CN107760134A - A kind of water paint and preparation method thereof - Google Patents
A kind of water paint and preparation method thereof Download PDFInfo
- Publication number
- CN107760134A CN107760134A CN201711054420.8A CN201711054420A CN107760134A CN 107760134 A CN107760134 A CN 107760134A CN 201711054420 A CN201711054420 A CN 201711054420A CN 107760134 A CN107760134 A CN 107760134A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- extraordinary
- paint
- base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention provides a kind of water paint, and it is made up of the component of following specific parts by weight：35 parts of 7% extraordinary 20 parts of silicate liquid, 5 parts of water, 40 parts of base paint and base-material；The water paint has good color unfading, and the application for passing through pearl essence so that there is the water paint can possess multiple color for it, the defects of existing water paint color is more single be avoided, so as to more be liked by consumer；And the present invention discloses the preparation method of the water paint simultaneously, whole preparation process is easily operated, and it is convenient that material obtains, and has relatively low cost.
Description
【Technical field】
The present invention relates to building field finishing material, and in particular to a kind of water paint and preparation method thereof.
【Background technology】
Water paint is that compared with the coating of organic solvent, water paint both subtracted as medium and the coating of dilution with water
The discharge of rare solvent (VOC) can save organic material resource again, be volatilized so as to greatly reduce organic solvent in coating
To the fire hazard in the pollution and work progress of air, water is resource extremely abundant on the earth, and it is taken conveniently, and cost is low
It is honest and clean, used as the solvent in coating, destruction or less will not be produced to water resource.Therefore, water paint had both reduced volatilization
The discharge of property organic solvent, can save resource, the energy, while convenience in transport and storage again.With the enhancing of people's environmental consciousness,
It is also more and more tighter to the relevant environmental regulation of the production and application of chemical products so that water paint has turned into modern coatings industry hair
The main flow direction of exhibition.
Used water paint in the market, mostly using water-based acrylic acid synthesizing resin emulsion as base-material, and by titanium
The water paint that white powder is pigment, calcium carbonate is main stuffing, this coating there is color colour retention difference with color more
The defects of single.
【The content of the invention】
The technical problems to be solved by the invention are to provide a kind of water paint and preparation method thereof.
The present invention is that solve above-mentioned technical problem by the following technical programs：A kind of water paint, the water paint by
The component of following specific parts by weight is made：
35 parts of 7% extraordinary 20 parts of silicate liquid, 5 parts of water, 40 parts of base paint and base-material；
Wherein：
7% extraordinary silicate liquid is mixed by following parts by weight of component and with 800r/min Rate Dispersion to uniformly without particle
And obtain：70 parts of 928 parts of water, 2 parts of industrial preservative and extraordinary silicate；
Base-material is made up of the component of following parts by weight：221.5 parts of water, 1 part of AMP95 multifunctional assistants, industrial preservative 1
Part, 10 parts of propane diols, 10 parts of lauryl alcohol fat, 250 parts of silicone acrylic emulsion, 6 parts of 50%TT-935 thickeners and mineral oil antifoam agent
0.5 part；
Base paint is made up of the component of following parts by weight：629 parts of water, 2 parts of industrial preservative, anion surfactant 4
Part, 10 parts of propane diols, 8 parts of lauryl alcohol fat, 4 parts of mineral oil antifoam agent, 25 parts of organic siliconresin, 1 part of AMP95 multifunctional assistants,
75 parts of nacreous mica powder, above-mentioned 7% extraordinary 40 parts of silicate liquid, 200 parts of 2179 acrylic elastic emulsion, polyurethane thickener 2
Part.
At the same time, the preparation method of above-mentioned water paint is disclosed, the preparation method specifically includes following operating procedure：
(1), the preparation of 7% extraordinary silicate liquid：Weigh the component for getting out following parts by weight：928 parts of water, industrial antisepsis
70 parts of the parts by weight of agent 2 and extraordinary silicate, each component is mixed and with 800r/min Rate Dispersion to uniformly being produced without particle
7% extraordinary silicate liquid, it is stand-by；
(2), the preparation of base-material：Weigh the component for getting out following parts by weight：221.5 parts of water, AMP95 multifunctional assistants 1
Part, 1 part of industrial preservative, 10 parts of propane diols, 10 parts of lauryl alcohol fat, 250 parts of silicone acrylic emulsion, 6 parts of 50%TT-935 thickeners and
0.5 part of mineral oil antifoam agent；First by water, AMP95 multifunctional assistants, industrial preservative, propane diols, lauryl alcohol fat and silicone acrylic emulsion
Mix and stirred with 400-600r/min speed, 50%TT-935 thickeners, completely stirring are added during stirring
Mineral oil antifoam agent is put into again after uniformly, is continued to be stirred until homogeneous and is produced the base-material, it is stand-by；
(3), the preparation of base paint：Weigh the component for getting out following parts by weight：629 parts of water, 2 parts of industrial preservative, the moon
4 parts of ionic surface active agent, 10 parts of propane diols, 8 parts of lauryl alcohol fat, 4 parts of mineral oil antifoam agent, 25 parts of organic siliconresin, AMP95
1 part of multifunctional assistant, 75 parts of nacreous mica powder, 7% extraordinary 40 parts of silicate liquid, 2179 acrylic acid elasticity made from step (1)
2 parts of 200 parts of emulsion and polyurethane thickener；First take 490 parts of water, and by industrial preservative, anion surfactant, third
Glycol, lauryl alcohol fat and 2 parts of mineral oil antifoam agents add, and are stirred using 400-600r/min stir speed (S.S.)；Then throw
Enter organic siliconresin, stirred using 600-1000r/min stir speed (S.S.)；AMP95 multifunctional assistants are added afterwards,
1200r/min disperses 30min；Then remaining 2 parts of mineral oil antifoam agents are added, after stirring, put into 2179 acrylic acid bullets
7% extraordinary silicate liquid made from property emulsion and step (1), 1000r/min speed stir；Add remaining 139
Part water stirs, and adds polyurethane thickener under 800-1000r/min revolution afterwards, is adopted after adding polyurethane thickener
10min is stirred with 900-1000r/min stir speed (S.S.)；It is eventually adding nacreous mica powder and stirs and produces the base paint,
It is stand-by；
(4), prepared by final products：Weigh the component for getting out following parts by weight：7% extraordinary silicic acid made from step (1)
40 parts of base paint made from 20 parts of saline solution, 5 parts of water, 35 parts of base-material made from step (2) and step (3)；First by 7% extraordinary silicon
Hydrochlorate liquid is mixed and stirred for uniformly, adding base paint afterwards with water, and uses dispersion impeller to be made with 200r/min speed stirring
Required colorful particle, be subsequently added into base-material it is well mixed then the i.e. described water paint of final products.
Further, the viscosity of the water paint is adjusted using 20%TT-935 thickeners.
The beneficial effects of the present invention are：
A kind of water paint is provided, not only with good color unfading, and by the application of nacreous mica powder,
Enable it that there is the water paint to possess multiple color, avoid the defects of existing water paint color is more single, from
And more it can be liked by consumer；The preparation method of the water paint is disclosed simultaneously, and whole method is easily operated, and material obtains
It is convenient to take, and has relatively low cost.
【Embodiment】
A kind of water paint of the present invention, the water paint are made up of the component of following specific parts by weight：
35 parts of 7% extraordinary 20 parts of silicate liquid, 5 parts of water, 40 parts of base paint and base-material；
Wherein：
7% extraordinary silicate liquid is mixed by following parts by weight of component and with 800r/min Rate Dispersion to uniformly without particle
And obtain：70 parts of 928 parts of water, 2 parts of industrial preservative and extraordinary silicate；
Base-material is made up of the component of following parts by weight：221.5 parts of water, 1 part of AMP95 multifunctional assistants, industrial preservative 1
Part, 10 parts of propane diols, 10 parts of lauryl alcohol fat, 250 parts of silicone acrylic emulsion, 6 parts of 50%TT-935 thickeners and mineral oil antifoam agent
0.5 part；
Base paint is made up of the component of following parts by weight：629 parts of water, 2 parts of industrial preservative, anion surfactant 4
Part, 10 parts of propane diols, 8 parts of lauryl alcohol fat, 4 parts of mineral oil antifoam agent, 25 parts of organic siliconresin, 1 part of AMP95 multifunctional assistants,
75 parts of nacreous mica powder, above-mentioned 7% extraordinary 40 parts of silicate liquid, 200 parts of 2179 acrylic elastic emulsion, polyurethane thickener 2
Part.
At the same time, the invention provides the preparation method of above-mentioned water paint, the preparation method to specifically include following behaviour
Make step：
(1), the preparation of 7% extraordinary silicate liquid：Weigh the component for getting out following parts by weight：928 parts of water, industrial antisepsis
70 parts of the parts by weight of agent 2 and extraordinary silicate, each component is mixed and 800r/min Rate Dispersion without particle to uniformly producing
7% extraordinary silicate liquid, it is stand-by；
(2), the preparation of base-material：Weigh the component for getting out following parts by weight：221.5 parts of water, AMP95 multifunctional assistants 1
Part, 1 part of industrial preservative, 10 parts of propane diols, 10 parts of lauryl alcohol fat, 250 parts of silicone acrylic emulsion, 6 parts of 50%TT-935 thickeners and
0.5 part of mineral oil antifoam agent；First water, AMP95 multifunctional assistants, industrial preservative, propane diols, two alcohol esters and silicone acrylic emulsion are mixed
The speed for merging 400r/min stirs, and 50%TT-935 thickeners is added during stirring, after stirring completely
Mineral oil antifoam agent is put into again, is continued to be stirred until homogeneous and is produced the base-material, it is stand-by；
(3), the preparation of base paint：Weigh the component for getting out following parts by weight：629 parts of water, 2 parts of industrial preservative, the moon
4 parts of ionic surface active agent, 10 parts of propane diols, 8 parts of lauryl alcohol fat, 4 parts of defoamer, 25 parts of organic siliconresin, AMP95 are multi-functional
1 part of auxiliary agent, 75 parts of nacreous mica powder, 7% extraordinary 40 parts of silicate liquid, 2179 acrylic elastic emulsions 200 made from step (1)
2 parts of part and polyurethane thickener；First take 490 parts of water, and by industrial preservative, anion surfactant, propane diols, ten
Two alcohol esters and 2 parts of mineral oil antifoam agents add, and are stirred using 400-600r/min stir speed (S.S.)；Then put into organic
Silicones, stirred using 600-1000r/min stir speed (S.S.)；AMP95 multifunctional assistants, 1200r/min are added afterwards
Scattered 30min at a high speed；Then remaining 2 parts of mineral oil antifoam agents are added, after stirring, put into 2179 acrylic elastic emulsions
With step (1) made from 7% extraordinary silicate liquid, 1000r/min high-speed stirreds are uniform；Add remaining 139 parts of water stirring
Uniformly, polyurethane thickener is added under 800-1000r/min revolution afterwards, 900- is used after adding polyurethane thickener
1000r/min stir speed (S.S.) stirring 10min；It is eventually adding nacreous mica powder and stirs and produces the base paint, it is stand-by；
(4), prepared by final products：Weigh the component for getting out following parts by weight：7% extraordinary silicic acid made from step (1)
40 parts of base paint made from 20 parts of saline solution, 5 parts of water, 35 parts of base-material made from step (2) and step (3)；First by 7% extraordinary silicon
Hydrochlorate liquid is mixed and stirred for uniformly, adding base paint afterwards with water, and using needed for the support of dispersion impeller 200r/min stirring at low speed
Colorful particle, be subsequently added into base-material it is well mixed then the i.e. described water paint of final products.
In the present invention, the viscosity of water paint can be adjusted by using 20%TT-935 thickeners.And need
Illustrate, pearl essence has multiple color, can be selected according to demand；In each step preparation process of the present invention, each group
The input or addition divided are to weigh ready amount in the case of without additional description；In addition, involved by the present invention
Percentage is mass percent in the case of without specified otherwise；And it should be noted that industry employed in the present invention
Preservative steps this MC preservative from sea visitor, and AMP95 multifunctional assistants are DOW Chemical AMP95 multifunctional assistants, and TT-935 increases
Thick dose is DOW Chemical TT-935 thickeners.
In order to be preferably described to the present invention, applicant illustrates following examples.
Embodiment 1
928kg water, 2kg industrial preservatives and 70kg special type silicate are weighed, each component is mixed into simultaneously 800r/min high speeds
The 7% extraordinary silicate liquid that 1000kg is uniformly produced without particle is dispersed to, it is stand-by；
Weigh 221.5kg water, 1kg AMP95 multifunctional assistants, 1kg industrial preservatives, 10kg propane diols, 10kg lauryl alcohols
Fat and 250kg silicone acrylic emulsions simultaneously mix, and 400r/min stirring at low speed adds 6kg's to uniform during stirring at low speed
50%TT-935 thickeners, put into 0.5kg mineral oil antifoam agents again after stirring completely, continue to be stirred until homogeneous and produce
500kg base-material, it is stand-by；
Weigh 490kg water, 2kg industrial preservatives, 4kg anion surfactants, 10kg propane diols, 8kg lauryl alcohols fat,
And 2kg mineral oil antifoam agents and mix, stirred using 400r/min stir speed (S.S.)；Then 25kg organosilicon trees are put into
Fat, stirred using 800r/min stir speed (S.S.)；1kg AMP95 multifunctional assistants are added afterwards, and 1200r/min divides at a high speed
Dissipate 30min；Then 2kg defoamers are added, after stirring, successively put into 200kg 2179 acrylic elastic emulsions and
7% extraordinary silicate liquid made from 40kg, 1000r/min high-speed stirreds are uniform；Add 139kg water to stir, Zhi Hou
2kg polyurethane thickeners are added under 800r/min revolution, 1000r/min stir speed (S.S.) is used after addition polyurethane thickener
Stir 10min；It is eventually adding 75kg nacreous mica powder and stirs and produces base paint, it is stand-by；
7% extraordinary silicate liquid and 50kg water made from 200kg is weighed to be mixed and stirred for uniformly.400kg systems are added afterwards
The base paint obtained, and colorful particle of the dispersion impeller needed for the support of 200r/min stirring at low speed is used, it is subsequently added into 350kg and is made
Base-material it is well mixed then final products are the water paint.
Embodiment 2
Compared with Example 1, difference existing for the present embodiment is：
(a) 490kg water, 2kg industrial preservatives, 4kg anion surfactants, 10kg propane diols, 8kg lauryl alcohols are weighed
Fat and 2kg mineral oil antifoam agents simultaneously mix, and are stirred afterwards using 600r/min stir speed (S.S.)；(b) it is organic to put into 25kg
After silicones, the stir speed (S.S.) used is 600r/min；(c) 2kg polyurethane thickeners are added under 900r/min revolution
Enter；(d) add after polyurethane thickener and 10min is stirred using 900r/min stir speed (S.S.).
Embodiment 3
Compared with Example 1, difference existing for the present embodiment is：
(a) 490kg water, 2kg industrial preservatives, 4kg anion surfactants, 10kg propane diols, 8kg lauryl alcohols are weighed
Fat and 2kg mineral oil antifoam agents simultaneously mix, and are stirred afterwards using 500r/min stir speed (S.S.)；(b) it is organic to put into 25kg
After silicones, the stir speed (S.S.) used is 1000r/min；(c) 2kg polyurethane thickeners are under 1000r/min revolution
Add；(d) add after polyurethane thickener and 10min is stirred using 950r/min stir speed (S.S.).
In addition, in order to verify the performance of water paint of the present invention, the water paint obtained by above-described embodiment 1-3 is carried out
Performance detection, testing result are as shown in table 1 below.And through as shown in Table 1, water paint of the present invention not only there is good color to protect
Color performance；And it is preferable with the performance such as water resistance, alkali resistance, adhesive strength is high, and the features such as be easy to construction.
The water paint performance measurement result of table 1
To sum up, water paint of the present invention has good color unfading, and the application for passing through pearl essence so that its
Can possess multiple color with the water paint, avoid the defects of existing water paint color is more single, so as to
More liked by consumer；The preparation method of the water paint is disclosed simultaneously, and whole method is easily operated, and material obtains just
Victory, there is relatively low cost.
Claims (3)
- A kind of 1. water paint, it is characterised in that：The water paint is made up of the component of following specific parts by weight：35 parts of 7% extraordinary 20 parts of silicate liquid, 5 parts of water, 40 parts of base paint and base-material；Wherein：7% extraordinary silicate liquid mixed by following parts by weight of component and with 800r/min Rate Dispersion to uniformly without particle and ：70 parts of 928 parts of water, 2 parts of preservative and extraordinary silicate；Base-material is made up of the component of following parts by weight：221.5 parts of water, 1 part of AMP95 multifunctional assistants, 1 part of industrial preservative, third 0.5 part of 10 parts of glycol, 10 parts of lauryl alcohol fat, 250 parts of silicone acrylic emulsion, 6 parts of 50%TT-935 thickeners and mineral oil antifoam agent；Base paint is made up of the component of following parts by weight：629 parts of water, 2 parts of industrial preservative, 4 parts of anion surfactant, third 1 part of 10 parts of glycol, 8 parts of lauryl alcohol fat, 4 parts of mineral oil antifoam agent, 25 parts of organic siliconresin, AMP95 multifunctional assistants mica pearl 75 parts of light powder, above-mentioned 7% extraordinary 40 parts of silicate liquid, 200 parts of 2179 acrylic elastic emulsion, 2 parts of polyurethane thickener.
- A kind of 2. preparation method of the water paint described in claim 1, it is characterised in that：The preparation method specifically includes as follows Operating procedure：(1), the preparation of 7% extraordinary silicate liquid：Weigh the component for getting out following parts by weight：928 parts of water, industrial preservative 2 70 parts of parts by weight and extraordinary silicate, each component is mixed and with 600-800r/min Rate Dispersion to being without particle uniformly 7% extraordinary silicate liquid is obtained, it is stand-by；(2), the preparation of base-material：Weigh the component for getting out following parts by weight：221.5 parts of water, 1 part of AMP95 multifunctional assistants, work 1 part of industry preservative, 10 parts of propane diols, 10 parts of lauryl alcohol fat, 250 parts of silicone acrylic emulsion, 6 parts of 50%TT-935 thickeners and mineral Oily 0.5 part of defoamer；First water, AMP95 multifunctional assistants, industrial preservative, propane diols, lauryl alcohol fat are mixed with silicone acrylic emulsion And 400-600r/min speed stirs, 50%TT-935 thickeners are added during stirring, are stirred completely Put into mineral oil antifoam agent again afterwards, continue to be stirred until homogeneous and produce the base-material, it is stand-by；(3), the preparation of base paint：Weigh the component for getting out following parts by weight：629 parts of water, 2 parts of industrial preservative, anion 4 parts of surfactant, 10 parts of propane diols, 8 parts of lauryl alcohol fat, 4 parts of mineral oil antifoam agent, 25 parts of organic siliconresin, the more work(of AMP95 Can 1 part of auxiliary agent, 75 parts of nacreous mica powder, 7% extraordinary 40 parts of silicate liquid, 2179 acrylic elastic emulsions made from step (1) 200 parts and 2 parts of polyurethane thickener；First take 490 parts of water, and by industrial preservative, anion surfactant, propane diols, Lauryl alcohol fat and 2 parts of mineral oil antifoam agents add, and are stirred using 400-600r/min stir speed (S.S.)；Then input has Machine silicones, stirred using 600-1000r/min stir speed (S.S.)；AMP95 multifunctional assistants, 1200r/ are added afterwards Min Rate Dispersions 30min；Then remaining 2 parts of mineral oil antifoam agents are added, after stirring, input 2179 acrylic acid elasticity 7% extraordinary silicate liquid made from emulsion and step (1), 800-1000r/min speed stir；Add remaining 139 Part water stirs, and adds polyurethane thickener under 800-1000r/min revolution afterwards, is adopted after adding polyurethane thickener 10min is stirred with 900-1000r/min stir speed (S.S.)；It is eventually adding nacreous mica powder and stirs and produces the base paint, It is stand-by；(4), prepared by final products：Weigh the component for getting out following parts by weight：7% extraordinary silicate liquid made from step (1) 20 parts, 5 parts of water, 40 parts of base paint made from 35 parts of base-material made from step (2) and step (3)；First by 7% extraordinary silicate Liquid is mixed and stirred for uniformly, adding base paint afterwards with water, and uses dispersion impeller to be made required with 200r/min speed stirring Colorful particle, be subsequently added into base-material it is well mixed then the i.e. described water paint of final products.
- A kind of 3. preparation method of water paint according to claim 2, it is characterised in that：The viscosity of the water paint Adjusted using 20%TT-935 thickeners.