CN105440813A - Preparation method of environment-friendly soundproof paint - Google Patents
Preparation method of environment-friendly soundproof paint Download PDFInfo
- Publication number
- CN105440813A CN105440813A CN201510953177.8A CN201510953177A CN105440813A CN 105440813 A CN105440813 A CN 105440813A CN 201510953177 A CN201510953177 A CN 201510953177A CN 105440813 A CN105440813 A CN 105440813A
- Authority
- CN
- China
- Prior art keywords
- parts
- preparation
- minute
- environment
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a preparation method of an environment-friendly soundproof paint, which is prepared from the following raw materials in parts by weight: 2 to 6 parts of ionic chain extender, 20 to 30 parts of heavy calcium carbonate, 1 to 3 parts of nonionic chain extender, 3 to 15 parts of talcum powder, 1 to 1.5 parts of hydroxymethyl cellulose, 0.1 to 0.5 part of catalyst, 0.1 to 0.5 part of polypropylene fiber, 25 to 35 parts of inorganic filling material, 0.3 to 1 part of mildew preventive agent, 10 to 40 parts of glycerin, 0.3 to 1 part of dispersant, 1 to 3 parts of neutralizer, 8 to 15 parts of deionized water, and 10 to 40 parts of bentonite. The environment-friendly soundproof paint has a high soundproof performance and will not generate any substance that is harmful to human body and environment.
Description
Technical field
The present invention relates to a kind of preparation method of environmental protection deadener.
Background technology
The sound-proof material of existing traditional architectural decoration is all based on glass fibre, its shortcoming is that glass fiber material is to low-frequency sound-absorbing weak effect, does not have fire retardation, can not mosquito proof, and not only material itself is harmful, also obnoxious flavour can be produced when burning.
The sound pollution that modern society occurs, especially room noise pollute to the harm of healthy and daily life gradually by people are paid attention to, and therefore, a lot of modern architecture needs when design the soundproof effect considering its inside.Sound-proof material not only can improve indoor tonequality environment, and also plays very important effect to noise control.The kind of traditional building sound-proof material is a lot, and common mainly contains gypsum decorative acoustic board, glass wool decoration acoustic absorption, rock (ore deposit) cotton decoration acoustic absorption, pearlite decorative acoustic board, polystyrene foamed plastics decoration acoustic absorption, metal finishing acoustic board, perforated microstructure acoustic board etc.These acoustic boards, owing to being subject to limitation of size, not easily being stored, are transported, assembled, and some material surface also needs supplementary protection and ornament layer.And rock (ore deposit) cotton material is harmful, if improper use has carcinogenic danger; Polystyrene foamed plastics acoustic board ventilation property and thermotolerance bad, meet fire can discharge harmful gas; And porous metal plate sound-absorbing material and perforated microstructure acoustic board, cost is too high, is not also widely used.
All advocating under energy-saving and environmental protection, green overall background in the current whole world, building energy-saving, green become a large task of construction industry.In the current whole world, upholstery or can only accomplish energy-conservation, can only sound insulation be accomplished, i.e. sound insulation will be possessed simultaneously but also energy-conservation manufacturing cost higher comparatively speaking, therefore studying a kind of low cost, to possess again coating that is energy-conservation, the large function of sound insulation two very necessary.
Summary of the invention
The object of the invention is to: just to prior art defect, provide that a kind of soundproof effect is good, safety and environmental protection, deadener.
The technical solution used in the present invention is such:
A preparation method for environmental protection deadener, preparation process is as follows:
(1) by ionic chainextender 2-6 part, coarse whiting 20-30 part, nonionic chainextender 1-3 part, talcum powder 3-15 part, puts into and stirs 5-10 minute with agitator, and temperature, at 25-30 DEG C, then sends into storage tank;
(2) by Walocel MT 20.000PV 1-1.5 part, catalyzer 0.1-0.5 part, polypropylene fibre 0.1-0.5 part is put into agitator and is stirred 8-10 minute, and temperature, at 30-5 DEG C, then puts into another storage tank stand-by;
(3) mixture handled well in step (1) and step (2) has been delivered to mineral filler 25-35 part with two volume pumps respectively simultaneously, mould inhibitor 0.3-1 part, glycerine 10-40 part, in the mixing tank of dispersion agent 0.3-1 part, by neutralizing agent 1-3 part of all the other components, deionized water 8-15 part, wilkinite 10-40 part is sent in mixing tank with another volume pump successively simultaneously, be uniformly mixed 15-20 minute, temperature controls at 25 DEG C, and after finally stirring, inspection is dispatched from the factory.
Further, powder flame-proof agent 15-25 part is also added in described step (2), wetting agent 0.2-0.5 part, tolylene diisocyanate 20-40 part.
In sum, owing to have employed technique scheme, the invention has the beneficial effects as follows: sound-proofing properties of the present invention is high, the material to human body and bad environmental can not be produced.
Embodiment
All features disclosed in this specification sheets, or the step in disclosed all methods or process, except mutually exclusive feature and/or step, all can combine by any way.
Arbitrary feature disclosed in this specification sheets (comprising any accessory claim and summary), unless specifically stated otherwise, all can be replaced by other equivalences or the alternative features with similar object.That is, unless specifically stated otherwise, each feature is an example in a series of equivalence or similar characteristics.
A kind of environmental protection deadener, is made up of the raw material of following weight part: ionic chainextender 2-6 part, coarse whiting 20-30 part, nonionic chainextender 1-3 part, talcum powder 3-15 part, Walocel MT 20.000PV 1-1.5 part, catalyzer 0.1-0.5 part, polypropylene fibre 0.1-0.5 part, mineral filler 25-35 part, mould inhibitor 0.3-1 part, glycerine 10-40 part, dispersion agent 0.3-1 part, neutralizing agent 1-3 part, deionized water 8-15 part, wilkinite 10-40 part.
Preferably, powder flame-proof agent 15-25 part is also comprised, wetting agent 0.2-0.5 part, tolylene diisocyanate 20-40 part.
Preferably, ionic chainextender 3 parts, coarse whiting 25 parts, nonionic chainextender 2 parts, talcum powder 8 parts, Walocel MT 20.000PV 1 part, catalyzer 0.4 part, polypropylene fibre 0.3 part, mineral filler 28 parts, mould inhibitor 0.8 part, glycerine 20 parts, dispersion agent 0.7 part, neutralizing agent 2 parts, deionized water 10 parts, wilkinite 30 parts.
Preferably, described powder flame-proof agent 20 parts, wetting agent 0.3 part, tolylene diisocyanate 30 parts.
A preparation method for environmental protection deadener, preparation process is as follows:
(1) by ionic chainextender 2-6 part, coarse whiting 20-30 part, nonionic chainextender 1-3 part, talcum powder 3-15 part, puts into and stirs 5-10 minute with agitator, and temperature, at 25-30 DEG C, then sends into storage tank;
(2) by Walocel MT 20.000PV 1-1.5 part, catalyzer 0.1-0.5 part, polypropylene fibre 0.1-0.5 part is put into agitator and is stirred 8-10 minute, and temperature, at 30-5 DEG C, then puts into another storage tank stand-by;
(3) mixture handled well in step (1) and step (2) has been delivered to mineral filler 25-35 part with two volume pumps respectively simultaneously, mould inhibitor 0.3-1 part, glycerine 10-40 part, in the mixing tank of dispersion agent 0.3-1 part, by neutralizing agent 1-3 part of all the other components, deionized water 8-15 part, wilkinite 10-40 part is sent in mixing tank with another volume pump successively simultaneously, be uniformly mixed 15-20 minute, temperature controls at 25 DEG C, and after finally stirring, inspection is dispatched from the factory.
Preferably, powder flame-proof agent 15-25 part is also added in described step (2), wetting agent 0.2-0.5 part, tolylene diisocyanate 20-40 part.
Above-described specific embodiment, further describes object of the present invention, technical scheme and beneficial effect, and institute it should be understood that and the foregoing is only specific embodiments of the invention, is not limited to the present invention.The present invention expands to any new feature of disclosing in this manual or any combination newly, and the step of the arbitrary new method disclosed or process or any combination newly.
Claims (2)
1. a preparation method for environmental protection deadener, is characterized in that: preparation process is as follows:
(1) by ionic chainextender 2-6 part, coarse whiting 20-30 part, nonionic chainextender 1-3 part, talcum powder 3-15 part, puts into and stirs 5-10 minute with agitator, and temperature, at 25-30 DEG C, then sends into storage tank;
(2) by Walocel MT 20.000PV 1-1.5 part, catalyzer 0.1-0.5 part, polypropylene fibre 0.1-0.5 part is put into agitator and is stirred 8-10 minute, and temperature, at 30-5 DEG C, then puts into another storage tank stand-by;
(3) mixture handled well in step (1) and step (2) has been delivered to mineral filler 25-35 part with two volume pumps respectively simultaneously, mould inhibitor 0.3-1 part, glycerine 10-40 part, in the mixing tank of dispersion agent 0.3-1 part, by neutralizing agent 1-3 part of all the other components, deionized water 8-15 part, wilkinite 10-40 part is sent in mixing tank with another volume pump successively simultaneously, be uniformly mixed 15-20 minute, temperature controls at 25 DEG C, and after finally stirring, inspection is dispatched from the factory.
2. the preparation method of environmental protection deadener according to claim 1, is characterized in that: also add powder flame-proof agent 15-25 part in described step (2), wetting agent 0.2-0.5 part, tolylene diisocyanate 20-40 part.