CN107724086A - A kind of silicone softening agent and preparation method thereof - Google Patents
A kind of silicone softening agent and preparation method thereof Download PDFInfo
- Publication number
- CN107724086A CN107724086A CN201710821118.4A CN201710821118A CN107724086A CN 107724086 A CN107724086 A CN 107724086A CN 201710821118 A CN201710821118 A CN 201710821118A CN 107724086 A CN107724086 A CN 107724086A
- Authority
- CN
- China
- Prior art keywords
- parts
- softening agent
- oil
- silicone softening
- essential oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of silicone softening agent and preparation method thereof, the silicone softening agent includes the raw material of following parts by weight:20 30 parts of amido silicon oil, 5 10 parts of dimethylaminoethyl methacrylate, 5 10 parts of emulsifying agent, 5 10 parts of turkey red oil, 35 parts of octadecylisocyanate, 10 15 parts of octamethylcyclotetrasiloxane, 46 parts of citric acid, 5 10 parts of diatomite, 35 parts of APEO, 5 10 parts of plants essential oil, 50 80 parts of deionized water.After the silicone softening agent application of the present invention, the stiffness of fabric declines a lot, and shearing rigidity and bending stiffness all decline a lot, and creasy recovery angle increase is a lot, and flexibility improves a lot.The silicone softening agent manufacturing process of the present invention is simple to operation, and low in raw material price easily obtains, and nontoxic, human body is not stimulated, volatility is low.
Description
Technical field
The invention belongs to technical field of textile auxiliary agent, specifically relates to a kind of silicone softening agent and preparation method thereof.
Background technology
Softening agent is a kind of quiet, the coefficient of kinetic friction chemical substance that can change fiber.When changing confficient of static friction, hand
Thoughts and feelings touches with smooth sense, is easy to move on fiber or fabric;It is fine between fiber and fiber when changing the coefficient of kinetic friction
Structure is easy to be mutually shifted, that is, fiber or fabric it is easily deformable.
Soft finish is the important finishing process in dyeing and printing process.Textile in process, through repeatedly processing after
Feel can become coarse, and general synthetic fabrics is worse, especially Superfine Fibre Fabric.In order that fabric has softness, slided
Refreshing, comfortable feel, it is necessary to arranged to it, widely used at present arranged with softening agent.In addition in chemistry
Softening agent largely is used during fibre spinning, the spinning of various fibers, weaving etc., because with textile processing
A large amount of uses of high speed and short liquor ratio mode, the phase mutual friction increase between fabric and equipment between fabric, be also easy to produce scratch,
Phenomena such as bar defect.It can make fiber that there is the flexible smooth being adapted with processing conditions to avoid damage in itself using softening agent.
Therefore fabric is a kind of important textile auxiliary with softening agent.
Fabric of organosilicon finishing auxiliaries has a wide range of applications in terms of textile finishing.The auxiliary agent can not only be handled naturally
Fabric, it can also handle the various synthetic fibers such as terylene, nylon.Crease-proofing textiles containing, antifouling, antistatic, anti-pilling after processing,
It is plentiful, soft, high resilience and gloss, there is style sliding, refreshing, very.Organosilicon processing can also improve the intensity of fiber, subtract
Light abrasion.Silicone softening agent is that product quality, increase are improved in a kind of up-and-coming softening agent, and textile printing and dyeing processing
A kind of important auxiliary agent of added value of product.
Domestic most fabrics after silicone softening agent arranges are in hydrophobicity, enable a wearer to feel sultry, and be difficult to wash
Wash;Also often there is demulsification floating oil phenomenon in many products.And the hydrophilic polyether silicone oil of tradition, though there is preferable hydrophily and water
Dissolubility, but flexibility and finishing effect durability are poor.Therefore the silicone softening agent with excellent flexibility is developed with very
Strong realistic meaning.
The content of the invention
It is an object of the invention to provide a kind of silicone softening agent and preparation method, to solve to carry in above-mentioned background technology
The problem of going out.
To achieve the above object, the present invention provides following technical scheme:
A kind of silicone softening agent, according to parts by weight, including following components:Amido silicon oil 20-30 parts, methacrylic acid
Dimethylaminoethyl 5-10 parts, emulsifying agent 5-10 parts, turkey red oil 5-10 parts, octadecylisocyanate 3-5 parts, the silicon of prestox four
Oxygen alkane 10-15 parts, citric acid 4-6 parts, diatomite 5-10 parts, APEO 3-5 parts, plants essential oil 5-10 parts, deionized water
50-80 parts.
Preferably, the emulsifying agent is AEO, APES, sorbitan fatty acid
It is one or more than one kinds of in ester, paregal O.
Preferably, the plants essential oil is Lavender, Peppermint essential oil, lemon, jasmine essential oil, rhodamine toner
It is one or more than one kinds of in oil, yulan essential oil, cape jasmine flower essential oil, narcissus flower essential oil.
Preferably, described silicone softening agent, according to parts by weight, including following components:20 parts of amido silicon oil, methyl
5 parts of dimethylaminoethyl acrylate, 5 parts of emulsifying agent, 5 parts of turkey red oil, 3 parts of octadecylisocyanate, octamethylcyclotetrasiloxane
10 parts, 4 parts of citric acid, 5 parts of diatomite, 3 parts of APEO, 5 parts of plants essential oil, 50 parts of deionized water.
Preferably, described silicone softening agent, according to parts by weight, including following components:25 parts of amido silicon oil, methyl
8 parts of dimethylaminoethyl acrylate, 8 parts of emulsifying agent, 8 parts of turkey red oil, 4 parts of octadecylisocyanate, octamethylcyclotetrasiloxane
13 parts, 5 parts of citric acid, 8 parts of diatomite, 4 parts of APEO, 8 parts of plants essential oil, 65 parts of deionized water.
Preferably, described silicone softening agent, according to parts by weight, including following components:Amido silicon oil 20-30 parts,
Dimethylaminoethyl methacrylate 5-10 parts, emulsifying agent 5-10 parts, turkey red oil 5-10 parts, octadecylisocyanate 3-5 parts,
Octamethylcyclotetrasiloxane 10-15 parts, citric acid 4-6 parts, diatomite 5-10 parts, APEO 3-5 parts, plants essential oil 5-10
Part, deionized water 50-80 parts.
Preferably, a kind of preparation method of the silicone softening agent, is comprised the following steps that:
(1) amido silicon oil 20-30 parts, dimethylaminoethyl methacrylate 5-10 parts, emulsifying agent are added in a kettle
5-10 parts, deionized water 50-80 parts, 60-70 DEG C is warming up to, 1000-3000 revs/min, stirs 20-30 minutes;
(2) temperature is raised to 70-80 DEG C, adds octamethylcyclotetrasiloxane 10-15 parts, APEO 3-5 parts, 500-
1000 revs/min, stir 20-30 minutes;
(3) it is cooled to 40-50 DEG C, adds octadecylisocyanate 3-5 parts, citric acid 4-6 parts, 500-1000 revs/min
Clock, stir 20-30 minutes;
(4) 30-40 DEG C is cooled to, turkey red oil 5-10 parts is added, 500-1000 revs/min, stirs 20-30 minutes;
(5) 20-30 DEG C is cooled to, diatomite 5-10 parts, plants essential oil 5-10 parts is added, 500-1000 revs/min, stirs
20-30 minutes;
(6) stirring is closed down, the silicone softening agent prepared;
(7) stand and be cooled in stirred tank liquid silicone softening agent and be less than 20 DEG C, blowing encapsulation, finished product.
Compared with prior art, the beneficial effects of the invention are as follows:
1st, after silicone softening agent of the invention application, the stiffness of fabric declines a lot, and shearing rigidity is firm with bending
Degree all declines a lot, and creasy recovery angle increase is a lot, and flexibility improves a lot.
2nd, silicone softening agent of the invention is stable, not stratified, not oil spill.
3rd, after silicone softening agent application fabric of the invention, fabric has more soft, fluffy, smooth feel.
4th, after silicone softening agent application fabric of the invention, the performance of fabric in itself such as air-moisture-permeable etc. will not occur
Change.
5th, silicone softening agent manufacturing process of the invention is simple to operation, and low in raw material price easily obtains, and nontoxic nothing
Evil, is not stimulated human body, volatility is low.
6th, mutual compatibility, synergy between various raw materials used in silicone softening agent of the invention, collectively constitute performance
Excellent product.
7th, the addition of plants essential oil, the softness of fabric is improved.
8th, technique is simplified, safe operation is simple, is easy to industrialized production.
9th, after softening agent application fabric of the invention, fabric is not easy yellowing, can ensure the color transparent of fabric, smoothly
It is submissive, reduce fabric ages performance.
10th, use of the invention can receive good economic benefit.
Example is embodied
The invention discloses a kind of silicone softening agent, according to parts by weight, including following components:Amido silicon oil 20-30
Part, dimethylaminoethyl methacrylate 5-10 parts, emulsifying agent 5-10 parts, turkey red oil 5-10 parts, octadecylisocyanate 3-5
Part, octamethylcyclotetrasiloxane 10-15 parts, citric acid 4-6 parts, diatomite 5-10 parts, APEO 3-5 parts, plants essential oil 5-
10 parts, deionized water 50-80 parts.
Present invention also offers a kind of preparation method of silicone softening agent, comprise the following steps that:
(1) amido silicon oil 20-30 parts, dimethylaminoethyl methacrylate 5-10 parts, emulsifying agent are added in a kettle
5-10 parts, deionized water 50-80 parts, 60-70 DEG C is warming up to, 1000-3000 revs/min, stirs 20-30 minutes;
(2) temperature is raised to 70-80 DEG C, adds octamethylcyclotetrasiloxane 10-15 parts, APEO 3-5 parts, 500-
1000 revs/min, stir 20-30 minutes;
(3) it is cooled to 40-50 DEG C, adds octadecylisocyanate 3-5 parts, citric acid 4-6 parts, 500-1000 revs/min
Clock, stir 20-30 minutes;
(4) 30-40 DEG C is cooled to, turkey red oil 5-10 parts is added, 500-1000 revs/min, stirs 20-30 minutes;
(5) 20-30 DEG C is cooled to, diatomite 5-10 parts, plants essential oil 5-10 parts is added, 500-1000 revs/min, stirs
20-30 minutes;
(6) stirring is closed down, the silicone softening agent prepared;
(7) stand and be cooled in stirred tank liquid silicone softening agent and be less than 20 DEG C, blowing encapsulation, finished product.
Embodiment 1
The invention discloses a kind of silicone softening agent, according to parts by weight, including following components:20 parts of amido silicon oil,
5 parts of dimethylaminoethyl methacrylate, 5 parts of emulsifying agent, 5 parts of turkey red oil, 3 parts of octadecylisocyanate, the silicon of prestox four
10 parts of oxygen alkane, 4 parts of citric acid, 5 parts of diatomite, 3 parts of APEO, 5 parts of plants essential oil, 50 parts of deionized water.
Present invention also offers a kind of preparation method of silicone softening agent, comprise the following steps that:
(1) 20 parts of amido silicon oil, 5 parts of dimethylaminoethyl methacrylate are added in a kettle, 5 parts of emulsifying agent, are gone
50 parts of ionized water, 60 DEG C are warming up to, 1000 revs/min, is stirred 20 minutes;
(2) temperature is raised to 70 DEG C, is added 10 parts of octamethylcyclotetrasiloxane, 3 parts of APEO, 500 revs/min, is stirred
Mix 20 minutes;
(3) 40 DEG C are cooled to, 3 parts of octadecylisocyanate, 4 parts of citric acid is added, 500 revs/min, stirs 20 points
Clock;
(4) 30 DEG C are cooled to, 5 parts of turkey red oil is added, 800 revs/min, stirs 20 minutes;
(5) 20 DEG C are cooled to, 5 parts of diatomite, 5 parts of plants essential oil is added, 900 revs/min, stirs 20 minutes;
(6) stirring is closed down, the silicone softening agent prepared;
(7) stand and be cooled in stirred tank liquid silicone softening agent and be less than 20 DEG C, blowing encapsulation, finished product.
Embodiment 2
The invention discloses a kind of silicone softening agent, according to parts by weight, including following components:25 parts of amido silicon oil,
8 parts of dimethylaminoethyl methacrylate, 8 parts of emulsifying agent, 8 parts of turkey red oil, 4 parts of octadecylisocyanate, the silicon of prestox four
13 parts of oxygen alkane, 5 parts of citric acid, 8 parts of diatomite, 4 parts of APEO, 8 parts of plants essential oil, 65 parts of deionized water.
Present invention also offers a kind of preparation method of silicone softening agent, comprise the following steps that:
(1) 25 parts of amido silicon oil, 8 parts of dimethylaminoethyl methacrylate are added in a kettle, 8 parts of emulsifying agent, are gone
65 parts of ionized water, 65 DEG C are warming up to, 2000 revs/min, is stirred 25 minutes;
(2) temperature is raised to 75 DEG C, is added 13 parts of octamethylcyclotetrasiloxane, 4 parts of APEO, 800 revs/min, is stirred
Mix 25 minutes;
(3) 45 DEG C are cooled to, 4 parts of octadecylisocyanate, 5 parts of citric acid is added, 900 revs/min, stirs 25 points
Clock;
(4) 35 DEG C are cooled to, 8 parts of turkey red oil is added, 900 revs/min, stirs 25 minutes;
(5) 25 DEG C are cooled to, 8 parts of diatomite, 8 parts of plants essential oil is added, 900 revs/min, stirs 25 minutes;
(6) stirring is closed down, the silicone softening agent prepared;
(7) stand and be cooled in stirred tank liquid silicone softening agent and be less than 20 DEG C, blowing encapsulation, finished product.
Embodiment 3
The invention discloses a kind of silicone softening agent, according to parts by weight, including following components:30 parts of amido silicon oil,
10 parts of dimethylaminoethyl methacrylate, 10 parts of emulsifying agent, 10 parts of turkey red oil, 5 parts of octadecylisocyanate, prestox four
15 parts of siloxanes, 6 parts of citric acid, 10 parts of diatomite, 5 parts of APEO, 10 parts of plants essential oil, 80 parts of deionized water.
Present invention also offers a kind of preparation method of silicone softening agent, comprise the following steps that:
(1) in a kettle add 30 parts of amido silicon oil, 10 parts of dimethylaminoethyl methacrylate, 10 parts of emulsifying agent,
80 parts of deionized water, 70 DEG C are warming up to, 3000 revs/min, is stirred 30 minutes;
(2) temperature is raised to 80 DEG C, is added 15 parts of octamethylcyclotetrasiloxane, 5 parts of APEO, 1000 revs/min, is stirred
Mix 30 minutes;
(3) 50 DEG C are cooled to, 5 parts of octadecylisocyanate, 6 parts of citric acid is added, 1000 revs/min, stirs 30 points
Clock;
(4) 40 DEG C are cooled to, 10 parts of turkey red oil is added, 1000 revs/min, stirs 30 minutes;
(5) 30 DEG C are cooled to, 10 parts of diatomite, 10 parts of plants essential oil is added, 1000 revs/min, stirs 30 minutes;
(6) stirring is closed down, the silicone softening agent prepared;
(7) stand and be cooled in stirred tank liquid silicone softening agent and be less than 20 DEG C, blowing encapsulation, finished product.
Embodiment 4
The invention discloses a kind of silicone softening agent, according to parts by weight, including following components:30 parts of amido silicon oil,
10 parts of dimethylaminoethyl methacrylate, 10 parts of emulsifying agent, 5 parts of turkey red oil, 3 parts of octadecylisocyanate, prestox four
10 parts of siloxanes, 4 parts of citric acid, 5 parts of diatomite, 5 parts of APEO, 10 parts of plants essential oil, 80 parts of deionized water.
Present invention also offers a kind of preparation method of silicone softening agent, comprise the following steps that:
(1) in a kettle add 30 parts of amido silicon oil, 10 parts of dimethylaminoethyl methacrylate, 10 parts of emulsifying agent,
80 parts of deionized water, 70 DEG C are warming up to, 3000 revs/min, is stirred 20 minutes;
(2) temperature is raised to 80 DEG C, is added 10 parts of octamethylcyclotetrasiloxane, 5 parts of APEO, 900 revs/min, is stirred
Mix 30 minutes;
(3) 45 DEG C are cooled to, 3 parts of octadecylisocyanate, 4 parts of citric acid is added, 1000 revs/min, stirs 20 points
Clock;
(4) 30 DEG C are cooled to, 5 parts of turkey red oil is added, 800 revs/min, stirs 30 minutes;
(5) 20 DEG C are cooled to, 5 parts of diatomite, 10 parts of plants essential oil is added, 1000 revs/min, stirs 20 minutes;
(6) stirring is closed down, the silicone softening agent prepared;
(7) stand and be cooled in stirred tank liquid silicone softening agent and be less than 20 DEG C, blowing encapsulation, finished product.
Test case
The softening agent that embodiment 1,2,3,4 is respectively adopted in the fabric of four pieces of formed objects carries out soft treatment, test result
It is as follows:
Embodiment | Stiffness | Creasy recovery angle | Shearing rigidity | Bending stiffness |
Former cloth | 3.05 | 110 | 1.72 | 0.7022 |
1 | 1.42 | 172 | 1.42 | 0.4505 |
2 | 1.29 | 185 | 1.28 | 0.3924 |
3 | 1.12 | 198 | 1.19 | 0.3323 |
4 | 1.20 | 192 | 1.20 | 0.3433 |
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention includes appended claims and its equivalent limits.
Claims (7)
- A kind of 1. silicone softening agent, it is characterised in that:The silicone softening agent includes the raw material of following parts by weight:Amino Silicone oil 20-30 parts, dimethylaminoethyl methacrylate 5-10 parts, emulsifying agent 5-10 parts, turkey red oil 5-10 parts, octadecyl are different Cyanate 3-5 parts, octamethylcyclotetrasiloxane 10-15 parts, citric acid 4-6 parts, diatomite 5-10 parts, APEO 3-5 parts, plant Thing essential oil 5-10 parts, deionized water 50-80 parts.
- 2. silicone softening agent according to claim 1, it is characterised in that:The emulsifying agent is aliphatic alcohol polyethenoxy It is one or more than one kinds of in ether, APES, sorbitan fatty acid ester, paregal O.
- 3. silicone softening agent according to claim 1, it is characterised in that:The plants essential oil is Lavender, thin Lotus essential oil, lemon, jasmine essential oil, Rosa Damascana, yulan essential oil, cape jasmine flower essential oil, one kind in narcissus flower essential oil or Person more than one.
- 4. silicone softening agent according to claim 1, it is characterised in that:According to parts by weight, including following components:Ammonia 20 parts of base silicone oil, 5 parts of dimethylaminoethyl methacrylate, 5 parts of emulsifying agent, 5 parts of turkey red oil, 3 parts of octadecylisocyanate, 10 parts of octamethylcyclotetrasiloxane, 4 parts of citric acid, 5 parts of diatomite, 3 parts of APEO, 5 parts of plants essential oil, deionized water 50 Part.
- 5. silicone softening agent according to claim 1, it is characterised in that:According to parts by weight, including following components:Ammonia 25 parts of base silicone oil, 8 parts of dimethylaminoethyl methacrylate, 8 parts of emulsifying agent, 8 parts of turkey red oil, 4 parts of octadecylisocyanate, 13 parts of octamethylcyclotetrasiloxane, 5 parts of citric acid, 8 parts of diatomite, 4 parts of APEO, 8 parts of plants essential oil, deionized water 65 Part.
- 6. silicone softening agent according to claim 1, it is characterised in that:According to parts by weight, including following components:Ammonia 30 parts of base silicone oil, 10 parts of dimethylaminoethyl methacrylate, 10 parts of emulsifying agent, 10 parts of turkey red oil, octadecylisocyanate 5 Part, 15 parts of octamethylcyclotetrasiloxane, 6 parts of citric acid, 10 parts of diatomite, 5 parts of APEO, 10 parts of plants essential oil, deionization 80 parts of water.
- A kind of 7. preparation method of any described silicone softening agent in 1-6 using the claims, it is characterised in that:Tool Body step is as follows:Step 1, amido silicon oil 20-30 parts, dimethylaminoethyl methacrylate 5-10 parts, emulsifying agent 5- are added in a kettle 10 parts, deionized water 50-80 parts, 60-70 DEG C is warming up to, 1000-3000 revs/min, stirs 20-30 minutes;Step 2, temperature is raised to 70-80 DEG C, adds octamethylcyclotetrasiloxane 10-15 parts, APEO 3-5 parts, 500- 1000 revs/min, stir 20-30 minutes;Step 3, it is cooled to 40-50 DEG C, adds octadecylisocyanate 3-5 parts, citric acid 4-6 parts, 500-1000 revs/min Clock, stir 20-30 minutes;Step 4,30-40 DEG C is cooled to, turkey red oil 5-10 parts is added, 500-1000 revs/min, stirs 20-30 minutes;Step 5,20-30 DEG C is cooled to, diatomite 5-10 parts, plants essential oil 5-10 parts is added, 500-1000 revs/min, stirs 20-30 minutes;Step 6, stirring is closed down, the silicone softening agent prepared;Step 7, stand and be cooled in stirred tank liquid silicone softening agent and be less than 20 DEG C, blowing encapsulation, finished product.