CN107892554A - A kind of preparation method of spun gold white glaze pottery handicraft - Google Patents
A kind of preparation method of spun gold white glaze pottery handicraft Download PDFInfo
- Publication number
- CN107892554A CN107892554A CN201711130574.0A CN201711130574A CN107892554A CN 107892554 A CN107892554 A CN 107892554A CN 201711130574 A CN201711130574 A CN 201711130574A CN 107892554 A CN107892554 A CN 107892554A
- Authority
- CN
- China
- Prior art keywords
- parts
- hours
- slurry
- kiln
- biscuit
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of preparation method of spun gold white glaze pottery handicraft, comprise the following steps：Step 1: obtained slurry is through filter mud and after mixing mud, it is standby；Step 2: after slurry injection base substrate in-mold molding or hand pulled blank forming, dry, repair, the biscuit burnt till takes out standby；Step 3: raw material ground-coat enamel material is taken according to parts by weight, it is standby；Step 4: raw material glaze material is taken according to parts by weight, it is standby；Step 5: carrying out applying ground-coat enamel and cover-coat enamel in biscuit outer surface, after the completion of pouring glaze, base substrate is repaired；Step 6: the biscuit of step 5 is put into kiln, burnt using High Temperature Gas.Pottery handicraft produced by the present invention has white background color, and irregular spun gold is distributed on background color, and the length of spun gold and respectively density change according to ceramic type and glazing thickness, has unique artistic effect.
Description
Technical field
The present invention relates to pottery technical field of artware manufacture, and in particular to a kind of making of spun gold white glaze pottery handicraft
Method.
Background technology
Rarity-pottery of state, starts from Tang, is contained in Song, because originating in an ancient unit of weight state of Gu（Modern Yuzhou）And gain the name.Pottery is with typical case
Two liquid phase separation glazes based on, have opal effect a kind of porcelain product.Northern Song Dynasty mid-term, pottery product take off among celadon system
Grain husk and go out, gradually form oneself unique technique, progressively ripe in kiln around centered on the god Hou of Yuzhou, late period in the Northern Song Dynasty
Frightened generation glamour and powerful vitality are burst out as new porcelain kind, achieves significant achievements.Northern Song Dynasty pottery based on small-sized implements,
Tire color is greyish white and tire matter is fine and smooth, and glaze colours is simple and elegant uniform, and nature of glass opalescence sense is strong, based on reddish black, sky blue, bluish white, pale blue.Separately
Outside, in pottery firing start to apply using cupric oxide as photoghraphic coupler, and it is naturally dizzy dissipate, wonderful interest is infinite, there is that " pottery is hung up red festoons, valency
Say in value Liancheng ".During the ancestor of emblem, Eight Diagrams hole is set up hired kiln and burnt paper as sacrificial offerings imperial palace porcelain near Gu Juntai, is referred to as an ancient unit of weight platform kiln afterwards, its
Product is mainly to display device, based on floral organ and living utensil, represents the highest level of pottery technique.In the late Qing Dynasty, with collection
Heat is risen, and pottery has the saying of " there is ten thousand strings of cash in family, be not as a piece of as pottery ", for referring to the product of an ancient unit of weight platform kiln, and historical facts.
The content of the invention
It is an object of the invention to provide a kind of preparation method of spun gold white glaze pottery handicraft, obtained pottery handicraft tool
There is white background color, irregular spun gold is distributed on background color, the length of spun gold and respectively density are according to ceramic type and glazing
Thickness and change, there is unique artistic effect.
The technical solution adopted by the present invention is：A kind of preparation method of spun gold white glaze pottery handicraft, comprises the following steps：
Step 1: take Tang's ditch soil 35~40%, Datong District's soil 30~35%, camwood knag soil 6~10%, white arid soil according to percentage by weight
12~16% and albite 8~12%, above-mentioned raw materials are crushed respectively it is rearmounted enter ball mill, add the water of raw material gross weight 40%,
Start wet-milling 12 hours, the slurry by wet-milling crosses 200 mesh sieves, takes out and stands 24 hours, and obtained slurry through filter mud and is mixed
It is standby after mud；
Step 2: after slurry prepared by step 1 injects base substrate in-mold molding or hand pulled blank forming, molding blank is taken
Go out, dry, repair, firing 3.5-4 hours in 800-900 DEG C of kiln are put into after wiping base with water, truce is cooled to room temperature, burnt till
Biscuit takes out standby；
Step 3: take nepheline 15-20 parts according to parts by weight, burn talcum 20-30 parts, feldspar 10-15 parts, kaolin 6-8 parts, just
Beautiful 2-6 parts, 3 parts of manganese carbonate, actinolite 5-8 parts, above-mentioned raw materials are crushed respectively it is rearmounted enter ball mill, add raw material gross weight
32% water, start wet-milling 15 hours, the slurry by wet-milling crosses 300 mesh sieves, takes out and stands 12 hours, by the water content of slurry
45% is adjusted to, obtains ground-coat enamel material, it is standby；
Step 4: according to parts by weight take plant ash 25-35 parts, kaolin 8-10 parts, Zijin soil 6-10 parts, talcum 10-15 parts,
Actinolite 15-20 parts, corundum 4-6 parts, apatite 6-8 parts, manganese carbonate 1-5 parts, calcite 5-10 parts and di-iron trioxide 1-5
Part, above-mentioned raw materials are crushed respectively it is rearmounted enter ball mill, add the water of raw material gross weight 30%, start wet-milling 16 hours, through overly moist
The slurry of mill crosses 350 mesh sieves, takes out and stands 12 hours, the water content of slurry is adjusted into 46%, obtains glaze material, standby；
Step 5: wiping base is carried out to biscuit made of step 2 with water, with waddy according to the clockwise or inverse time while wiping base
The direction of pin is stirred to ground-coat enamel material made of step 3, during stirring since the center of slurry, and is gradually moved to circumference,
Mixing time is 20 minutes, after the completion of stirring, the biscuit after wiping base is put into ground-coat enamel slurry, poured in biscuit outer surface
Glaze, after the completion of pouring glaze, after body drying, by way of glaze spraying, glaze material made from step 4 is uniformly imposed on base substrate,
Biscuit is obtained after drying；
Step 6: the biscuit of step 5 is put into kiln, burnt using High Temperature Gas, open gas tank valve, starting point timing of fighting is opened
Begin, it is using the time point as starting point that the following time, which calculates, and pressure is adjusted to 0.01MPa, and rear flashboard pulls open 120cm, and wicket is beaten
Open 280cm；2.2 hours are fired, kiln temperature rises to 140 DEG C, and pressure is adjusted to 0.02 MPa；3 hours are fired, kiln temperature rises to 320
℃；6 hours are fired, kiln temperature rises to 560 DEG C；Fire 5.5 hours, kiln temperature rises to 780 DEG C；Programming rate control is at 3 DEG C/minute afterwards
Clock, when kiln temperature is controlled at 900-920 DEG C, with tight flashboard；Fire 6.5 hours afterwards, when kiln temperature rises to 1000 DEG C, pressure is adjusted to
0.03 MPa, start to be incubated；8 hours kiln temperatures are fired afterwards and rise to 1100 DEG C, and into reduction phase, pressure is adjusted to 1.5 MPa；Work as burning
8 hours kiln temperatures of system rise to 1250 DEG C, into strong reduction phase；10 hours kiln temperatures are fired afterwards rises to 1350 DEG C；Kiln temperature control afterwards exists
Between 1250 DEG C -1350 DEG C, weak reduction is carried out, is fired 12 hours, it is rear to stop firing, fire and complete.
Beneficial effect
Pottery handicraft produced by the present invention has white background color, and irregular spun gold, the length of spun gold are distributed on background color
Density changes according to ceramic type and glazing thickness respectively, has unique artistic effect, in the tea set and art of top grade
Have wide practical use in porcelain.
Embodiment
Further technical scheme is illustrated below in conjunction with embodiment.
Embodiment 1
A kind of preparation method of spun gold white glaze pottery handicraft, comprises the following steps：
Step 1: Tang's ditch soil 35%, Datong District's soil 35%, camwood knag soil 10%, white arid soil 12% and sodium is taken to grow according to percentage by weight
Stone 8%, above-mentioned raw materials are crushed respectively it is rearmounted enter ball mill, add the water of raw material gross weight 40%, start wet-milling 12 hours, pass through
The slurry of wet-milling crosses 200 mesh sieves, takes out and stands 24 hours, standby by obtained slurry through filter mud and after mixing mud；
Step 2: after slurry prepared by step 1 injects base substrate in-mold molding or hand pulled blank forming, molding blank is taken
Go out, dry, repair, be put into 800 DEG C of kiln and fire 4 hours after wiping base with water, truce is cooled to room temperature, and the biscuit burnt till takes out
It is standby；
Step 3: take 16 parts of nepheline according to parts by weight, burn 25 parts of talcum, 12 parts of feldspar, 6 parts of kaolin, 4 parts of corundum, carbonic acid
3 parts of manganese, 6 parts of actinolite, above-mentioned raw materials are crushed respectively it is rearmounted enter ball mill, add raw material gross weight 32% water, start shooting wet-milling
15 hours, the slurry by wet-milling crossed 300 mesh sieves, takes out and stands 12 hours, the water content of slurry is adjusted into 45%, obtained on earth
Glaze, it is standby；
Step 4: according to parts by weight take 30 parts of plant ash, 8 parts of kaolin, Zijin soil 8 parts, 12 parts of talcum, 16 parts of actinolite,
2 parts of 5 parts of corundum, 8 parts of apatite, 2 parts of manganese carbonate, 8 parts of calcite and di-iron trioxide, above-mentioned raw materials are crushed respectively rearmounted
Enter ball mill, add the water of raw material gross weight 30%, start wet-milling 16 hours, the slurry by wet-milling crosses 350 mesh sieves, takes out quiet
Put 12 hours, the water content of slurry is adjusted to 46%, obtains glaze material, it is standby；
Step 5: wiping base is carried out to biscuit made of step 2 with water, with waddy according to the clockwise or inverse time while wiping base
The direction of pin is stirred to ground-coat enamel material made of step 3, during stirring since the center of slurry, and is gradually moved to circumference,
Mixing time is 20 minutes, after the completion of stirring, the biscuit after wiping base is put into ground-coat enamel slurry, poured in biscuit outer surface
Glaze, after the completion of pouring glaze, after body drying, by way of glaze spraying, glaze material made from step 4 is uniformly imposed on base substrate,
Biscuit is obtained after drying；
Step 6: the biscuit of step 5 is put into kiln, burnt using High Temperature Gas, open gas tank valve, starting point timing of fighting is opened
Begin, it is using the time point as starting point that the following time, which calculates, and pressure is adjusted to 0.01MPa, and rear flashboard pulls open 120cm, and wicket is beaten
Open 280cm；2.2 hours are fired, kiln temperature rises to 140 DEG C, and pressure is adjusted to 0.02 MPa；3 hours are fired, kiln temperature rises to 320
℃；6 hours are fired, kiln temperature rises to 560 DEG C；Fire 5.5 hours, kiln temperature rises to 780 DEG C；Programming rate control is at 3 DEG C/minute afterwards
Clock, when kiln temperature is controlled at 900-920 DEG C, with tight flashboard；Fire 6.5 hours afterwards, when kiln temperature rises to 1000 DEG C, pressure is adjusted to
0.03 MPa, start to be incubated；8 hours kiln temperatures are fired afterwards and rise to 1100 DEG C, and into reduction phase, pressure is adjusted to 1.5 MPa；Work as burning
8 hours kiln temperatures of system rise to 1250 DEG C, into strong reduction phase；10 hours kiln temperatures are fired afterwards rises to 1350 DEG C；Kiln temperature control afterwards exists
Between 1250 DEG C -1350 DEG C, weak reduction is carried out, is fired 12 hours, it is rear to stop firing, fire and complete.
Embodiment 2：
A kind of preparation method of spun gold white glaze pottery handicraft, comprises the following steps：
Step 1: take Tang's ditch soil 40%, Datong District's soil 30%, camwood knag soil 6%, white arid soil 12% and albite according to percentage by weight
12%, above-mentioned raw materials are crushed respectively it is rearmounted enter ball mill, add the water of raw material gross weight 40%, start wet-milling 12 hours, pass through
The slurry of wet-milling crosses 200 mesh sieves, takes out and stands 24 hours, standby by obtained slurry through filter mud and after mixing mud；
Step 2: after slurry prepared by step 1 injects base substrate in-mold molding or hand pulled blank forming, molding blank is taken
Go out, dry, repair, be put into 900 DEG C of kiln and fire 4 hours after wiping base with water, truce is cooled to room temperature, and the biscuit burnt till takes out
It is standby；
Step 3: take 16 parts of nepheline according to parts by weight, burn 25 parts of talcum, 12 parts of feldspar, 6 parts of kaolin, 4 parts of corundum, carbonic acid
3 parts of manganese, 6 parts of actinolite, above-mentioned raw materials are crushed respectively it is rearmounted enter ball mill, add raw material gross weight 32% water, start shooting wet-milling
15 hours, the slurry by wet-milling crossed 300 mesh sieves, takes out and stands 12 hours, the water content of slurry is adjusted into 45%, obtained on earth
Glaze, it is standby；
Step 4: according to parts by weight take 25 parts of plant ash, 8 parts of kaolin, Zijin soil 6 parts, 10 parts of talcum, 15 parts of actinolite,
5 parts of 6 parts of corundum, 8 parts of apatite, 5 parts of manganese carbonate, 10 parts of calcite and di-iron trioxide, after above-mentioned raw materials are crushed respectively
Ball mill is inserted, adds the water of raw material gross weight 30%, start wet-milling 16 hours, the slurry by wet-milling crosses 350 mesh sieves, takes out
12 hours are stood, the water content of slurry is adjusted to 46%, obtains glaze material, it is standby；
Step 5: wiping base is carried out to biscuit made of step 2 with water, with waddy according to the clockwise or inverse time while wiping base
The direction of pin is stirred to ground-coat enamel material made of step 3, during stirring since the center of slurry, and is gradually moved to circumference,
Mixing time is 20 minutes, after the completion of stirring, the biscuit after wiping base is put into ground-coat enamel slurry, poured in biscuit outer surface
Glaze, after the completion of pouring glaze, after body drying, by way of glaze spraying, glaze material made from step 4 is uniformly imposed on base substrate,
Biscuit is obtained after drying；
Step 6: the biscuit of step 5 is put into kiln, burnt using High Temperature Gas, open gas tank valve, starting point timing of fighting is opened
Begin, it is using the time point as starting point that the following time, which calculates, and pressure is adjusted to 0.01MPa, and rear flashboard pulls open 120cm, and wicket is beaten
Open 280cm；2.2 hours are fired, kiln temperature rises to 140 DEG C, and pressure is adjusted to 0.02 MPa；3 hours are fired, kiln temperature rises to 320
℃；6 hours are fired, kiln temperature rises to 560 DEG C；Fire 5.5 hours, kiln temperature rises to 780 DEG C；Programming rate control is at 3 DEG C/minute afterwards
Clock, when kiln temperature is controlled at 900-920 DEG C, with tight flashboard；Fire 6.5 hours afterwards, when kiln temperature rises to 1000 DEG C, pressure is adjusted to
0.03 MPa, start to be incubated；8 hours kiln temperatures are fired afterwards and rise to 1100 DEG C, and into reduction phase, pressure is adjusted to 1.5 MPa；Work as burning
8 hours kiln temperatures of system rise to 1250 DEG C, into strong reduction phase；10 hours kiln temperatures are fired afterwards rises to 1350 DEG C；Kiln temperature control afterwards exists
Between 1250 DEG C -1350 DEG C, weak reduction is carried out, is fired 12 hours, it is rear to stop firing, fire and complete.
Embodiment 3：
A kind of preparation method of spun gold white glaze pottery handicraft, comprises the following steps：
Step 1: take Tang's ditch soil 36%, Datong District's soil 32%, camwood knag soil 8%, white arid soil 12% and albite according to percentage by weight
12%, above-mentioned raw materials are crushed respectively it is rearmounted enter ball mill, add the water of raw material gross weight 40%, start wet-milling 12 hours, pass through
The slurry of wet-milling crosses 200 mesh sieves, takes out and stands 24 hours, standby by obtained slurry through filter mud and after mixing mud；
Step 2: after slurry prepared by step 1 injects base substrate in-mold molding or hand pulled blank forming, molding blank is taken
Go out, dry, repair, be put into 850 DEG C of kiln and fire 3.5 hours after wiping base with water, truce is cooled to room temperature, and the biscuit burnt till takes
Go out standby；
Step 3: take 120 parts of nepheline according to parts by weight, burn 30 parts of talcum, 15 parts of feldspar, 6 parts of kaolin, 2 parts of corundum, carbonic acid
3 parts of manganese, 5 parts of actinolite, above-mentioned raw materials are crushed respectively it is rearmounted enter ball mill, add raw material gross weight 32% water, start shooting wet-milling
15 hours, the slurry by wet-milling crossed 300 mesh sieves, takes out and stands 12 hours, the water content of slurry is adjusted into 45%, obtained on earth
Glaze, it is standby；
Step 4: take plant ash 35, kaolin 10, Zijin soil 10, talcum 15, actinolite 15, corundum 4, phosphorus according to parts by weight
Lime stone 6, manganese carbonate 1, calcite 5 and di-iron trioxide 1, above-mentioned raw materials are crushed respectively it is rearmounted enter ball mill, add raw material
The water of gross weight 30%, start wet-milling 16 hours, the slurry by wet-milling crosses 350 mesh sieves, takes out and stands 12 hours, by slurry
Water content is adjusted to 46%, obtains glaze material, standby；
Step 5: wiping base is carried out to biscuit made of step 2 with water, with waddy according to the clockwise or inverse time while wiping base
The direction of pin is stirred to ground-coat enamel material made of step 3, during stirring since the center of slurry, and is gradually moved to circumference,
Mixing time is 20 minutes, after the completion of stirring, the biscuit after wiping base is put into ground-coat enamel slurry, poured in biscuit outer surface
Glaze, after the completion of pouring glaze, after body drying, by way of glaze spraying, glaze material made from step 4 is uniformly imposed on base substrate,
Biscuit is obtained after drying；
Step 6: the biscuit of step 5 is put into kiln, burnt using High Temperature Gas, open gas tank valve, starting point timing of fighting is opened
Begin, it is using the time point as starting point that the following time, which calculates, and pressure is adjusted to 0.01MPa, and rear flashboard pulls open 120cm, and wicket is beaten
Open 280cm；2.2 hours are fired, kiln temperature rises to 140 DEG C, and pressure is adjusted to 0.02 MPa；3 hours are fired, kiln temperature rises to 320
℃；6 hours are fired, kiln temperature rises to 560 DEG C；Fire 5.5 hours, kiln temperature rises to 780 DEG C；Programming rate control is at 3 DEG C/minute afterwards
Clock, when kiln temperature is controlled at 900-920 DEG C, with tight flashboard；Fire 6.5 hours afterwards, when kiln temperature rises to 1000 DEG C, pressure is adjusted to
0.03 MPa, start to be incubated；8 hours kiln temperatures are fired afterwards and rise to 1100 DEG C, and into reduction phase, pressure is adjusted to 1.5 MPa；Work as burning
8 hours kiln temperatures of system rise to 1250 DEG C, into strong reduction phase；10 hours kiln temperatures are fired afterwards rises to 1350 DEG C；Kiln temperature control afterwards exists
Between 1250 DEG C -1350 DEG C, weak reduction is carried out, is fired 12 hours, it is rear to stop firing, fire and complete.
The above described is only a preferred embodiment of the present invention, any formal limitation not is made to the present invention, though
So the present invention is disclosed above with preferred embodiment, but is not limited to the present invention, any to be familiar with this professional technology people
Member, without departing from the scope of the present invention, when the technology contents using the disclosure above make out a little change or repair
The equivalent embodiment for equivalent variations is adornd, as long as being the technical spirit according to the present invention without departing from technical solution of the present invention content
Any simple modification, equivalent change and modification made to above example, in the range of still falling within technical solution of the present invention.
Claims (1)
- A kind of 1. preparation method of spun gold white glaze pottery handicraft, it is characterised in that：Comprise the following steps：Step 1: take Tang's ditch soil 35~40%, Datong District's soil 30~35%, camwood knag soil 6~10%, white arid soil according to percentage by weight 12~16% and albite 8~12%, above-mentioned raw materials are crushed respectively it is rearmounted enter ball mill, add the water of raw material gross weight 40%, Start wet-milling 12 hours, the slurry by wet-milling crosses 200 mesh sieves, takes out and stands 24 hours, and obtained slurry through filter mud and is mixed It is standby after mud；Step 2: after slurry prepared by step 1 injects base substrate in-mold molding or hand pulled blank forming, molding blank is taken Go out, dry, repair, firing 3.5-4 hours in 800-900 DEG C of kiln are put into after wiping base with water, truce is cooled to room temperature, burnt till Biscuit takes out standby；Step 3: take nepheline 15-20 parts according to parts by weight, burn talcum 20-30 parts, feldspar 10-15 parts, kaolin 6-8 parts, just Beautiful 2-6 parts, 3 parts of manganese carbonate, actinolite 5-8 parts, above-mentioned raw materials are crushed respectively it is rearmounted enter ball mill, add raw material gross weight 32% water, start wet-milling 15 hours, the slurry by wet-milling crosses 300 mesh sieves, takes out and stands 12 hours, by the water content of slurry 45% is adjusted to, obtains ground-coat enamel material, it is standby；Step 4: according to parts by weight take plant ash 25-35 parts, kaolin 8-10 parts, Zijin soil 6-10 parts, talcum 10-15 parts, Actinolite 15-20 parts, corundum 4-6 parts, apatite 6-8 parts, manganese carbonate 1-5 parts, calcite 5-10 parts and di-iron trioxide 1-5 Part, above-mentioned raw materials are crushed respectively it is rearmounted enter ball mill, add the water of raw material gross weight 30%, start wet-milling 16 hours, through overly moist The slurry of mill crosses 350 mesh sieves, takes out and stands 12 hours, the water content of slurry is adjusted into 46%, obtains glaze material, standby；Step 5: wiping base is carried out to biscuit made of step 2 with water, with waddy according to the clockwise or inverse time while wiping base The direction of pin is stirred to ground-coat enamel material made of step 3, during stirring since the center of slurry, and is gradually moved to circumference, Mixing time is 20 minutes, after the completion of stirring, the biscuit after wiping base is put into ground-coat enamel slurry, poured in biscuit outer surface Glaze, after the completion of pouring glaze, after body drying, by way of glaze spraying, glaze material made from step 4 is uniformly imposed on base substrate, Biscuit is obtained after drying；Step 6: the biscuit of step 5 is put into kiln, burnt using High Temperature Gas, open gas tank valve, starting point timing of fighting is opened Begin, it is using the time point as starting point that the following time, which calculates, and pressure is adjusted to 0.01MPa, and rear flashboard pulls open 120cm, and wicket is beaten Open 280cm；2.2 hours are fired, kiln temperature rises to 140 DEG C, and pressure is adjusted to 0.02 MPa；3 hours are fired, kiln temperature rises to 320 ℃；6 hours are fired, kiln temperature rises to 560 DEG C；Fire 5.5 hours, kiln temperature rises to 780 DEG C；Programming rate control is at 3 DEG C/minute afterwards Clock, when kiln temperature is controlled at 900-920 DEG C, with tight flashboard；Fire 6.5 hours afterwards, when kiln temperature rises to 1000 DEG C, pressure is adjusted to 0.03 MPa, start to be incubated；8 hours kiln temperatures are fired afterwards and rise to 1100 DEG C, and into reduction phase, pressure is adjusted to 1.5 MPa；Work as burning 8 hours kiln temperatures of system rise to 1250 DEG C, into strong reduction phase；10 hours kiln temperatures are fired afterwards rises to 1350 DEG C；Kiln temperature control afterwards exists Between 1250 DEG C -1350 DEG C, weak reduction is carried out, is fired 12 hours, it is rear to stop firing, fire and complete.