CN107904753A - A kind of wool fiber cladding polyester filament fabric blended with cotton fiber and its weaving process - Google Patents
A kind of wool fiber cladding polyester filament fabric blended with cotton fiber and its weaving process Download PDFInfo
- Publication number
- CN107904753A CN107904753A CN201711436948.1A CN201711436948A CN107904753A CN 107904753 A CN107904753 A CN 107904753A CN 201711436948 A CN201711436948 A CN 201711436948A CN 107904753 A CN107904753 A CN 107904753A
- Authority
- CN
- China
- Prior art keywords
- wool
- cotton
- fiber
- fabric
- yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the blended cladding polyester filament fabric of a kind of wool fiber and cotton fiber and its weaving process.The fabric by wool fiber and pure cotton fiber it is blended after coat polyester filament again, braiding forms, and the main good moisture adsorption and releasing for utilizing wool fiber, good hand feeling, warmth retention property are good, comfortable and easy to wear, improve pure cotton it is elastic bad the defects of；Also there is good skin affinity characteristic, carry out cladding polyester filament after blended again, polyester filament has the characteristics that high intensity, crease resistance are good, and the fusion of three has accomplished have complementary advantages.
Description
Technical field
It is blended more particularly to a kind of wool fiber and cotton fiber the present invention relates to a kind of blended yarn weaved fabric and its weaving process
Coat polyester filament fabric and its weaving process.
Background technology
With the continuous change in weaving market, weaving industry-by-industry constantly merges, and the boundary of present industry-by-industry is more next
Fuzzyyer, cotton spinning originally, bast fibre spinning, the boundary subsidiary factory of wool spinning are clear, and market requires comprehensive performance more and more complete textile,
So that various fiber blends, novel spinning form is continuously emerged to meet this requirement in market；Weaving enterprise how is lifted at the same time
The market competitiveness and lifting value of the product of industry, are that current domestic spin looks forward to one of faced major issue；And as people disappear
The flat increasingly raising of water wasting, clothes home textile is not re-used as simple decoration, and assigns clothes some specific functions, and beautiful jade Sai Er is fine
Dimension has broad mass market with its good draping property.
Wool, it is one of natural fiber that the mankind utilize earliest in weaving.Wool fiber is soft and flexible, by
In the wool of curling, contain substantial amounts of air；And the coefficient of overall heat transmission of air is very low, can effectively prevent cool exterior air into
Enter and distributed with hot inside air, thus can reach very high heat insulating ability.
Meanwhile wool has splendid moisture adsorption and releasing, can constantly absorb the moisture and sweat distributed from human body, and by it
It is discharged into air, so that wool product keeps dry and comfortable, comfortably.Its gloss is soft, and high resilience is not easy to stain, and makes throughout the year
With holding comfort is remained to, wool product has the features such as good hand feeling, warmth retention property are good, comfortable and easy to wear.
The features such as cotton fiber snugness of fit is good is it is obvious that still intolerant to wrinkle, poor flexibility also than more prominent, how by naturally
Cellucotton and wool fiber carry out blended, the advantage for polyester filament of arranging in pairs or groups in suitable ratio, accomplish that three has complementary advantages, obtain
High performance fabric, is the technical problem to be solved in the present invention.
The content of the invention
The present invention provides a kind of wool fiber and the blended cladding terylene length of cotton fiber aiming at above-mentioned defect
Silk face fabric and its weaving process.Natural fiber cotton and wool fiber carry out blended, main good suction, the moisture releasing for utilizing wool fiber
Property, good hand feeling, warmth retention property are good, comfortable and easy to wear, improve pure cotton it is elastic bad the defects of；Also there is the good affine spy of skin
Property, cladding polyester filament is carried out after blended again, polyester filament has the characteristics that high intensity, crease resistance are good, and the fusion of three is accomplished
Have complementary advantages.
A kind of wool fiber of present invention cladding polyester filament fabric blended with cotton fiber and its weaving process technical solution
For a kind of wool fiber and the blended cladding polyester filament fabric of cotton fiber, the fabric are mixed by wool fiber and pure cotton fiber
Polyester filament is coated after spinning again, braiding forms.The blended wrap yarn is cotton/wool 45s+T20D (cotton/wool/terylenes 65/
17/18), in yarn fiber 65% cotton fiber of content and 17% wool, T20D is a kind of polyester filament, in yarn fibers fiber
Content 18%.
Fabric is formed by warp thread and weft yarns, and the warp thread is：Cotton/wool 45s+T20D, the weft yarn are：
Cotton/40 yards of wool 45s+T20D, Cheng Buhou length, 120 inches of breadth, shrinkage：Warp thread 7.0%, weft yarn 3.2%, warp count：
140 pieces/inch, 95 pieces/inch of weft count, warp-wise strength：360-420N, broadwise strength：300-380N, yarn-using amount：Warp thread
0.2168kg/y, weft yarn 0.1437kg/y, cotton junction impurity：8/2, every square metre without slurry dry weight 129g/m2。
A kind of wool fiber and the blended cladding polyester filament fabric weaving process of cotton fiber, comprise the following steps that：
(1) warping process：
Warp thread cotton/wool 45s+T20D to be drawn from doff bobbin respectively, one width of composition has the yarn sheet of uniform tension,
In parallel to each other tightly around on warp beam；
(2) size mixing process；
(3) sizing operation：
The slurries modulated are injected separately into sizing groove with stock pump is led, by warp thread by the slurries in sizing groove, during sizing
Using the process program of " highly concentrated, low viscous, to permeate, protect coated, high pressure, high speed " again；
(4) denting process：
Warp thread is sequentially passed through into menopause tablet, heald and reed by the method for fabric knitting technological requirement defined.
(5) weaving process：By opening, wefting insertion, beat up, batch cooperation with feeding system of warp, make through weft yarn according to design
Requirement interweave with forming fabric；
(6) arranging process：Test, measure to fabric on cloth inspecting machine, by manually being repaired to fabric defect.
In step (1), in the warping process, warp yarn count cotton/wool 45s+T20D (cotton/wool/terylenes 65/17/
18), bobbin number 700, per spindle nose part 700, through the number of axle 12,300 meters of warped length, warping speed 650r/min.
Step (2) is sized mixing process, is specially：0.5m is added in mixing cirtern3Water, microwave synthetic slurry DF-AG：
87.5kg, PVAC polyvinylalcohol 1799：20kg, Kuraray PVA205Mb：15kg, puts into mixing cirtern, then adds water to 0.8m3,
Steam is passed through, the temperature in mixing cirtern is progressivelyed reach more than 96 DEG C, pressure about 1MPa, pH value 7, boiling 45 minutes or so is simultaneously high
Speed stirring to slurries reach complete gelatinization state；Simmer 30 minutes；
In step (3), total quantity of warps 8400 × 2 (two beams of a loom laterally side by side), Cut Mark Length 39m, slurry groove temperature >=92
DEG C, stock tank viscosity 7-9 seconds, squeezing pressure 22KN, speed 60-65m/min, pressure：Cylinder side 22KN, warp beam side 12KN, temperature 92
DEG C, sizing rate of yarn reaches 14~16%, and regain 6-7.5%, side disk width 1695mm, boils vexed time 90min.(regain
Refer to the ratio of moisture and cotton yarn weight being reserved in after slashing drying in yarn, with percentage)
Note：Stock tank viscosity refers to for 7-9 seconds：At 92 DEG C, the slurries of 100ml flow through (funnel the time required to funneling viscosimeter
Water number is 4.1 seconds to formula viscosimeter at normal temperatures).
In step (4), porter is made in Great Britain：90.3 tooth/2 inch, reed length：3810mm, heald frame number of pages：5 × 1, reed width 124.03
Inch, using straight arrangement, its method of gaiting is：A1, A2, A3, A4, A5, body reed enter number and enter that (three yarns are through a reed for 3
In dent), menopause tablet Drafting Method wears A1, A2, A3, A4, A5, A6 to be suitable.(which page heald frame digitized representation warp thread is through on, A
Represent warp thread)
In step (5), using ZAX-N-360 type looms, 290 degree of opening time, 90 scale of back beam height is (on back rest stand-off
The numerical value of plane on plan range wallboard), back rest front and back position is 3 scales (having marking on stand-off), warp stop frame 0 scale of height,
Warp stop frame is 300mm apart from the distance of last page heald frame, 120 inches of split on machine, speed 450r/min；Weft yarn number cotton/
Wool 45s+T20D, 95 pieces/inch of weft count, heald frame number of pages 5 × 1.
Beneficial effects of the present invention are：The fabric of the present invention is by natural fiber pure cotton and fleece fibre blended spinning composite covered yarn
Technology, using the moisture absorption of wool fiber, ventilative, elastic good, warmth retention property, the high intensity of polyester filament, the characteristics of crease resistance is good, changes
The defects of being apt to pure cotton crease resistance and bad elasticity, while there is good moisture absorbing, skin-friendly, human body can be fully absorbed
Sweat, the shortcoming of cotton fiber is compensate for after reducing bacteria breed, with cotton blend, comfortable and easy to wear, and fabric is soft, the glutinous cunning of feel
Plentiful, well-pressed, quality is frivolous, it is also very outstanding that adverse reaction wrinkle resistance will not occur with human contact.
Embodiment：
For a better understanding of the present invention, below with instantiation come the technical solution that the present invention will be described in detail, but this
Invention is not limited thereto.
Embodiment 1
A kind of wool fiber and the blended cladding polyester filament fabric weaving process of cotton fiber, fabric is by warp thread and weft yarns
Form, warp thread is：Cotton/wool 45s+T20D (cotton/wool/terylene 65/17/18), weft yarn is：Cotton/wool 45s+T20D (cotton/
Wool/terylene 65/17/18), for yarn quality：Average strength 149CN, ultimate strength CV%7.76%, extension at break 4.8%, stretches
40 yards of long CV%8.5%, Cheng Buhou length, 120 inches of breadth, shrinkage：Warp thread 7.0%, weft yarn 3.2%, warp count：140
Piece/inch, 95 pieces/inch of weft count, warp count：140 pieces/inch, 95 pieces/inch of weft count, warp-wise strength：360-
420N, broadwise strength：300-380N, yarn-using amount：0.2168kg/y, weft yarn 0.1437kg/y, cotton junction impurity：8/2.
A kind of wool fiber and the weaving process of the blended cladding polyester filament fabric of cotton fiber, comprise the following steps that：
(1) warping process：
Warp thread cotton/wool 45s+T20D (cotton/wool/terylene 65/17/18) is drawn from doff bobbin respectively, is formed
One width has the yarn sheet of uniform tension, in parallel to each other tightly around on warp beam, warp yarn count cotton/wool 45s+T20D (cotton/
Wool/terylene 65/17/18), bobbin number 700, per spindle nose part 700, through the number of axle 12,300 meters of warped length, warping speed
650r/min, tension rail distance 4mm, tension rail time delay 3.2s, tension piece time delay 3.2s (s represents the second).
(2) size mixing process：
0.5m is added in mixing cirtern3Water, microwave synthetic slurry DF-AG：87.5kg, PVAC polyvinylalcohol 1799：
20kg, Kuraray PVA205Mb：15kg, puts into mixing cirtern, then adds water to 0.8m3, steam is passed through, makes the temperature in mixing cirtern
Degree progressivelyes reach more than 96 DEG C, pressure about 1MPa, and pH value 7, simultaneously high-speed stirred to slurries reach complete paste for boiling 45 minutes or so
Change state, simmers 30 minutes；
(3) sizing operation：
The slurries modulated are injected separately into sizing groove with stock pump is led, by warp thread by the slurries in sizing groove, will be modulated
Good slurries are injected separately into sizing groove with leading stock pump, by warp thread by the slurries in sizing groove, during sizing using " it is highly concentrated, low viscous,
Permeate again, protect coated, high pressure, high speed " process program, squeezing pressure 22KN, speed 60-65m/min, sizing rate of yarn reaches 14
~16%, regain 6.0~7.5%；
In sizing operation, total quantity of warps 8400 × 2 (two beams of a loom laterally side by side), Cut Mark Length 39m, slurry groove temperature >=92
DEG C, stock tank viscosity 7-9 seconds, squeezing pressure 22KN, speed 65m/min, pressure：Cylinder side 22KN, warp beam side 12KN, 92 DEG C of temperature,
Regain 6-7.5%, side disk width 1525mm × 2, boil vexed time 90min；Quality index is shown in Table 1.
Table 1
(4) denting process：
Warp thread is sequentially passed through into menopause tablet, heald and reed, porter English by the method for fabric knitting technological requirement defined
System：90.3, reed length：3810mm, heald frame number of pages：5 × 1,124.01 inches of reed width, using straight arrangement；Its method of gaiting is：A1、A2、
A3, A4, A5, body reed enter number and enter for 3, and menopause tablet Drafting Method wears A1, A2, A3, A4, A5, A6 to be suitable.
(which page heald frame digitized representation warp thread is through on, and A represents warp thread)
(5) weaving process：Using ZAX-N-360 type looms, 290 degree of opening time, back beam height 90 scale (back rest stand-off
The numerical value of plane on upper plan range wallboard), back rest front and back position is 3 scales (having marking on stand-off), warp stop frame 0 quarter of height
Degree, warp stop frame are 300mm apart from the distance of last page heald frame, 120 inches of split on machine, speed 450r/min；By opening,
Wefting insertion, beat up, batch cooperation with feeding system of warp, makes to interweave with forming fabric according to the requirement of design through weft yarn；
Fabric, warp thread：Cotton/wool 45s+T20D (cotton/wool/terylene 65/17/18), weft yarn：Cotton/wool 45s+T20D
(cotton/wool/terylene 65/17/18)
(6) arranging process：Test, measure to fabric on cloth inspecting machine, by manually being repaired to fabric defect, under final
120 ± 0.5 inches of machine split, physical index is shown in Table 2.Warp-wise strength：360-420N, broadwise strength：300-380N.
Table 2
The fabric overall quality being made into is preferable, and fabric good hand touch is well-pressed, and the frivolous water imbibition good permeability of quality connects with human body
Touch that adverse reaction wrinkle resistance will not occur is also very outstanding.
Claims (9)
1. a kind of wool fiber and the blended cladding polyester filament fabric of cotton fiber, it is characterised in that the fabric is fine by wool
Polyester filament is coated after peacekeeping pure cotton fiber is blended again, braiding forms.
2. a kind of wool fiber according to claim 1 and the blended cladding polyester filament fabric of cotton fiber, it is characterised in that
The blended wrap yarn is cotton/wool 45s+T20D, and 65% cotton fiber of content of fiber and 17% wool, T20D are one in yarn
Kind polyester filament, in yarn fibers fiber content 18%.
3. a kind of wool fiber according to claim 1 and the blended cladding polyester filament fabric of cotton fiber, it is characterised in that
Fabric is formed by warp thread and weft yarns, and the warp thread is：Cotton/wool 45s+T20D, the weft yarn are：Cotton/wool 45s
40 yards of+T20D, Cheng Buhou length, 120 inches of breadth, shrinkage：Warp thread 7.0%, weft yarn 3.2%, warp count：140/English
It is very little, 95 pieces/inch of weft count, warp-wise strength：360-420N, broadwise strength：300-380N, yarn-using amount：Warp thread 0.2168kg/
Y, weft yarn 0.1437kg/y, cotton junction impurity：8/2, every square metre without slurry dry weight 129g/m2。
4. a kind of wool fiber and the blended cladding polyester filament fabric weaving process of cotton fiber, it is characterised in that including following work
Skill step：
(1) warping process：
Warp thread cotton/wool 45s+T20D is drawn from doff bobbin respectively, one width of composition has the yarn sheet of uniform tension, mutually
Abreast tightly around on warp beam；
(2) size mixing process；
(3) sizing operation：
The slurries modulated are injected separately into sizing groove with stock pump is led, by warp thread by the slurries in sizing groove, when sizing uses
The process program of " highly concentrated, low viscous, to permeate again, protect coated, high pressure, high speed "；
(4) denting process：
Warp thread is sequentially passed through into menopause tablet, heald and reed by the method for fabric knitting technological requirement defined.
(5) weaving process：By opening, wefting insertion, beat up, batch cooperation with feeding system of warp, make through weft yarn according to design will
Intertexture is asked to form fabric；
(6) arranging process：Test, measure to fabric on cloth inspecting machine, by manually being repaired to fabric defect.
5. weaving process according to claim 4, it is characterised in that in step (1), in the warping process, through yarn count
Number cotton/wool 45s+T20D, bobbin number 700, per spindle nose part 700, through the number of axle 12,300 meters of warped length, warping speed
650r/min。
6. weaving process according to claim 4, it is characterised in that step (2) is sized mixing process, is specially：In mixing cirtern
Interior addition 0.5m3Water, microwave synthetic slurry DF-AG：87.5kg, PVAC polyvinylalcohol 1799：20kg, Kuraray PVA205Mb：
15kg, puts into mixing cirtern, then adds water to 0.8m3, steam is passed through, the temperature in mixing cirtern is progressivelyed reach more than 96 DEG C,
Pressure about 1MPa, pH value 7, boiling 45 minutes or so and high-speed stirred to slurries reach complete gelatinization state；Simmer 30 minutes i.e.
Can.
7. weaving process according to claim 4, it is characterised in that in step (3), total quantity of warps 8400 × 2, ink length
Spend 39m, slurry groove temperature >=92 DEG C, stock tank viscosity 7-9 seconds, squeezing pressure 22KN, speed 60-65m/min, pressure：Cylinder side 22KN,
Warp beam side 12KN, 92 DEG C of temperature, sizing rate of yarn reach 14~16%, and regain 6-7.5%, side disk width 1695mm, is boiled vexed
Time 90min.
8. weaving process according to claim 4, it is characterised in that in step (4), porter is made in Great Britain：90.3 tooth/2 inch,
Reed is grown：3810mm, heald frame number of pages：5 × 1,124.03 inches of reed width, using straight arrangement, its method of gaiting is：A1、A2、A3、A4、
A5, body reed enter number and enter for 3, and menopause tablet Drafting Method wears A1, A2, A3, A4, A5, A6 to be suitable.
9. weaving process according to claim 4, it is characterised in that in step (5), using ZAX-N-360 type looms, open
290 degree of time of mouth, 90 scale of back beam height, back rest front and back position are 3 scales, and warp stop frame 0 scale of height, warp stop frame distance is finally
The distance of one page heald frame is 300mm, 120 inches of split on machine, speed 450r/min；Weft yarn number cotton/wool 45s+T20D, latitude
95 pieces/inch of yarn density, heald frame number of pages 5 × 1.