CN107740268A - Mould proof smooth fluffy softening agent of a kind of fabric and preparation method thereof - Google Patents
Mould proof smooth fluffy softening agent of a kind of fabric and preparation method thereof Download PDFInfo
- Publication number
- CN107740268A CN107740268A CN201710897080.9A CN201710897080A CN107740268A CN 107740268 A CN107740268 A CN 107740268A CN 201710897080 A CN201710897080 A CN 201710897080A CN 107740268 A CN107740268 A CN 107740268A
- Authority
- CN
- China
- Prior art keywords
- parts
- fabric
- softening agent
- mould proof
- smooth fluffy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses mould proof smooth fluffy softening agent of a kind of fabric and preparation method thereof, the mould proof smooth fluffy softening agent of the fabric includes the raw material of following parts by weight：Natural 20 30 parts of cotton wax, 10 15 parts of sorbitan fatty acid ester, 10 15 parts of sodium metasilicate, 5 10 parts of diatomite, 10 15 parts of sodium acid carbonate, 59 parts of borax, 13 parts of triethanolamine, 10 20 parts of ethanol, 35 parts of DBSA, 5 10 parts of magnesium chloride, 5 10 parts of epoxychloropropane, 35 parts of butyl titanate, 5 10 parts of Jasmine juice, 30 50 parts of deionized water.After the mould proof smooth fluffy softening agent application of fabric of the present invention, the stiffness of fabric declines a lot, and shearing rigidity and bending stiffness all decline a lot, and creasy recovery angle increase is a lot, and smooth fluffy flexibility improves a lot, and fabric can reach permanent mould proof.The mould proof smooth fluffy softening agent manufacturing process of fabric of the present invention is simple to operation, and low in raw material price easily obtains, and nontoxic, human body is not stimulated, volatility is low.
Description
Technical field
The invention belongs to technical field of textile auxiliary agent, specifically relate to a kind of mould proof smooth fluffy softening agent of fabric and its
Preparation method.
Background technology
Softening agent is a kind of quiet, the coefficient of kinetic friction chemical substance that can change fiber.When the static friction system for changing fiber
During number, feel, which touches fabric, smooth sense, is easy to move on fiber or fabric；When changing the coefficient of kinetic friction, fiber and fibre
Fine structure between dimension is easy to be mutually shifted, that is, fiber or fabric it is easily deformable.
Soft finish is the important finishing process in dyeing and printing process.Textile in process, through repeatedly processing after
Feel can become coarse, and general synthetic fabrics feel is worse, especially Superfine Fibre Fabric.Put down in order that fabric has
Sliding, fluffy, soft, smooth, comfortable feel, it is necessary to arranged to it, widely used at present carried out with softening agent
Arrange.In addition softening agent largely is used during chemical fibre spinning, the spinning of various fibers, weaving etc., because
With a large amount of uses of textile processing high speed and short liquor ratio mode, the phase mutual friction between fabric and equipment between fabric
Increase, phenomena such as being also easy to produce scratch, bar defect.It can make fiber that there is the softness being adapted with processing conditions to put down in itself using softening agent
Slip is to avoid damage to.Therefore fabric is a kind of important textile auxiliary with softening agent.
With the improvement of living standards, the requirement more and more higher to textile material, it is desirable to which fabric has necessarily smooth fluffy
The soft wrinkle resistance of pine, to the quality requirements of smooth fluffy softening agent also more and more higher, which also promotes smooth fluffy softening agent
Development.
The content of the invention
It is an object of the invention to provide a kind of mould proof smooth fluffy softening agent of fabric and preparation method, to solve the above-mentioned back of the body
The problem of being proposed in scape technology.
To achieve the above object, the present invention provides following technical scheme：
The mould proof smooth fluffy softening agent of a kind of fabric, according to parts by weight, including following components：Natural cotton wax 20-30 parts,
Sorbitan fatty acid ester 10-15 parts, sodium metasilicate 10-15 parts, diatomite 5-10 parts, sodium acid carbonate 10-15 parts, borax 5-9
Part, triethanolamine 1-3 parts, ethanol 10-20 parts, DBSA 3-5 parts, magnesium chloride 5-10 parts, epoxychloropropane 5-10
Part, butyl titanate 3-5 parts, Jasmine juice 5-10 parts, deionized water 30-50 parts.
Preferably, the ethanol is absolute ethyl alcohol, and purity is pure to analyze.
Preferably, the mould proof smooth fluffy softening agent of described fabric, according to parts by weight, including following components：Natural cotton
20 parts of wax, 10 parts of sorbitan fatty acid ester, 10 parts of sodium metasilicate, 5 parts of diatomite, 10 parts of sodium acid carbonate, 5 parts of borax, three second
1 part of hydramine, 10 parts of ethanol, 3 parts of DBSA, 5 parts of magnesium chloride, 5 parts of epoxychloropropane, 3 parts of butyl titanate, jasmine
5 parts of juice of flower, 30 parts of deionized water.
Preferably, the mould proof smooth fluffy softening agent of described fabric, according to parts by weight, including following components：Natural cotton
25 parts of wax, 13 parts of sorbitan fatty acid ester, 13 parts of sodium metasilicate, 8 parts of diatomite, 13 parts of sodium acid carbonate, 7 parts of borax, three second
2 parts of hydramine, 15 parts of ethanol, 4 parts of DBSA, 8 parts of magnesium chloride, 8 parts of epoxychloropropane, 4 parts of butyl titanate, jasmine
8 parts of juice of flower, 40 parts of deionized water.
Preferably, the mould proof smooth fluffy softening agent of described fabric, according to parts by weight, including following components：Natural cotton
30 parts of wax, 15 parts of sorbitan fatty acid ester, 15 parts of sodium metasilicate, 10 parts of diatomite, 15 parts of sodium acid carbonate, 9 parts of borax, three second
3 parts of hydramine, 20 parts of ethanol, 5 parts of DBSA, 10 parts of magnesium chloride, 10 parts of epoxychloropropane, 5 parts of butyl titanate, jasmine
10 parts of jasmine juice, 50 parts of deionized water.
A kind of preparation method of the mould proof smooth fluffy softening agent of fabric, is comprised the following steps that：
(1) natural cotton wax 20-30 parts, sorbitan fatty acid ester 10-15 parts, deionization are added inside three-necked flask
Water 30-50 parts, in 70-80 DEG C of heating of oil bath pan, nitrogen protection, the speed for being passed through nitrogen is 1-2L/min, keeps charging flatly,
Insertion agitator flatly, mixing speed are 1000-2000 revs/min, reaction time 3-4h；
(2) first by borax 5-9 parts, triethanolamine 1-3 parts, ethanol 10-20 parts, with ultrasonic disperse 10-20 minutes, ultrasonic work(
Rate is 1200-1500W, obtains homogeneous solution；
(3) homogeneous solution of step (2) is added in the solution of step (1), 500-1000 revs/min, 20-30 points of stirring
Clock；
(4) temperature is reduced to 50-60 DEG C, adds epoxychloropropane 5-10 parts, butyl titanate 3-5 parts, sodium metasilicate 10-15
Part, DBSA 3-5 parts, magnesium chloride 5-10 parts, 500-1000 revs/min, stir 20-30 minutes；
(5) 40-50 DEG C is cooled to, adds Jasmine juice 5-10 parts, diatomite 5-10 parts, sodium acid carbonate 10-15 parts,
500-1000 revs/min, stir 1-2 hours；
(6) 20-30 DEG C is cooled to, closes down stirring, the mould proof smooth fluffy softening agent of the liquid fabric prepared；
(7) stand and be cooled to the mould proof smooth fluffy softening agent of liquid fabric in three-necked flask less than 20 DEG C, blowing encapsulation, system
Obtain finished product.
Compared with prior art, the beneficial effects of the invention are as follows：
1st, after the mould proof smooth fluffy softening agent application of fabric of the invention, the stiffness of fabric declines a lot, and shearing is firm
Degree and bending stiffness all decline a lot, and creasy recovery angle increase is a lot, and smooth fluffy flexibility raising is a lot, and fabric can reach
It is permanent mould proof.
2nd, after the mould proof smooth fluffy softening agent application fabric of fabric of the invention, fabric has excellent smooth fluffy soft
Soft feel, the sense of touch of fabric, sliding sense are greatly improved, and suede class, fiber, the fluffy degree of fabric are improved.
3rd, the mould proof smooth fluffy softening agent wide adaptability of fabric of the invention, is applicable various fibers.
4th, the mould proof smooth fluffy softening agent environmental protection of fabric of the invention, without APEO.
5th, the mould proof smooth fluffy softening agent manufacturing process of fabric of the invention is simple to operation, and low in raw material price easily obtains
, and it is nontoxic, human body is not stimulated, volatility is low.
6th, mutual compatibility, synergy between various raw materials used in the mould proof smooth fluffy softening agent of fabric of the invention, altogether
With the product that component property is excellent.
7th, the addition of sodium acid carbonate, the smooth fluffy softness of fabric is improved.
8th, technique is simplified, safe operation is simple, is easy to industrialized production.
9th, after smooth fluffy softening agent application fabric of the invention, fabric is not easy yellowing, can ensure the color of fabric
It is transparent, it is smooth submissive, reduce fabric ages.
10th, use of the invention can receive good economic benefit.
Example is embodied
The invention discloses a kind of mould proof smooth fluffy softening agent of fabric, according to parts by weight, including following components：Naturally
Cotton wax 20-30 parts, sorbitan fatty acid ester 10-15 parts, sodium metasilicate 10-15 parts, diatomite 5-10 parts, sodium acid carbonate 10-
15 parts, borax 5-9 parts, triethanolamine 1-3 parts, ethanol 10-20 parts, DBSA 3-5 parts, magnesium chloride 5-10 parts, ring
Oxygen chloropropane 5-10 parts, butyl titanate 3-5 parts, Jasmine juice 5-10 parts, deionized water 30-50 parts.
Present invention also offers a kind of preparation method of the mould proof smooth fluffy softening agent of fabric, comprise the following steps that：
(1) natural cotton wax 20-30 parts, sorbitan fatty acid ester 10-15 parts, deionization are added inside three-necked flask
Water 30-50 parts, in 70-80 DEG C of heating of oil bath pan, nitrogen protection, the speed for being passed through nitrogen is 1-2L/min, keeps charging flatly,
Insertion agitator flatly, mixing speed are 1000-2000 revs/min, reaction time 3-4h；
(2) first by borax 5-9 parts, triethanolamine 1-3 parts, ethanol 10-20 parts, with ultrasonic disperse 10-20 minutes, ultrasonic work(
Rate is 1200-1500W, obtains homogeneous solution；
(3) homogeneous solution of step (2) is added in the solution of step (1), 500-1000 revs/min, 20-30 points of stirring
Clock；
(4) temperature is reduced to 50-60 DEG C, adds epoxychloropropane 5-10 parts, butyl titanate 3-5 parts, sodium metasilicate 10-15
Part, DBSA 3-5 parts, magnesium chloride 5-10 parts, 500-1000 revs/min, stir 20-30 minutes；
(5) 40-50 DEG C is cooled to, adds Jasmine juice 5-10 parts, diatomite 5-10 parts, sodium acid carbonate 10-15 parts,
500-1000 revs/min, stir 1-2 hours；
(6) 20-30 DEG C is cooled to, closes down stirring, the mould proof smooth fluffy softening agent of the liquid fabric prepared；
(7) stand and be cooled to the mould proof smooth fluffy softening agent of liquid fabric in three-necked flask less than 20 DEG C, blowing encapsulation, system
Obtain finished product.
Embodiment 1
The invention discloses a kind of mould proof smooth fluffy softening agent of fabric, according to parts by weight, including following components：Naturally
20 parts of cotton wax, 10 parts of sorbitan fatty acid ester, 10 parts of sodium metasilicate, 5 parts of diatomite, 10 parts of sodium acid carbonate, 5 parts of borax, three
1 part of monoethanolamine, 10 parts of ethanol, 3 parts of DBSA, 5 parts of magnesium chloride, 5 parts of epoxychloropropane, 3 parts of butyl titanate, jasmine
5 parts of jasmine juice, 30 parts of deionized water.
Present invention also offers a kind of preparation method of the mould proof smooth fluffy softening agent of fabric, comprise the following steps that：
(1) natural 20 parts of cotton wax, 10 parts of sorbitan fatty acid ester, deionized water 30 are added inside three-necked flask
Part, in 70 DEG C of heating of oil bath pan, nitrogen protection, the speed for being passed through nitrogen is 1L/min, keeps charging flatly, flatly insertion stirring
Device, mixing speed are 1000 revs/min, reaction time 3h；
(2) first by 5 parts of borax, 1 part of triethanolamine, 10 parts of ethanol, with ultrasonic disperse 10 minutes, ultrasonic power 1200W,
Obtain homogeneous solution；
(3) homogeneous solution of step (2) is added in the solution of step (1), 900 revs/min, stirred 20 minutes；
(4) temperature is reduced to 50 DEG C, adds 5 parts of epoxychloropropane, 3 parts of butyl titanate, 10 parts of sodium metasilicate, dodecyl
3 parts of benzene sulfonic acid, 5 parts of magnesium chloride, 900 revs/min, stir 20 minutes；
(5) 40 DEG C are cooled to, 5 parts of Jasmine juice, 5 parts of diatomite, 10 parts of sodium acid carbonate is added, 900 revs/min, stirs
Mix 1 hour；
(6) 20 DEG C are cooled to, closes down stirring, the mould proof smooth fluffy softening agent of the liquid fabric prepared；
(7) stand and be cooled to the mould proof smooth fluffy softening agent of liquid fabric in three-necked flask less than 20 DEG C, blowing encapsulation, system
Obtain finished product.
Embodiment 2
The invention discloses a kind of mould proof smooth fluffy softening agent of fabric, according to parts by weight, including following components：Naturally
25 parts of cotton wax, 13 parts of sorbitan fatty acid ester, 13 parts of sodium metasilicate, 8 parts of diatomite, 13 parts of sodium acid carbonate, 7 parts of borax, three
2 parts of monoethanolamine, 15 parts of ethanol, 4 parts of DBSA, 8 parts of magnesium chloride, 8 parts of epoxychloropropane, 4 parts of butyl titanate, jasmine
8 parts of jasmine juice, 40 parts of deionized water.
Present invention also offers a kind of preparation method of the mould proof smooth fluffy softening agent of fabric, comprise the following steps that：
(1) natural 25 parts of cotton wax, 13 parts of sorbitan fatty acid ester, deionized water 40 are added inside three-necked flask
Part, in 75 DEG C of heating of oil bath pan, nitrogen protection, the speed for being passed through nitrogen is 1.5L/min, keeps charging flatly, and insertion flatly is stirred
Device is mixed, mixing speed is 1500 revs/min, reaction time 3.5h；
(2) first by 7 parts of borax, 2 parts of triethanolamine, 15 parts of ethanol, with ultrasonic disperse 15 minutes, ultrasonic power 1500W,
Obtain homogeneous solution；
(3) homogeneous solution of step (2) is added in the solution of step (1), 800 revs/min, stirred 25 minutes；
(4) temperature is reduced to 55 DEG C, adds 8 parts of epoxychloropropane, 4 parts of butyl titanate, 13 parts of sodium metasilicate, dodecyl
4 parts of benzene sulfonic acid, 8 parts of magnesium chloride, 900 revs/min, stir 25 minutes；
(5) 45 DEG C are cooled to, 8 parts of Jasmine juice, 8 parts of diatomite, 13 parts of sodium acid carbonate is added, 800 revs/min, stirs
Mix 1.5 hours；
(6) 25 DEG C are cooled to, closes down stirring, the mould proof smooth fluffy softening agent of the liquid fabric prepared；
(7) stand and be cooled to the mould proof smooth fluffy softening agent of liquid fabric in three-necked flask less than 20 DEG C, blowing encapsulation, system
Obtain finished product.
Embodiment 3
The invention discloses a kind of mould proof smooth fluffy softening agent of fabric, according to parts by weight, including following components：Naturally
30 parts of cotton wax, 15 parts of sorbitan fatty acid ester, 15 parts of sodium metasilicate, 10 parts of diatomite, 15 parts of sodium acid carbonate, 9 parts of borax, three
3 parts of monoethanolamine, 20 parts of ethanol, 5 parts of DBSA, 10 parts of magnesium chloride, 10 parts of epoxychloropropane, 5 parts of butyl titanate,
10 parts of Jasmine juice, 50 parts of deionized water.
Present invention also offers a kind of preparation method of the mould proof smooth fluffy softening agent of fabric, comprise the following steps that：
(1) natural 30 parts of cotton wax, 15 parts of sorbitan fatty acid ester, deionized water 50 are added inside three-necked flask
Part, in 80 DEG C of heating of oil bath pan, nitrogen protection, the speed for being passed through nitrogen is 2L/min, keeps charging flatly, flatly insertion stirring
Device, mixing speed are 2000 revs/min, reaction time 4h；
(2) first by 8 parts of borax, 3 parts of triethanolamine, 20 parts of ethanol, with ultrasonic disperse 20 minutes, ultrasonic power 1500W,
Obtain homogeneous solution；
(3) homogeneous solution of step (2) is added in the solution of step (1), 1000 revs/min, stirred 30 minutes；
(4) temperature is reduced to 60 DEG C, adds 10 parts of epoxychloropropane, 5 parts of butyl titanate, 15 parts of sodium metasilicate, dodecane
5 parts of base benzene sulfonic acid, 10 parts of magnesium chloride, 1000 revs/min, stir 30 minutes；
(5) it is cooled to 50 DEG C, adds 10 parts of Jasmine juice, 10 parts of diatomite, 15 parts of sodium acid carbonate, 1000 revs/min,
Stirring 2 hours；
(6) 30 DEG C are cooled to, closes down stirring, the mould proof smooth fluffy softening agent of the liquid fabric prepared；
(7) stand and be cooled to the mould proof smooth fluffy softening agent of liquid fabric in three-necked flask less than 20 DEG C, blowing encapsulation, system
Obtain finished product.
Embodiment 4
The invention discloses a kind of mould proof smooth fluffy softening agent of fabric, according to parts by weight, including following components：Naturally
30 parts of cotton wax, 15 parts of sorbitan fatty acid ester, 10 parts of sodium metasilicate, 5 parts of diatomite, 15 parts of sodium acid carbonate, 9 parts of borax, three
3 parts of monoethanolamine, 20 parts of ethanol, 3 parts of DBSA, 5 parts of magnesium chloride, 10 parts of epoxychloropropane, 4 parts of butyl titanate,
8 parts of Jasmine juice, 30 parts of deionized water.
Present invention also offers a kind of preparation method of the mould proof smooth fluffy softening agent of fabric, comprise the following steps that：
(1) natural 30 parts of cotton wax, 15 parts of sorbitan fatty acid ester, deionized water 30 are added inside three-necked flask
Part, in 80 DEG C of heating of oil bath pan, nitrogen protection, the speed for being passed through nitrogen is 2L/min, keeps charging flatly, flatly insertion stirring
Device, mixing speed are 1000 revs/min, reaction time 4h；
(2) first by 9 parts of borax, 3 parts of triethanolamine, 20 parts of ethanol, with ultrasonic disperse 20 minutes, ultrasonic power 1200W,
Obtain homogeneous solution；
(3) homogeneous solution of step (2) is added in the solution of step (1), 1000 revs/min, stirred 20 minutes；
(4) temperature is reduced to 60 DEG C, adds 10 parts of epoxychloropropane, 4 parts of butyl titanate, 10 parts of sodium metasilicate, dodecane
3 parts of base benzene sulfonic acid, 5 parts of magnesium chloride, 800 revs/min, stir 20 minutes；
(5) 40 DEG C are cooled to, 8 parts of Jasmine juice, 5 parts of diatomite, 15 parts of sodium acid carbonate is added, 900 revs/min, stirs
Mix 2 hours；
(6) 30 DEG C are cooled to, closes down stirring, the mould proof smooth fluffy softening agent of the liquid fabric prepared；
(7) stand and be cooled to the mould proof smooth fluffy softening agent of liquid fabric in three-necked flask less than 20 DEG C, blowing encapsulation, system
Obtain finished product.
Test case
The smooth fluffy softening agent progress that embodiment 1,2,3,4 is respectively adopted in the fabric of four pieces of formed objects is smooth fluffy soft
Supple-settlement, test result are as follows：
| Embodiment | Stiffness | Creasy recovery angle | Shearing rigidity | Bending stiffness |
| Former cloth | 3.32 | 130 | 1.72 | 0.8522 |
| 1 | 1.48 | 179 | 1.48 | 0.4405 |
| 2 | 1.19 | 184 | 1.33 | 0.3934 |
| 3 | 1.06 | 192 | 1.21 | 0.3543 |
| 4 | 1.12 | 190 | 1.28 | 0.3763 |
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention includes appended claims and its equivalent limits.
Claims (6)
- A kind of 1. mould proof smooth fluffy softening agent of fabric, it is characterised in that：The mould proof smooth fluffy softening agent of the fabric is included such as The raw material of lower parts by weight：Natural cotton wax 20-30 parts, sorbitan fatty acid ester 10-15 parts, sodium metasilicate 10-15 parts, diatom Native 5-10 parts, sodium acid carbonate 10-15 parts, borax 5-9 parts, triethanolamine 1-3 parts, ethanol 10-20 parts, DBSA 3- 5 parts, magnesium chloride 5-10 parts, epoxychloropropane 5-10 parts, butyl titanate 3-5 parts, Jasmine juice 5-10 parts, deionized water 30-50 parts.
- 2. the mould proof smooth fluffy softening agent of fabric according to claim 1, it is characterised in that：The ethanol is anhydrous second Alcohol, purity are pure to analyze.
- 3. the mould proof smooth fluffy softening agent of fabric according to claim 1, it is characterised in that：According to parts by weight, including Following components：Natural 20 parts of cotton wax, 10 parts of sorbitan fatty acid ester, 10 parts of sodium metasilicate, 5 parts of diatomite, sodium acid carbonate 10 Part, 5 parts of borax, 1 part of triethanolamine, 10 parts of ethanol, 3 parts of DBSA, 5 parts of magnesium chloride, 5 parts of epoxychloropropane, titanium Sour 3 parts of four butyl ester, 5 parts of Jasmine juice, 30 parts of deionized water.
- 4. the mould proof smooth fluffy softening agent of fabric according to claim 1, it is characterised in that：According to parts by weight, including Following components：Natural 25 parts of cotton wax, 13 parts of sorbitan fatty acid ester, 13 parts of sodium metasilicate, 8 parts of diatomite, sodium acid carbonate 13 Part, 7 parts of borax, 2 parts of triethanolamine, 15 parts of ethanol, 4 parts of DBSA, 8 parts of magnesium chloride, 8 parts of epoxychloropropane, titanium Sour 4 parts of four butyl ester, 8 parts of Jasmine juice, 40 parts of deionized water.
- 5. the mould proof smooth fluffy softening agent of fabric according to claim 1, it is characterised in that：According to parts by weight, including Following components：Natural 30 parts of cotton wax, 15 parts of sorbitan fatty acid ester, 15 parts of sodium metasilicate, 10 parts of diatomite, sodium acid carbonate 15 Part, 9 parts of borax, 3 parts of triethanolamine, 20 parts of ethanol, 5 parts of DBSA, 10 parts of magnesium chloride, 10 parts of epoxychloropropane, 5 parts of butyl titanate, 10 parts of Jasmine juice, 50 parts of deionized water.
- 6. the preparation method of any mould proof smooth fluffy softening agent of described fabric in a kind of 1-5 using the claims, its It is characterised by：Comprise the following steps that：Step 1, natural cotton wax 20-30 parts, sorbitan fatty acid ester 10-15 parts, deionization are added inside three-necked flask Water 30-50 parts, in 70-80 DEG C of heating of oil bath pan, nitrogen protection, the speed for being passed through nitrogen is 1-2L/min, keeps charging flatly, Insertion agitator flatly, mixing speed are 1000-2000 revs/min, reaction time 3-4h；Step 2, first by borax 5-9 parts, triethanolamine 1-3 parts, ethanol 10-20 parts, with ultrasonic disperse 10-20 minutes, ultrasonic work( Rate is 1200-1500W, obtains homogeneous solution；Step 3, the homogeneous solution of step 2 is added in the solution of step 1,500-1000 revs/min, stirs 20-30 minutes；Step 4, temperature is reduced to 50-60 DEG C, adds epoxychloropropane 5-10 parts, butyl titanate 3-5 parts, sodium metasilicate 10-15 Part, DBSA 3-5 parts, magnesium chloride 5-10 parts, 500-1000 revs/min, stir 20-30 minutes；Step 5,40-50 DEG C is cooled to, adds Jasmine juice 5-10 parts, diatomite 5-10 parts, sodium acid carbonate 10-15 parts, 500-1000 revs/min, stir 1-2 hours；Step 6,20-30 DEG C is cooled to, closes down stirring, the mould proof smooth fluffy softening agent of the liquid fabric prepared；Step 7, stand and be cooled to the mould proof smooth fluffy softening agent of liquid fabric in three-necked flask less than 20 DEG C, blowing encapsulation, system Obtain finished product.