CN107778650A - Polyolefine resin composition and using its vistanex formed body and use its dust catcher - Google Patents
Polyolefine resin composition and using its vistanex formed body and use its dust catcher Download PDFInfo
- Publication number
- CN107778650A CN107778650A CN201710719953.7A CN201710719953A CN107778650A CN 107778650 A CN107778650 A CN 107778650A CN 201710719953 A CN201710719953 A CN 201710719953A CN 107778650 A CN107778650 A CN 107778650A
- Authority
- CN
- China
- Prior art keywords
- vistanex
- hollow member
- resin composition
- composition
- polyolefine resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to polyolefine resin composition and using its vistanex formed body and use its dust catcher.Polyolefine resin composition (50) contains:Vistanex (51), granular hollow member (52) and elastomer components (53).The surface of hollow member (52) has non-compatibility to vistanex (51).And then polyolefine resin composition (50) is not contained for improving the affine composition of hollow member of the surface of hollow member (52) to the compatibility of vistanex (51).Thus, there is provided:Family's electrical article is with polyolefine resin composition (50) being used in part, having lightweight and excellent impact resistance.
Description
Technical field
This disclosure relates to it is suitable for the polyolefine resin composition of the resin-formed body of dust catcher part and uses it
Vistanex formed body and use its dust catcher.
Background technology
It is excellent for the mechanical strength and molding processibility of the polyolefine resin composition of principal component with polypropylene etc., and be honest and clean
Valency and light weight.Therefore, polyolefine resin composition is widely used in various fields.
Particularly, it is in the field of electrical article, it is desirable to lightweight.Therefore, the shaping of polyolefine resin composition is passed through
The obtained part of resin-formed body (vistanex formed body) all the time as family's electrical article is widely used.
In recent years, in the field of family's electrical article, further lightweight is sought.Therefore, for example carried out making polyene in the past
The wall thickness of hydrocarbon resin formed body reduces, reduces the research such as weight.
However, when wall thickness becomes too small, there is the worry of the reductions such as rigidity or the impact resistance of vistanex formed body.Cause
This, in the past, such as known in No. 5542733 publications of Japanese Patent No. (following, be denoted as " patent document 1 ") etc. has:To polyolefin
Resin-formed body, various fillers are added to suppress the reduction of rigidity or impact resistance etc. and realize light-weighted method.Now, make
For filler, such as use the hollow packing for having inorganic system.It should be noted that as representational hollow packing, can enumerate
The hollow packing of glass system.
In the vistanex formed body of patent document 1, as matrix material (mother metal), the polyolefin tree such as polypropylene is used
Fat.Moreover, as hollow packing, formed with the first layer comprising silane coupler and Malaysia is included on the surface of hollow member
Anhydride modified polyolefin resin and the second layer combined with first layer.That is, disclose and hollow packing is dispersed with vistanex
Composition vistanex formed body.
That is, in the vistanex formed body of patent document 1, the surface for making hollow packing is two-layer structure.Moreover, especially
It is the maleic anhydride modified vistanex by being used as the second layer, realizing the breakage of hollow packing prevents the raising of effect.Enter
And by making the surface of hollow packing be two-layer structure, make to improve with the adaptation of the vistanex as matrix material.Also
Disclose, it is possible thereby to improve the intensity of vistanex formed body.
But, it is known that using technology disclosed above, it can not fully improve the impact resistance of vistanex formed body.
Particularly, in use, user holds at least a portion (handle part) and used, hand takes family's electrical article of type
In the case of, in use, there is the worry of the part in addition to handle part of an electrical article and the object collision of surrounding.According to using feelings
Condition, have from the hand of user departs from and worry that family's electrical article is fallen.For example, in the case that family's electrical article is dust catcher, dust suction
Inhalation apparatus (suction nozzle) of device etc. has the possibility with the collision of various objects in use.
Therefore, the hand of the possibility fallen when having the collision with other objects, using is taken in family's electrical article of type etc., for
The part easily collided, it is desirable to higher than common impact resistance.
However, in the case of the vistanex formed body of patent document 1, hollow packing and matrix material (polyolefin tree
Fat) adaptation it is high, therefore, there is the worry that impact resistance reduces.Thus, for example there is inhalation apparatus that can not realize dust catcher etc.
The worry of required sufficient impact resistance.
The content of the invention
The disclosure provides:Be suitable as an electrical article part, polyolefine resin composition and use its polyolefin
Resin-formed body and the dust catcher using vistanex formed body.
The polyolefine resin composition of the disclosure contains:Vistanex, granular hollow member and elastomer components.
It is following to form:The surface of hollow member has non-compatibility to vistanex, and the polyolefine resin composition does not contain
Hollow member is affine composition.
According to above-mentioned composition, polyolefine resin composition as the vistanex of matrix material (mother metal) for being mixed with
Hollow member and elastomer components.Now, hollow member does not contain the affine composition of hollow member, therefore, to vistanex not
Show compatibility.
Therefore, by the mixing of hollow member, the lightweight of polyolefine resin composition can be carried out.And then hollow structure
The surface of part is non-compatibility, accordingly, it is difficult to vistanex set.Therefore, it is made up of polyolefine resin composition poly-
Even if olefin resin formed body applies impact, the interface of hollow member is also easily slided relative to vistanex.Thus, with poly-
Olefin resin compared with the vistanex formed body that hollow member set is formed, can be greatly reduced using hollow member as rise
The possibility put and cracked in vistanex formed body.
And then polyolefine resin composition contains elastomer components.Elastomer components, can be with by being combined with hollow member
Impact resistance is improved tremendously.As a result, using the vistanex formed body of polyolefine resin composition can realize into
The lightweight of one step and obtain excellent impact resistance.Therefore, can be by polyolefine resin composition particularly suitable for requiring
The vistanex formed body of impact resistance is family's electrical article part etc..
In addition, the vistanex formed body of the disclosure is at least uses the household electrical appliances system that forms of polyolefine resin composition
Product part.As vistanex formed body, such as the inhalation apparatus of dust catcher can be enumerated etc..
In addition, the standby part being made up of vistanex formed body of the dust catcher of the disclosure.
According to the composition of the disclosure, it can obtain being suitable as an electrical article part, lightweight can be realized and excellent
Impact resistance polyolefine resin composition.Thus, it is possible to realize:Seek lightweight and it is high it is impact resistance, using poly-
The vistanex formed body of olefin resin composition and the dust catcher using vistanex formed body.
Brief description of the drawings
Figure 1A is the sectional view of the schematical composition for the polyolefine resin composition for showing embodiment of the present disclosure.
Figure 1B is the sectional view for the schematical composition for showing conventional polyolefine resin composition.
Fig. 2 is the vistanex formed body for showing to possess embodiment of the present disclosure as inhalation apparatus, paper bag type
Tank (canister) type dust catcher composition the stereogram of one.
Fig. 3 is the vistanex formed body for showing to possess embodiment of the present disclosure as inhalation apparatus, cyclone type
Pot dust catcher composition the stereogram of one.
Fig. 4 is the stereogram of one of the composition for showing the dust catcher possessed inhalation apparatus shown in Fig. 2 or Fig. 3.
Embodiment
Hereinafter, to embodiment of the present disclosure, while referring to the drawings while illustrate.It should be noted that the disclosure not by
The restriction of the embodiment.
(embodiment)
The polyolefine resin composition of the disclosure is used for the vistanex formed body for forming family's electrical article part.
Specifically, the polyolefine resin composition of the disclosure contains:Illustrate individually below, vistanex, particle
The hollow member of shape and elastomer components etc..The surface of hollow member has non-compatibility to vistanex.And then polyolefin
Resin combination is formed as follows:Do not contain for improving the hollow member of the surface of hollow member to the compatibility of vistanex
Affine composition.
[vistanex]
As long as contained vistanex is to make at least one kind of polymerizing olefin monomers in the polyolefine resin composition of the disclosure
The polymer formed is just not particularly limited.As long as typically for make ethene, propylene (propylene), 1- butylene, 1- amylenes, 1- oneself
Polymer obtained from least one kind of polymerization of the alpha-olefins such as alkene, 4-methyl-1-pentene, 1- octenes.
As vistanex, such as polyethylene kind, PP type, ethylene copolymer etc. can be enumerated.As specific
Polyethylene kind, high density polyethylene (HDPE) (HDPE), low density polyethylene (LDPE) (LDPE), straight-chain low density polyethylene can be enumerated
(LLDPE), ultra-low density polyethylene (VLDPE, ULDPE) etc..As PP type, homo-polypropylene, random poly- third can be enumerated
Alkene, block polypropylene etc..As ethylene copolymer, ethylene propylene copolymer, Ethylene Vinyl Ester Copolymers, second can be enumerated
Alkene vinyl silane compound copolymer, ethene (methyl) acrylic compounds copolymer etc..Now, vistanex
Can be used only a kind, can also it is appropriately combined two or more and use.
It should be noted that the vistanex as the disclosure, in polyethylene kind, PP type, ethylene copolymer etc.
In, the particularly preferred PP type low with the compatibility of double glazing.
It is contained in addition to polypropylene in random polypropylene or block polypropylene in PP type for PP type
The species of monomer be not particularly limited.For example, can be the alpha-olefins such as ethene, or example removes in ethylene copolymer
Polymerizable compound outside alpha-olefin.In addition, above-mentioned ethylene copolymer can be random copolymer, block copolymer, also may be used
Think graft copolymer.
And then for vistanex such as molecular weight (number-average molecular weight Mn or weight average molecular weight Mw), vertical structure rule
The physical property such as whole property (in the case that there is side chain) or (non-) crystallinity, density (proportion), glass transition point (Tg), without spy
Do not limit.Therefore, the physical property of vistanex can be appropriate according to the species of family's electrical article part as shaping object
Setting.
It should be noted that when wanting to make a house electrical article part lightweight as far as possible, it is preferred that side considers and other things
Property take into account, side selection density (proportion) is tried one's best small vistanex.
[hollow member]
As long as contained hollow member is graininess in the polyolefine resin composition of the disclosure and inside is hollow shape
Just it is not particularly limited.The material of hollow member is not particularly limited, and can typically enumerate inorganic system's material such as glass, ceramics
Material.Specifically, as hollow member, such as the hollow packing (double glazing) of the glass systems such as Glassbubbles can be enumerated
Deng.The surface of double glazing is low (having non-compatibility) to the compatibility of vistanex, therefore, is particularly suitable as this public affairs
The hollow member opened.
In addition, for hollow member physical property such as average grain diameter, compressive resistance, real density, heat endurance, without spy
Do not limit.Therefore, the physical property of hollow member can suitably be set according to family's electrical article as shaping object with the species of part
It is fixed.
In the disclosure, the surface of hollow member is formed as follows as described above:There is non-compatibility to vistanex.
It should be noted that non-compatibility for example can be by making the surface of hollow member and the surface point of vistanex
Contact angle θ (the contact angle θ of water) when not contacted with water quantizes.That is, non-compatibility can be by using the hollow structure of composition
The material of part or the sample that vistanex is shaped to regulation shape, contact angle θ is determined using known contact angle meter,
So as to be quantized to evaluate.
Typically, the vistanex of the disclosure has the characteristic that the contact angle θ of water is fallen into the range of 85~100 °.Example
Such as, representational vistanex is that the contact angle θ of polyacrylic water is fallen into the range of 95~98 °.In addition, the water of polyethylene
Contact angle θ be 88 ° or so.Therefore, it is possible to the water of matrix material (resin) that is used as the vistanex of the disclosure
In the range of as long as contact angle θ is 85~100 °.
On the other hand, if the contact angle θ of the water on the surface of hollow member be less than 10 °, i.e. 0~10 ° in the range of be
Can.And then in the range of the contact angle θ of water is if less than 5 °, i.e. 0~5 °, then more preferably.
Herein, with contact angle θ judge the compatibility to water, i.e. it is hydrophilic whether there is when, typically, by contact angle θ be 30 ° work
Judge for critical value.That is, contact angle θ then judges there is hydrophily if less than 30 °.Moreover, generally, if contact angle θ
For less than 10 °, then judge the surface of measure has very high compatibility (Superhydrophilic) to water.On the other hand, contact angle θ is such as
Fruit is more than 90 °, then judges that determined surface has property, the i.e. water repellency for making water resilience.
It should be noted that hydrophily of the vistanex of the disclosure without the degree for playing water repellency.It is and hollow
The surface of component possesses the state for playing Superhydrophilic as described above.
That is, whether the surface of the hollow member of the disclosure has non-compatibility can be according to contact angle θ vistanex
Quantized to evaluate.
[elastomer components]
Contained elastomer components are by can be with the polyene as matrix material in the polyolefine resin composition of the disclosure
The composition of hydrocarbon resin mixing is formed.Therefore, for elastomer components, the shape included using the composition as polyolefine resin composition
State, when being shaped to vistanex formed body, as long as not causing substantial influence, then it can include arbitrary composition.
As elastomer components, such as thermoplastic elastomer (TPE), diene series rubber, non-diene series rubber etc. can be enumerated.Make
For specific thermoplastic elastomer (TPE), styrene series elastomer, olefin-based elastomer, vinyl chloride elastomer, amino can be enumerated
Formic acid ester based elastomers, acid amides based elastomers etc..As diene series rubber, vinyl benzene rubber, isoprene can be enumerated
Rubber, butadiene-based rubber etc..As non-diene series rubber, butyl rubber, ethylene propylene rubber, ethylene, propylene two can be enumerated
Alkene rubber, urethane rubber etc..Now, elastomer components can be used only a kind, can also it is appropriately combined two or more and
Use.
It should be noted that the elastomer components as the disclosure, thermoplastic elastomer (TPE), diene series rubber, non-diene series
In rubber etc., the elastomer or rubber or elastomer or rubber comprising alkene structures of styryl structures are particularly preferably included.
And then among them, particularly preferred styrene series elastomer.
As long as the above-mentioned elastomer comprising styryl structures or rubber comprising styrene skeleton and have caoutchouc elasticity can
Think any.Specifically, such as styrene series elastomer or vinyl benzene rubber etc. can be enumerated.
Styrene series elastomer (styrene butadiene thermoplasticelastomer (TPE-S;Styrene-Butadiene
Thermoplastic Elastomer)) as long as including polystyrene, polybutadiene or polyisoprene etc..Need to illustrate
, the principal component that polystyrene is formed in molecule is hard segment.Polybutadiene or polyisoprene form in molecule it is secondary into
Divide i.e. soft chain segment.
In addition, as long as vinyl benzene rubber has styrene skeleton such as being SB (SBR)
Diene series rubber can be thought arbitrarily.
As specific styrene series elastomer or vinyl benzene rubber, such as styrene-butadiene fourth can be enumerated
Alkene-styrene block copolymer (SBBS), SBS (SBS), styrene-ethylene fourth
Alkene-styrene block copolymer (SEBS), hydrogenated styrene-butadiene rubber (HSBR), styrene-ethylene butylene-ethene
Block copolymer (SEBC), styrene-ethylene propylene-styrenic block polymers (SEPS) etc..Now, vinyl benzene rubber
Or styrene series elastomer can be used only a kind, can also it is appropriately combined two or more and use.And then vinyl benzene rubber or
It can be used in styrene series elastomer with appropriately combined elastomer in addition.
It should be noted that the styrene series elastomer as the disclosure, be particularly preferably selected from by above-mentioned SEBS, SEPS,
At least one kind of styrene series elastomer in the group of SBS, SEB (styrene-ethylene-butadiene block copolymer) composition.That is, benzene second
The easy differential of alkene based elastomers dissipates, and therefore, easily plays the performance as rubber, therefore more preferably.
It should be noted that commonly known, styrene series elastomer is difficult to the particularly polypropylene in vistanex
It is compatible.Therefore, in the polyolefine resin composition of the disclosure, for vistanex, mixing has the surface of non-compatibility
Hollow member.That is, for matrix material, by two kinds be difficult to mix used into subassembly.Thus, as described later, can be with
The impact resistance of gained vistanex formed body is improved tremendously.
As long as in addition, elastomer or rubber comprising alkene structures comprising olefin skeletal as hard segment, comprising rubber or
Elastomer components can be thought arbitrarily as soft chain segment.Specifically, such as olefin-based elastomer or olefin-based rubber can be enumerated
Glue etc..
As long as olefin-based elastomer does not just have comprising the hard segment being made up of polyolefin and the soft chain segment being made up of rubber constituent
It is particularly limited to.Specifically, such as compounding (blending) ethylene-propylene can be enumerated in the polyolefin such as polypropylene or polyethylene
The olefin-based elastomer that the rubber constituents such as rubber form.Furthermore it is possible to enumerate compounding polyolefin and rubber constituent and partial cross-linked
The olefin-based elastomer formed;It is compounded polyolefin and rubber constituent and the fully crosslinked olefin-based elastomer formed etc..And then can
Make olefinic monomer, with the olefin-based elastomer that forms of monomer copolymerization as rubber constituent etc. to enumerate.Now, olefin-based elasticity
Body can be used only a kind, can also it is appropriately combined two or more and use.
Now, as olefin-based rubber, as long as just not having comprising vinyl monomer or propylene monomer etc. and with caoutchouc elasticity
It is particularly limited to.Specifically, as olefin-based rubber, such as ethylene propylene rubber (EPR, EPM), ethylene, propylene two can be enumerated
Alkene rubber (EPT, EPDM), vinyl-vinyl acetate copolymer (ethylene-vinylacetate rubber) etc..
It should be noted that above-mentioned olefin-based elastomer or olefin-based rubber bag contain the structure from alkene.Therefore, this public affairs
The matrix material for the polyolefine resin composition opened i.e. vistanex has compatibility.It is thus regarded that vistanex and bullet
Property body composition compatibility improve.
In contrast, the surface of hollow member is as described above, there is non-compatibility to vistanex.Therefore, it is elastic
In the case that body composition is olefin-based elastomer, elastomer components, which are also turned into, has non-compatibility.It is thus regarded that based on hollow
The effect of the compounding of component is well played.As a result, the polyolefin tree obtained by polyolefine resin composition can be improved
The impact resistance of fat formed body.
Wherein, shown in embodiment as be described hereinafter, it is known that, for elastomer components, styrene series elastomer (embodiment 6) with
Olefin-based rubber (embodiment 7) is compared, and plays good impact resistance.Result, it is believed that with elastomer components to vistanex
Compatibility it is high when compare, it is further good to the effect of the impact resistance of the compounding based on hollow member when compatibility is low
Ground is played.
[other compositions]
The polyolefine resin composition of the disclosure in addition to above-mentioned, vistanex, hollow member and elastomer components,
In the range of the effect of the disclosure, effect is not damaged, known other compositions can be contained.
Specifically, as other compositions, such as antioxidant, light stabilizer, ultra-violet absorber, anti-quiet can be enumerated
Electric agent, dispersant, nucleator, plasticizer, nertralizer, colouring agent (pigment, dyestuff), foaming agent, lubricant, fire retardant, anti-copper
Evil agent, packing material (excluding above-mentioned hollow member) etc..
Now, in other compositions, hollow member of the surface without raising hollow member to the compatibility of vistanex
Affine composition.
If during composition affine comprising hollow member, the surface of hollow member has well affine to vistanex
Property.Now, hollow member is bonded to the vistanex as matrix material.Pass through set, as described later, vistanex
The impact resistance of formed body reduces.As a result, using hollow member is starting point and vistanex formed body easily ruptures.
That is, the above-mentioned affine composition of hollow member is as with compatibility of the surface to vistanex for improving hollow member
The composition of property be defined.As the affine composition of specific hollow member, it is not particularly limited, such as surface can be enumerated and changed
Matter agent, modified resin etc..
Surface modifier is used for the surfaction for making hollow member, and directly improves surface to the affine of vistanex
Property.As surface modifier, such as silane coupler (with reference to patent document 1) etc. can be enumerated.
In addition, modified resin is in the same manner as surfactant, comprising:There is the position of compatibility to the surface of hollow member
With the position to vistanex with compatibility.Therefore, modified resin is folded between hollow member and vistanex
When, the compatibility on the surface of hollow member improves indirectly.As modified resin, such as maleic anhydride modified polyene can be enumerated
Hydrocarbon (with reference to patent document 1 and comparative example 2 described later) etc..
It should be noted that in the case that the surface of hollow member does not have sufficient non-compatibility to vistanex,
Or want in the case of further improving non-compatibility (i.e., it is desirable to reduce compatibility as far as possible), in polyolefine resin composition
Following composition can also be included.Specifically, can also include:With the affine composition of hollow member have adverse effect into
Point, i.e., the composition that makes the surface of hollow member be reduced to the compatibility of vistanex and (make non-compatibility raising).
[polyolefine resin composition]
Hereinafter, using Figure 1A and Figure 1B, the schematical composition of the polyolefine resin composition of the disclosure is illustrated.
The polyolefine resin composition of the disclosure contains vistanex, hollow member and elastomer components as described above
And form.And then also contain other compositions as needed.But the polyolefine resin composition of the disclosure does not contain hollow structure
Part is affine composition.
Figure 1A is the sectional view of the schematical composition for the polyolefine resin composition 50 for showing the disclosure.Figure 1B is to show
The sectional view of the schematical composition of conventional polyolefine resin composition 60.
The polyolefine resin composition 50 of the disclosure as shown in Figure 1A, in the vistanex 51 as matrix material
In be dispersed with hollow member 52 and form.At this point, it is same composition with conventional polyolefine resin composition 60.
Moreover, in the polyolefine resin composition 50 of the disclosure, the surface of hollow member 52 has to vistanex 51
Non- compatibility, and then, as described above, without the affine composition of hollow member.Therefore, hollow member 52 is difficult to and vistanex
51 is closely sealed.Think, between the surface of hollow member 52 and vistanex 51 formed with it is such shown in Figure 1A dotted line,
Interface 54.Thus, even if applying impact, hollow member to the vistanex formed body being made up of polyolefine resin composition 50
52 are easily slided by interface 54 in vistanex 51.As a result, the kinetic energy of impact is easily dispersed without concentrating.
And then the polyolefine resin composition 50 of the disclosure includes elastomer components 53.Such as Figure 1A institutes of elastomer components 53
Show like that, be scattered in polyolefine resin composition 50, exist in around hollow member 52.Now, thus it is speculated that:Hollow member
Existing elastomer components 53 in a manner of absorbing the kinetic energy of the impact applied to vistanex formed body to play around 52
Effect.
Specifically, it is high to the compatibility of vistanex 51 in the case that elastomer components 53 are, for example, olefin-based.Cause
This, is scattered in vistanex 51 elastomer components 53 good (such as uniform).Thus speculate:Vistanex formed body
Good impact resistance can be obtained using the action effect of elastomer components 53 (with reference to embodiment 7 described later).
On the other hand, in the case that elastomer components 53 are, for example, polystyrene, compared with olefin-based, to vistanex
51 compatibility is low.If compatibility is low, elastomer components 53 will not be well dispersed within vistanex 51.Therefore,
Originally, disclosure people etc. speculates for research:The impact resistance of vistanex formed body may not improve.However, ground
Study carefully, as a result understand, shown in 1~embodiment of embodiment 6 as be described hereinafter like that, in the case that elastomer components 53 are polystyrene,
Compared with olefin-based, better impact resistance can be obtained.For its reason, disclosure people etc. think be probably due to,
In vistanex 51, the elastomer components 53 of polystyrene are deficiently mixed to the molecule of vistanex 51.Supposition can
Can the molecules of thus elastomer components 53 play good caoutchouc elasticity, improve impact resistance.
As more than, for the polyolefine resin composition 50 of the disclosure, the surface of hollow member 52 has to matrix material
Non- compatibility, and include elastomer components 53.Thus, it is possible to realize the polyolefine resin composition with good impact resistance
50。
On the other hand, as illustrated in figure ib, conventional polyolefine resin composition 60 includes the affine composition of hollow member.
Therefore, as being filled out in Figure 1B shown in black region, around hollow member 52, due to the effect of the affine composition of hollow member
And form the firm closed surface 61 with polyolefine resin composition 60.In the vistanex to polyolefine resin composition 60
In the case that formed body applies impact, closed surface 61 is difficult to the kinetic energy for disperseing, absorbing impact.Therefore, polyolefine resin composition
60 impact concentration with hollow member 52 for starting point.Its result thinks that conventional polyolefine resin composition 60 can not be realized good
Good impact resistance.
It should be noted that vistanex, hollow member and elasticity as described above, in polyolefine resin composition
The content (such as containing ratio, compounding rate) of body composition is not particularly limited.I.e., it is possible to according to the polyolefin tree as shaping object
Each conditions such as the species of fat formed body, purposes, size, use environment and suitably set.
For example, when the gross weight of vistanex, hollow member and elastomer components is set into 100 weight %, hollow structure
In the range of as long as the content of part is 1~50 weight %.And then the content of hollow member is if 5~30 weight %'s
In the range of, then more preferably.That is, in the range of if 5~30 weight %, then it is easier to realize target lightweight.Furthermore it is possible to
Further equably it is kneaded, therefore, it is easier to maintain desired intensity.
That is, when the content of hollow member is less than 1 weight %, other each conditions, but polyolefine resin composition are additionally depended on
In the weight rate of hollow member diminish.Therefore, it is impossible to fully obtain to light-weighted effect.On the other hand, hollow member
Content more than 50 weight % when, in polyolefine resin composition it is hollow member, bulk density is relative becomes big.Therefore, also
Depending on other each conditions, but the workability during mixing of each composition during polyolefine resin composition manufacture reduces sometimes.Enter
And the mechanical property of gained polyolefine resin composition reduces sometimes.
In addition, for the content of elastomer components, the gross weight of vistanex, hollow member and elastomer components is set
For 100 weight % when, as long as the content of elastomer components be 1~30 weight % in the range of.And then elastomer components
Content is more preferably in the range of 5~20 weight %.That is, in the range of if 5~20 weight %, then target is more easily achieved
Weight reduction rate.And then the possibility for reaching desired intensity can be improved.
That is, when the content of elastomer components is less than 1 weight %, other each conditions are additionally depended on, but vistanex combines
" concentration " of contained elastomer components is not high (low) in thing.Therefore, sometimes can not be abundant in gained polyolefine resin composition
It is expected that the raising of impact resistance.
On the other hand, when the content of elastomer components is more than 30 weight %, other each conditions, but polyolefin tree are additionally depended on
" concentration " of contained elastomer components uprises in oil/fat composition.Now, the impact resistance of polyolefine resin composition improves, but
Ratio as the vistanex of matrix material reduces.Therefore, the intensity decreases of polyolefine resin composition are worried.In addition,
Elastomer components are relatively expensive compared with other compositions.Therefore, when the content of elastomer components is more than 30 weight %, also carry on a shoulder pole
The high cost of heart polyolefine resin composition.
That is, the polyolefine resin composition of the disclosure is free of other compositions, only comprising vistanex, hollow member and bullet
During property body composition, when the gross weight of vistanex, hollow member and elastomer components is set into 100 weight %, polyolefin tree
In the range of as long as the content of fat is 20~98 weight %.And then the content of vistanex is if it is considered that double glazing
With the difference of the addition of elastomer, then more preferably in the range of 50~90 weight %.
When the content of vistanex is less than 20 weight %, other each conditions, but the ratio drop of matrix material are additionally depended on
It is low.Therefore, the intensity decreases of polyolefine resin composition are worried.On the other hand, the content of vistanex is more than 98 weight %
When, additionally depend on other each conditions, but worry can not sufficiently to measure in polyolefine resin composition containing hollow member and
At least one of elastomer components.Therefore, worry that the lightweight of polyolefine resin composition, impact resistance reduce.
It should be noted that the polyolefine resin composition of the disclosure can also contain except vistanex, hollow member
With the other compositions outside elastomer components.The surface for being used for improving hollow member is free of in other compositions to vistanex
The affine composition of hollow member of compatibility.
Now, the content of other compositions is not particularly limited.I.e., it is possible to according to addition other compositions purpose or its
Species of his composition etc. and be properly added necessary amount.
[manufacture method of polyolefine resin composition]
Hereinafter, the manufacture method of the polyolefine resin composition of the disclosure is illustrated.
First, at least by vistanex, hollow member and elastomer components and other compositions as needed with
Arbitrary order, arbitrary compounding amount are compounded.Now, exclude for the surface for improving hollow member to vistanex
The affine composition of hollow member of compatibility.
Then, each composition being compounded for example is kneaded in known kneading machine.Now, made as needed
Grain.
Then, will be for example molded by the mixture being kneaded in known forming machine.Thus, manufacture has regulation
Compounding amount polyolefine resin composition.
It should be noted that the kneading machine used during compounding can be adapted to use known kneading machine.Specifically, such as
Single screw extrusion machine, double screw extruder, super mixer, Henschel mixer, Banbury mixer, roll-type can be enumerated to mix
The kneading machines such as conjunction machine, brabender plasticorder, kneader.These kneading machines can possess the composition that can be granulated.In addition, in profit
, can also be by vistanex, hollow member, elastomer components and its being compounded as needed before being kneaded with kneading machine
At least any one is kneaded and manufactured in advance in his composition.
That is, the polyolefine resin composition of the disclosure by vistanex, hollow member and elastomer components it is each into
Point mixing or after being kneaded the granulation carried out and obtain.
Then, gained polyolefine resin composition is molded for example using known various forming machines with vistanex
The form of body is molded.As specific forming machine, it is not particularly limited, such as injection (mo(u)lding) machine can be used, be extruded into
Type machine, panel forming machine, vacuum forming machine etc..
Thus, vistanex formed body is at least formed using polyolefine resin composition.Now, comprising except polyolefin
Material (such as antioxidant etc.) outside resin combination, can also form vistanex formed body.Thus, it is possible to obtain
Vistanex formed body with good impact resistance.
Moreover, gained vistanex formed body is not particularly limited, the evaluation of the impact resistance of following middle explanation is used
Method etc. is evaluated.
Illustrated such in embodiment as be described hereinafter etc. in present embodiment, first, what will be obtained by the above method is poly-
Olefin resin composition is shaped to the thick tabulars of such as 1.6mm, forms the test film of vistanex formed body.
Then, the test film of formation is stood 3 hours for example in thermostat with -10 DEG C.Afterwards, relative to test film,
Fall 250g weight.
Then, the maximum height that measurement test film is not destroyed.Thus, based on maximum height, evaluation test piece (polyolefin
Resin combination) impact resistance.Now, the numerical value of maximum height is bigger, and impact resistance is more excellent.
It should be noted that in the disclosure, polyolefine resin composition considers the application being in electrical article part.Cause
This, if for be more than 100cm with maximum height characteristic polyolefine resin composition.
That is, when maximum height is less than 100cm, can only obtain with having carried out light-weighted conventional gather using hollow member
Olefin resin composition is equal extent or the impact resistance below it.It is therefore preferable that at least have maximum height be 100cm with
On impact resistance polyolefine resin composition.It should be noted that the upper limit of maximum height is not particularly limited, but it is expected
Numerical value is larger.However, the upper limit in physical property is limited according to the composition of polyolefine resin composition.
As more than, the polyolefine resin composition of the disclosure contain said polyolefins resin, hollow member and elastomer into
Point, other compositions as needed etc. and form.
[vistanex formed body]
Hereinafter, vistanex formed body obtained from the shaping as said polyolefins resin combination is said
It is bright.
The purposes of the vistanex formed body of the disclosure is not particularly limited, and as representational purposes, can enumerate
Family's electrical article part etc..In addition, the species of specific family electrical article is not particularly limited, such as the family that hand takes type can be enumerated
Electrical article etc..
Family's electrical article of type is taken for hand, user holds at least a portion and used.Now, hand takes family's electrical article of type
Have when in use with the collision of the object of surrounding, fall etc. and to worry.Therefore, it is desirable to hand takes family's electrical article of type by with good
The part of impact resistance is formed.
It should be noted that as hand take type family's electrical article, specifically, for example, can enumerate dust catcher, drying machine,
Electric razor, hand power stirring device, electric water bottle (insulating pot) etc..
As representational one of vistanex formed body, the inhalation apparatus of dust catcher can be enumerated.
The inhalation apparatus of dust catcher collides with various objects in use, it is therefore desirable to the resistance to punching higher than common part
Hitting property.That is, particularly preferred one of vistanex formed body (family's electrical article part) as the disclosure, can enumerate
The inhalation apparatus of dust catcher.Therefore, also include in the disclosure:The vistanexes such as the inhalation apparatus comprising following middle explanation are molded
The dust catcher of body.
The specific of the dust catcher of the disclosure is constructed without being particularly limited to, and can enumerate various types of dust catchers.Such as
The pot dust catcher 10 of the paper bag mode shown in Fig. 2, pot dust catcher 20 of cyclone manner shown in Fig. 3 etc. can be enumerated.
First, the composition of the pot dust catcher 10 of paper bag mode is specifically described.
As shown in Figure 2, the pot dust catcher 10 of paper bag mode possesses:Main body of dust collector 11, flexible pipe 12, handle part
13rd, nearly body operating portion 14, extension tube 15 and inhalation apparatus 30 etc..
Main body of dust collector 11 internally possesses the dust storage chamber of not shown electric blowing machine and paper bag type.In addition, dust suction
Device main body 11 possesses one wheel pairs 16 in both sides.And then main body of dust collector 11 possesses the electricity that can be accommodated in inside at rear portion
Source flexible cord (not shown).
One end of flexible pipe 12 is anterior detachably connected with main body of dust collector 11.The other end of flexible pipe 12 and extension tube 15
One end it is detachably connected.
The other end of extension tube 15 and inhalation apparatus 30 are detachably connected.The structure in a manner of it can stretch of extension tube 15
Into.
Nearly body operating portion 14 is provided with above the other end of flexible pipe 12.It is provided near nearly body operating portion 14 and is used to hold
The handle part 13 of the other end of flexible pipe 12.
Moreover, using the action of the electric blowing machine in main body of dust collector 11, from one end of flexible pipe 12 to main body of dust collector
Suction is produced in 11.Thus, the inside for the flexible pipe 12 being connected with main body of dust collector 11, the inside of extension tube 15 and inhalator
Suction is also produced in the not shown suction inlet of tool 30.
In addition, main body of dust collector 11 is movably formed using one wheel pairs 16 on swept surface.
As more than, the pot dust catcher 10 of paper bag mode is formed.
Hereinafter, the action to the pot dust catcher 10 of paper bag mode illustrates.
Pot dust catcher 10 in use, first, user extracts not shown mains cord from main body of dust collector 11 out,
The attaching plug of front end is inserted into outlet.Then, user holds handle part 13, operates nearly body operating portion 14, connects
The power supply of main body of dust collector 11.Thus, electric blowing machine is acted, and suction is produced in the suction inlet of inhalation apparatus 30.
Then, user holds handle part 13, as needed, while moving main body of dust collector 11, while making inhalation apparatus 30
Moved on the swept surfaces such as ground.Thus, it is present in the dust of swept surface from the suction inlet suction of inhalation apparatus 30.From suction
The dust for entering the suction of utensil 30 is absorbed in the dust storage chamber of the paper bag type in main body of dust collector 11 by extension tube 15, flexible pipe 12.
As more than, the pot dust catcher 10 of paper bag type acts.
Then, the composition of the pot dust catcher 20 of cyclone manner is illustrated.
As shown in Figure 3, the pot dust catcher 20 of cyclone manner possesses:Main body of dust collector 21, flexible pipe 22, handle part
23rd, nearly body operating portion 24, extension tube 25 and inhalation apparatus 30 etc..
Main body of dust collector 21 is built-in with not shown electric blowing machine at rear portion, holds in the anterior dust that is removably provided with
Device incorporating section 28.Dust collecting container incorporating section 28 is accommodated with the dust collecting container 27 for being internally used for separation and collection dust.
One end of flexible pipe 22 is anterior detachably connected with main body of dust collector 21.The other end of flexible pipe 22 and extension tube 25
One end it is detachably connected.
The other end of extension tube 25 and inhalation apparatus 30 are detachably connected.The structure in a manner of it can stretch of extension tube 25
Into.
Nearly body operating portion 24 is provided with above the other end of flexible pipe 22.It is provided near nearly body operating portion 24 and is used for handle
Hold the handle part 23 of the other end of flexible pipe 22.
Moreover, using the action of the electric blowing machine in main body of dust collector 21, from one end of flexible pipe 22 to main body of dust collector
Dust collecting container 27 in 11 produces suction.Thus, in the inside of the flexible pipe 22 being connected with main body of dust collector 21, extension tube 25
Suction is also produced in the not shown suction inlet of portion and inhalation apparatus 30.
In addition, main body of dust collector 21 is movably formed using one wheel pairs 26 on swept surface.
As more than, the pot dust catcher 20 of cyclone manner is formed.
Hereinafter, the action to the pot dust catcher 20 of cyclone manner illustrates.
Pot dust catcher 20 in use, first, user extracts not shown mains cord from main body of dust collector 21 out,
The attaching plug of front end is inserted into outlet.Then, user holds handle part 23, operates nearly body operating portion 24, connects
The power supply of main body of dust collector 21.Thus, electric blowing machine is acted, and suction is produced in the suction inlet of inhalation apparatus 30.
Then, user holds handle part 23, as needed, while moving main body of dust collector 21, while making inhalation apparatus 30
Moved on swept surface.Thus, it is present in the dust of swept surface from the suction inlet suction of inhalation apparatus 30.From inhalation apparatus
The dust of 30 suctions is collected in positioned at the anterior dust collecting container incorporating section of main body of dust collector 21 by extension tube 25, flexible pipe 22
Dust collecting container 27 in 28.
As more than, the pot dust catcher 20 of cyclone manner acts.
Hereinafter, using Fig. 4, pot dust catcher 10 to paper bag mode or make in the pot dust catcher 20 of cyclone manner
The composition of inhalation apparatus 30 illustrates.
As shown in Figure 4, inhalation apparatus 30 has the profile of substantially T-shaped (including T-shaped).Inhalation apparatus 30 has
It is standby:Inhalation apparatus main body 31, movable part 32, connecting section 33 etc..Inhalation apparatus main body 31 is (including rectangular with approximately parallelepiped body shape
Body shape) formed, it is provided with movable part 32 in a manner of Neng Gou Oscillating are dynamic in the central rear of length direction.
Not shown suction inlet is provided with below inhalation apparatus main body 31, the inside of suction inlet and movable part 32 connects
It is logical.Movable part 32 moves along Xia Oscillating Shang the direction orthogonal with the length direction of inhalation apparatus main body 31.In the another of movable part 32
End is provided with connecting section 33.The front end (other end) of connecting section 33 and extension tube 15,25 is detachably connected.
Now, as shown in Figure 4, inhalation apparatus 30 is made up of multiple components rather than is made up of single component
's.Therefore, part or all of component of inhalation apparatus 30 is made up of the vistanex formed body of the above-mentioned disclosure.Now,
Inhalation apparatus 30 for example only can require the position of more excellent impact resistance by the polyolefine resin composition 50 of the disclosure
Form.In addition, it is overall that inhalation apparatus main body 31 can be for example made up of the polyolefine resin composition 50 of the disclosure.And then can
With by the polyolefine resin composition 50 of the disclosure formed easily with the collision such as wall, before inhalation apparatus main body 31
Component or form inhalation apparatus main body 31 two sides component.
It should be noted that the specific composition in pot dust catcher 10,20 shown in Fig. 2 and Fig. 3 is not particularly limited in
Above-mentioned composition.For example, known various compositions in the field using dust catcher can be adapted to.
As described above, the polyolefine resin composition of the disclosure mixes for the vistanex as matrix material
Conjunction has hollow member and elastomer components.Hollow member is not to show that the state of compatibility is formed to vistanex.
Therefore, by the mixing of hollow member, polyolefine resin composition lightweight can be made.
And then the surface of hollow member is formed in a manner of not to vistanex set.Therefore, to by vistanex
In the case that the vistanex formed body that composition is formed applies impact, the interface of hollow member is easily in vistanex
Slide.Thus, it is possible to it is greatly reduced caused by the concentration of impact using hollow member to be starting point, vistanex formed body
The generation of crackle.
In addition, the polyolefine resin composition of the disclosure includes elastomer components and formed.Elastomer components pass through with
Empty Component composition, as described above, it can with tremendous improve the impact resistance of polyolefine resin composition.As a result, use
The vistanex formed body of polyolefine resin composition can realize good lightweight, and can also further realize excellent
Impact resistance.Therefore, vistanex formed body particularly suitable for require high impact resistance family's electrical article part,
Such as the component such as inhalation apparatus of dust catcher.
(embodiment)
Hereinafter, to the characteristic of the polyolefine resin composition of the disclosure, it is specifically described based on embodiment and comparative example.
It should be noted that the disclosure is not limited to this, those skilled in the art without departing from the scope of the disclosure, can be with
Carry out various changes, modifications and variations.
(evaluation of measuring method)
First, below to the evaluation of measuring side of the physical property such as in embodiment and comparative example, real density, impact resistance experiment
Method illustrates.
[real density]
The real density of the sample panel obtained in embodiment or comparative example is to use real density meter (Alfamirage Co., Ltd.
System, trade name:MD-300S) determine.
[impact resistance experiment]
The impact resistance experiment of the sample panel obtained in embodiment or comparative example is carried out using following method.
First, by the sample panel of making in thermostat (ESPEC Corp. systems, trade name:PDR-3KP stood in), with -10
DEG C keep 3 hours.Afterwards, sample panel is taken out rapidly from thermostat, the weight for making 250g from various height is fallen.
Then, the not destroyed maximum height for falling caused sample panel of weight is determined.
It should be noted that the numerical value that impact resistance tests maximum height as described above is bigger, the resistance to of sample panel is represented
Impact is higher.
Therefore, shown in (table 1) and (table 2) described later:Numerical value obtained from the numerical value of maximum height is distinguished with 3 stages
Any stage is categorized as, evaluates result obtained from impact resistance.Specifically, if maximum height is less than 60cm, evaluate
For the low "×" of impact resistance.It is slightly lower " △ " to be then evaluated as impact resistance if more than 60cm and below 100cm for maximum height.
Moreover, maximum height is if it exceeds 100cm, then be evaluated as the high "○" of impact resistance.
Benchmark based on more than, evaluate the impact resistance of embodiment or the sample panel of comparative example.
(embodiment 1)
The sample panel of embodiment 1 is formed making with following.
As vistanex, polypropylene (Japan Polypropylene Corporation systems, trade name are used:
BC03B).As hollow member, double glazing (Sumitomo 3M Limited systems, trade name are used:Glassbubbles
iM16K).As elastomer components, SEBS (Asahi Kasei Corporation's system, trade name are used:H1062).
Then, in the container of pre-prepd mixing in advance, with as the above-mentioned weight % of polypropylene constituent 85, hollow
The mode of the weight % of 10 weight % and SEBS composition of glass ingredient 5 weight ratio, is compounded each composition.Then, by the composition of compounding
Equably stir, each composition is mixed in advance, make mixture.
Afterwards, the mixture of making is put into double screw extruder, is kneaded when mixture is heated, pellet is made
Grain.It should be noted that the barrel temperatures set of double screw extruder is 200 DEG C.Thus, the polyolefin tree of embodiment 1 is made
Oil/fat composition.
Then, gained pellet is shaped to 70mm × 60mm × 1.6mm sample panel in injection (mo(u)lding) machine.Need to illustrate
, injection moulding condition is set to 200 DEG C of forming temperature, 40 DEG C of mold temperature.Thus, the vistanex of embodiment 1 is made
Formed body.
The composition of gained sample panel is:The weight % of polypropylene constituent 85, weight %, the SEBS composition 5 of double glazing composition 10
Weight %.Now, it is affine to the compatibility of polypropylene constituent, hollow member without the surface for improving double glazing composition
Composition.
Sample panel by the measure of above-mentioned real density and impact resistance test evaluation by above-mentioned making.Its result is shown
In following (table 1) and (table 2).
(embodiment 2)
The sample panel of embodiment 2 is made with following composition.
It should be noted that the sample panel of embodiment 2, as vistanex, makes in the same manner as the sample panel of embodiment 1
With polypropylene, as hollow member, using double glazing, and as elastomer components, SEBS is used.Now, make polypropylene, in
The weight of the content (compounding amount) of empty glass and SEBS composition than respectively 75 weight %, 5 weight % and 20 weight % so with
Embodiment 1 is differently compounded.
Then, in addition to mix ratio, similarly to Example 1, the polyolefine resin composition (pellet) of embodiment 2 is made
With the vistanex formed body (sample panel) of embodiment 2.
The composition of gained sample panel is:The weight % of polypropylene constituent 75, weight %, the SEBS composition 20 of double glazing composition 5
Weight %.Now, it is affine to the compatibility of polypropylene constituent, hollow member without the surface for improving double glazing composition
Composition.
Sample panel by the measure of above-mentioned real density and impact resistance test evaluation by above-mentioned making.Its result is shown
In following (table 1).
(embodiment 3)
The sample panel of embodiment 3 is made with following composition.
It should be noted that the sample panel of embodiment 3, as vistanex, makes in the same manner as the sample panel of embodiment 1
With polypropylene, as hollow member, using double glazing, and as elastomer components, SEBS is used.Now, make polypropylene, in
The weight of the content (compounding amount) of empty glass and SEBS composition than respectively 90 weight %, 5 weight % and 5 weight % so with reality
Example 1 is applied differently to be compounded.
Then, in addition to mix ratio, similarly to Example 1, the polyolefine resin composition (pellet) of embodiment 3 is made
With the vistanex formed body (sample panel) of embodiment 3.
The composition of gained sample panel is:The weight % of polypropylene constituent 90, the weight of 5 weight %, SEBS composition of double glazing composition 5
Measure %.Now, without for improve the surface of double glazing composition to the compatibility of polypropylene constituent, hollow member is affine into
Point.
Sample panel by the measure of above-mentioned real density and impact resistance test evaluation by above-mentioned making.Its result is shown
In following (table 1).
(embodiment 4)
The sample panel of embodiment 4 is made with following composition.
It should be noted that the sample panel of embodiment 4, as vistanex, makes in the same manner as the sample panel of embodiment 1
With polypropylene, as hollow member, using double glazing, and as elastomer components, SEBS is used.Now, make polypropylene, in
The weight of the content (compounding amount) of empty glass and SEBS composition than respectively 50 weight %, 30 weight % and 20 weight % so with
Embodiment 1 is differently compounded.
Then, in addition to mix ratio, similarly to Example 1, the polyolefine resin composition (pellet) of embodiment 4 is made
With the vistanex formed body (sample panel) of embodiment 4.
The composition of gained sample panel is:The weight % of polypropylene constituent 50, weight %, the SEBS composition 20 of double glazing composition 30
Weight %.Now, it is affine to the compatibility of polypropylene constituent, hollow member without the surface for improving double glazing composition
Composition.
Sample panel by the measure of above-mentioned real density and impact resistance test evaluation by above-mentioned making.Its result is shown
In following (table 1).
(embodiment 5)
The sample panel of embodiment 5 is made with following composition.
It should be noted that the sample panel of embodiment 5 in the same manner as the sample panel of embodiment 1, as vistanex, uses
Polypropylene, as hollow member, using double glazing, and as elastomer components, use SEBS.Now, polypropylene, hollow is made
The weight of the content of glass and SEBS compositions (compounding amount) than respectively 65 weight %, 30 weight % and 5 weight % so with reality
Example 1 is applied differently to be compounded.
Then, in addition to mix ratio, similarly to Example 1, the polyolefine resin composition (pellet) of embodiment 5 is made
With the vistanex formed body (sample panel) of embodiment 5.
The composition of gained sample panel is:The weight % of polypropylene constituent 65, weight %, the SEBS composition 5 of double glazing composition 30
Weight %.Without for improving the surface of double glazing composition to the compatibility of polypropylene constituent, hollow member is affine composition.
Sample panel by the measure of above-mentioned real density and impact resistance test evaluation by above-mentioned making.Its result is shown
In following (table 1).
(comparative example 1)
The sample panel of comparative example 1 is made with following composition.
It should be noted that for the sample panel of comparative example 1, as vistanex, using polypropylene, as hollow structure
Part, using double glazing, it is compounded in a manner of weight is than respectively becoming 90 weight % and 10 weight %.
Then, elastomer components are not compounded, in addition, similarly to Example 1, the polyolefin tree of comparison example 1
The vistanex formed body (sample panel) of oil/fat composition (pellet) and comparative example 1.
The composition of gained sample panel is:The weight % of polypropylene constituent 90, the weight % of double glazing composition 10, elastomer components
0 weight %.Now, without the surface for improving double glazing composition to the compatibility of polypropylene constituent, hollow member parent
And composition.
Sample panel by the measure of above-mentioned real density and impact resistance test evaluation by above-mentioned making.Its result is shown
In following (table 1).
(comparative example 2)
The sample panel of comparative example 2 is made with following composition.
It should be noted that for the sample panel of comparative example 2, using as being used as the weight of polypropylene 87 of vistanex
Measure %, as hollow member the weight % of double glazing 10 and maleated polypropylene (RIKEN VITAMIN CO.,
LTD. system, trade name:MG-400P) 3 weight % weight than mode, be compounded each composition.
Then, elastomer components are not compounded, in addition, similarly to Example 1, the polyolefin tree of comparison example 2
The vistanex formed body (sample panel) of oil/fat composition (pellet) and comparative example 2.
The composition of gained sample panel is:The weight % of polypropylene constituent 90, the weight % of double glazing composition 10, elastomer components
0 weight %.Now, comprising as improving the hollow member of the surface of double glazing composition to the compatibility of polypropylene constituent
The maleated polypropylene of affine composition.
Sample panel by the measure of above-mentioned real density and impact resistance test evaluation by above-mentioned making.Its result is shown
In following (table 1).
(table 1)
Note) in comparative example 2,3 weight % of compounding maleated polypropylene replaces elastomer components (SEBS).
(contrast of embodiment 1~5 and comparative example 1,2)
From the result of (table 1), for adding the hollow glass as hollow member as the polypropylene of vistanex
During glass, the Arbitrary Samples plate of embodiment and comparative example all in accordance with double glazing addition and density (real density) is reduced.Now
Understand, by the optimization of injection pressure during sample sheet metal forming, the destruction of double glazing can be avoided, polyolefin tree can be made
The further lightweight of fat formed body.
In addition, from the result of embodiment 1~5, Arbitrary Samples plate shows good impact resistance.
On the other hand understand, the impact resistance of the sample panel of comparative example 1 is slightly worse, the impact resistance of the sample panel of comparative example 2
It is obvious to reduce.
It is thought that because the sample panel of comparative example 1 is free of elastomer components.Thus, it can be known that by only including polyolefin tree
Fat and the vistanex formed body of the polyolefine resin composition of hollow member shaping can realize lightweight, but be difficult to improve
Impact resistance.
In addition, the sample panel of comparative example 2 is in the same manner as comparative example 1, without elastomer components, comprising as hollow member parent
With the maleated polypropylene of composition.Therefore, the surface of hollow member is further improved to the compatibility of vistanex.By
This, hollow member uprises (with reference to patent document 1) to the adaptation of the vistanex as matrix material.Therefore, to sample
When plate applies impact, easily cracked at the interface of vistanex and hollow member.Its result thinks, vistanex into
The impact resistance of type body reduces.
On the other hand, the sample panel of embodiment 1~5 is free of the affine composition of hollow member, includes elastomer components.Therefore,
Hollow member is low to the adaptation of vistanex.And then speculate:By being compounded elastomer components, as described above, hollow structure
The kinetic energy of part is absorbed.Its result thinks that the impact resistance of sample panel improves.
In addition, from the contrast of embodiment 2 and 3 and the contrast of embodiment 4 and 5, make in above-mentioned preferable scope
During addition (content) increase of elastomer components, compared with the situation without elastomer components, good resistance to punching can be obtained
Hitting property.
(embodiment 6)
The sample panel of embodiment 6 is made with following composition.
It should be noted that in the sample panel of embodiment 6, as elastomer components, using SEPS (KURARAY CO.,
LTD systems, trade name:S2004), in addition, it is set to composition similarly to Example 1.
Then, the polyolefine resin composition (pellet) of embodiment 6 and the vistanex formed body of embodiment 6 are made
(sample panel).
The composition of gained sample panel is:The weight % of polypropylene constituent 85, weight %, the SEPS composition 5 of double glazing composition 10
Weight %.Now, it is affine to the compatibility of polypropylene constituent, hollow member without the surface for improving double glazing composition
Composition.
Sample panel by the measure of above-mentioned real density and impact resistance test evaluation by above-mentioned making.Its result is shown
In following (table 2).
(embodiment 7)
The sample panel of embodiment 7 is made with following composition.
It should be noted that in the sample panel of embodiment 7, as elastomer components, the ethylene propylene as olefin-based is used
Alkene rubber (EPR, Mitsui Chemicals, Inc's system, trade name:P0280) and without using polystyrene, in addition, it is set to and real
Apply the same composition of example 1.
Then, the polyolefine resin composition (pellet) of embodiment 7 and the vistanex formed body of embodiment 7 are made
(sample panel).
The composition of gained sample panel is:The weight % of polypropylene constituent 85, the weight %, EPR (olefin-based of double glazing composition 10
Elastomer) 5 weight %.Now, without the surface for improving double glazing composition to the compatibility, hollow of polypropylene constituent
Component is affine composition.
Sample panel by the measure of above-mentioned real density and impact resistance test evaluation by above-mentioned making.Its result is shown
In following (table 2).
(table 2)
Note) comparative example 2 MA-g-PP be maleated polypropylene abbreviation.
(contrast of embodiment 1,6,7 and comparative example 2)
Understood when contrasting embodiment 1 and 6 shown in (table 2), when elastomer components are SEBS or SEPS, as long as being styrene
System, just can realize good impact resistance and lightweight.
In addition, from the result of embodiment 7, elastomer components add the EPR rather than benzene second as olefin-based rubber
In the case of alkene based elastomers, good impact resistance and lightweight can also be realized.
On the other hand, the sample panel of comparative example 2 is free of elastomer components, includes the Malaysia as the affine composition of hollow member
Sour modified polypropene (MA-g-PP).Now, judgement can realize lightweight.However, understand when compared with embodiment 1,6,7, than
It is substantially poor compared with the impact resistance of example 2.
In addition, as shown in (table 2), as elastomer components, styrene series elastomer or polystyrene are not limited to
Rubber, or other elastomers or rubber.I.e. understand, the species regardless of elastomer components, by with hollow member
Combination, it is possible to realize good impact resistance.
Now, the sample panel of embodiment 6 has impact resistance of the maximum height for 200cm or so, but the sample of embodiment 7
Plate is the impact resistance that maximum height is 110cm.From the result, as elastomer components, benzene is compounded compared with olefin-based
During the elastomer components of ethene system, impact resistance further improves.
It should be noted that the disclosure is not limited to the record of above-mentioned embodiment, can be in the model shown in claim
Enclose the interior various changes of progress.That is, for by disclosed technical scheme is appropriately combined respectively in different embodiments, multiple variations
Obtained from embodiment, be also contained in the protection domain of the disclosure.
As described above, the polyolefine resin composition of the disclosure contains:Vistanex, granular hollow structure
Part and elastomer components.There is non-compatibility with the surface of hollow member to vistanex and the vistanex combines
The mode that thing does not contain the affine composition of hollow member is formed.
According to this composition, during polyolefine resin composition as the vistanex of matrix material (mother metal) for being mixed with
Empty component and elastomer components.Now, hollow member does not contain the affine composition of hollow member, and therefore, vistanex is not shown
Show compatibility.Thus, by mixing hollow member, it is possible to achieve the lightweight of polyolefine resin composition.And then hollow member
Surface to vistanex not set.Therefore, even if the vistanex formed body being made up of polyolefine resin composition is applied
Add impact, the interface of hollow member is also easily slided to vistanex.Thus, with vistanex and hollow member set and
The vistanex formed body of composition is compared, and can be greatly reduced using hollow member as starting point and in vistanex formed body
The possibility cracked.
And then polyolefine resin composition includes elastomer components.Elastomer components, can be with by being combined with hollow member
Impact resistance is improved tremendously.As a result, using the vistanex formed body of polyolefine resin composition can realize into
The lightweight of one step and excellent impact resistance can be obtained.Therefore, can by polyolefine resin composition particularly suitable for
Family's electrical article part that vistanex formed body by requiring impact resistance is formed etc..
In addition, for the polyolefine resin composition of the disclosure, by hollow member, vistanex and elastomer components
When gross weight is set to 100 weight %, can with the content of hollow member turn into 1~50 weight % in the range of, elastomer components
Content turn into 1~30 weight % in the range of mode be compounded.
In addition, for the polyolefine resin composition of the disclosure, vistanex at least can be made up of polypropylene, hollow
Component is made up of glass, and elastomer components can include styrene series elastomer, vinyl benzene rubber, olefin-based elastomer and alkene
In hydrocarbon system rubber at least any one.
In addition, for the polyolefine resin composition of the disclosure, elastomer components can include be selected from by SEBS, SEPS,
At least one kind of styrene series elastomer in the group of SBS, SEB composition.
, can be by model that the contact angle θ with water is 85~100 ° in addition, for the polyolefine resin composition of the disclosure
The mode of the vistanex of characteristic in enclosing is formed, and the surface of hollow member is using the contact angle θ with water as 0~10 ° of model
The mode of characteristic in enclosing is formed.
In addition, the vistanex formed body of the disclosure can be the polyolefine resin composition at least using above-mentioned composition
And the family's electrical article part formed.It should be noted that as family's electrical article part, such as the suction of dust catcher can be enumerated
Enter utensil etc..
In addition, the dust catcher of the disclosure can possess the part being made up of the above-mentioned vistanex formed body formed.
Claims (8)
1. a kind of polyolefine resin composition, it contains:Vistanex, granular hollow member and elastomer components,
The surface of the hollow member has non-compatibility to the vistanex, and the polyolefine resin composition is free of
There is the affine composition of hollow member.
2. polyolefine resin composition according to claim 1, wherein, by the hollow member, the vistanex
When being set to 100 weight % with the gross weight of the elastomer components, the content of the hollow member is 1~50 weight % scope
In the range of the content of interior, described elastomer components is 1~30 weight %.
3. polyolefine resin composition according to claim 1, wherein, the vistanex is at least by polypropylene structure
Into, the hollow member is made up of glass,
The elastomer components are included in styrene series elastomer, vinyl benzene rubber, olefin-based elastomer and olefin-based rubber
At least any one.
4. polyolefine resin composition according to claim 1, wherein, the elastomer components include be selected from by SEBS,
At least one kind of styrene series elastomer in the group of SEPS, SBS, SEB composition.
5. polyolefine resin composition according to claim 1, wherein, the vistanex has the contact angle θ of water
For the characteristic in the range of 85~100 °,
It is the characteristic in the range of 0~10 ° that the surface of the hollow member, which has the contact angle θ of water,.
6. a kind of vistanex formed body, it is that at least usage right requires that the polyolefine resin composition described in 1 is formed
Family's electrical article part.
7. vistanex formed body according to claim 6, wherein, described electrical article is with the suction that part is dust catcher
Enter utensil.
8. a kind of dust catcher, it possesses:The portion being made up of the vistanex formed body described in claim 6 or claim 7
Part.