CN107828258A - A kind of calligraphy and painting mounting anti-blushing agent - Google Patents
A kind of calligraphy and painting mounting anti-blushing agent Download PDFInfo
- Publication number
- CN107828258A CN107828258A CN201711027609.8A CN201711027609A CN107828258A CN 107828258 A CN107828258 A CN 107828258A CN 201711027609 A CN201711027609 A CN 201711027609A CN 107828258 A CN107828258 A CN 107828258A
- Authority
- CN
- China
- Prior art keywords
- parts
- calligraphy
- blushing agent
- painting
- mounting anti
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of calligraphy and painting mounting anti-blushing agent, is related to art work mounting technical field, and calligraphy and painting mounting anti-blushing agent includes following component：Adhesive, atlapulgite, ceramic, modified meerschaum particle, polyvinyl alcohol resin, sepiolite fibre, N NMAs, asbestos wool, mica powder, land plaster, butyl titanate, modified oxidized polyethylene, nano medical stone powder, Tissuemat E, lauric monoglyceride, Glycerin, mixed triester with caprylic acid capric acid, polyvinyl chloride emulsion, sodium gluconate, carboxymethyl chitosan；The present invention prepares calligraphy and painting mounting anti-blushing agent; dampproof protection against insects stable performance; with good wet-heat resisting, ageing-resistant performance; preparation method is simple; process conditions are easily realized; stable performance, the calligraphy and painting moisture protection measures of resting period length are obtained, and it is moistureproof for the mounting of calligraphy and painting various forms, reduce production cost and maintenance cost.
Description
Technical field：
The present invention relates to art work field of mounting, and in particular to a kind of calligraphy and painting mounting anti-blushing agent.
Background technology：
The complete calligraphy and painting of one width is to be unable to do without mounting, it is necessary to make its more aesthetically pleasing, and be easy to preserve, spread and collect
's.Because calligraphy and painting be drawn in mostly on breakable rice paper or thin,tough silk class article on.Mounting is a kind of distinctive protection in China and U.S.
Change the technology of painting and calligraphy and rubbings, can reach taller and bigger on aesthetic.
Mounting is further divided into former mounting and remounted, and original mounting is exactly that the picture newly finished is entered luggage by the program of mounting
Mounting.Remount exactly to those original mounting it is bad or due to management collection keeping be not good at, occur ghost come off, make moist it is mouldy,
The rotten fracture of grain, the painting and calligraphy handed down from ancient times for damaged by rats of damaging by worms carry out mounting.It is firm, attractive in appearance by the painting and calligraphy of mounting, it is easy to collect and arranges sight
Reward.And the ancient painting remounted, it can also extend its vitality.
Either former mounting is still remounted, and the mounting such as calligraphy and painting is completed, it is desirable to is reached firm, attractive in appearance, is easy to collection and cloth
Put and view and admire.The present invention provides a kind of calligraphy and painting mounting anti-blushing agent, extends the calligraphy and painting holding time, prevents life of mildewing of being made moist during preservation
Phenomena such as worm, occurs.
The content of the invention：
The technical problems to be solved by the invention are to provide a kind of calligraphy and painting mounting anti-blushing agent, prevent calligraphy and painting during preservation
Phenomena such as being made moist because of factors such as environment occurs, and extends the calligraphy and painting holding time.
Gallery mounting frame is selected by China fir, paulownia is wooden and red, white, pine material and the mounting timber frame prepared,
Timber frame easily makes moist, the moisture absorption, thus preferably prevents outer mounting frame from making moist, be solve means that calligraphy and painting makes moist it
One.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of calligraphy and painting mounting anti-blushing agent：
The calligraphy and painting mounting anti-blushing agent includes each component of following parts by weight：Adhesive 5-11 parts, atlapulgite 15-20
Part, ceramic 5-10 parts, modified meerschaum particle 2-3 parts, polyvinyl alcohol resin 1-2 parts, sepiolite fibre 0.5-1 parts, N-
NMA 0.3-0.5 parts, asbestos wool 0.1-0.3 parts, mica powder 25-35 parts, land plaster 20-25 parts, the fourth of metatitanic acid four
Ester 0.5-3 parts, modified oxidized polyethylene 0.5-3 parts, nano medical stone powder 2-4 parts, Tissuemat E 3-5 parts, lauric monoglyceride
Ester 0.3-0.5 parts, Glycerin, mixed triester with caprylic acid capric acid 0.3-0.5 parts, polyvinyl chloride emulsion 8-15 parts, sodium gluconate 1-2 parts, carboxymethyl shell
Glycan 0.2-0.4 parts.
Wherein described modified meerschaum particle is made from the following raw materials in parts by weight：Sepiolite particle 2-4 parts, vinyl chloride
10-15 parts, acrylic acid 3-5 parts, carboxymethyl cellulose 0.5-1 parts, trifluoro propyl methyl cyclotrisiloxane 0.3-0.5 parts, over cure
Sour potassium 0.01-0.02 parts, nano titanium oxide 1-2 parts, lauryl sodium sulfate 0.05-0.1 parts, water 20-30 parts；Modified Hai Pao
The preparation method of stone particle is that lauryl sodium sulfate and carboxymethyl cellulose first are added to the water into stirring until being completely dissolved, so
Sepiolite particle, vinyl chloride, acrylic acid, nano titanium oxide and trifluoro propyl methyl cyclotrisiloxane 800- are added afterwards
1000rpm/min stirs 0.5-1h, is eventually adding 70-80 DEG C of reaction 2-4h of remaining raw material, is produced after cooling.
The modified oxidized polyethylene is made up of the raw material of following parts by weight：Oxidic polyethylene 10-15 parts, crosslinking are poly-
Tie up ketone 0.5-1 parts, HPMA 0.05-0.1 parts, hydroxyethyl cellulose 0.5-3 parts, water 5-8 parts, its preparation method
For：PVPP and HPMA are added into oxidic polyethylene, 115-120 DEG C of insulation grinding is warming up under grinding
15min, hydroxyethyl cellulose is added, continue, in 115-120 DEG C of insulation grinding 15min, to be then transferred in 0-5 DEG C of environment and seal
1h is stood, and adds 50-55 DEG C of water, is sufficiently mixed and stands 30min after 50-55 DEG C of insulation, it is dry that gained mixed liquor is sent into spraying
In dry machine, dry gained particle and micro mist is made through micronizer, as modified oxidized polyethylene.
A kind of calligraphy and painting mounting anti-blushing agent, step are as follows：
(1) in parts by weight, after taking mica to clean, it is placed in pulverizer and is crushed to 600-800 mesh, sieving obtains mica
Powder；
(2) in parts by weight, choose dry gypsum to be placed in pulverizer, be crushed to 700-800 mesh, sieving obtains gypsum
Powder；
(3) in parts by weight, nano medical stone is taken, after rinsing 5-10min with clear water, naturally dry, is placed in pulverizer
1000-1200 mesh is crushed to, sieving obtains nano medical stone powder；
(4) mixed powder is prepared：Mica powder, land plaster, nano medical stone powder after crushing are taken, is placed in mixer, middling speed is mixed
After closing 20-30min, mixed powder is obtained；
(5) polyvinyl alcohol resin 1-2 parts, sepiolite fibre 0.5-1 parts are added into 35-40 DEG C of heating for dissolving in 8-10 part water
Completely, pH is then adjusted to 6.5-7.5, adds mixed powder and sodium gluconate 1-2 parts, carboxymethyl chitosan 0.2-0.4 parts are simultaneously
Mixed at high speed is uniform, obtains polyvinyl alcohol resin mixed liquor；
(6) by adhesive 5-11 parts, atlapulgite 15-20 parts, ceramic 5-10 parts, modified meerschaum particle 2-3 parts,
N hydroxymethyl acrylamide 0.3-0.5 parts add 70-80 DEG C of reaction 3-5h in container jointly, add 2-9 parts step (5) and obtain
Polyvinyl alcohol resin mixed liquor stirred at same temperature, lauric monoglyceride 0.3-0.5 parts, pungent are added after cooling
Glycerol decanoate 0.3-0.5 parts, asbestos wool 0.1-0.3 parts stirring 10-15min, obtain calligraphy and painting mounting anti-blushing agent base-material, standby；
(7) butyl titanate 0.5-3 parts, modified oxidized polyethylene 0.5-3 parts are poured into retort, then into retort
Calligraphy and painting mounting anti-blushing agent base-material is added, is uniformly mixed, stands 3-5h；
(8) Tissuemat E 3-5 parts, polyvinyl chloride emulsion 8-15 parts, step (7) material are added in retort again, stirring
It is well mixed, it is placed in after mixed material is placed in into retort sealing in water-bath, heating water bath to constant temperature underwater curing after 80 DEG C
1-3h, produce calligraphy and painting mounting anti-blushing agent.
It is highly preferred that the adhesive is epoxy resin adhesive；Specially epoxy resin E-51, epoxy resin E-
44th, the one or more in double amino-phenol epoxy resin and butadiene bifunctional epoxy resin.
Calligraphy and painting mounting anti-blushing agent application method is：
After 60-100 DEG C of calligraphy and painting mounting anti-blushing agent is heated into diluent liquid, treat that liquid cooling is directly brushed to 40-60 DEG C
The material such as mounting formation plate, mounting frame and mounting thin,tough silk, paper, brocade, thin silk fabric.
The present invention is advantageous in that：Acted synergistically between each component of the present invention, obtained calligraphy and painting mounting anti-blushing agent
Can be stable, there is good wet-heat resisting, ageing-resistant performance, bonding strength reaches more than 1000N/m, Punctured Strength up to 40J with
On, solve caused hydraulic performance decline after traditional anti-blushing agent moisture absorption, the problems such as layering of coming unglued, water resistance decline；And make
Preparation Method is simple, and process conditions are easily realized, obtains stable performance, the calligraphy and painting mounting anti-blushing agent of resting period length.
Embodiment：
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific embodiment is closed, the present invention is expanded on further.
Embodiment 1：
A kind of calligraphy and painting mounting anti-blushing agent：
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of calligraphy and painting mounting anti-blushing agent：
The calligraphy and painting mounting anti-blushing agent includes each component of following parts by weight：5 parts of adhesive, 15 parts of atlapulgite, ceramics
5 parts of micro mist, 2 parts of modified meerschaum particle, 1 part of polyvinyl alcohol resin, 0.5 part of sepiolite fibre, N hydroxymethyl acrylamide 0.3
Part, 0.1 part of asbestos wool, 25 parts of mica powder, 20 parts of land plaster, 0.5 part of butyl titanate, modified oxidized polyethylene 0.6 part, nanometer
2 parts of medical stone powder, 3 parts of Tissuemat E, 0.4 part of lauric monoglyceride, 0.35 part of Glycerin, mixed triester with caprylic acid capric acid, polyvinyl chloride emulsion 8
Part, 1 part of sodium gluconate, 0.2 part of carboxymethyl chitosan.
Wherein described modified meerschaum particle is made from the following raw materials in parts by weight：2 parts of sepiolite particle, vinyl chloride 10
Part, 3 parts of acrylic acid, 0.5 part of carboxymethyl cellulose, 0.3 part of trifluoro propyl methyl cyclotrisiloxane, 0.01 part of potassium peroxydisulfate, receive
1 part of titanium dioxide of rice, 0.05 part of lauryl sodium sulfate, 20 parts of water；The preparation method of modified meerschaum particle is first by 12
Sodium alkyl sulfate and carboxymethyl cellulose are added to the water stirring until being completely dissolved, and then add sepiolite particle, vinyl chloride, third
Olefin(e) acid, nano titanium oxide and trifluoro propyl methyl cyclotrisiloxane 1000rpm/min stirring 0.5h, are eventually adding remaining raw material
80 DEG C of reaction 2h, are produced after cooling.
The modified oxidized polyethylene is made up of the raw material of following parts by weight：10 parts of oxidic polyethylene, the poly- dimension of crosslinking
0.5 part of ketone, 0.05 part of HPMA, 1.5 parts of hydroxyethyl cellulose, 5 parts of water, its preparation method are：To the poly- second of oxidation
PVPP and HPMA are added in alkene, 115 DEG C of insulation grinding 15min are warming up under grinding, add hydroxyl second
Base cellulose, continue, in 120 DEG C of insulation grinding 15min, to be then transferred to sealing and standing 1h in 0-5 DEG C of environment, and add 50 DEG C of water,
It is sufficiently mixed and stands 30min after 50 DEG C of insulations, gained mixed liquor is sent into spray dryer, dries gained particle through Ultramicro-powder
Micro mist is made in broken machine, as modified oxidized polyethylene.
A kind of calligraphy and painting mounting anti-blushing agent, step are as follows：
(1) in parts by weight, after taking mica to clean, it is placed in pulverizer and is crushed to 600 mesh, sieving obtains mica powder；
(2) in parts by weight, choose dry gypsum to be placed in pulverizer, be crushed to 700 mesh, sieving obtains land plaster；
(3) in parts by weight, nano medical stone is taken, after rinsing 5min with clear water, naturally dry, is placed in pulverizer and crushes
To 1000 mesh, sieving obtains nano medical stone powder；
(4) mixed powder is prepared：Mica powder, land plaster, nano medical stone powder after crushing are taken, is placed in mixer, middling speed is mixed
After closing 20min, mixed powder is obtained；
(5) completely, then 40 DEG C in 1 part of polyvinyl alcohol resin, sepiolite fibre 0.5 part of addition, 8 parts of water are dissolved by heating
PH is adjusted to 7.0, adds 1 part of mixed powder and sodium gluconate, simultaneously mixed at high speed is uniform for 0.2 part of carboxymethyl chitosan, obtains poly- second
Enol resin mixture liquor；
(6) by 5 parts of adhesive, 15 parts of atlapulgite, 5 parts of ceramic, 2 parts of modified meerschaum particle, N- methylols third
0.3 part of acrylamide is common to add 80 DEG C of reaction 3h in container, adds the polyvinyl alcohol resin mixed liquor that 2 parts of steps (5) obtain
Stirred at same temperature, 0.4 part of lauric monoglyceride, 0.35 part of Glycerin, mixed triester with caprylic acid capric acid, asbestos wool are added after cooling
0.1 part of stirring 15min, obtains calligraphy and painting mounting anti-blushing agent base-material, standby；
(7) 0.5 part of butyl titanate, 0.6 part of modified oxidized polyethylene are poured into retort, then added into retort
Calligraphy and painting mounting anti-blushing agent base-material, is uniformly mixed, and stands 3h；
(8) 3 parts of Tissuemat E, 8 parts of polyvinyl chloride emulsion, step (7) material are added in retort again, are stirred
It is even, it is placed in after mixed material is placed in into retort sealing in water-bath, heating water bath produces to constant temperature underwater curing 3h after 80 DEG C
Calligraphy and painting mounting anti-blushing agent.
It is highly preferred that the adhesive is epoxy resin adhesive；Specially epoxy resin E-51, epoxy resin E-
44th, the one or more in double amino-phenol epoxy resin and butadiene bifunctional epoxy resin.
Calligraphy and painting mounting anti-blushing agent application method is：
By calligraphy and painting mounting anti-blushing agent, 80 DEG C are heated into diluent liquid, after treat that liquid cooling is smooth to 45 DEG C of direct brushing mountings
The material such as plate, mounting frame and mounting thin,tough silk, paper, brocade, thin silk fabric.
Embodiment 2：A kind of calligraphy and painting mounting anti-blushing agent：
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of calligraphy and painting mounting anti-blushing agent：
The calligraphy and painting mounting anti-blushing agent includes each component of following parts by weight：11 parts of adhesive, 20 parts of atlapulgite, ceramics
10 parts of micro mist, 3 parts of modified meerschaum particle, 2 parts of polyvinyl alcohol resin, 1 part of sepiolite fibre, N hydroxymethyl acrylamide 0.5
Part, 0.3 part of asbestos wool, 26 parts of mica powder, 215 parts of land plaster, 3 parts of butyl titanate, modified oxidized polyethylene 1.3 part, nanometer
4 parts of medical stone powder, 5 parts of Tissuemat E, 0.5 part of lauric monoglyceride, 0.5 part of Glycerin, mixed triester with caprylic acid capric acid, polyvinyl chloride emulsion 9
Part, 2 parts of sodium gluconate, 0.4 part of carboxymethyl chitosan.
Wherein described modified meerschaum particle is made from the following raw materials in parts by weight：4 parts of sepiolite particle, vinyl chloride 15
Part, 5 parts of acrylic acid, 1 part of carboxymethyl cellulose, 0.5 part of trifluoro propyl methyl cyclotrisiloxane, 0.02 part of potassium peroxydisulfate, nanometer
2 parts of titanium dioxide, 0.1 part of lauryl sodium sulfate, 20 parts of water；The preparation method of modified meerschaum particle is first by dodecyl
Sodium sulphate and carboxymethyl cellulose are added to the water stirring until being completely dissolved, and then add sepiolite particle, vinyl chloride, propylene
Acid, nano titanium oxide and trifluoro propyl methyl cyclotrisiloxane 1000r/min stirring 1h, it is anti-to be eventually adding 80 DEG C of remaining raw material
4h is answered, is produced after cooling.
The modified oxidized polyethylene is made up of the raw material of following parts by weight：15 parts of oxidic polyethylene, the poly- dimension of crosslinking
1 part of ketone, 0.1 part of HPMA, 0.5 part of hydroxyethyl cellulose, 5 parts of water, its preparation method are：Into oxidic polyethylene
PVPP and HPMA are added, 120 DEG C of insulation grinding 15min are warming up under grinding, add ethoxy fibre
Dimension element, continue, in 120 DEG C of insulation grinding 15min, to be then transferred to sealing and standing 1h in 0-5 DEG C of environment, and add 55 DEG C of water, fully
Mixing stands 30min after 50 DEG C of insulations, and gained mixed liquor is sent into spray dryer, dries gained particle through micronizer
Micro mist is made, as modified oxidized polyethylene.
A kind of calligraphy and painting mounting anti-blushing agent, step are as follows：
(1) in parts by weight, after taking mica to clean, it is placed in pulverizer and is crushed to 700 mesh, sieving obtains mica powder；
(2) in parts by weight, choose dry gypsum to be placed in pulverizer, be crushed to 700 mesh, sieving obtains land plaster；
(3) in parts by weight, nano medical stone is taken, after rinsing 10min with clear water, naturally dry, is placed in pulverizer inner powder
1000 mesh are broken to, sieving obtains nano medical stone powder；
(4) mixed powder is prepared：Mica powder, land plaster, nano medical stone powder after crushing are taken, is placed in mixer, middling speed is mixed
After closing 30min, mixed powder is obtained；
(5) 2 parts of polyvinyl alcohol resin, 1 part of sepiolite fibre are added into 35 DEG C of heating for dissolving in 8 parts of water completely, then will
PH is adjusted to 6.5, adds 2 parts of mixed powder and sodium gluconate, simultaneously mixed at high speed is uniform for 0.4 part of carboxymethyl chitosan, obtains polyethylene
Alcohol resin mixed liquor；
(6) by 11 parts of adhesive, 20 parts of atlapulgite, 10 parts of ceramic, 3 parts of modified meerschaum particle, N- methylols
0.5 part of acrylamide is common to add 80 DEG C of reaction 5h in container, adds the polyvinyl alcohol resin mixing that 5 parts of steps (5) obtain
Liquid is stirred at same temperature, and 0.5 part of lauric monoglyceride, 0.5 part of Glycerin, mixed triester with caprylic acid capric acid, asbestos wool are added after cooling
0.3 part of stirring 15min, obtains calligraphy and painting mounting anti-blushing agent base-material, standby；
(7) 3 parts of butyl titanate, 1.3 parts of modified oxidized polyethylene are poured into retort, then word is added into retort
Mounting anti-blushing agent base-material is drawn, is uniformly mixed, stands 5h；
(8) 5 parts of Tissuemat E, 9 parts of polyvinyl chloride emulsion, step (7) material are added in retort again, are stirred
It is even, it is placed in after mixed material is placed in into retort sealing in water-bath, heating water bath to constant temperature underwater curing 1-3h after 80 DEG C, i.e.,
Obtain calligraphy and painting mounting anti-blushing agent.
It is highly preferred that the adhesive is epoxy resin adhesive；Specially epoxy resin E-51, epoxy resin E-
44th, the one or more in double amino-phenol epoxy resin and butadiene bifunctional epoxy resin.
Calligraphy and painting mounting anti-blushing agent application method is：
After 90 DEG C of calligraphy and painting mounting anti-blushing agent is heated into diluent liquid, treat that liquid cooling is smooth to 40 DEG C of direct brushing mountings
The material such as plate, mounting frame and mounting thin,tough silk, paper, brocade, thin silk fabric.
To carrying out experiment investigation respectively in embodiment provided by the invention, by the calligraphy and painting prepared by embodiment 1 and embodiment 2
Mounting anti-blushing agent is investigated, and is detected with reference to GJB-2493-1995, with reference to shown in table 1, as a result such as table 2；
The calligraphy and painting mounting anti-blushing agent reference standard of table 1
| Project | Index |
| Moisture | It is not muddy, not stratified |
| Volatility≤ | 14 |
| Gelation >= | 50 |
| Albefaction | Not into white haze and nonluminous spot |
The calligraphy and painting mounting anti-blushing agent results of property of table 2
Shown by result above：Calligraphy and painting mounting anti-blushing agent prepared by the embodiment of the present invention, moistureproof performance is better than common mark
Standard, the calligraphy and painting mounting anti-blushing agent prepared by the present invention are applied to mounting frame etc., and moisture effect is more preferably；The calligraphy and painting mounting anti-blushing agent is
Gallery protection against the tide is brought convenience, effective practical effect, and price is low, and practicality is good, reduces production and maintenance cost.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (5)
- A kind of 1. calligraphy and painting mounting anti-blushing agent, it is characterised in that：Calligraphy and painting mounting anti-blushing agent includes each component of following parts by weight：Gluing Agent 5-11 parts, atlapulgite 15-20 parts, ceramic 5-10 parts, modified meerschaum particle 2-3 parts, polyvinyl alcohol resin 1-2 Part, sepiolite fibre 0.5-1 parts, N hydroxymethyl acrylamide 0.3-0.5 parts, asbestos wool 0.1-0.3 parts, mica powder 25-35 parts, Land plaster 20-25 parts, butyl titanate 0.5-3 parts, modified oxidized polyethylene 0.5-3 parts, nano medical stone powder 2-4 parts, poly- second Alkene wax 3-5 parts, lauric monoglyceride 0.3-0.5 parts, Glycerin, mixed triester with caprylic acid capric acid 0.3-0.5 parts, polyvinyl chloride emulsion 8-15 parts, Portugal Grape sodium saccharate 1-2 parts, carboxymethyl chitosan 0.2-0.4 parts.
- 2. calligraphy and painting mounting anti-blushing agent according to claim 1, it is characterised in that：The modified meerschaum particle is by following heavy The raw material of amount part is made：Sepiolite particle 2-4 parts, vinyl chloride 10-15 parts, acrylic acid 3-5 parts, carboxymethyl cellulose 0.5-1 parts, Trifluoro propyl methyl cyclotrisiloxane 0.3-0.5 parts, potassium peroxydisulfate 0.01-0.02 parts, nano titanium oxide 1-2 parts, dodecane Base sodium sulphate 0.05-0.1 parts, water 20-30 parts；The preparation method of modified meerschaum particle is first by lauryl sodium sulfate and carboxylic Methylcellulose is added to the water stirring until being completely dissolved, and then adds sepiolite particle, vinyl chloride, acrylic acid, nano-silica Change titanium and trifluoro propyl methyl cyclotrisiloxane 800-1000rpm/min stirring 0.5-1h, be eventually adding 70-80 DEG C of remaining raw material 2-4h is reacted, is produced after cooling.
- 3. calligraphy and painting mounting anti-blushing agent according to claim 2, it is characterised in that：The modified oxidized polyethylene is by as follows The raw material of parts by weight is made：Oxidic polyethylene 10-15 parts, PVPP 0.5-1 parts, HPMA 0.05-0.1 Part, hydroxyethyl cellulose 0.5-3 parts, water 5-8 parts；Its preparation method is：PVPP and water are added into oxidic polyethylene HPMA is solved, 115-120 DEG C of insulation grinding 15min is warming up under grinding, hydroxyethyl cellulose is added, continues in 115- 120 DEG C of insulation grinding 15min, are then transferred to sealing and standing 1h in 0-5 DEG C of environment, and add 50-55 DEG C of water, be sufficiently mixed after 50-55 DEG C of insulation stands 30min, and gained mixed liquor is sent into spray dryer, dries gained particle and is made through micronizer Micro mist, as modified oxidized polyethylene.
- 4. calligraphy and painting mounting anti-blushing agent according to claim 3, it is characterised in that：Calligraphy and painting mounting anti-blushing agent, step are as follows：(1) in parts by weight, after taking mica to clean, it is placed in pulverizer and is crushed to 600-800 mesh, sieving obtains mica powder；(2) in parts by weight, choose dry gypsum to be placed in pulverizer, be crushed to 700-800 mesh, sieving obtains land plaster；(3) in parts by weight, nano medical stone is taken, after rinsing 5-10min with clear water, naturally dry, is placed in pulverizer and crushes To 1000-1200 mesh, sieving obtains nano medical stone powder；(4) mixed powder is prepared：Mica powder, land plaster, nano medical stone powder after crushing are taken, is placed in mixer, middling speed mixing 20- After 30min, mixed powder is obtained；(5) 35-40 DEG C in polyvinyl alcohol resin 1-2 parts, sepiolite fibre 0.5-1 parts addition 8-10 part water has been dissolved by heating Entirely, pH is then adjusted to 6.5-7.5, adds mixed powder and sodium gluconate 1-2 parts, carboxymethyl chitosan 0.2-0.4 parts are simultaneously high Speed is well mixed, obtains polyvinyl alcohol resin mixed liquor；(6) by adhesive 5-11 parts, atlapulgite 15-20 parts, ceramic 5-10 parts, modified meerschaum particle 2-3 parts, N- hydroxyls Methacrylamide 0.3-0.5 parts add in container 70-80 DEG C of reaction 3-5h jointly, add 2-9 parts step (5) obtain it is poly- Vinyl alcohol resin mixed liquor is stirred at same temperature, and lauric monoglyceride 0.3-0.5 parts, pungent capric acid are added after cooling Glyceride 0.3-0.5 parts, asbestos wool 0.1-0.3 parts stirring 10-15min, obtain calligraphy and painting mounting anti-blushing agent base-material, standby；(7) butyl titanate 0.5-3 parts, modified oxidized polyethylene 0.5-3 parts are poured into retort, then added into retort Calligraphy and painting mounting anti-blushing agent base-material, is uniformly mixed, and stands 3-5h；(8) Tissuemat E 3-5 parts, polyvinyl chloride emulsion 8-15 parts, step (7) material are added in retort, be stirred again Uniformly, it is placed in after mixed material being placed in into retort sealing in water-bath, heating water bath to constant temperature underwater curing 1-3h after 80 DEG C, Produce calligraphy and painting mounting anti-blushing agent.
- A kind of 5. calligraphy and painting mounting anti-blushing agent, it is characterised in that：Calligraphy and painting mounting anti-blushing agent application method is：After 60-100 DEG C of calligraphy and painting mounting anti-blushing agent is heated into diluent liquid, treat liquid cooling to 40-60 DEG C of direct brushing mounting The material such as formation plate, mounting frame and mounting thin,tough silk, paper, brocade, thin silk fabric.