CN107879686A - A kind of water-permeable flexible tapestry brick - Google Patents
A kind of water-permeable flexible tapestry brick Download PDFInfo
- Publication number
- CN107879686A CN107879686A CN201610862530.6A CN201610862530A CN107879686A CN 107879686 A CN107879686 A CN 107879686A CN 201610862530 A CN201610862530 A CN 201610862530A CN 107879686 A CN107879686 A CN 107879686A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- tapestry brick
- permeable
- sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to decoration material field, proposes a kind of water-permeable flexible tapestry brick, is made up of the raw material of following weight part ratio：20 30 parts of pulverized fuel ash cement, middle 15 25 parts of sand, 15 25 parts of fine sand, 5 10 parts of silica flour, 15 parts of aluminium powder, 15 parts of sodium sulphate, press down 13 parts of alkaline agent, iron oxide pigment 2-5 parts；Product rigidity is enough, wear-resisting；Good weatherability, service life length；Material is simple and easy to get, and cost is not high；Product has certain porosity, can reach good permeable effect, meet the requirement of green ecological environment protection architecture.
Description
Technical field
The invention belongs to decoration material field, and in particular to a kind of water-permeable flexible tapestry brick.
Background technology
Flexible clay facing tile, it is to want raw material based on color modified inorganic mineral powder, adds a small amount of water soluble polymer
Polymer, by having flexible light-weight building decoration made of specific technique, this respect is different from porcelain tendre, is preferable
Traditional decoration building materials porcelain face brick alternative materials, suitable for the various newly-built walls such as concrete, building block, external wall outer insulation system
The energy-conservation of system and existing building is transformed with facing.Common flexible clay facing tile high expensive, resistance to phenology poor performance, so seeking
More preferable more economical facing tile product, is pursued always in building trade.
The content of the invention
For overcome the deficiencies in the prior art, a kind of low cost, good weatherability and the good flexible decorations of water-permeable and air permeable performance are prepared
Face brick, the present invention propose a kind of water-permeable flexible tapestry brick.
Technical scheme
A kind of water-permeable flexible tapestry brick, is made up of the raw material of following weight part ratio：Pulverized fuel ash cement 20-30 parts, middle sand 15-25
Part, fine sand 15-25 parts, silica flour 5-10 parts, aluminium powder 1-5 parts, sodium sulphate 1-5 parts, press down alkaline agent 1-3 parts, iron oxide pigment 2-5
Part.
The beneficial effects of the present invention are：
1. product rigidity is enough, wear-resisting.
2. good weatherability, service life length.
3. material is simple and easy to get, cost is not high.
4. product has certain porosity, good permeable effect can be reached, meet the requirement of green ecological environment protection architecture.
Embodiment
With reference to specific embodiment, the present invention is described in detail, and once embodiment will be helpful to those skilled in the art
The present invention is further understood, but the invention is not limited in any way.It should be pointed out that to one of ordinary skill in the art
For, without departing from the inventive concept of the premise, it can also make certain adjustments and improvements, these belong to the guarantor of the present invention
Protect scope.
Embodiment 1
A kind of water-permeable flexible tapestry brick, is made up of the raw material of following parts by weight：Pulverized fuel ash cement 20Kg, middle sand 15Kg, fine sand
16Kg, silica flour 5Kg, aluminium powder 2Kg, sodium sulphate 1Kg, press down alkaline agent 1Kg, iron oxide pigment 1Kg.
Embodiment 2
A kind of water-permeable flexible tapestry brick, is made up of the raw material of following parts by weight：Pulverized fuel ash cement 25Kg, middle sand 18Kg, fine sand
19Kg, silica flour 7Kg, aluminium powder 3Kg, sodium sulphate 3Kg, press down alkaline agent 2Kg, iron oxide pigment 3Kg.
Embodiment 3
A kind of water-permeable flexible tapestry brick, is made up of the raw material of following parts by weight：Pulverized fuel ash cement 30Kg, middle sand 15-25 parts, carefully
Sand 25Kg, silica flour 10Kg, aluminium powder 4Kg, sodium sulphate 4Kg, press down alkaline agent 3Kg, iron oxide pigment 4Kg.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art the invention discloses technical scope in, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should all be included within the scope of the present invention.
Claims (1)
- A kind of 1. water-permeable flexible tapestry brick, it is characterized in that being made up of the raw material of following weight part ratio：Pulverized fuel ash cement 20-30 parts, Middle sand 15-25 parts, fine sand 15-25 parts, silica flour 5-10 parts, aluminium powder 1-5 parts, sodium sulphate 1-5 parts, press down alkaline agent 1-3 parts, iron oxide Pigment 2-5 parts.