CN104194457B - Sand wall-like multicolor finish and preparation method thereof - Google Patents

Sand wall-like multicolor finish and preparation method thereof Download PDF

Info

Publication number
CN104194457B
CN104194457B CN201410438894.2A CN201410438894A CN104194457B CN 104194457 B CN104194457 B CN 104194457B CN 201410438894 A CN201410438894 A CN 201410438894A CN 104194457 B CN104194457 B CN 104194457B
Authority
CN
China
Prior art keywords
parts
color
sand
base paint
multicolor finish
Prior art date
Application number
CN201410438894.2A
Other languages
Chinese (zh)
Other versions
CN104194457A (en
Inventor
温宇莹
Original Assignee
亚士创能科技(上海)股份有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 亚士创能科技(上海)股份有限公司 filed Critical 亚士创能科技(上海)股份有限公司
Priority to CN201410438894.2A priority Critical patent/CN104194457B/en
Publication of CN104194457A publication Critical patent/CN104194457A/en
Application granted granted Critical
Publication of CN104194457B publication Critical patent/CN104194457B/en

Abstract

The invention provides a kind of sand wall-like multicolor finish and preparation method thereof.The component and the weight content of each component that the color-mixed base paint of the sand wall-like multicolor finish is included be:Deionized water:40 20 parts;Dispersant:0.1 1 parts;Defoamer:0.1 1 parts;Preservative:0.1 1 parts;Color sand:25 50 parts;Mica sheet:0.1 5 parts;Acrylic emulsion:30 10 parts;Coalescents:12 parts;Gel (includes deionized water, polymerization inhibitor and special modified synthesizing flaky zeopan):1.05 7.01 parts;Thickener:0.1 1 parts;Wherein electrical conductivity≤6 μ the S/cm of deionized water.The sand wall-like multicolor finish that the present invention is provided, including with filling system that artificial burning colorful sand is main aggregate, so that the good stability of sand wall-like multicolor finish, weatherability and water-tolerant, without colour fading risk, and the color-mixed base paint and continuous phase emulsion two-phase component of dispersed phase are comprised only in sand wall-like multicolor finish, production technology is relatively simple, can improve production efficiency.

Description

Sand wall-like multicolor finish and preparation method thereof

Technical field

The present invention relates to paint field, more specifically, it is related to a kind of sand wall-like multicolor finish and many color coatings of sand wall-like The preparation method of material.

Background technology

In recent years, water-in-water multicolor coating and its derived product (water-in-water multicolor coating containing sand) are because of its imitative stone effect true to nature Really, the characteristic such as low VOC (volatile organic matter) is used widely.Current water-in-water multicolor coating typically has two kinds of product shapes Formula, a kind of is that, with imitative plane marbling effect, the multicolor finish without sand, another kind is with imitative baked wheaten cake face marbling effect, contains The multicolor finish of sand.Any multicolor finish all possesses following general character:

Contain three phase components in multicolor finish system, i.e.,:Dispersed phase base paint, Protection glue and continuous phase (or cladding light Oil), need to prepare dispersed phase base paint in advance in its manufacturing process, and substep is added in Protection glue and continuous phase, is passed through Stirring obtains water-in-water multicolor coating, in dispersed phase base paint, typically using titanium dioxide, kaolin, calcium carbonate as filling out Material, using aqueous color paste (such as carbon black, iron oxide pigment and all kinds of organic pigments) as pigment coloring.

Because current water-in-water multicolor coating is three phase components, production technology is complex, coating system stability compared with Difference, meanwhile, using water-in-water multicolor coating obtained in the mode that aqueous color paste is mixed colours, easily because mill base weatherability is poor, system is water-fast The factors such as property difference cause to fade or grow dim after wall on coating.

The content of the invention

It is contemplated that at least solving one of technical problem present in prior art.

Therefore, the purpose of the first aspect of the invention is, there is provided a kind of sand wall-like multicolor finish, by weight content 30%~70% color-mixed base paint and the continuous phase emulsion composition of weight content 70%~30%;

The color-mixed base paint is grouped into by each group of following weight content:

Deionized water:40-20 parts;

Dispersant:0.1-1 parts;

Defoamer:0.1-1 parts;

Preservative:0.1-1 parts;

Color sand:25-50 parts;

Mica sheet:0.1-5 parts;

Acrylic emulsion:30-10 parts;

Coalescents:1-2 parts;

Gel:1.05-7.01 parts;

Thickener:0.1-1 parts;

Wherein, the component and the weight content of each component that the gel is included be:

The deionized water:1-5 parts;

Polymerization inhibitor:0-0.01 parts;

Special modified synthesizing flaky zeopan:0.05-2 parts;

And electrical conductivity≤6 μ the S/cm of the deionized water;The color sand is artificial burning colorful sand;The mica sheet it is straight Footpath is 3-5mm;The acrylic emulsion is from the pure acrylic latex that glass transition temperature is 0-20 DEG C;The dispersant is poly- carboxylic Acid ammonium salt dispersant;The defoamer is common mineral oils defoamer;The preservative derives for BIT class Thing;TEXANOL ester alcohol of the coalescents from Eastman Chemical;The polymerization inhibitor is selected and contains calcium, magnesium, aluminium and ammonium The salt-mixture of one or more in ion;The special modified synthesizing flaky zeopan selects RD, GTS, S-482's Any one appoints several mixing.

The form and aspect stabilization of above-mentioned multicolor finish, possesses high weatherability and water resistance, and without fading, growing dim etc., quality is asked Topic, and color-mixed base paint and continuous phase emulsion two-phase component are comprised only in multicolor finish, production technology is relatively simple, production efficiency It is high.

The purpose of the second aspect of the invention is, there is provided a kind of preparation method of sand wall-like multicolor finish.

To achieve the above object, the embodiment of one aspect of the invention provides a kind of toning base of sand wall-like multicolor finish Plinth paint, comprising component and the weight ratio of each component be:Deionized water:40-20 parts;Dispersant:0.1-1 parts;Defoamer:0.1- 1 part;Preservative:0.1-1 parts;Color sand:25-50 parts;Mica sheet:0.1-5 parts;Acrylic emulsion:30-10 parts;Coalescents:1- 2 parts;Gel:1.05-7.01 parts;Thickener:0.1-1 parts;Wherein, the gel is included component and the weight content of each component For:The deionized water:1-5 parts;Polymerization inhibitor:0-0.01 parts;Special modified synthesizing flaky zeopan:0.05-2 parts, And electrical conductivity≤6 μ the S/cm of the deionized water.

The color-mixed base paint of the sand wall-like multicolor finish that the above embodiment of the present invention is provided, using color sand as main aggregate, Ore in sand form is added after passing through with current water-in-water multicolor coating containing sand (to be prepared in water-in-water multicolor coating and added after viscosity stabilization Ore in sand form) mode compare, the stability of coating that the color-mixed base paint (dispersed phase) provided using above-described embodiment is made is higher, The system of effectively prevent is swollen, bleeding the problems such as;Meanwhile, the use of the color-mixed base paint so that be made up of the color-mixed base paint Sand wall-like multicolor finish in comprise only two kinds of components of color-mixed base paint and continuous phase emulsion, with existing water-in-water multicolor coating In typically contain dispersed phase base paint, Protection glue and compared with continuous phase emulsion three-phase component, its manufacture craft is simpler, can Production efficiency is obviously improved, while the stability of the system of raising.

In addition, the color-mixed base paint of the sand wall-like multicolor finish of the above embodiment of the present invention offer also has following additional skill Art feature:

According to one embodiment of present invention, the dispersant is polycarboxylic acids ammonium salt dispersant;The defoamer is common Mineral oil defoaming agent;The preservative is BIT analog derivative;The color sand is artificial burning colorful sand;It is described A diameter of 3-5mm of mica sheet;The acrylic emulsion is from the pure acrylic latex that glass transition temperature is 0-20 DEG C;It is described into The TEXANOL ester alcohols of film selection of auxiliary Eastman Chemical;The polymerization inhibitor is selected containing in calcium, magnesium, aluminium and ammonium ion The salt-mixture of one or more;The special modified synthesizing flaky zeopan selects RD, GTS, S-482 any one or Appoint several mixing.

According to one embodiment of present invention, the artificial burning colorful sand includes composite color paste and quartz sand, wherein described Composite color paste includes inorganic and/or organic pigment, uvioresistant auxiliary agent, dispersant and the acrylic emulsion.

According to one embodiment of present invention, the weight content of the color-mixed base paint is 40%, the continuous phase emulsion Weight content be 60%;Or, the weight content of the color-mixed base paint is 50%, the weight content of the continuous phase emulsion It is 50%.

The embodiment of third aspect present invention provides a kind of preparation method of sand wall-like multicolor finish, including following step Suddenly:Step S102, sequentially adds dispersant, the 0.1-1 mass parts of 0.1-1 mass parts in the deionized water to 40-20 mass parts Defoamer and 0.1-1 mass parts preservative, and stir, wherein the electrical conductivity≤6 μ S/cm of the deionized water;Step Rapid S104, sequentially adds the color sand of 25-50 mass parts and the mica sheet of 0.1-5 mass parts, and stir;Step S106, The acrylic emulsion of 30-10 mass parts is gradually added into again, and is slowly added to the coalescents of 1-2 mass parts, and stir;Step Rapid S108, adds and is changed by the deionized water of 1-5 mass parts, the polymerization inhibitor of 0-0.01 mass parts and the special of 0.05-2 mass parts Property the gel that is made of synthesizing flaky zeopan and 0.1-1 mass parts thickener, stir evenly, color-mixed base paint is obtained;Step Rapid S110, is repeated several times the step S102 to the step S108, prepares the color-mixed base paint of different colours;Step S112, by the color-mixed base paint continuous phase emulsion of addition of different colours, is obtained the sand wall-like multicolor finish, wherein institute It is 30%~70% to state the weight content of color-mixed base paint, and the weight content of the continuous phase emulsion is 70%~30%.

In addition, the preparation method of the sand wall-like multicolor finish of the above embodiment of the present invention offer also has following supplementary technology Feature:

According to one embodiment of present invention, in the step S104, the color sand is artificial burning colorful sand, by heat Wind calcine technology, it is compound by what is be made containing inorganic and/or organic pigment, uvioresistant auxiliary agent, dispersant and acrylic emulsion Mill base is sintered in quartz sand surface, and the artificial burning colorful sand of predetermined size is obtained by screening.

According to one embodiment of present invention, in the step S112, by controlling the speed of dispersing shear, it is obtained and contains There is the sand wall-like multicolor finish of different size color dot.

Additional aspect of the invention and advantage will become obvious in following description section, or by practice of the invention Recognize.

Brief description of the drawings

Of the invention above-mentioned and/or additional aspect and advantage will become from description of the accompanying drawings below to embodiment is combined Substantially and be readily appreciated that, wherein:

Fig. 1 is the schematic flow diagram of the preparation method of the sand wall-like multicolor finish according to one embodiment of the invention.

Specific embodiment

It is below in conjunction with the accompanying drawings and specific real in order to be more clearly understood that the above objects, features and advantages of the present invention Mode is applied to be further described in detail the present invention.It should be noted that in the case where not conflicting, the implementation of the application Feature in example and embodiment can be mutually combined.

Many details are elaborated in the following description in order to fully understand the present invention, but, the present invention may be used also Implemented with being different from mode described here using other, therefore, protection scope of the present invention does not receive following public tool The limitation of body embodiment.

A kind of sand wall-like multicolor finish for providing according to some embodiments of the invention, by the tune of weight content 30%~70% The continuous phase emulsion composition of color base paint and weight content 70%~30%;

The color-mixed base paint is grouped into by each group of following weight content:

Deionized water:40-20 parts;

Dispersant:0.1-1 parts;

Defoamer:0.1-1 parts;

Preservative:0.1-1 parts;

Color sand:25-50 parts;

Mica sheet:0.1-5 parts;

Acrylic emulsion:30-10 parts;

Coalescents:1-2 parts;

Gel:1.05-7.01 parts;

Thickener:0.1-1 parts;

Wherein, the component and the weight content of each component that the gel is included be:

The deionized water:1-5 parts;

Polymerization inhibitor:0-0.01 parts;

Special modified synthesizing flaky zeopan:0.05-2 parts;

And electrical conductivity≤6 μ the S/cm of the deionized water;The color sand is artificial burning colorful sand;The mica sheet it is straight Footpath is 3-5mm;The acrylic emulsion is from the pure acrylic latex that glass transition temperature is 0-20 DEG C;The dispersant is poly- carboxylic Acid ammonium salt dispersant;The defoamer is common mineral oils defoamer;The preservative derives for BIT class Thing;TEXANOL ester alcohol of the coalescents from Eastman Chemical;The polymerization inhibitor is selected and contains calcium, magnesium, aluminium and ammonium The salt-mixture of one or more in ion;The special modified synthesizing flaky zeopan selects RD, GTS, S-482's Any one appoints several mixing.

The color-mixed base paint of the sand wall-like multicolor finish that the above embodiment of the present invention is provided, using color sand as main aggregate, Ore in sand form is added after passing through with current water-in-water multicolor coating containing sand (to be prepared in water-in-water multicolor coating and added after viscosity stabilization Ore in sand form) mode compare, the stability of coating that the color-mixed base paint provided using above-described embodiment is made is higher, is prevented effectively from System is swollen, bleeding the problems such as;Meanwhile, the use of the color-mixed base paint so that the sand wall-like being made up of the color-mixed base paint Two kinds of components of color-mixed base paint (dispersed phase) and continuous phase emulsion are comprised only in multicolor finish, with existing water-in-water multicolor coating In typically contain dispersed phase base paint, Protection glue and compared with continuous phase emulsion three-phase component, its manufacture craft is simpler, can Production efficiency is obviously improved, while the stability of the system of raising.

In a specific embodiment of the invention, the electrical conductivity≤6 μ S/cm of the deionized water (micro-Siemens/centimetre), In case color-mixed base paint flocculates;

The dispersant is polycarboxylic acids ammonium salt dispersant, it is possible to provide preferable system water resistance;

The defoamer is common mineral oils defoamer;

The preservative is BIT analog derivative, with spectrum bactericidal properties;

The color sand is artificial burning colorful sand, rich color, form and aspect stabilization, low cost;

A diameter of 3-5mm of the mica sheet, is that natural mica is obtained after crushing;

The acrylic emulsion is 0-20 DEG C of pure acrylic latex from glass transition temperature, with excellent water resistance and Weatherability;

TEXANOL ester alcohol of the coalescents from Eastman Chemical (EASTMAN CHEMICAL COMPANY) (2,2,4- trimethyl -1,3 pentanediol mono isobutyrates), using the teaching of the invention it is possible to provide the excellent scrub resistance of film, color developing, stable storing Property etc.;

The polymerization inhibitor is selected and contains the salt-mixture of one or more in calcium, magnesium, aluminium and ammonium ion;

The special modified synthesizing flaky zeopan selects RD, GTS, S-482 any one or appoint several mixed Close.

In a specific example, the artificial burning colorful sand includes composite color paste and quartz sand, wherein the composite color paste Including inorganic and/or organic pigment, uvioresistant auxiliary agent, dispersant and the acrylic emulsion.By hot blast calcine technology, will The composite color paste being made containing inorganic and/or organic pigment, uvioresistant auxiliary agent, dispersant and acrylic emulsion is sintered in quartz Sand surface, and the artificial burning colorful sand of different-grain diameter is obtained by screening, the artificial burning colorful sand good waterproof performance, bonding is firm, Pliability is good, and weatherability is strong, rich color, form and aspect stabilization, low cost.

In a specific example of the invention, the weight content of the color-mixed base paint is 40%, the continuous phase emulsion Weight content be 60%.

In another specific example of the invention, the weight content of the color-mixed base paint is 50%, the continuous phase breast The weight content of liquid is 50%.

The sand wall-like multicolor finish that the above embodiment of the present invention is provided, including the above-mentioned toning with color sand as main stuffing Two kinds of components of base paint and continuous phase emulsion, on the one hand, the form and aspect stabilization of color sand, water resistance and good weatherability, and then cause many Color coating material not fugitive color, water resistance and good weatherability, the stability of coating are higher, and the system of effectively prevent is swollen, bleeding etc. is asked Topic, improves the quality of product, compared with the colorful sand wall-like texture coating of water-water of the prior art, does not use aqueous color paste Coloring, it is to avoid the problem (aqueous color paste particularly selected of caused multicolor finish colour fading after because being mixed colours using aqueous color paste In the case of weatherability difference);On the other hand, two kinds of components of sand wall-like multicolor finish, including color-mixed base paint and continuous phase emulsion, Compared with the colorful sand wall-like texture coating of the existing water-water containing three kinds of components, production technology is relatively simple, can improve product The production efficiency of product, reduces the quality risk that complex manufacturing is brought.

The embodiment of second aspect present invention provides a kind of preparation method of sand wall-like multicolor finish, as shown in figure 1, bag Include following steps:

Step S102, sequentially adds dispersant, the 0.1-1 matter of 0.1-1 mass parts in the deionized water to 40-20 mass parts The defoamer of part and the preservative of 0.1-1 mass parts are measured, and is stirred, the electrical conductivity≤6 μ S/cm of the deionized water;

Step S104, sequentially adds the color sand of 25-50 mass parts and the mica sheet of 0.1-5 mass parts, and stir;

Step S106, then the acrylic emulsion of 30-10 mass parts is gradually added into, and it is slowly added to the film forming of 1-2 mass parts Auxiliary agent, and stir;

Step S108, adds by the deionized water of 1-5 mass parts, the polymerization inhibitor of 0-0.01 mass parts and 0.05-2 mass Gel and the thickener of 0.1-1 mass parts that the special modified synthesizing flaky zeopan of part is made, stir evenly, and toning is obtained Base paint;

Step S110, is repeated several times the step S102 to the step S108, prepares the toning base of different colours Plinth paint;

Step S112, by the color-mixed base paint continuous phase emulsion of addition of different colours, is obtained the sand wall-like many Color coating material, wherein the weight content of the color-mixed base paint is 30%~70%, the weight content of the continuous phase emulsion is 70%~30%.

Further, in the step S104, the color sand is artificial burning colorful sand, by hot blast calcine technology, will be contained The composite color paste for having inorganic and/or organic pigment, uvioresistant auxiliary agent, dispersant and acrylic emulsion to be made is sintered in quartz sand Surface, and the artificial burning colorful sand of predetermined size is obtained by screening.

Further, in the step S112, by controlling the speed of dispersing shear, it is obtained and contains different size color dot The sand wall-like multicolor finish.

The color-mixed base paint and sand wall-like that present invention offer is further illustrated with reference to the specific embodiment in table 1 are more Color coating material.

Table 1

Below by taking the embodiment 1 of table 1 as an example, the preparation method of sand wall-like multicolor finish is illustrated:

1st, deionized water 40 mass parts electrical conductivity≤6 of the deionized water (μ S/cm) are added in the reactor of cleaning;

2nd, dispersion machine low or first gear (rotating speed is 300~600r/min) is opened, to sequentially adding the matter of dispersant 0.1 in reactor Amount part, the mass parts of defoamer 0.1, the mass parts of preservative 0.1 part, and stir;

3rd, dispersion machine mid ranger (rotating speed is 600~800r/min) is opened, and is manually sintered to being sequentially added in reactor The mass parts of color sand 25, the mass parts of mica sheet (diameter 3-5mm) 0.1, and stir;

4th, dispersing speed is kept, to being gradually added into the mass parts of acrylic emulsion 25 in reactor, and film forming is slowly added to The mass parts of auxiliary agent 2, and stir;

5th, to being added in reactor by the special of the deionized water of 5 mass parts, the polymerization inhibitor of 0.01 mass parts and 1 mass parts The gel and the thickener of 0.5 mass parts of modified synthesizing flaky zeopan composition, stir evenly, and the tune of a certain kind color is obtained Color base paint;

6th, by required preparation multicolor finish color dot requirement, repeat above step 1~5, prepare different colours toning Base paint;

7th, by required preparation multicolor finish color dot size requirement, by several times by above-mentioned color-mixed base paint by stirring plus (color-mixed base paint is 3 with the weight content ratio of continuous phase emulsion to enter continuous phase emulsion:7~7:3) in, many color coatings of sand wall-like are made Material.

In sum, during the present invention provides the color-mixed base paint of sand wall-like multicolor finish, including with artificial burning colorful sand it is The filling system of main aggregate, due to passing through hot blast calcine technology when artificial burning colorful sand is prepared, will be containing inorganic and/or have The composite color paste that machine pigment, uvioresistant auxiliary agent, dispersant and acrylic emulsion are made is sintered in quartz sand surface, possesses high Weatherability and water resistance, therefore in color-mixed base paint without physics add aqueous color paste, overcome current water-water colorful Colour fading that coating is brought because being mixed colours using aqueous color paste, the quality risk such as grow dim;Meanwhile, color-mixed base paint of the present invention Can be prepared by sand wall-like multicolor finish after adding continuous phase emulsion, comprised only in the multicolor finish dispersed phase color-mixed base paint and Continuous phase emulsion two-phase component, production technology is relatively simple, can improve production efficiency, and with current water-in-water multicolor coating containing sand Compared by way of rear addition ore in sand form (prepared in water-in-water multicolor coating and add ore in sand form after viscosity stabilization), it is of the invention many The stability of color coating material is higher, the system of effectively prevent is swollen, bleeding the problems such as, reduce the quality wind that brings of complex manufacturing Danger.

In the description of this specification, the description of term " one embodiment ", " some embodiments ", " specific embodiment " etc. Mean that the specific features, structure, material or the feature that are described with reference to the embodiment or example are contained in of the invention at least one real In applying example or example.In this manual, the schematic representation to above-mentioned term is not necessarily referring to identical embodiment or reality Example.And, the specific features of description, structure, material or feature can in one or more any embodiments or example with Suitable mode is combined.

The preferred embodiments of the present invention are the foregoing is only, is not intended to limit the invention, for the skill of this area For art personnel, the present invention can have various modifications and variations.It is all within the spirit and principles in the present invention, made any repair Change, equivalent, improvement etc., should be included within the scope of the present invention.

Claims (5)

1. a kind of sand wall-like multicolor finish, it is characterised in that contained by the color-mixed base paint and weight of weight content 30%~70% The continuous phase emulsion composition of amount 70%~30%;
The color-mixed base paint is grouped into by each group of following weight content:
Deionized water:40-20 parts;
Dispersant:0.1-1 parts;
Defoamer:0.1-1 parts;
Preservative:0.1-1 parts;
Color sand:25-50 parts;
Mica sheet:0.1-5 parts;
Acrylic emulsion:30-10 parts;
Coalescents:1-2 parts;
Gel:1.05-7.01 parts;
Thickener:0.1-1 parts;
Wherein, the component and the weight content of each component that the gel is included be:
The deionized water:1-5 parts;
Polymerization inhibitor:0-0.01 parts;
Special modified synthesizing flaky zeopan:0.05-2 parts;
And electrical conductivity≤6 μ the S/cm of the deionized water;The color sand is artificial burning colorful sand;The mica sheet it is a diameter of 3-5mm;The acrylic emulsion is from the pure acrylic latex that glass transition temperature is 0-20 DEG C;The dispersant is polycarboxylic acids ammonium Dipersant;The defoamer is common mineral oils defoamer;The preservative is BIT analog derivative;Institute State TEXANOL ester alcohol of the coalescents from Eastman Chemical;The polymerization inhibitor is selected and contains calcium, magnesium, aluminium and ammonium ion In the salt-mixture of one or more;The special modified synthesizing flaky zeopan selects RD, any of GTS, S-482 Plant or appoint several mixing;The artificial burning colorful sand includes composite color paste and quartz sand, wherein the composite color paste includes nothing Machine and/or organic pigment, uvioresistant auxiliary agent, dispersant and the acrylic emulsion.
2. sand wall-like multicolor finish according to claim 1, it is characterised in that
The weight content of the color-mixed base paint is 40%, and the weight content of the continuous phase emulsion is 60%;Or
The weight content of the color-mixed base paint is 50%, and the weight content of the continuous phase emulsion is 50%.
3. a kind of preparation method of sand wall-like multicolor finish, it is characterised in that comprise the following steps:
Step S102, sequentially adds dispersant, the 0.1-1 mass parts of 0.1-1 mass parts in the deionized water to 40-20 mass parts Defoamer and 0.1-1 mass parts preservative, and stir, wherein the electrical conductivity≤6 μ S/cm of the deionized water;
Step S104, sequentially adds the color sand of 25-50 mass parts and the mica sheet of 0.1-5 mass parts, and stir;
Step S106, then the acrylic emulsion of 30-10 mass parts and the coalescents of 1-2 mass parts are gradually added into, and stir equal It is even;
Step S108, adds by the deionized water of 1-5 mass parts, the polymerization inhibitor of 0-0.01 mass parts and 0.05-2 mass Gel and the thickener of 0.1-1 mass parts that the special modified synthesizing flaky zeopan of part is made, stir evenly, and toning is obtained Base paint;
Step S110, is repeated several times the step S102 to the step S108, prepares the color-mixed base paint of different colours;
Step S112, by the color-mixed base paint continuous phase emulsion of addition of different colours, is obtained many color coatings of sand wall-like Material, wherein the weight content of the color-mixed base paint is 30%~70%, the weight content of the continuous phase emulsion for 70%~ 30%.
4. the preparation method of sand wall-like multicolor finish according to claim 3, it is characterised in that
In the step S104, the color sand is artificial burning colorful sand, by hot blast calcine technology, will containing inorganic and/or The composite color paste that organic pigment, uvioresistant auxiliary agent, dispersant and acrylic emulsion are made is sintered in quartz sand surface, and passes through Screening obtains the described artificial burning colorful sand of predetermined size.
5. the preparation method of the sand wall-like multicolor finish according to claim 3 or 4, it is characterised in that
In the step S112, by controlling the speed of dispersing shear, the sand wall-like containing different size color dot is obtained Multicolor finish.
CN201410438894.2A 2014-08-29 2014-08-29 Sand wall-like multicolor finish and preparation method thereof CN104194457B (en)