CN106567175A - Ice-cold polyester functional fabric and production method thereof - Google Patents
Ice-cold polyester functional fabric and production method thereof Download PDFInfo
- Publication number
- CN106567175A CN106567175A CN201610955792.7A CN201610955792A CN106567175A CN 106567175 A CN106567175 A CN 106567175A CN 201610955792 A CN201610955792 A CN 201610955792A CN 106567175 A CN106567175 A CN 106567175A
- Authority
- CN
- China
- Prior art keywords
- ice
- cold
- yarn
- functional fabric
- production method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of textile production and specifically relates to ice-cold polyester functional fabric and a production method thereof. The fabric is satin fabric which is formed by warp yarn and weft yarn, wherein the wrap yarn is blended yarn formed by ice-cold polyester fiber and tencel fiber and the weft yarn is doubling yarn formed by doubled bamboo fiber. The production method comprises following steps: 1) beam-warping process; 2) sizing process; 3) denting; 4) weaving process. The yarn strength is increased by adopting blended yarn; the yarn feather is reduced so as to facilitate later sizing and weaving; the blended yarn is processed with sizing agent, which can effectively reduce the shrinkage of ice-cold polyester fiber and is convenient for weaving; doubled bamboo fiber is used as weft yarn; the cross sectional area of the weft yarn is doubled so that the weft direction strength is increased so as to facilitate the later high speed weaving; the production method is simple and efficient. The ice-cold polyester functional fabric has smooth hand feel, high strength and good anti-static-electricity performance and color fastness performance; the fabric is quick in cooling and heat dissipating.
Description
Technical field
The invention belongs to textile production technical field, and in particular to a kind of ice-cold terylene functional fabric and its producer
Method.
Background technology
With expanding economy, textile application field constantly expands, and especially the utilization on technical textile is outstanding
For protrusion, how to give textile more features, while the productive life for giving people brings more convenient, improve product
Core competitiveness, have important realistic meaning.A kind of ice-cold terylene functional fabric during drawn work because add
Ore deposit element class thin layer mica, so lower than cotton or other fabric lining temperature about 1～2 degree, can quick moisture absorbing and sweat releasing, Er Qietian
So nontoxic effect forever effectively, exactly needed for summer, is increasingly favored by people.But its weak point is that shrinkage is big, knits
Also big, technological design is complicated to make difficulty.Because its effect is good, demand is big, if above-mentioned deficiency can be overcome to obtain significant Jing
Ji benefit, therefore terylene functional fabric and its production method are current research emphasis.
The content of the invention
To solve the deficiencies in the prior art, the invention provides a kind of ice-cold terylene functional fabric and its production method.
The present invention solve the technical scheme that adopts of the deficiencies in the prior art for：A kind of ice-cold terylene functional fabric, it is served as reasons
The satin fabric that warp thread and weft yarn are constituted, wherein：Warp thread is the mixed yarn of ice-cold polyster fibre and tencel fiber, and weft yarn is nandina
The doubling of fiber × 2.
Specifically, warp thread is ice-cold polyster fibre and tencel fiber according to 45-55：What the blending rate of 45-55 was obtained
Blended Compact Yarn.Compact spinning technique is adopted during blending, yarn strength can be improved, reduce Yarn filoplume, be easy to rear operation sizing
Weaving.
Preferably, the blending rate of ice-cold polyster fibre and tencel fiber is 50 in the warp thread:50.
The weft yarn is the doubling of day bamboo fibre × 2, and doubling does not have the twist, therefore it is soft to remain day bamboo fibre fabric
The characteristic of smooth and velvet sense.And, so broadwise strength increases, have because weft cross-sectional product doubles in the weaving of rear operation
Weave beneficial to high speed.
Specifically, the mixed yarn in the warp thread is respectively 9.8～14.8tex with the number of the weft yarn.
Specifically, the Jing of ice-cold polyester fabric it is close be 785～790/10cm, filling density be 375～380/10cm, fabric width
For 269～270cm.
Present invention also offers the production method of above-mentioned ice-cold terylene functional fabric, comprises the following steps：
1) warping process：Warping is carried out to the mixed yarn of ice-cold polyster fibre and tencel fiber, warping speed is controlled 440
～460 ms/min, tension pulley average weight be 3.2～3.6g, using upper, middle and lower, it is front in after carry out arcuate segments；
2) sizing operation：Carrying out sizing to ice-cold polyster fibre and silk fiber blended yarn, sizing speed is 40～45 meters/
min；
Specifically, step 2) used in slurry including following weight portion each raw material：45.0～55.0 parts of phosphate ester
Starch, 14.5～15.5 parts of liquid propene, 20.0～30.0 parts of composite starch, 35.0～40.0 parts of rubber powder, 2.5～
4.5 parts of antistatic additive, 1.0～1.5 parts of bleeding agents, the slurry solid content is 11.4 ± 1%.Phosphate ester starch is from existing skill
Art, can be obtained by way of purchase, the JF-962 series of products of company's production.Liquid propene can pass through from prior art
The mode of purchase is obtained, for example：The DH-930 series of products of Wuhan Dong Mei companies production.Smooth agent can lead to from prior art
The mode for crossing purchase is obtained, for example：The serial DH-68 products of Wuhan Dong Mei companies production.The composite starch is commercially available prod,
For example：The TH-100 series of products that Suzhou Tian Hua enterprise developments Co., Ltd provides.
Preferably, step 2) used in slurry including following weight portion each raw material：50.0 parts of phosphate ester starch, 15
Part liquid propene, 25 parts of TH-100,37.5 parts of rubber powder, 4 parts of antistatic additive, 1 part of bleeding agent, slurry solid content is
11.4 ± 1%.
Preferably, using single stock tank sizing.
3) denting
Requirement according to looming draft design sequentially passes through menopause tablet, heald, reed, when passing, in strict accordance with suitable work is worn
Skill is penetrated.Denting passes operation, is last procedure in warp end preparing engineering.Passing for task is according to fabric
Requiring that the warp thread on beam of a loom is passed through according to certain rules menopause tablet, heald and reed, shed open is formed during to weave, introduce weft yarn
Required fabric is made into, can stop in time so in warp end break will not cause float.
4) weaving process
Warp thread (ice-cold polyster fibre and silk fiber blended yarn) and weft yarn (doublings of day bamboo fibre × 2) are interleaved
Obtain fabric.
Specifically, step 4) in：Loom speed is 460r/min, and warp tension is 2200 ± 50N, and heald level time is
310°.Meet when denting and weaving process parameter setting the Jing of ice-cold polyester fabric for producing it is close be 785～790/10cm,
Filling density is 375～380/10cm, fabric width is 269～270cm.
Specifically, step 4) in：Type is ZAX9100-280mm；It is 1 before and after back rest position, is highly 40；Warp stop frame
It is 5 before and after position, is highly 30；Page 1～7 heald frame height be respectively 110mm, 110mm, 110mm, 105mm, 105mm,
113mm、113mm；The big blade a values of page 1～7 heald frame amount of opening be respectively 90mm, 85mm, 80mm, 66mm, 115mm, 90mm,
80mm。
Wherein, ice-cold polyster fibre, tencel fiber, day bamboo fibre are commercially available prod, for example：Upper Hainan moral weaving is limited
Ice-cold polyester filament 75D/72F or 150D/144F of company's production etc..
A kind of production method of ice-cold terylene functional fabric provided by the present invention does a kind of warp thread with ice-cold polyster fibre
Material, using tencel fiber another kind of warp thread material is done, and both obtain mixed yarn according to certain blending rate, can using mixed yarn
Yarn strength is improved, Yarn filoplume is reduced, is easy to rear operation sizing for weaving, while entering to mixed yarn with the slurry of rational allocation
Row is processed, and effectively reduces the shrinkage factor of ice-cold polyster fibre, convenient weaving；Doubling with day bamboo fibre × 2 as weft yarn, because of weft yarn
Cross-sectional area doubles, so broadwise strength increases, is conducive to follow-up high speed to weave, and according to five piece three satin weave design group is flown
Knit, high-quality production can be completed on air-jet loom, generally process is simple, production efficiency is high.Ice provided by the present invention
Cool terylene functional fabric, rapid heat dissipation lower than other fabric lining temperature, soft, good permeability, antistatic good, strength are high,
With preferable snugness of fit.
Specific embodiment
The principle and feature of the present invention are described below, example is served only for explaining the present invention, is not intended to limit
Determine the scope of the present invention.
Embodiment 1
1) warping process
To ice-cold polyster fibre and silk fiber blended yarn, (blending ratio is 50：50) warping is carried out, the control of warping speed exists
440～460 ms/min, tension pulley average weight be 3.2～3.6g, using upper, middle and lower, it is front in after carry out arcuate segments；
2) sizing operation
Sizing is carried out to ice-cold polyster fibre and the silk fiber blended yarns of LF, sizing speed is 40～45 meters/min.
The slurry for using includes each raw material of following weight portion：45.0 parts of phosphate ester starch, 14.5 parts of liquid propene,
20.0 parts of composite starch, 35.0 parts of rubber powder, 2.5 parts of antistatic additive, 1.0 parts of bleeding agents, slurry solid content be 11.4 ±
1%, using single stock tank sizing.
3) denting
Requirement according to looming draft design sequentially passes through menopause tablet, heald, reed, when passing, in strict accordance with two kinds of Jing
The arrangement ratio of yarn (Jing and doup end) is penetrated.
4) weaving process
Warp thread (ice-cold polyster fibre and silk fiber blended yarn) and weft yarn (doublings of day bamboo fibre × 2) are interleaved
Obtain fabric.
Step 4) in：Loom speed is 460r/min, and warp tension is 2200 ± 50N, and heald level time is 310 °；Cloth machine machine
Type is ZAX9100-280mm；It is 1 before and after back rest position, is highly 40；It is 5 before and after menopause rack position, is highly 30；1～
The heald frame heights of page 7 are respectively 110mm, 110mm, 110mm, 105mm, 105mm, 113mm, 113mm；The heald frame amount of opening of page 1～7 is big
Blade a values are respectively 90mm, 85mm, 80mm, 66mm, 115mm, 90mm, 80mm.Meet when denting and weaving process parameter setting
The Jing of the ice-cold polyester fabric produced is close be 785～790/10cm, filling density be 375～380/10cm, fabric width be 269～
270cm。
Embodiment 2
1) warping process
To ice-cold polyster fibre and silk fiber blended yarn, (blending ratio is 45：55) warping is carried out, the control of warping speed exists
440～460 ms/min, tension pulley average weight be 3.2～3.6g, using upper, middle and lower, it is front in after carry out arcuate segments；
2) sizing operation
Sizing is carried out to ice-cold polyster fibre and silk fiber blended yarn, sizing speed is 40～45 meters/min.
Step 2) used in slurry including following weight portion each raw material：50.0 parts of phosphate ester starch, 15 parts of liquid
Body propylene, 25 parts of TH-100,37.5 parts of rubber powder, 4 parts of antistatic additive, 1 part of bleeding agent, slurry solid content be 11.4 ±
1%.
3) denting
Requirement according to looming draft design sequentially passes through menopause tablet, heald, reed, when passing, in strict accordance with two kinds of Jing
The arrangement ratio of yarn is penetrated.
4) weaving process
The ice-cold polyster fibre of warp thread and silk fiber blended yarn are interleaved with weft yarn for the doubling of nandina yarn × 2 and are obtained
Fabric.
Step 4) in：Loom speed is 460r/min, and warp tension is 2200 ± 50N, and heald level time is 310 °.
Step 4) in：Loom speed is 460r/min, and warp tension is 2200 ± 50N, and heald level time is 310 °；Loom machine
Type is ZAX9100-280mm；It is 1 before and after back rest position, is highly 40；It is 5 before and after menopause rack position, is highly 30；1～
The heald frame heights of page 7 are respectively 110mm, 110mm, 110mm, 105mm, 105mm, 113mm, 113mm；The heald frame amount of opening of page 1～7 is big
Blade a values are respectively 90mm, 85mm, 80mm, 66mm, 115mm, 90mm, 80mm.Meet when denting and weaving process parameter setting
The Jing of the ice-cold polyester fabric produced is close be 785～790/10cm, filling density be 375～380/10cm, fabric width be 269～
270cm。
Embodiment 3
1) warping process
To ice-cold polyster fibre and silk fiber blended yarn, (blending ratio is 55：45) warping is carried out, the control of warping speed exists
440～460 ms/min, tension pulley average weight be 3.2～3.6g, using upper, middle and lower, it is front in after carry out arcuate segments；
2) sizing operation
Sizing is carried out to ice-cold polyster fibre and silk fiber blended yarn, sizing speed is 40～45 meters/min.
Step 2) used in slurry including following weight portion each raw material：55.0 parts of phosphate ester starch, 15.5 parts
Liquid propene, 30.0 parts of composite starch, 40.0 parts of rubber powder, 4.5 parts of antistatic additive, 1.5 parts of bleeding agents, the slurry is containing solid
Measure as 11.4 ± 1%.
3) denting
Requirement according to looming draft design sequentially passes through menopause tablet, heald, reed, when passing, in strict accordance with two kinds of Jing
The arrangement ratio of yarn is penetrated.
4) weaving process
The ice-cold polyster fibre of warp thread and silk fiber blended yarn are interleaved with weft yarn for the doubling of nandina yarn × 2 and are obtained
Fabric.
Step 4) in：Loom speed is 460r/min, and warp tension is 2200 ± 50N, and heald level time is 310 °.
Step 4) in：Loom speed is 460r/min, and warp tension is 2200 ± 50N, and heald level time is 310 °；Loom machine
Type is ZAX9100-280mm；It is 1 before and after back rest position, is highly 40；It is 5 before and after menopause rack position, is highly 30；1～
The heald frame heights of page 7 are respectively 110mm, 110mm, 110mm, 105mm, 105mm, 113mm, 113mm；The heald frame amount of opening of page 1～7 is big
Blade a values are respectively 90mm, 85mm, 80mm, 66mm, 115mm, 90mm, 80mm.Meet when denting and weaving process parameter setting
The Jing of the ice-cold polyester fabric produced is close be 785～790/10cm, filling density be 375～380/10cm, fabric width be 269～
270cm。
The ice-cold terylene functional fabric that embodiment 1 to 3 is obtained, rapid heat dissipation lower than other fabric lining temperature, feel are soft
Soft, good permeability, antistatic good, strength are high, with preferable snugness of fit.
The better embodiment of the present invention is the foregoing is only, not to limit the present invention, all spirit in the present invention
Within principle, any modification, equivalent substitution and improvements made etc. should be included within the scope of the present invention.
Claims (10)
1. a kind of ice-cold terylene functional fabric, it is characterised in that the fabric is the satin fabric being made up of warp thread and weft yarn, its
In：Warp thread is the mixed yarn of ice-cold polyster fibre and tencel fiber, and weft yarn is the doubling of day bamboo fibre × 2.
2. a kind of ice-cold terylene functional fabric according to claim 1, it is characterised in that the warp thread is that ice-cold terylene is fine
Peacekeeping tencel fiber is according to 45～55:The Blended Compact Yarn that 45～55 blending rate is obtained.
3. a kind of ice-cold terylene functional fabric according to claim 1, it is characterised in that ice-cold terylene is fine in the warp thread
The blending rate of peacekeeping tencel fiber is 50:50.
4. a kind of ice-cold terylene functional fabric according to claim 1, it is characterised in that mixed yarn and institute in the warp thread
The number for stating weft yarn is respectively 9.8～14.8tex.
5. a kind of ice-cold terylene functional fabric according to any one of Claims 1-4, it is characterised in that it is 785 that Jing is close～
790/10cm, filling density be 375～380/10cm, fabric width be 269～270cm.
6. a kind of production method of the ice-cold terylene functional fabric as described in any one of claim 1 to 5, it is characterised in that bag
Include following steps：
1) warping process：Warping is carried out to ice-cold polyster fibre and silk fiber blended yarn, warping speed is controlled 440～460
M/min, tension pulley weight be 3.2～3.6g, using upper, middle and lower, it is front in after carry out arcuate segments；
2) sizing operation：Sizing is carried out to ice-cold polyster fibre and silk fiber blended yarn, sizing speed is 40～45 meters/min；
3) denting：Technique is worn using suitable；
4) weaving process：Warp thread and weft yarn are interleaved and obtain fabric.
7. a kind of production method of ice-cold terylene functional fabric according to claim 6, it is characterised in that step 2) in make
Slurry includes each raw material of following weight portion：45.0～55.0 parts of phosphate ester starch, 14.5～15.5 parts of liquid third
Alkene, 20.0～30.0 parts of composite starch, 35.0～40.0 parts of rubber powder, 2.5～4.5 parts of antistatic additive, 1.0～1.5 parts ooze
Agent thoroughly.
8. a kind of production method of ice-cold terylene functional fabric according to claim 6, it is characterised in that step 2) in adopt
With single stock tank sizing.
9. a kind of production method of ice-cold terylene functional fabric according to claim 6, it is characterised in that step 4) in：
Loom speed is 460r/min, and warp tension is 2200 ± 50N, and heald level time is 310 °.
10. a kind of production method of ice-cold terylene functional fabric according to claim 6, it is characterised in that step 4) in：
Loom type is ZAX9100-280mm；It is 1 before and after back rest position, is highly 40；It is 5 before and after menopause rack position, is highly
30；The heald frame height of page 1～7 is respectively 110mm, 110mm, 110mm, 105mm, 105mm, 113mm, 113mm；The heald frame of page 1～7 is opened
The big blade a values of mouth amount are respectively 90mm, 85mm, 80mm, 66mm, 115mm, 90mm, 80mm.