CN107841005A - 一种易加工的补强型丁腈橡胶及其制备方法 - Google Patents
一种易加工的补强型丁腈橡胶及其制备方法 Download PDFInfo
- Publication number
- CN107841005A CN107841005A CN201610833900.3A CN201610833900A CN107841005A CN 107841005 A CN107841005 A CN 107841005A CN 201610833900 A CN201610833900 A CN 201610833900A CN 107841005 A CN107841005 A CN 107841005A
- Authority
- CN
- China
- Prior art keywords
- nitrile rubber
- reinforced type
- easy processing
- rubber
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供了一种易加工补强型丁腈橡胶及其制备方法，所述的易加工丁腈橡胶包含基础胶和一种补强型增塑剂，通过混炼技术制得。所述的补强型增塑剂是在丁腈橡胶中加入烯烃复分解催化剂和防焦型橡胶补强剂反应得到，该易加工补强型丁腈橡胶产品相对于基础胶，以增塑剂加入量计，其门尼粘度降低0.5单位/份，拉伸强度提高0.05MPa/份以上，延迟焦烧时间1‑15s/份。
Description
技术领域
本本发明涉及一种丁腈橡胶及其制备方法，具体涉及一种补强型易加工的丁腈橡胶及其制备方法。
背景技术
乳液聚合丁腈橡胶生胶门尼粘度一般为40-100ML1+4 100℃，混炼胶门尼一般要求低于90ML1+4 100℃；生胶强度较低，一般只有4.5±0.5MPa，其强度的提高主要靠后加工过程的补强剂予以提高，一般可达20.5-26.5MPa。补强剂主要有炭黑、白炭黑、纳米碳酸钙以及蒙脱土等无机粉体，无机粉体自团聚比较严重，要实现其与橡胶的混合需要较高的能量，一般需要在开炼机或密炼机上进行长时间的反复捏合和混炼。开炼或密炼工序中，一般都需要加入一定量的增塑剂。通常是种能使胶料具有一定柔软性的低分子物质，它们能增加胶料的可塑性，流动性，粘着性，以便于压型和成型等工艺操作。以及有助于粉末状配合剂分散和降低混炼温度，提高橡胶的可加工性。
丁腈橡胶由于其腈基的极性作用，耐油性较好，常用于胶管、胶带、密封材料等领域，橡胶加工中使用最多的石油系增塑剂，主要包括芳烃油、石蜡油、环烷油、重油、石蜡、凡士林、沥青、石油树脂等等，不适用与丁腈橡胶加工体系。丁腈橡胶一般采用邻苯二甲酸二-2-乙基己酯等酯类物质。CN200310108748.5一种二元酸酯增塑剂及其制造方法，其特征是，它由己二酸与醚醇在115～125℃和84～97KPa真空减压条件下，经酯化反应而成。这种增塑剂具有相容性好、挥发损失小、不易被抽出洗去的特征，对于改善聚合物材料的低温柔顺性具有明显的效果，而且不牺牲材料本身的性能。特别适用于像丁腈橡胶、丙烯酸酯橡胶、氯醚橡胶之类极性橡胶，而且也可用于乙烯基树脂、纤维素树脂等。CN97181179.2低单体含量的聚氨酯预聚物，含有自由NCO基团的低单体含量的聚氨酯预聚物,从多羟基醇和不同反应活性的二异氰酸酯制备,其特征是相对反应较慢的二异氰酸酯的NCO基团与反应快速的二异氰酸酯的NCO基团的比率。预聚物通过两阶段反应制备。本发明的预聚物适用于粘结塑料制品、金属和纸张,尤其是膜材料。专利报道的这类增塑剂多是酯类增塑剂，这类增塑剂对丁腈橡胶的相容性较好，有较好增塑的效果，但没有补强效果，且在产品使用过程中易发生析出。
丁腈橡胶的门尼焦烧时间可以衡量胶料产生焦烧的难易，焦烧时间越长，则加工过程越不易发生早期硫化的现象。焦烧时间通常可以通过门尼粘度计来测定，为门尼粘度转矩达到10％所需的时间，用T10表示，在标准测试配方下丁腈橡胶的T10为3-4min。
发明内容
本发明目的是提供一种易加工补强型丁腈橡胶及其制备方法，具体是将低分子量的具有补强功能的增塑剂在炼胶工序中加入丁腈橡胶中制得，该橡胶的门尼粘度显著降低，拉伸强度大幅提高。
所述的易加工补强型丁腈橡胶，以质量份计，包括：100份丁腈橡胶和1-100份补强型增塑剂，优选为20-80份补强型增塑剂；所述的补强型增塑剂是通过如下方法制得：将丁腈橡胶溶解于溶剂中配制成0.1％w-20％w，优选为1％w～15％w的溶液，以100质量份橡胶计，向溶液中加入0.5-1.5份，优选为0.8-1.2份的烯烃复分解催化剂和10-60份，优选为40-50份防焦型橡胶补强剂，在15-50℃，优选为20-30℃隔绝空气和水，反应0.5-5小时,优选为1-2小时，反应后的胶液经溶剂脱出，得到补强型增塑剂。本发明所述的防焦型橡胶补强剂是由防焦剂和补强剂通过烯烃复分解反应制得，所述的防焦剂是含烯不饱和取代基的亚硝基化合物、有机酸类或硫代亚酰胺类物；所述的补强剂是含烯不饱和取代基的有机硅烷化合物。
本发明所述的防焦型橡胶补强剂具体制备方法包括：防焦剂和补强剂以1：(0.1～5.0)摩尔比混合，用溶剂配制成1％～30％质量浓度的溶液，向溶液中加入占防焦剂和补强剂总物质的量的0.01～0.1％的烯烃复分解催化剂，隔绝空气和水，常温反应0.5～8h后，采用真空脱溶剂装置将溶剂脱出，制得防焦型橡胶补强剂。
所述的防焦剂是含烯不饱和取代基的亚硝基化合物或有机酸类或硫代亚酰胺类物，可以是N-亚硝基二(乙烯基苯)胺、N-亚硝基-苯乙烯基-β-萘胺、N-亚硝基-2-丙烯基-2,4-二甲基-1,2-二氢喹啉聚合物，乙烯基苯甲酸、乙烯基水杨酸、丁烯基水杨酸、乙烯基邻苯二甲酸、N-乙烯基环己基硫代邻苯二甲酰亚胺、N-丙烯基环己基硫代邻苯二甲酰亚胺等；
本发明所制备补强型增塑剂的Mn为200-8000。
本发明所述的溶剂为结构中不含烯的能够溶解丁腈橡胶的溶剂；选自氯仿、氯苯、丙酮、丁酮等。
本发明所述的补强剂为含烯不饱和取代基的有机硅烷化合物其结构式为：
其中：
R4－含有2～18个碳的不饱和烯烃脂肪族链段，可以是乙烯基、丙烯基、异丙烯基、异戊烯基、3-戊烯基、6-辛烯基、三甲基乙烯基、1-庚烯基、甲基丙烯酰氧基丙基、甲基丙烯酰氧基，优选乙烯基；
R1、R3－含有1～12个碳的烷氧基，6～12个碳的芳氧基，3～12个碳的硅氧基，可以是甲氧基、乙氧基、丙氧基、异丙氧基、正丁氧基、己氧基、戊氧基、正庚氧基、异辛氧基、正壬氧基、苯氧基、氯苯氧基、烯丙氧基、苄氧基、三甲基硅氧基，优选甲氧基，乙氧基；R1和R3设定为含有烷氧基的目的是在丁腈橡胶加工时通过热和酸的作用使烷氧基水解，从而在橡胶体系内形成-O-Si-空间网络结构，从而对基质橡胶起到补强作用；如果有机硅烷中只有一个烷氧基，其水解之后则仅形成二聚体，不能形成-O-Si-空间网络结构，起不到补强的作用。
R2可以是和R1相同的基团，还可以是含有1～20个碳的饱和链段，含有3～8个碳的环烷基、或含有6～8个碳的芳香基；优选甲基，乙基，甲氧基，乙氧基。
所述的补强剂的结构式中R1、R2、R3和R4最好其中的至少一个取代基含有腈基基团，便于在极性溶剂中溶解，提高与丁腈橡胶的相容性，增强反应活性。
本发明所述的补强剂可以是一腈乙烯基三乙氧基硅烷、乙烯基二乙氧基-二腈乙基硅烷、乙烯基三甲氧基硅烷、乙烯基二戊氧基-己基硅烷、异丙烯基二正丁氧基乙基硅烷等。
本发明所述的烯烃复分解催化剂是一种钌卡宾络合物催化剂，可以是二氯·(邻-异丙氧基苯亚甲基)·(三环己基膦)合钌(Ⅱ)二氯·[邻-异丙氧基苯亚甲基]·[1,3-双(2,4,6-三甲基苯基)-2-咪唑啉亚基]合钌等具有相似功能的Grubbs系列催化剂或其他具有烯烃复分解功能的金属卡宾催化剂，优选
本发明还提供了所述的易加工补强型丁腈橡胶的制备方法，主要包括：将所述的补强型增塑剂与丁腈橡胶按比例混炼即可制得易加工补强型丁腈橡胶。
所述的混炼可以在开炼机或密炼机上进行，优选采用开炼机。
本发明所述的混炼工艺采用橡胶的常规混炼技术即可。混炼温度、混炼次数混炼时间等均不做特殊限定。
本发明还提供所述的易加工丁腈橡胶的优选的制备方法，包括：将所述的丁腈橡胶先在开炼机上在50-60℃下混炼4-6次，再加入所述的补强型增塑剂混炼5-7次，制得易加工补强型丁腈橡胶。
本发明制得的易加工丁腈橡胶相对于基础胶，以添加增塑剂量计算，门尼粘度降低0.5单位/份，拉伸强度提高0.05MPa/份以上。
本发明中未作特别说明的“份”均是指质量份。
本发明依据的技术原理为：
上述化学反应方程式(1)以乙烯基苯甲酸为防焦剂和乙烯基三乙氧基硅烷为补强剂进行烯烃复分解反应制得防焦型橡胶补强剂；式(2)为丁腈橡胶在烯烃复分解催化剂作用下分子量降低，同时与式(1)生成的防焦型橡胶补强剂发生反应在侧基上引入了补强基团和防焦基团。
该增塑剂为丁腈橡胶与防焦型橡胶补强剂剂复分解反应的产物，与丁腈橡胶具有相似的组成，因其低分子量对橡胶起到软化作用。通常橡胶加工配方中采用脂类为增塑剂，并加入补强剂剂、防焦剂等小分子助剂，该助剂极易被炭黑吸附到表面减低其作用效果。本方案将防焦剂、补强剂与软化剂化学键合，能够有效补强，并阻止橡胶的焦烧。
具体实施方式
本发明具体实施所需的原料助剂如下所述：
(1)丁腈橡胶NBR3305、NBR2907，工业级，兰州石化分公司；
(2)一腈乙烯基三乙氧基硅烷、乙烯基二乙氧基-二腈乙基硅烷、乙烯基三甲氧基硅烷、乙烯基二戊氧基-己基硅烷、异丙烯基二正丁氧基乙基硅烷，试剂级，上海汇普硅氧烷有限公司；
(3)烯烃复分解催化剂：钌卡宾催化剂，500mg/瓶，纯度≥98％w，百灵威科技有限公司；
(4)氯仿、氯苯、丙酮、丁酮，试剂级，百灵威科技有限公司；
(5)2-乙烯基苯甲酸、3-乙烯基邻苯二甲酸，试剂级，甘肃银城助剂公司；
将增塑剂在开炼机上与丁腈橡胶共混，测试生胶门尼粘度、焦烧时间及橡胶力学性能；橡胶门尼粘度和焦烧时间按照GB/T 1232.1-2000测试，橡胶力学性能按照GB/T 528-2009测试，橡胶增塑剂分子量采用GPC测试。
以下所述的“份”均为质量份；所述的“％”均为质量百分数，未作特殊说明均按照橡胶干基质量为100计算。
实施例1：
将防焦剂2-乙烯基苯甲酸和补强剂一腈乙烯基三乙氧基硅烷以1.0：5.0摩尔比混合，用己烷溶剂配制成30％质量浓度的溶液，向溶液中加入占防焦剂和补强剂总物质的量的0.1％的烯烃复分解催化剂隔绝空气和水，常温反应8h后，采用真空脱溶剂装置将溶剂脱出，制得防焦橡胶补强剂1-1。
将100份丁腈橡胶NBR3305溶解于氯仿溶剂中配制成1.3％浓度溶液，加入0.66份的烯烃复分解催化剂和13份防焦型橡胶补强剂1-1，在15.9℃隔绝空气和水，反应0.53小时，反应后的胶液经溶剂脱出，得到补强型增塑剂，测得其Mn为6800。
将100份丁腈橡胶NBR3305在开炼机上78℃混炼4次，加入10份所制得的补强型增塑剂再混炼4次，制得易加工补强型丁腈橡胶，经测试，门尼粘度由55降低至49，拉伸强度由23.3MPa提高到25.3MPa，焦烧时间由189s提高到245s。
对比例1：
与实施例1相比，其它条件相同，不同之处在于不加防焦型橡胶补强剂，具体为：将100份丁腈橡胶NBR3305溶解于氯仿溶剂中配制成1.3％浓度溶液，加入0.66份的烯烃复分解催化剂在15.9℃隔绝空气和水，反应0.53小时，反应后的胶液经溶剂脱出，得到增塑剂，测得其Mn为9800。
将100份丁腈橡胶NBR3305在开炼机上78℃混炼4次，加入10份所制得的补强型增塑剂再混炼4次，制得易加工补强型丁腈橡胶，经测试，门尼粘度由55降低至52，拉伸强度为25.2MPa，没有提高，焦烧时间短至140s。
实施例2：
将防焦剂3-乙烯基邻苯二甲酸和补强剂乙烯基二乙氧基甲基硅烷以1.0：0.1摩尔比混合，用己烷溶剂配制成1％质量浓度的溶液，向溶液中加入占防焦剂和补强剂总物质的量的0.01％的烯烃复分解催化剂隔绝空气和水，常温反应0.5h后，采用真空脱溶剂装置将溶剂脱出，制得防焦型橡胶补强剂2-1。
将100份丁腈橡胶NBR3305溶解于丙酮溶剂中配制成10％浓度溶液，加入0.9份烯烃复分解催化剂和48份防焦型橡胶补强剂2-1，在49℃隔绝空气和水，反应4.6小时，反应后的胶液经溶剂脱出，得到补强型增塑剂产品，测得其Mn为3100。
将100份丁腈橡胶NBR3305和14份所制得的补强型增塑剂在开炼机上混炼均匀，制得易加工补强型丁腈橡胶，经测试，门尼粘度由55降低至36，拉伸强度由23.3MPa提高到27.5MPa，焦烧时间由181s提高到243s。
对比例2：
与实施例2相比，其它条件相同，不同之处在于不加烯烃复分解催化剂，具体为：将防焦剂3-乙烯基邻苯二甲酸和补强剂乙烯基二乙氧基甲基硅烷以1.0：0.1摩尔比混合，用己烷溶剂配制成1％质量浓度的溶液，隔绝空气和水，常温反应0.5h后，采用真空脱溶剂装置将溶剂脱出，制得防焦型橡胶补强剂2-2。
将100份丁腈橡胶NBR3305溶解于丙酮溶剂中配制成10％浓度溶液，加入48份防焦型橡胶补强剂2-2，在49℃隔绝空气和水，反应4.6小时，反应后的胶液经溶剂脱出，得到补强型增塑剂产品，测得其Mn为171000。
将100份丁腈橡胶NBR3305和14份所制得的补强型增塑剂在开炼机上混炼均匀，制得易加工补强型丁腈橡胶，经测试，门尼粘度为55，没有降低，拉伸强度由23.3MPa提高到26.5MPa，焦烧时间由181s提高到185。
实施例3：
将防焦剂3-乙烯基邻苯二甲酸和补强剂乙烯基三甲氧基硅烷以1.0：4.0摩尔比混合，用己烷溶剂配制成10％质量浓度的溶液，向溶液中加入占防焦剂和补强剂总物质的量的0.09％的烯烃复分解催化剂隔绝空气和水，常温反应4.5h后，采用真空脱溶剂装置将溶剂脱出，制得防焦型橡胶补强剂3-1。
将100份丁腈橡胶NBR2907基础胶溶解于氯苯溶剂中配制成3.5％浓度溶液，加入0.53份的烯烃复分解催化剂和25.6份防焦型橡胶补强剂3-1，在25℃隔绝空气和水，反应2.5小时，反应后的胶液经溶剂脱出，得到补强型增塑剂，测得Mn为2500。
将100份丁腈橡胶NBR2907和30份所制得的补强型增塑剂在密炼机上混炼均匀，制得易加工补强型丁腈橡胶，经测试，门尼粘度由75降低为45，拉伸强度由24.3MPa提高到27.6MPa，焦烧时间由185s提高到262s。
对比例3：
与实施例3相比，其它条件相同，不同之处在于采用邻苯二甲酸二-2-乙基己酯作为增塑剂，具体为：将100份丁腈橡胶和30份邻苯二甲酸二-2-乙基己酯在密炼机上混炼均匀，制得易加工补强型丁腈橡胶，经测试，门尼粘度由75降低为43，拉伸强度由24.3MPa降低至23.5MPa，焦烧时间为187s。
实施例4：
将防焦剂2-乙烯基苯甲酸和补强剂乙烯基二戊氧基-己基硅烷以1.0：3.0摩尔比混合，用己烷溶剂配制成15％质量浓度的溶液，向溶液中加入占防焦剂和补强剂总物质的量的0.029％的烯烃复分解催化剂隔绝空气和水，常温反应4.8h后，采用真空脱溶剂装置将溶剂脱出，制得防焦型橡胶补强剂4-1。
将100份丁腈橡胶NBR2907基础胶溶解于丁酮溶剂中配制成9％浓度溶液，加入1.45份的烯烃复分解催化剂和11份防焦型橡胶补强剂4-1，在15℃隔绝空气和水，反应4.9小时，反应后的胶液经溶剂脱出，得到补强型增塑剂，测得Mn为3800。
将100份丁腈橡胶NBR2907在开炼机上60℃混炼4次，加入35份该补强型增塑剂混炼5次，制得易加工补强型丁腈橡胶，经测试，门尼粘度由75降低为48，拉伸强度由24.3MPa提高到26.7MPa，焦烧时间由185s提高到294s。
对比例4：
与实施例4相比，其它条件相同，不同之处在于采用补强剂乙烯基戊氧基-二己基硅烷，仅含有一个硅氧烷，具体为：将防焦剂2-乙烯基苯甲酸和补强剂乙烯基戊氧基-二己基硅烷以1.0：3.0摩尔比混合，用己烷溶剂配制成15％质量浓度的溶液，向溶液中加入占防焦剂和补强剂总物质的量的0.029％的烯烃复分解催化剂隔绝空气和水，常温反应4.8h后，采用真空脱溶剂装置将溶剂脱出，制得防焦型橡胶补强剂4-2。
将100份丁腈橡胶NBR2907基础胶溶解于丁酮溶剂中配制成9％浓度溶液，加入1.45份的烯烃复分解催化剂和11份防焦型橡胶补强剂4-2，在15℃隔绝空气和水，反应4.9小时，反应后的胶液经溶剂脱出，得到补强型增塑剂，测得Mn为3850。
将100份丁腈橡胶NBR2907在开炼机上60℃混炼4次，加入35份该补强型增塑剂混炼5次，制得易加工补强型丁腈橡胶，经测试，门尼粘度由75降低为50，拉伸强度由26.3MPa提高到26.4MPa，没有明显变化，抗老化性能差，焦烧时间由185s提高到296s。
实施例5：
将防焦剂2-乙烯基苯甲酸和补强剂乙烯基二戊氧基-己基硅烷以1.0：3.7摩尔比混合，用己烷溶剂配制成19％质量浓度的溶液，向溶液中加入占防焦剂和补强剂总物质的量的0.05％的烯烃复分解催化剂隔绝空气和水，常温反应7h后，采用真空脱溶剂装置将溶剂脱出，制得防焦型橡胶补强剂5-1。
将100份丁腈橡胶NBR3305溶解于氯仿溶剂中配制成4％浓度溶液，加入0.9份的烯烃复分解催化剂和22份防焦型橡胶补强剂5-1，在35℃隔绝空气和水，反应4小时，反应后的胶液经溶剂脱出，得到补强型增塑剂，测得Mn为1500。
将100份丁腈橡胶NBR3305和40份所制得的补强型增塑剂在开炼机上混炼均匀，制得易加工补强型丁腈橡胶，经测试，门尼粘度由55降低至38，拉伸强度由23.3MPa提高到26.4MPa，焦烧时间由185s提高到274s。
对比例5：
与实施例5相比，其它条件相同，不同之处在于采用补强剂、防焦剂在后加工工序中加入，具体为：将100份丁腈橡胶NBR3305溶解于氯仿溶剂中配制成4％浓度溶液，加入0.9份的烯烃复分解催化剂在35℃隔绝空气和水，反应4小时，反应后的胶液经溶剂脱出，得到补强型增塑剂，测得Mn为5500。
将100份丁腈橡胶NBR3305和40份所制得的补强型增塑剂和相当于增塑剂22份橡胶补强剂乙烯基二戊氧基-己基硅烷和12份防焦剂2-乙烯基苯甲酸在开炼机上混炼均匀，制得易加工补强型丁腈橡胶，门尼粘度由55降低至44，拉伸强度由23.3MPa提高到23.5MPa，强度略有提高，焦烧时间由185s提高到194s。
实施例6：
将防焦剂2-乙烯基苯甲酸和补强剂异丙烯基二正丁氧基乙基硅烷以1.0：4.5摩尔比混合，用己烷溶剂配制成25％质量浓度的溶液，向溶液中加入占防焦剂和补强剂总物质的量的0.06％的烯烃复分解催化剂隔绝空气和水，常温反应4h后，采用真空脱溶剂装置将溶剂脱出，制得防焦型橡胶补强剂6-1。
将100份丁腈橡胶NBR3305溶解于氯苯溶剂中配制成19％浓度溶液，加入1.2份的烯烃复分解催化剂和55份防焦型橡胶补强剂6-1，在28℃隔绝空气和水，反应3.2小时，反应后的胶液经溶剂脱出，得到补强型增塑剂，测得Mn为450。
将100份丁腈橡胶NBR3305在开炼机上70℃混炼3次，加入1.1份该补强型增塑剂混炼5次，制得易加工补强型丁腈橡胶，经测试，门尼粘度由55降低至45，拉伸强度由23.3MPa提高到23.8MPa，焦烧时间由184s提高到281s。
对比例6：
与实施例6相比，其它条件相同，不同之处在于采用邻苯二甲酸二-2-乙基己酯作为增塑剂，同时加入补强剂，具体为：将100份丁腈橡胶NBR3305在开炼机上70℃混炼3次，加入1.1份邻苯二甲酸二-2-乙基己酯和相对于己酯质量为55份橡胶补强剂异丙烯基二正丁氧基乙基硅烷，在开炼机上70℃再混炼3次，制得易加工补强型丁腈橡胶，经测试，门尼粘度由55降低至48，拉伸强度没有提高，焦烧时间由184s提高到284s。
实施例7：
将防焦剂2-乙烯基苯甲酸和补强剂乙烯基三甲氧基硅烷以1.0：4.5摩尔比混合，用己烷溶剂配制成25％质量浓度的溶液，向溶液中加入占防焦剂和补强剂总物质的量的0.06％的烯烃复分解催化剂隔绝空气和水，常温反应4h后，采用真空脱溶剂装置将溶剂脱出，制得防焦型橡胶补强剂7-1。
将100份丁腈橡胶NBR3305溶解于丁酮溶剂中配制成8％浓度溶液，加入0.95份烯烃复分解催化剂和48份防焦型橡胶补强剂7-1，在48℃隔绝空气和水，反应3.2小时，反应后的胶液经溶剂脱出，得到补强型增塑剂产品，测得其Mn为750。
将100份丁腈橡胶NBR3305和70份所制得的补强型增塑剂在密炼机上混炼均匀，制得丁腈橡胶产品，经测试，门尼粘度由55降低至20，拉伸强度由23.3MPa提高到24.9MPa，焦烧时间由185s提高到294s。
对比例7：
与实施例7相比，其它条件相同，不同之处在于增塑剂制备过程中先加入复分解催化剂反应完之后，再加入补强剂再反应一段时间，再加入防焦剂反应一段时间，具体为：将100份丁腈橡胶NBR3305溶解于己烷溶剂中配制成8％浓度溶液，加入0.95份烯烃复分解催化剂48℃隔绝空气和水反应2h，再加入48份橡胶补强剂乙烯基三甲氧基硅烷，在48℃隔绝空气和水，反应1.2小时，再加入10份防焦剂2-乙烯基苯甲酸，在48℃隔绝空气和水，反应2小时，反应后的胶液经溶剂脱出，得到补强型增塑剂产品，测得其Mn为13400。
将100份丁腈橡胶NBR3305和70份所制得的补强型增塑剂在密炼机上混炼均匀，制得丁腈橡胶产品，经测试，门尼粘度由55降低至53，拉伸强度由23.3MPa提高到23.8MPa，焦烧时间由185s提高到198s。
Claims (20)
1.一种易加工补强型丁腈橡胶，以质量份计，包括：100份丁腈橡胶和1-100份补强型增塑剂；其特征在于所述的补强型增塑剂是通过如下方法制得：将丁腈橡胶溶解于溶剂中配制成0.1％w-20％w的溶液，以100质量份橡胶计，向溶液中加入0.5-1.5份的烯烃复分解催化剂和10-60份防焦型橡胶补强剂，在15-50℃，隔绝空气和水，反应0.5-5小时，优选为1-2小时，反应后的胶液经溶剂脱出，得到补强型增塑剂；所述的防焦型橡胶补强剂是由防焦剂和补强剂通过烯烃复分解反应制得，所述的防焦剂是含烯不饱和取代基的亚硝基化合物、有机酸类或硫代亚酰胺类物；所述的补强剂是含烯不饱和取代基的有机硅烷化合物。
2.如权利要求1所述的易加工补强型丁腈橡胶，其特征在于所述的易加工补强型丁腈橡胶中包含20-80份补强型增塑剂。
3.如权利要求1所述的易加工补强型丁腈橡胶，其特征在于所制备的补强型增塑剂的Mn为200-8000。
4.如权利要求1所述的易加工补强型丁腈橡胶，其特征在于所述的溶剂为结构中不含烯的能够溶解丁腈橡胶的溶剂。
5.如权利要求1所述的易加工补强型丁腈橡胶，其特征在于所述的溶剂选自氯仿、氯苯、丙酮或丁酮。
6.如权利要求1所述的易加工补强型丁腈橡胶，其特征在于所述的防焦型橡胶补强剂的制备方法为：将防焦剂和补强剂以1：(0.1～5.0)摩尔比混合，用溶剂配制配制成1％～30％质量浓度的溶液，向溶液中加入占防焦剂和补强剂总物质的量的0.01～0.1％的烯烃复分解催化剂，隔绝空气和水，常温反应0.5～8h后，采用真空脱溶剂装置将溶剂脱出，制得防焦型橡胶补强剂。
7.如权利要求6所述的易加工补强型丁腈橡胶，其特征在于所述的防焦剂选自N-亚硝基二(乙烯基苯)胺、N-亚硝基-苯乙烯基-β-萘胺、N-亚硝基-2-丙烯基-2,4-二甲基-1,2-二氢喹啉聚合物，乙烯基苯甲酸、乙烯基水杨酸、丁烯基水杨酸、乙烯基邻苯二甲酸、N-乙烯基环己基硫代邻苯二甲酰亚胺、或N-丙烯基环己基硫代邻苯二甲酰亚胺。
8.如权利要求1所述的易加工补强型丁腈橡胶，其特征在于在所述的补强型增塑剂制备过程中，以100质量份丁腈橡胶计，加入0.8-1.2份烯烃复分解催化剂。
9.如权利要求1所述的易加工补强型丁腈橡胶，其特征在于在所述的补强型增塑剂制备过程中，以100质量份丁腈橡胶计，加入40-50份防焦型橡胶补强剂。
10.如权利要求1所述的易加工补强型丁腈橡胶，其特征在于所述的丁腈橡胶溶解于溶剂中配制成浓度为1％w～15％w的溶液。
11.如权利要求1所述的易加工补强型丁腈橡胶，其特征在于所述的补强剂为含烯不饱和取代基的有机硅烷化合物。
12.如权利要求1所述的易加工补强型丁腈橡胶，其特征在于所述的补强剂的结构式为：其中：R4为含有2～18个碳的不饱和烯烃脂肪族链段；R1、R3为含有1～12个碳的烷氧基、6～12个碳的芳氧基或3～12个碳的硅氧基；R2为与R1相同的基团，或者为含有1～20个碳的饱和链段、含有3～8个碳的环烷基、或含有6～8个碳的芳香基。
13.如权利要求12所述的易加工补强型丁腈橡胶，其特征在于所述的补强剂结构式中的R4选自乙烯基、丙烯基、异丙烯基、异戊烯基、3-戊烯基、6-辛烯基、三甲基乙烯基、1-庚烯基、甲基丙烯酰氧基丙基或甲基丙烯酰氧基。
14.如权利要求12所述的易加工补强型丁腈橡胶，其特征在于所述的补强剂结构式中的R1、R3分别选自甲氧基、乙氧基、丙氧基、异丙氧基、正丁氧基、正己氧基、正戊氧基、正庚氧基、异辛氧基、正壬氧基、苯氧基、氯苯氧基、烯丙氧基、苄氧基或三甲基硅氧基。
15.如权利要求12所述的易加工补强型丁腈橡胶，其特征在于所述的补强剂结构式中的R1、R2、R3和R4中至少一个取代基含有腈基基团。
16.如权利要求1所述的易加工补强型丁腈橡胶，其特征在于所述的补强剂选自一腈乙烯基三乙氧基硅烷、乙烯基二乙氧基-二腈乙基硅烷、乙烯基三甲氧基硅烷、乙烯基二戊氧基-己基硅烷或异丙烯基二正丁氧基乙基硅烷。
17.如权利要求1所述的易加工补强型丁腈橡胶，其特征在于所述的烯烃复分解催化剂为具有烯烃复分解功能的金属卡宾类催化剂。
18.如权利要求1所述的易加工补强型丁腈橡胶，其特征在于所述的烯烃复分解催化剂选自二氯·(邻-异丙氧基苯亚甲基)·(三环己基膦)合钌二氯·[邻-异丙氧基苯亚甲基]·[1,3-双(2,4,6-三甲基苯基)-2-咪唑啉亚基]合钌
19.一种如权利要求1所述的易加工补强型丁腈橡胶的制备方法，其特征在于主要包括将所述的补强型增塑剂与丁腈橡胶按比例混炼制得。
20.如权利要求17所述的易加工补强型丁腈橡胶的制备方法，其特征在于包括：将所述的丁腈橡胶在开炼机上在50-60℃下混炼4-6次，再加入所述的补强型增塑剂混炼5-7次，制得易加工补强型丁腈橡胶。