CN101994190A - Method for making ultraviolet screening bamboo fiber fabric - Google Patents

Method for making ultraviolet screening bamboo fiber fabric Download PDF

Info

Publication number
CN101994190A
CN101994190A CN2009100180713A CN200910018071A CN101994190A CN 101994190 A CN101994190 A CN 101994190A CN 2009100180713 A CN2009100180713 A CN 2009100180713A CN 200910018071 A CN200910018071 A CN 200910018071A CN 101994190 A CN101994190 A CN 101994190A
Authority
CN
China
Prior art keywords
bamboo fibre
preparation
warp
ultraviolet
resistant fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2009100180713A
Other languages
Chinese (zh)
Inventor
苗耐刚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2009100180713A priority Critical patent/CN101994190A/en
Publication of CN101994190A publication Critical patent/CN101994190A/en
Pending legal-status Critical Current

Abstract

The invention relates to a method for making ultraviolet screening bamboo fiber fabric, which is characterized in that warps and wefts are interweaved to make the fabric, wherein the warps and the wefts are both bamboo fiber yarns, the warp yarn has the specification of 21-60*2, the weft yarn has the specification of 21-60*1, the warp density is 66-76/inch, the weft density is 64-90/inch, and the breadth of tmaterial is 180-250cm. Tests prove that the ultraviolet screening bamboo fiber fabric reaches the standard of ultraviolet screening products.

Description

A kind of preparation method of bamboo fibre ultraviolet-resistant fabric
Technical field
The invention belongs to field of textiles, provide a kind of preparation method of bamboo fibre ultraviolet-resistant fabric.
Background technology
Bamboo fibre yarn raw material is selected bamboo fibre for use, belong to green product, the knit fabric and the clothes of the yarn production made from this raw material, have the individual style that obviously is different from cotton, die model cellulose fibre: ABRASION RESISTANCE, high-hygroscopicity, quick-drying, highly-breathable, drapability are all good, feel satiny plentiful, as the silk softness, anti-mould and anti-moth is antibiotic, wear cool and comfortable, the effect of beauty and skin care is arranged, dyeability is good, gloss is beautiful, and the better anti-bacterial effect and the feature of environmental protection are arranged, comply with the modern and pursue healthy comfortable trend.The present invention just provides a kind of preparation method of bamboo fibre ultraviolet-resistant fabric.
Summary of the invention
The present invention is achieved in that a kind of preparation method of bamboo fibre ultraviolet-resistant fabric, it is characterized in that: this lining is to be interweaved by warp and parallel to form, and warp and parallel all adopt the bamboo fibre yarn.Warp thread props up * 2 lines for bamboo fibre 21--60, and weft yarn is that 21--60 props up * 1 line, through close be the 66--76/ inch, filling density is the 64--90/ inch, fabric width is the FIGURED CLOTH of 180--250cm.
Its technology of the production of this lining is:
1, winding process: winder speed 380--450m/min, single yarn tension be controlled at single thread force 8% in.
2, whole footpath technology: speed of a motor vehicle 550--650m/min, pretension bar playback delay time is 22--27min, pretension bar actuation time is 22--27min; The yarn clip board open hour are 42--48min.
3, slashing technique: select two guarantor property slurry JSC-7 grafting joint copolymerization starch for use, slurry viscosity is at 7.5-8.5S, and the rate of sizing is at 8%-9%, regain 10%-12%; Slurry groove temperature is controlled at about 80--90 ℃, and drying tube temperature is 100-110 ℃.
4, weaving process: relative humidity should not be greater than 70%, and warp tension is as far as possible little, the path position line: adopt low back beam process, back beam height is 90mm, and stopping footpath frame height is 30mm, and front and back position is 70mm.
Adopt the bamboo fibre fabric of above explained hereafter, through national cotton textile quality supervision and test center, test center of China Textile Academy detects proof: bamboo fibre fabric can be described as " antiultraviolet product ".Detect through weapon industry nonmetallic materials physics and chemistry inspection center, the bamboo fibre fabric of our exploitation can be used as " BDU " lining.As seen, this bamboo fibre fabric has well to the ultraviolet screener effect, thereby guaranteed that human body is not subjected to ultraviolet injury, especially atmospheric expansion of the ozone hole, the ultraviolet ray of passing through is more and more, human body is damaged more serious, the particularity of bamboo fibre fabric is for the health that guarantees human body, and is significant.
The specific embodiment
The present invention will be described in detail below in conjunction with example, but be not limited to this embodiment.
Kind 1: warp thread is bamboo fibre 60 * 2 lines, and weft yarn is 60 pure bamboo fiber garns, through close be 70/ inch, filling density is 80/ inch, fabric width is the FIGURED CLOTH of 250cm.
Its technology of the production of this lining is:
1, winding process: winder speed 380--450m/min, single yarn tension be controlled at single thread force 8% in.
2, whole footpath technology: speed of a motor vehicle 550--650m/min, pretension bar playback delay time is 22--27min, pretension bar actuation time is 22--27min; The yarn clip board open hour are 42--48min.
3, slashing technique: select two guarantor property slurry JSC-7 grafting joint copolymerization starch for use, slurry viscosity is at 7.5-8.5S, and the rate of sizing is at 8%-9%, regain 10%-12%; Slurry groove temperature is controlled at about 80--90 ℃, and drying tube temperature is 100-110 ℃.
4, weaving process: relative humidity should not be greater than 70%, and warp tension is as far as possible little, the path position line: adopt low back beam process, back beam height is 90mm, and stopping footpath frame height is 30mm, and front and back position is 70mm.

Claims (5)

1. the preparation method of a bamboo fibre ultraviolet-resistant fabric, it is characterized in that: this lining is to be interweaved by warp and parallel to form, warp and parallel all adopt the bamboo fibre yarn, warp thread props up * 2 lines for bamboo fibre 21--60, weft yarn is that 21--60 props up * 1 line, through close be the 66--76/ inch, filling density is the 64--90/ inch, fabric width is the FIGURED CLOTH of 180--250cm.
2. the preparation method of a kind of bamboo fibre ultraviolet-resistant fabric according to claim 1 is characterized in that winding process: winder speed 380--450m/min, single yarn tension be controlled at single thread force 8% in.
3. the preparation method of a kind of bamboo fibre ultraviolet-resistant fabric according to claim 1 is characterized in that whole footpath technology: speed of a motor vehicle 550--650m/min, and pretension bar playback delay time is 22--27min, and pretension bar actuation time is 22--27min; The yarn clip board open hour are 42--48min.
4. the preparation method of a kind of bamboo fibre ultraviolet-resistant fabric according to claim 1, it is characterized in that slashing technique: select two guarantor property slurry JSC-7 grafting joint copolymerization starch for use, slurry viscosity is at 7.5-8.5S, and the rate of sizing is at 8%-9%, regain 10%-12%; Slurry groove temperature is controlled at about 80--90 ℃, and drying tube temperature is 100-110 ℃.
5. the preparation method of a kind of bamboo fibre ultraviolet-resistant fabric according to claim 1, it is characterized in that the weaving process configuration: relative humidity should not be greater than 70%, warp tension is as far as possible little, path position line: adopt low back beam process, back beam height is 90mm, stopping footpath frame height is 30mm, and front and back position is 70mm.
CN2009100180713A 2009-08-25 2009-08-25 Method for making ultraviolet screening bamboo fiber fabric Pending CN101994190A (en)