- Pending
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B11/00—Calcium sulfate cements
- C04B11/002—Mixtures of different CaSO4-modifications, e.g. plaster of Paris and anhydrite, used as cements
Abstract
一种石膏建筑材料,属于建筑领域,包括5%‑70%半水石膏和无水Ⅲ型石膏的混合物,20%‑80%的无水Ⅱ型石膏,其他成分为杂质;所述的半水石膏和无水Ⅲ型石膏的混合物,是将磷石膏煅烧温度在200°C‑360°C时产生的无水Ⅲ型石膏与130°C‑200°C时产生的半水石膏的混合物;这是在磷石膏煅烧过程中形成的混合物;所述的无水Ⅱ型石膏,是将磷石膏煅烧到360°C时产生的无水Ⅱ型石膏;所述的杂质是磷石膏煅烧时磷石膏内部含有的其他物质经煅烧后形成的杂质;具有强度高,耐水性强,凝固速度快,成本低的特点。
Description
技术领域
本发明属于建筑领域,特别涉及一种用于建筑工程材料的石膏混合材料。
背景技术
石膏建筑行业常用的一种建筑材料,现有的建筑石膏,大多采用β型半水石膏和α型半水石膏;其中,β型石膏的生产方式主要是采用将含有两个结晶水的二水石膏煅烧到160°C-200°C,使二水石膏脱去大部分结晶水,形成β型半水石膏;α型半水石膏是采用将含有两个结晶水的二水石膏通过高压或者蒸煮的方式将二水石膏加热到135°C-200°C使其脱去大部分结晶水,生产α型半水石膏;半水石膏具有无收缩、微膨胀、无污染、凝固快、能够再生利用的性能的绿色建筑材料,但是其耐水性差,强度低,因此,阻碍了石膏作为绿色建筑材料的推广和应用。
发明内容
随针对现有建筑石膏存在的上述问题,本发明提出一种石膏建筑材料,其特征在于:包括5%-70%半水石膏和无水Ⅲ型石膏的混合物,20%-80%的无水Ⅱ型石膏,其他成分为杂质;所述的半水石膏和无水Ⅲ型石膏的混合物,是将磷石膏煅烧温度在200°C-360°C时产生的无水Ⅲ型石膏与130°C-200°C时产生的半水石膏的混合物;这是在磷石膏煅烧过程中形成的混合物;所述的无水Ⅱ型石膏,是将磷石膏煅烧到360°C时产生的无水Ⅱ型石膏;所述的杂质是磷石膏煅烧时磷石膏内部含有的其他物质经煅烧后形成的杂质;所述的半水石膏、无水Ⅱ型石膏、无水Ⅲ型石膏以及杂质都是粉状。
有益效果
本发明的有益效果在于,强度高,实验证明能够达到现有建筑石膏的3-4倍,耐水性是β型半水石膏的3-5倍,能够更好的更广泛的将石膏用于建筑工程。
具体实施方式
为了进一部说明本发明的技术方案,现以不同的应用方式为例,说明本发明的具体实施方式;实施例一,选用半水及无水Ⅲ型石膏混合物为10%-60%,无水Ⅱ型石膏不低于20%,以上皆为磷石膏煅烧后的粉状体,将其混合,形成早强型石膏建材,其特点,是早期强度高,但是耐水软化系数较低,应用时加水根据不同用途,将其搅拌成不同稠度,即可应用。
实施例二,选用半水及无水Ⅲ型石膏混合物1%-10%,无水Ⅱ型石膏不低于80%(其中包括杂质),因为在磷石膏煅烧中,杂质是伴随着煅烧的进行而混杂在石膏粉中的,难以与石膏粉分离;将其混合搅拌,即可根据不同用途使用,其特点是,早期强度低,凝固时间长,水化速度较慢,耐水性能好,软化系数高。
实施例三,将半水石膏和无水Ⅱ型石膏粉中加入5%的水泥,10%-20%的矿粉,1%-5%的减水剂,混合后能够制作高强度耐水石膏材料,其性能与水泥相似,但是不会收缩,避免了使用水泥造成的开裂和凝固时间长的缺陷。
以上各种配比是根据不同的使用场所而做适当的调整,混合后的石膏建材可以用作制作砌块,喷筑墙体,装饰板,隔墙板,功能板,风烟道,装饰线条,还可以做砌筑、抹灰、自流平等预拌砂浆,因为其价格低,是由磷石膏废料采用在先申请专利(一种磷石膏的煅烧方法)煅烧而成,所有其成本低;由于其凝固速度快,所有施工速度块,效率高;由于其强度高,所以能够代替水泥施工,并且不存在收缩问题。
Claims (1)
1.一种石膏建筑材料,其特征在于:包括5%-70%半水石膏和无水Ⅲ型石膏的混合物,20%-80%的无水Ⅱ型石膏,其他成分为杂质;所述的半水石膏和无水Ⅲ型石膏的混合物,是将磷石膏煅烧温度在200°C-360°C时产生的无水Ⅲ型石膏与130°C-200°C时产生的半水石膏的混合物;这是在磷石膏煅烧过程中形成的混合物;所述的无水Ⅱ型石膏,是将磷石膏煅烧到360°C时产生的无水Ⅱ型石膏;所述的杂质是磷石膏煅烧时磷石膏内部含有的其他物质经煅烧后形成的杂质;所述的半水石膏、无水Ⅱ型石膏、无水Ⅲ型石膏以及杂质都是粉状。
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CN201711233421.9A CN107793055A (zh) | 2017-11-30 | 2017-11-30 | 一种石膏建筑材料 |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CN201711233421.9A CN107793055A (zh) | 2017-11-30 | 2017-11-30 | 一种石膏建筑材料 |
Publications (1)
Publication Number | Publication Date |
---|---|
CN107793055A true CN107793055A (zh) | 2018-03-13 |
Family
ID=61537224
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
CN201711233421.9A Pending CN107793055A (zh) | 2017-11-30 | 2017-11-30 | 一种石膏建筑材料 |
Country Status (1)
Country | Link |
---|---|
CN (1) | CN107793055A (zh) |
Cited By (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN108383464A (zh) * | 2018-04-09 | 2018-08-10 | 郑州三迪建筑科技有限公司 | 磷石膏隧道防火浆料 |
CN108775120A (zh) * | 2018-08-08 | 2018-11-09 | 郑州三迪建筑科技有限公司 | 一种网面石膏板 |
WO2020029136A1 (zh) * | 2018-08-08 | 2020-02-13 | 郑州三迪建筑科技有限公司 | 一种网面石膏板 |
CN113996411A (zh) * | 2021-11-30 | 2022-02-01 | 泰山石膏有限公司 | 一种建筑石膏促凝剂的生产装置及促凝剂的制备方法和应用 |
Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN101096295A (zh) * | 2006-06-30 | 2008-01-02 | 张冯 | 干法氟石膏与建筑石膏混合料 |
CN102976703A (zh) * | 2012-12-10 | 2013-03-20 | 重庆建大建筑材料有限公司 | 耐水型磷石膏抹灰砂浆干粉料 |
CN104310823A (zh) * | 2014-09-26 | 2015-01-28 | 青岛精益信电子技术有限公司 | 一种磷石膏改性方法 |
CN106745162A (zh) * | 2017-02-23 | 2017-05-31 | 北京工业大学 | 一种孔隙状半水石膏的制备方法 |
-
2017
- 2017-11-30 CN CN201711233421.9A patent/CN107793055A/zh active Pending
Patent Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN101096295A (zh) * | 2006-06-30 | 2008-01-02 | 张冯 | 干法氟石膏与建筑石膏混合料 |
CN102976703A (zh) * | 2012-12-10 | 2013-03-20 | 重庆建大建筑材料有限公司 | 耐水型磷石膏抹灰砂浆干粉料 |
CN104310823A (zh) * | 2014-09-26 | 2015-01-28 | 青岛精益信电子技术有限公司 | 一种磷石膏改性方法 |
CN106745162A (zh) * | 2017-02-23 | 2017-05-31 | 北京工业大学 | 一种孔隙状半水石膏的制备方法 |
Cited By (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN108383464A (zh) * | 2018-04-09 | 2018-08-10 | 郑州三迪建筑科技有限公司 | 磷石膏隧道防火浆料 |
CN108775120A (zh) * | 2018-08-08 | 2018-11-09 | 郑州三迪建筑科技有限公司 | 一种网面石膏板 |
WO2020029136A1 (zh) * | 2018-08-08 | 2020-02-13 | 郑州三迪建筑科技有限公司 | 一种网面石膏板 |
CN113996411A (zh) * | 2021-11-30 | 2022-02-01 | 泰山石膏有限公司 | 一种建筑石膏促凝剂的生产装置及促凝剂的制备方法和应用 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CN107793055A (zh) | 一种石膏建筑材料 | |
CN101671133B (zh) | 一种改性低碱度硫铝酸盐水泥 | |
CN100534945C (zh) | 化工石膏建材及其制造方法 | |
RU2547866C2 (ru) | Добавка для гидравлического вяжущего материала на основе клинкера из белита и сульфоалюмината-феррита кальция | |
RU2014146785A (ru) | Размерностабильные геополимерные композиции и способ | |
CN105330182A (zh) | 一种白色快凝快硬高贝利特硫铝酸盐水泥熟料、应用及其生产工艺 | |
CN104355657B (zh) | 防腐加气砖 | |
CN103332892A (zh) | 一种工业废渣干混砂浆 | |
CN102765906B (zh) | 一种利用萤石矿渣生产加气空心砖方法 | |
CN109824329B (zh) | 自密实找平混凝土及其制备方法和用途 | |
CN108117356A (zh) | 一种工业废料制高强度干混砂浆 | |
CN105084852A (zh) | 一种磷石膏基复合保温砂浆的制备方法 | |
RU2014138999A (ru) | Способ изготовления цемента, строительных растворов, бетонных композиций, содержащих наполнитель на основе карбоната кальция, содержащий кремнийорганическое вещество, причем вышеупомянутый "смешанный наполнитель" обработан суперпластификатором, получаемые цементные композиции и цементные материалы и их применения | |
CN102964108B (zh) | 泡沫沥青钢渣混合料及其制备方法 | |
CN104291729A (zh) | 一种混凝土引气剂及其制备方法 | |
CN105481321A (zh) | 一种改性石膏基地坪砂浆及其制备和应用 | |
Negmatov et al. | Setting Time of Powder Composites and the Effect of Chemical Reagents | |
CN109704693B (zh) | 一种硫铝酸盐水泥基自密实砂浆及其使用方法 | |
CN103708762A (zh) | 一种蒸压加气混凝土用稳定增强剂 | |
WO2013046000A1 (en) | Method for the production of a building material | |
CN111807739A (zh) | 一种快凝水镁石-磷酸盐基胶凝材料及其制备方法和应用 | |
CN1528696A (zh) | 石膏尾矿砖的制造方法 | |
DE102009005610B3 (de) | Verfahren zur Herstellung eines hydraulischen Bindemittels | |
Munavvarkhanov et al. | The chemical reagents influence on the regulation of the powder composite materials setting time for construction purposes | |
CN107586086A (zh) | 一种高强度加气砖的制备方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
PB01 | Publication | ||
PB01 | Publication | ||
SE01 | Entry into force of request for substantive examination | ||
SE01 | Entry into force of request for substantive examination | ||
RJ01 | Rejection of invention patent application after publication |
Application publication date: 20180313 |
|
RJ01 | Rejection of invention patent application after publication |