CN107760254A - 一种高阻燃防火硅酮密封胶 - Google Patents

一种高阻燃防火硅酮密封胶 Download PDF

Info

Publication number
CN107760254A
CN107760254A CN201711127518.1A CN201711127518A CN107760254A CN 107760254 A CN107760254 A CN 107760254A CN 201711127518 A CN201711127518 A CN 201711127518A CN 107760254 A CN107760254 A CN 107760254A
Authority
CN
China
Prior art keywords
parts
flame
silicone sealant
fireproof silicone
retardancfireproof fireproof
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711127518.1A
Other languages
English (en)
Inventor
王婷
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sichuan Kelixin New Material Co Ltd
Original Assignee
Sichuan Kelixin New Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sichuan Kelixin New Material Co Ltd filed Critical Sichuan Kelixin New Material Co Ltd
Priority to CN201711127518.1A priority Critical patent/CN107760254A/zh
Publication of CN107760254A publication Critical patent/CN107760254A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种高阻燃防火硅酮密封胶，是由下述质量份数的成分制备而成的：端羟基聚二甲基硅氧烷60～120份、阻燃剂40～100份、无机填料50～80份、交联剂10～30份、偶联剂1‑4份、催化剂4～8份、防老剂3‑7份，所述密封胶具有优异的阻燃性能、耐老化、加工方便、质量稳定的优点。

Description

一种高阻燃防火硅酮密封胶
技术领域
本发明涉及高分子结构密封胶技术领域，特别是涉及一种高阻燃防火硅酮密封胶。
背景技术
密封胶使用时是一种流动的或可挤注的不定形材料，能嵌填封闭接缝，能依靠干燥、温度变化、溶剂挥发、化学交联与基材稳定粘结，并逐渐定型成为塑性固态、粘弹态或弹性密封材料。为保证密封功能，密封胶应具备以下基本特性：良好的嵌填、挤注施工性，储存稳定，无毒或低毒害；对液体、气体等介质低渗透性；能承受接缝位移并随伸缩运动而变形；在接缝中经受反复变形后，能保证充分恢复其性能和形状；有足够强度，能承受应力；与接缝基面粘结稳定，不发生剥离和脱胶；高温下不过度软化，低温下不脆裂；耐气候，不粉化、龟裂、溶解或过度收缩，有足够寿命；特定场合使用时有特定性能，如：耐磨、抗穿刺、耐腐蚀、抗滚压、不燃、不污染、绝缘或导电等。
发明内容
本发明主要解决的技术问题是提供一种高阻燃防火硅酮密封胶，具有优异的阻燃性能、耐老化、加工方便、质量稳定的优点。
为解决上述技术问题，本发明采用的一个技术方案是：
提供一种高阻燃防火硅酮密封胶，是由下述质量份数的成分制备而成的：
端羟基聚二甲基硅氧烷60～120份、
阻燃剂40～100份、
无机填料50～80份
交联剂10～30份
偶联剂1-4份
催化剂4～8份、
防老剂3-7份
进一步的，所述聚二甲基硅氧烷的粘度为20000～40000Pa·s。
进一步的，所述阻燃剂为氮系阻燃剂20-50份和无机阻燃剂20-50份的混合阻燃剂。
更进一步的，所述氮系阻燃剂为三聚氰胺、三聚氰胺尿酸盐(MAC)中的一种或多种的混合物。
更进一步的，所述无机阻燃剂为三氧化二锑、氢氧化镁、氢氧化铝及硅系阻燃剂中的一种或几种的混合物。
进一步的，所述无机填料为经过表面改性的超细碳酸钙或气相白炭黑。
进一步的，所述交联剂为甲基三甲氧基硅烷、甲基三乙氧基硅烷、乙烯基三丁酮肟基硅烷或四丁酮肟基硅烷中的一种或多种的混合物。
进一步的，所述偶联剂为γ-氨丙基甲基二乙氧基硅烷、N-(β-氨乙基)-γ-氨丙基甲基二甲氧基硅烷、γ-氨丙基三乙氧基硅烷、γ-(2,3-环氧丙氧)丙基三甲氧基硅烷的任意一种或几种；所述交联剂为甲基三甲氧基硅烷、二甲基二甲氧基硅烷、甲基三乙氧基硅烷、聚甲基三乙氧基硅烷的任意一种或几种。
进一步的，所述催化剂为钛酸异丙酯、钛酸丁酯或二月桂酸二丁基锡的任意一种或几种。
进一步的，所述防老剂为防老剂A、防老剂RD、防老剂4010、防老剂264任意一种或几种。
本发明与现有技术相比有如下优点：
1)交联剂采用烷氧基硅烷，不仅能够加深密封胶的交联深度，提高硬度和其拉伸粘结强度。交联剂同时与偶联剂配合使用，还可以增强粘结力、调整固化时间，方便施工。
2)所述阻燃剂为氮系阻燃剂20-50份和无机阻燃剂20-50份的混合阻燃，当其配合使用，具有良好的协同阻燃效应，阻燃效果不会随着胶存放时间的延长而变差。
3)选用的填料无毒、绿色环保。
具体实施方式
实施例一
一种高阻燃防火硅酮密封胶，是由下述质量份数的成分制备而成的：
端羟基聚二甲基硅氧烷60份、
阻燃剂40份、
无机填料50份
交联剂10份
偶联剂1份
催化剂4份、
防老剂3份
所述聚二甲基硅氧烷的粘度为20000Pa·s，所述阻燃剂为三聚氰胺、三氧化二锑，所述无机填料为经过表面改性的超细碳酸钙，所述交联剂为甲基三甲氧基硅烷，所述偶联剂为γ-氨丙基甲基二乙氧基硅烷，所述催化剂为钛酸异丙酯，所述防老剂为防老剂A。
实施例二
端羟基聚二甲基硅氧烷80份、
阻燃剂60份、
无机填料60份
交联剂150份
偶联剂2份
催化剂4份、
防老剂4份
所述聚二甲基硅氧烷的粘度为20000Pa·s，所述阻燃剂为磷酸三甲苯酯(TCP)、氢氧化镁，所述无机填料为经过表面改性的超细碳酸钙，所述交联剂为甲基三乙氧基硅烷，所述偶联剂为N-(β-氨乙基)-γ-氨丙基甲基二甲氧基硅烷；所述催化剂为钛酸丁酯，所述防老剂为防老剂RD。
实施例三
端羟基聚二甲基硅氧烷100份、
阻燃剂80份、
无机填料60份
交联剂20份
偶联剂3份
催化剂6份、
防老剂4份
所述聚二甲基硅氧烷的粘度为30000Pa·s，所述阻燃剂为氢氧化铝和三聚氰胺的配合，所述无机填料为气相白炭黑，所述交联剂为乙烯基三丁酮肟基硅烷或四丁酮肟基硅烷，所述偶联γ-氨丙基三乙氧基硅烷；所述催化剂为二月桂酸二丁基锡，所述防老剂为防老剂4010。
实施例四
端羟基聚二甲基硅氧烷120份、
阻燃剂100份、
无机填料80份
交联剂30份
偶联剂4份
催化剂8份、
防老剂7份
所述聚二甲基硅氧烷的粘度为40000Pa·s，所述阻燃剂为氢氧化铝和三聚氰胺尿酸盐(MAC)的配合，所述无机填料为气相白炭黑，所述交联剂为四丁酮肟基硅烷中，所述偶联剂为γ-(2,3-环氧丙氧)丙基三甲氧基硅烷；所述催化剂为二月桂酸二丁基锡，所述防老剂为防老剂264。
实施例五
上述任一实施例中的高阻燃防火硅酮密封胶，是由下述制备步骤制备而成的：按照配方重量称好原料，先将端羟基聚二甲基硅氧烷、无机填料和阻燃剂加入高速搅拌机中搅拌混合均匀，再加入交联剂、偶联剂、催化剂、防老剂，充分搅拌，混合均匀后通入双螺杆混炼挤出机中制得产品。
测试结果
表一
抗拉强度 伸长率 撕裂强度 位移能力
实施例一 3.0MPa 400％ 24MPa 32级
实施例二 3.2MPa 420％ 26MPa 32级
实施例三 3.3MPa 430％ 28MPa 34级
实施例四 4.5MPa 430％ 30MPa 34级
以上仅是本发明的优选实施方式，应当指出的是，上述优选实施方式不应视为对本发明的限制，本发明的保护范围应当以权利要求所限定的范围为准。对于本技术领域的普通技术人员来说，在不脱离本发明的精神和范围内，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (10)

1.一种高阻燃防火硅酮密封胶，是由下述质量份数的成分制备而成的：
端羟基聚二甲基硅氧烷60～120份、
阻燃剂40～100份、
无机填料50～80份
交联剂10～30份
偶联剂1-4份
催化剂4～8份、
防老剂3-7份。
2.如权利要求1所述的高阻燃防火硅酮密封胶，其特征在于，所述聚二甲基硅氧烷的粘度为20000～40000Pa·s。
3.如权利要求1所述的高阻燃防火硅酮密封胶，其特征在于，所述阻燃剂为氮系阻燃剂20-50份和无机阻燃剂20-50份的混合阻燃剂。
4.如权利要求3所述的高阻燃防火硅酮密封胶，其特征在于，所述氮系阻燃剂为三聚氰胺、三聚氰胺尿酸盐(MAC)中的一种或多种的混合物。
5.如权利要求3所述的阻燃型硅酮结构密封胶，其特征在于，所述无机阻燃剂为三氧化二锑、氢氧化镁、氢氧化铝及硅系阻燃剂中的一种或几种的混合物。
6.如权利要求1所述的高阻燃防火硅酮密封胶，其特征在于，所述无机填料为经过表面改性的超细碳酸钙或气相白炭黑。
7.如权利要求1所述的高阻燃防火硅酮密封胶，其特征在于，所述交联剂为甲基三甲氧基硅烷、甲基三乙氧基硅烷、乙烯基三丁酮肟基硅烷或四丁酮肟基硅烷中的一种或多种的混合物。
8.如权利要求1所述的高阻燃防火硅酮密封胶，其特征在于，所述偶联剂为γ-氨丙基甲基二乙氧基硅烷、N-(β-氨乙基)-γ-氨丙基甲基二甲氧基硅烷、γ-氨丙基三乙氧基硅烷、γ-(2,3-环氧丙氧)丙基三甲氧基硅烷的任意一种或几种；所述交联剂为甲基三甲氧基硅烷、二甲基二甲氧基硅烷、甲基三乙氧基硅烷、聚甲基三乙氧基硅烷的任意一种或几种。
9.如权利要求1所述的高阻燃防火硅酮密封胶，其特征在于，所述催化剂为钛酸异丙酯、钛酸丁酯或二月桂酸二丁基锡中的一种或几种的混合物。
10.如权利要求1所述的高阻燃防火硅酮密封胶，其特征在于，所述防老剂为防老剂A、防老剂RD、防老剂4010、防老剂264中的一种或几种的混合物。
CN201711127518.1A 2017-11-15 2017-11-15 一种高阻燃防火硅酮密封胶 Pending CN107760254A (zh)