CN107738460A - 一种塑料薄膜的制备工艺 - Google Patents
一种塑料薄膜的制备工艺 Download PDFInfo
- Publication number
- CN107738460A CN107738460A CN201710821579.1A CN201710821579A CN107738460A CN 107738460 A CN107738460 A CN 107738460A CN 201710821579 A CN201710821579 A CN 201710821579A CN 107738460 A CN107738460 A CN 107738460A
- Authority
- CN
- China
- Prior art keywords
- film
- plastic sheeting
- preparation technology
- raw material
- glue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种塑料薄膜的制备工艺,包括以下步骤:第一步倒入塑料薄膜原料,将塑料薄膜原料倒入模具中;第二步加热,将塑料薄膜原料加热成液体;第三步制成薄膜,将液体制成薄膜;第四步喷胶压合,将一卷薄膜通过滚动机械并放置在传送平台上,另一卷薄膜通过滚动机械置于传送平台薄膜的上方,并通过设备将棉丝均匀置于传送平台薄膜上,然后喷胶水,通过压合机械将上下薄膜压合起来;第五步干燥,让胶水干燥凝固;第六步卷起,将粘合的薄膜卷起来;本发明生产工艺制作出来的塑料薄膜不仅具有良好的韧性,而且防止塑料断开,能让塑料薄膜增加使用寿命,还能重复使用,这样也可以减少塑料的污染。
Description
技术领域
本发明涉及一种制备工艺,尤其是一种塑料薄膜的制备工艺。
背景技术
塑料薄膜在我们的日常生活中应用广泛,由于塑料较薄导致断裂,所以现有生产制造出的塑料薄膜使用寿命都比较短,而且还会严重影响产品质量,从而影响产品使用。
发明内容
针对现有技术上存在的不足,本发明提供一种塑料薄膜的制备工艺。
为了实现上述目的,本发明是通过如下的技术方案来实现:一种塑料薄膜的制备工艺,其特征在于,包括以下步骤:
第一步倒入塑料薄膜原料,将塑料薄膜原料倒入模具中;
第二步加热,将塑料薄膜原料加热成液体;
第三步制成薄膜,将液体制成薄膜;
第四步喷胶压合,将一卷薄膜通过滚动机械并放置在传送平台上,另一卷薄膜通过滚动机械置于传送平台薄膜的上方,并通过设备将棉丝均匀置于传送平台薄膜上,然后喷胶水,通过压合机械将上下薄膜压合起来;
第五步干燥,让胶水干燥凝固;
第六步卷起,将粘合的薄膜卷起来;
前述的一种塑料薄膜的制备工艺,其特征在于,所述胶水为浓度3%的钛酸丁脂石油醚溶液。
前述的一种塑料薄膜的制备工艺,其特征在于,所述棉丝的直径为0.01-0.03毫米。
前述的一种塑料薄膜的制备工艺,其特征在于,所述棉丝沿着薄膜长度方向设置。
前述的一种塑料薄膜的制备工艺,其特征在于,所述单层薄膜的厚度为0.2-0.4毫米。
前述的一种塑料薄膜的制备工艺,其特征在于,所述胶水采用喷雾设备喷射于薄膜上。
借由上述技术方案,本发明的有益效果是:本发明生产工艺制作出来的塑料薄膜不仅具有良好的韧性,而且防止塑料断开,能让塑料薄膜增加使用寿命,还能重复使用,这样也可以减少塑料的污染。
具体实施方式
为使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施方式,进一步阐述本发明。
一种塑料薄膜的制备工艺,包括以下步骤:
第一步倒入塑料薄膜原料,将塑料薄膜原料倒入模具中;
第二步加热,将塑料薄膜原料加热成液体;
第三步制成薄膜,将液体制成薄膜;
第四步喷胶压合,将一卷薄膜通过滚动机械并放置在传送平台上,另一卷薄膜通过滚动机械置于传送平台薄膜的上方,并通过设备将棉丝均匀置于传送平台薄膜上,然后喷胶水,通过压合机械将上下薄膜压合起来;
第五步干燥,让胶水干燥凝固;
第六步卷起,将粘合的薄膜卷起来;
优选地,所述胶水为浓度3%的钛酸丁脂石油醚溶液。
优选地,所述棉丝的直径为0.01-0.03毫米。
优选地,所述棉丝沿着薄膜长度方向设置。
优选地,所述单层薄膜的厚度为0.2-0.4毫米。
优选地,所述胶水采用喷雾设备喷射于薄膜上。
本发明生产工艺制作出来的塑料薄膜不仅具有良好的韧性,而且防止塑料断开,能让塑料薄膜增加使用寿命,还能重复使用,这样也可以减少塑料的污染。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (6)
1.一种塑料薄膜的制备工艺,其特征在于,包括以下步骤:
第一步倒入塑料薄膜原料,将塑料薄膜原料倒入模具中;
第二步加热,将塑料薄膜原料加热成液体;
第三步制成薄膜,将液体制成薄膜;
第四步喷胶压合,将一卷薄膜通过滚动机械并放置在传送平台上,另一卷薄膜通过滚动机械置于传送平台薄膜的上方,并通过设备将棉丝均匀置于传送平台薄膜上,然后喷胶水,通过压合机械将上下薄膜压合起来;
第五步干燥,让胶水干燥凝固;
第六步卷起,将粘合的薄膜卷起来。
2.根据权利要求1所述的一种塑料薄膜的制备工艺,其特征在于,所述胶水为浓度3%的钛酸丁脂石油醚溶液。
3.根据权利要求1所述的一种塑料薄膜的制备工艺,其特征在于,所述棉丝的直径为0.01-0.03毫米。
4.根据权利要求3所述的一种塑料薄膜的制备工艺,其特征在于,所述棉丝沿着薄膜长度方向设置。
5.根据权利要求1所述的一种塑料薄膜的制备工艺,其特征在于,所述单层薄膜的厚度为0.2-0.4毫米。
6.根据权利要求1所述的一种塑料薄膜的制备工艺,其特征在于,所述胶水采用喷雾设备喷射于薄膜上。