongshan Xiangshi Machinery Equipment Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhongshan Xiangshi Machinery Equipment Co Ltd filed Critical Zhongshan Xiangshi Machinery Equipment Co Ltd
Priority to CN201510548142.6A priority Critical patent/CN105239744B/en
Publication of CN105239744A publication Critical patent/CN105239744A/en
Application granted granted Critical
Publication of CN105239744B publication Critical patent/CN105239744B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a kind of fireproof partition laminate, described fireproof partition laminate includes the surface layer and bottom being made up of glass fabric or non-woven fabrics, inorganic mixture is filled between described surface layer and bottom, wherein described inorganic mixture includes following components:Sawdust, land plaster, perlite, magnesia, magnesium chloride, glutinous rice flour, urea acid resin, oxalic acid, lime, copper sulphate, asbestos, aerosil, alundum (Al2O3).The invention aims to overcome weak point of the prior art there is provided one kind can effectively reduce timber utilization rate, and the fireproof partition laminate of good flame retardation effect.

Description

Fireproof partition laminate
Technical field
The present invention relates to a kind of fireproof partition laminate.
Background technology
With the development and the continuous improvement of people's living standard of society, all kinds of architecture indoor finishing amounts are increasing, make Ornament materials is also just developing towards flame-retarded, fire retardantization direction.Wanted because general ornament materials can not meet to use Ask, therefore all kinds of flame-retardant composite fancy vener materials are come out one after another, some disclosed flame-proof sheet materials are generally in solid wood board in the prior art Upper coating fire retardant, these flame-retardant boards not only need to consume substantial amounts of timber, and it really can not effectively separate burning things which may cause a fire disaster, Wet weather easily deforms or the problems such as surface from mildewing.
The content of the invention
The invention aims to overcome weak point of the prior art effectively to reduce timber there is provided one kind to use Rate, and the fireproof partition laminate of good flame retardation effect.
In order to achieve the above object, the present invention uses following scheme:
A kind of fireproof partition laminate, it is characterised in that described fireproof partition laminate is included by glass fabric or nonwoven Surface layer and bottom that cloth is constituted, are filled with inorganic mixture, wherein described inorganic mixing between described surface layer and bottom Thing includes following components by weight:
Fireproof partition laminate as described above, it is characterised in that described inorganic mixture includes with the following group by weight Point:
Fireproof partition laminate as described above, it is characterised in that the density of described glass fabric is 70g/ ㎡, institute The density for the non-woven fabrics stated is 18g/ ㎡.
Fireproof partition laminate as described above, it is characterised in that the thickness of fireproof partition laminate is 2~50mm.
In summary, the present invention is relative to prior art its advantage:
The function of each component in the present invention:Sawdust has the function of increase sheet material toughness;Land plaster has increase hard The characteristics of spending;The effect of perlite or vermiculite is the hardness and fire protecting performance for improving product;The effect of magnesia is to speed up reaction; Magnesium chloride has the effect of increase intensity, solidification, and fire protecting performance;Glutinous rice flour has increase degree of adhesion, intensity, the work of anti-folding degree With;Urea acid resin has the effect of the toughness of increase plate;Oxalic acid has the effect for preventing from getting damp;Lime, which has, prevents the work of the accumulation of salt in the surface soil With;Copper sulphate has peptizaiton.
Fireproof partition laminate fire protecting performance of the present invention is that A1 grades of non-ignitable product, burst size of methanal are zero, natural environmental-protective, intensity Height, resistance to compression degree, anti-folding degree, toughness is suitable with solid wood, can replace solid wood board, nontoxic smokeless, insect prevention, moistureproof and waterproof can effectively drop The use of low timber.
Embodiment
The present invention is described further with reference to embodiment:
Embodiment 1
Fireproof partition laminate of the present invention, including the surface layer and bottom being made up of density for 70g/ ㎡ glass fabric, Inorganic mixture is filled between described surface layer and bottom, wherein described inorganic mixture includes following components:
The method of manufacture fireproof partition laminate of the present invention comprises the following steps:
A, according to gauge thickness, adjust the size of mold machine tool;Wherein the thickness of fireproof partition laminate can be 2~50mm, The thickness of fireproof partition laminate chooses 2mm in the present embodiment, so the size of adjustment mold machine tool is to corresponding position;
B, in the first layer overlay glass fabric in described mold machine tool bottom;Said components are mixed in proportion Inorganic mixture uniformly is configured to, the inorganic mixture prepared is poured into above-mentioned mold machine tool;It is then covered with layer of glass Fabric;
C, make reverse mould heat treatment to above-mentioned mold machine tool, sizing, which took out the laminate in mold machine tool after 4~6 hours, to exist It is dried in automatic drier, temperature is 90~120 DEG C, and drying time is 15~24 hours, produces fireproof partition laminate.
Embodiment 2
Fireproof partition laminate of the present invention, including the surface layer and bottom being made up of density for 18g/ ㎡ non-woven fabrics, described Surface layer and bottom between be filled with inorganic mixture, wherein described inorganic mixture include following components:
The method of manufacture fireproof partition laminate of the present invention comprises the following steps:
A, according to gauge thickness, adjust the size of mold machine tool;Wherein the thickness of fireproof partition laminate can be 2~50mm, The thickness of fireproof partition laminate chooses 5mm in the present embodiment, so the size of adjustment mold machine tool is to corresponding position;
B, in the first layer overlay non-woven fabrics in described mold machine tool bottom;Said components are mixed evenly in proportion and matched somebody with somebody Inorganic mixture is made, the inorganic mixture prepared is poured into above-mentioned mold machine tool;It is then covered with layer of non-woven fabric;
C, make reverse mould heat treatment to above-mentioned mold machine tool, sizing, which took out the laminate in mold machine tool after 4~6 hours, to exist Dry and be dried in cellar for storing things, temperature is 70~90 DEG C, and drying time is 15~24 hours, produces fireproof partition laminate.
Embodiment 3
Fireproof partition laminate of the present invention, including by density for the 70g/ ㎡ surface layer that constitutes of glass fabric and by density The bottom constituted for 18g/ ㎡ non-woven fabrics, is filled with inorganic mixture, wherein described between described surface layer and bottom Inorganic mixture includes following components:
The method of manufacture fireproof partition laminate of the present invention comprises the following steps:
A, according to gauge thickness, adjust the size of mold machine tool;Wherein the thickness of fireproof partition laminate can be 2~50mm, The thickness of fireproof partition laminate chooses 10mm in the present embodiment, so the size of adjustment mold machine tool is to corresponding position;
B, in the first layer overlay non-woven fabrics in described mold machine tool bottom;Said components are mixed evenly in proportion and matched somebody with somebody Inorganic mixture is made, the inorganic mixture prepared is poured into above-mentioned mold machine tool;It is then covered with layer of glass fabric;
C, make reverse mould heat treatment to above-mentioned mold machine tool, sizing, which took out the laminate in mold machine tool after 4~6 hours, to exist It is dried in automatic drier, temperature is 90~120 DEG C, and drying time is 15~24 hours, produces fireproof partition laminate.
Embodiment 4
Fireproof partition laminate of the present invention, including the surface layer and bottom being made up of density for 70g/ ㎡ glass fabric, Inorganic mixture is filled between described surface layer and bottom, wherein described inorganic mixture includes following components:
The method of manufacture fireproof partition laminate of the present invention comprises the following steps:
A, according to gauge thickness, adjust the size of mold machine tool;Wherein the thickness of fireproof partition laminate can be 2~50mm, The thickness of fireproof partition laminate chooses 15mm in the present embodiment, so the size of adjustment mold machine tool is to corresponding position;
B, in the first layer overlay glass fabric in described mold machine tool bottom;Said components are mixed in proportion Inorganic mixture uniformly is configured to, the inorganic mixture prepared is poured into above-mentioned mold machine tool;It is then covered with layer of glass Fabric;
C, make reverse mould heat treatment to above-mentioned mold machine tool, sizing, which took out the laminate in mold machine tool after 4~6 hours, to exist It is dried in automatic drier, temperature is 90~120 DEG C, and drying time is 15~24 hours, produces fireproof partition laminate.
Embodiment 5
Fireproof partition laminate of the present invention, including the surface layer and bottom being made up of density for 18g/ ㎡ non-woven fabrics, described Surface layer and bottom between be filled with inorganic mixture, wherein described inorganic mixture include following components:
The method of manufacture fireproof partition laminate of the present invention comprises the following steps:
A, according to gauge thickness, adjust the size of mold machine tool;Wherein the thickness of fireproof partition laminate can be 2~50mm, The thickness of fireproof partition laminate chooses 20mm in the present embodiment, so the size of adjustment mold machine tool is to corresponding position;
B, in the first layer overlay non-woven fabrics in described mold machine tool bottom;Said components are mixed evenly in proportion and matched somebody with somebody Inorganic mixture is made, the inorganic mixture prepared is poured into above-mentioned mold machine tool;It is then covered with layer of non-woven fabric;
C, make reverse mould heat treatment to above-mentioned mold machine tool, sizing, which took out the laminate in mold machine tool after 4~6 hours, to exist Dry and be dried in cellar for storing things, temperature is 70~90 DEG C, and drying time is 15~24 hours, produces fireproof partition laminate.
Embodiment 6
Fireproof partition laminate of the present invention, including by density for the 70g/ ㎡ surface layer that constitutes of glass fabric and by density The bottom constituted for 18g/ ㎡ non-woven fabrics, is filled with inorganic mixture, wherein described between described surface layer and bottom Inorganic mixture includes following components:
The method of manufacture fireproof partition laminate of the present invention comprises the following steps:
A, according to gauge thickness, adjust the size of mold machine tool;Wherein the thickness of fireproof partition laminate can be 2~50mm, The thickness of fireproof partition laminate chooses 25mm in the present embodiment, so the size of adjustment mold machine tool is to corresponding position;
B, in the first layer overlay non-woven fabrics in described mold machine tool bottom;Said components are mixed evenly in proportion and matched somebody with somebody Inorganic mixture is made, the inorganic mixture prepared is poured into above-mentioned mold machine tool;It is then covered with layer of glass fabric;
C, make reverse mould heat treatment to above-mentioned mold machine tool, sizing, which took out the laminate in mold machine tool after 4~6 hours, to exist It is dried in automatic drier, temperature is 90~120 DEG C, and drying time is 15~24 hours, produces fireproof partition laminate.
Embodiment 7
Fireproof partition laminate of the present invention, including the surface layer and bottom being made up of density for 70g/ ㎡ glass fabric, Inorganic mixture is filled between described surface layer and bottom, wherein described inorganic mixture includes following components:
The method of manufacture fireproof partition laminate of the present invention comprises the following steps:
A, according to gauge thickness, adjust the size of mold machine tool;Wherein the thickness of fireproof partition laminate can be 2~50mm, The thickness of fireproof partition laminate chooses 30mm in the present embodiment, so the size of adjustment mold machine tool is to corresponding position;
B, in the first layer overlay glass fabric in described mold machine tool bottom;Said components are mixed in proportion Inorganic mixture uniformly is configured to, the inorganic mixture prepared is poured into above-mentioned mold machine tool;It is then covered with layer of glass Fabric;
C, make reverse mould heat treatment to above-mentioned mold machine tool, sizing, which took out the laminate in mold machine tool after 4~6 hours, to exist It is dried in automatic drier, temperature is 90~120 DEG C, and drying time is 15~24 hours, produces fireproof partition laminate.
Embodiment 8
Fireproof partition laminate of the present invention, including the surface layer and bottom being made up of density for 70g/ ㎡ glass fabric, Inorganic mixture is filled between described surface layer and bottom, wherein described inorganic mixture includes following components:
The method of manufacture fireproof partition laminate of the present invention comprises the following steps:
A, according to gauge thickness, adjust the size of mold machine tool;Wherein the thickness of fireproof partition laminate can be 2~50mm, The thickness of fireproof partition laminate chooses 35mm in the present embodiment, so the size of adjustment mold machine tool is to corresponding position;
B, in the first layer overlay glass fabric in described mold machine tool bottom;Said components are mixed in proportion Inorganic mixture uniformly is configured to, the inorganic mixture prepared is poured into above-mentioned mold machine tool;It is then covered with layer of glass Fabric;
C, make reverse mould heat treatment to above-mentioned mold machine tool, sizing, which took out the laminate in mold machine tool after 4~6 hours, to exist Dry and be dried in cellar for storing things, temperature is 70~90 DEG C, and drying time is 15~24 hours, produces fireproof partition laminate..
Embodiment 9
Fireproof partition laminate of the present invention, including the surface layer and bottom being made up of density for 70g/ ㎡ glass fabric, Inorganic mixture is filled between described surface layer and bottom, wherein described inorganic mixture includes following components:
The method of manufacture fireproof partition laminate of the present invention comprises the following steps:
A, according to gauge thickness, adjust the size of mold machine tool;Wherein the thickness of fireproof partition laminate can be 2~50mm, The thickness of fireproof partition laminate chooses 40mm in the present embodiment, so the size of adjustment mold machine tool is to corresponding position;
B, in the first layer overlay glass fabric in described mold machine tool bottom;Said components are mixed in proportion Inorganic mixture uniformly is configured to, the inorganic mixture prepared is poured into above-mentioned mold machine tool;It is then covered with layer of glass Fabric;
C, make reverse mould heat treatment to above-mentioned mold machine tool, sizing, which took out the laminate in mold machine tool after 4~6 hours, to exist It is dried in automatic drier, temperature is 90~120 DEG C, and drying time is 15~24 hours, produces fireproof partition laminate.
Embodiment 10
Fireproof partition laminate of the present invention, including the surface layer and bottom being made up of density for 70g/ ㎡ glass fabric, Inorganic mixture is filled between described surface layer and bottom, wherein described inorganic mixture includes following components:
The method of manufacture fireproof partition laminate of the present invention comprises the following steps:
A, according to gauge thickness, adjust the size of mold machine tool;Wherein the thickness of fireproof partition laminate can be 2~50mm, The thickness of fireproof partition laminate chooses 50mm in the present embodiment, so the size of adjustment mold machine tool is to corresponding 50mm positions;
B, in the first layer overlay glass fabric in described mold machine tool bottom;Said components are mixed in proportion Inorganic mixture uniformly is configured to, the inorganic mixture prepared is poured into above-mentioned mold machine tool;It is then covered with layer of glass Fabric;
C, make reverse mould heat treatment to above-mentioned mold machine tool, sizing, which took out the laminate in mold machine tool after 4~6 hours, to exist It is dried in automatic drier, temperature is 90~120 DEG C, and drying time is 15~24 hours, produces fireproof partition laminate.
Embodiment 11
Fireproof partition laminate of the present invention, including the surface layer and bottom being made up of density for 70g/ ㎡ glass fabric, Inorganic mixture is filled between described surface layer and bottom, wherein described inorganic mixture includes following components:
The method of manufacture fireproof partition laminate of the present invention comprises the following steps:
A, according to gauge thickness, adjust the size of mold machine tool;Wherein the thickness of fireproof partition laminate can be 2~50mm, The thickness of fireproof partition laminate chooses 50mm in the present embodiment, so the size of adjustment mold machine tool is to corresponding 50mm positions;
B, in the first layer overlay glass fabric in described mold machine tool bottom;Said components are mixed in proportion Inorganic mixture uniformly is configured to, the inorganic mixture prepared is poured into above-mentioned mold machine tool;It is then covered with layer of glass Fabric;
C, make reverse mould heat treatment to above-mentioned mold machine tool, sizing, which took out the laminate in mold machine tool after 4~6 hours, to exist It is dried in automatic drier, temperature is 90~120 DEG C, and drying time is 15~24 hours, produces fireproof partition laminate.
Embodiment 12
Fireproof partition laminate of the present invention, including the surface layer and bottom being made up of density for 70g/ ㎡ glass fabric, Inorganic mixture is filled between described surface layer and bottom, wherein described inorganic mixture includes following components:
The method of manufacture fireproof partition laminate of the present invention comprises the following steps:
A, according to gauge thickness, adjust the size of mold machine tool;Wherein the thickness of fireproof partition laminate can be 2~50mm, The thickness of fireproof partition laminate chooses 50mm in the present embodiment, so the size of adjustment mold machine tool is to corresponding 50mm positions;
B, in the first layer overlay glass fabric in described mold machine tool bottom;Said components are mixed in proportion Inorganic mixture uniformly is configured to, the inorganic mixture prepared is poured into above-mentioned mold machine tool;It is then covered with layer of glass Fabric;
C, make reverse mould heat treatment to above-mentioned mold machine tool, sizing, which took out the laminate in mold machine tool after 4~6 hours, to exist It is dried in automatic drier, temperature is 90~120 DEG C, and drying time is 15~24 hours, produces fireproof partition laminate.
Embodiment 13
Fireproof partition laminate of the present invention, including the surface layer and bottom being made up of density for 70g/ ㎡ glass fabric, Inorganic mixture is filled between described surface layer and bottom, wherein described inorganic mixture is included with the following group by weight Point:
The method of manufacture fireproof partition laminate of the present invention comprises the following steps:
A, according to gauge thickness, adjust the size of mold machine tool;Wherein the thickness of fireproof partition laminate can be 2~50mm, The thickness of fireproof partition laminate chooses 50mm in the present embodiment, so the size of adjustment mold machine tool is to corresponding 50mm positions;
B, in the first layer overlay glass fabric in described mold machine tool bottom;Said components are mixed in proportion Inorganic mixture uniformly is configured to, the inorganic mixture prepared is poured into above-mentioned mold machine tool;It is then covered with layer of glass Fabric;
C, make reverse mould heat treatment to above-mentioned mold machine tool, sizing, which took out the laminate in mold machine tool after 4~6 hours, to exist It is dried in automatic drier, temperature is 90~120 DEG C, and drying time is 15~24 hours, produces fireproof partition laminate.
Fireproof partition laminate in the present invention 1 to 13 passes through GB8624-2006《Construction material and product burns performance point Level》Examine, combustibility meets A1 grades of regulation requirement, combustibility reaches A1 grades;Rupture strength be 1.909~ 2.362Mpa;Compressive resistance is 65.213~72.564Mpa;1.5~1.7mm of bending resistance degree;Soaked 96 hours with 40% acid-base solution Massless problem.The fire protection flame retarding timber floor manufactured using fireproof partition laminate of the present invention passes through GB20286-2006《Public field Institute's fire-retardant product and the requirement of component combustibility and mark》Examine, combustibility reaches Br1-s, and tl grades, smoke toxicity is less than tl grades Reach accurate safe ZA3Level.

Claims (1)

1. a kind of fireproof partition laminate, it is characterised in that:The fireproof partition laminate includes the glass fibre for 70g/ ㎡ by density Surface layer and bottom that fabric is constituted, are filled with inorganic mixture between described surface layer and bottom, wherein described is inorganic mixed Compound includes following components:
The method of manufacture fireproof partition laminate comprises the following steps:
A, according to gauge thickness, adjust the size of mold machine tool;Wherein the thickness of fireproof partition laminate is 50mm, so adjustment mould Has the size of lathe to corresponding 50mm positions;
B, in the first layer overlay glass fabric in described mold machine tool bottom;Said components are mixed evenly in proportion Inorganic mixture is configured to, the inorganic mixture prepared is poured into above-mentioned mold machine tool;It is then covered with layer of glass fabric;
C, make reverse mould heat treatment to above-mentioned mold machine tool, sizing took out the laminate in mold machine tool automatic after 4~6 hours It is dried in drying machine, temperature is 90~120 DEG C, and drying time is 15~24 hours, produces fireproof partition laminate.
CN201510548142.6A 2015-08-28 2015-08-28 Fireproof partition laminate Active CN105239744B (en)