CN107724092A - Pure cotton woven and its processing method - Google Patents
Pure cotton woven and its processing method Download PDFInfo
- Publication number
- CN107724092A CN107724092A CN201710899357.1A CN201710899357A CN107724092A CN 107724092 A CN107724092 A CN 107724092A CN 201710899357 A CN201710899357 A CN 201710899357A CN 107724092 A CN107724092 A CN 107724092A
- Authority
- CN
- China
- Prior art keywords
- pure cotton
- cotton woven
- processing
- processing method
- enzyme
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of pure cotton woven and its processing method.The processing method of the pure cotton woven comprises the following steps：Pre-treatment, alkali mercerized processing, the continuous enzyme of open width wash processing：Under conditions of speed 14m/min~26m/min, carry out the continuous cloth feeding of open width and continuously pad to wash to carry out continuous enzyme in 0.1g/L~0.5g/L enzyme washing lotion by cellulase mass concentration, mechanical friction is carried out with deflector roll, washing, drying inactivation, soft treatment, preshrunk processing, obtains pure cotton woven finished product.The pure cotton woven finished product that the processing method of the pure cotton woven of the present invention obtains is without fabric defects such as folding line, cloth cover wrinkles, production efficiency can be significantly improved simultaneously, the cloth cover of pure cotton woven finished product can be made bright and clean, it is soft comfortable, with good finish, pliability and smooth sense, and make cloth cover that there is qualified strength simultaneously.
Description
Technical field
The present invention relates to textile technology field, more particularly to a kind of pure cotton woven and its processing method.
Background technology
Traditionally, in the process of pure cotton woven, its enzyme washes journey and typically uses rope form Continuous maching or use
The enzyme that open width batch (-type) is banked up washes technique, but the two ways easily causes pure cotton woven to produce fabric defect, such as folding line, cloth
Face wrinkle etc., while production efficiency is relatively low.
The content of the invention
Based on this, it is necessary to provide one kind and be not easy to make pure cotton woven produce the fabric defects such as folding line, fold and production effect
The higher pure cotton woven of rate and its processing method.
A kind of processing method of pure cotton woven, comprises the following steps：
Pre-treatment；
Alkali mercerized processing；
The continuous enzyme of open width washes processing：, will be pure after alkali mercerized processing under conditions of speed 14m/min~26m/min
Cotton woven carries out the continuous cloth feeding of open width, and continuously pads and washed by the enzyme that cellulase mass concentration is 0.1g/L~0.5g/L
Carry out continuous enzyme in liquid to wash, open width continues through multiple deflector rolls and carries out mechanical friction, open width continuous washing with deflector roll, and open width connects
Continuous drying inactivation, obtains enzyme and washes pure cotton woven；
Soft treatment；
Preshrunk is handled, and obtains pure cotton woven finished product.
In wherein some embodiments, in the step of continuous enzyme of the open width washes processing, speed is 14m/min~20m/
Min, the mass concentration of enzyme washing lotion cellulase is 0.18g/L~0.5g/L, and it is 6min~8min to pad the time.
In wherein some embodiments, in the step of continuous enzyme of the open width washes processing, speed is 15 ± 0.5m/min,
The mass concentration of enzyme washing lotion cellulase is 0.28g/L~0.32g/L.
In wherein some embodiments, in the step of continuous enzyme of the open width washes processing, a diameter of the 20 of the deflector roll
± 1cm, total number is 250~270, in the adjacent deflector roll of any two continuously sequentially passed through along the pure cotton woven
The distance of axis is 0.3m~1.1m.
In wherein some embodiments, in the step of continuous enzyme of the open width is washed, dry the temperature of inactivation for 105~
115℃。
In wherein some embodiments, in the step of soft treatment, used softening agent changes for ternary polymerization
Property silicone oil, speed is 75m/min~85m/min, temperature be 145 DEG C~155 DEG C, drying time is 18~27s.
Include singing successively in wherein some embodiments, the step of the pre-treatment and desizing.
In wherein some embodiments, in the step of alkali mercerized processing, the concentration of alkali lye is 22~26 Baume degrees,
Processing time is 50~70s.
In wherein some embodiments, in the step of preshrunk is handled, speed is 49m/min~51m/min.
The pure cotton woven that the processing method processing of pure cotton woven described in any of the above-described embodiment obtains.
The processing method of the pure cotton woven of the present invention is a kind of brand-new finishing technique, will be through pre-treatment and alkali mercerized place
Pure cotton woven after reason is washed by the continuous enzyme of open width and passes through the mechanical friction effect with deflector roll, and by screening speed and fiber
The technological parameters such as the mass concentration of plain enzyme enzyme washing lotion, the enzyme digestion reaction of pure cotton woven is effectively facilitated, makes the pure cotton finally obtained
Woven finished product can significantly improve production efficiency without fabric defects such as folding line, cloth cover wrinkles.In addition, the pure cotton of the present invention
The processing method of woven can make the cloth cover of pure cotton woven finished product bright and clean, soft comfortable, have good finish,
Pliability and smooth sense, and make cloth cover that there is qualified strength simultaneously.
Embodiment
The processing method of the pure cotton woven of the present invention is described in further detail below in conjunction with specific embodiment.
Softening agent：Ternary polymerization modified silicon oil, model：TF620, purchased from Guangzhou east Qi textile technologies Co., Ltd.
Embodiment 1
A kind of processing method of pure cotton woven is present embodiments provided, the single thread yarn count of used pure cotton woven is
60S, its processing method comprise the following steps：
(1) pre-treatment：
Pre-treatment is carried out by traditional pre-treating technology to pure cotton woven, includes singing successively, desizing.
(2) alkali mercerized processing：
Pure cotton woven through pre-treatment is immersed in the alkali lye of 24 Baume degrees and carry out the alkali mercerized processing of mercerising, processing time
For 1min.
(3) the continuous enzyme of open width washes processing：
Under conditions of speed 15m/min, the pure cotton woven after alkali mercerized processing is subjected to the continuous cloth feeding of open width, and
Continuous pad is washed by cellulase mass concentration to carry out continuous enzyme in 0.3g/L enzyme washing lotion, and open width continues through multiple lead
Roller simultaneously carries out mechanical friction, open width continuous washing, the inactivation of open width continuous drying with deflector roll.
Wherein, in this step, pad time of the pure cotton woven after alkali mercerized processing in enzyme washing lotion is 7min；Lead
Roller is stainless steel fabric guide roll, and a diameter of 20 ± 1cm, the total number of deflector roll is 261, is continuously sequentially passed through along pure cotton woven
The distance of axis of the adjacent deflector roll of any two be 0.3~1.1m；The temperature of drying inactivation is 110 DEG C.
(4) soft treatment：
Pure cotton woven after enzyme is washed pads carries out soft treatment, speed in the softening agent of ternary polymerization modified silicon oil
For 80m/min, temperature is 150 DEG C, and drying time is 20~25s.
(5) preshrunk is handled：
To after soft treatment pure cotton woven carry out preshrunk processing, speed 50m/min, obtain pure cotton woven into
Product.
Embodiment 2
A kind of processing method of pure cotton woven is present embodiments provided, the single thread yarn count of used pure cotton woven is
50S, its processing method comprise the following steps：
(1) pre-treatment：
Pre-treatment is carried out by traditional pre-treating technology to pure cotton woven, includes singing successively, desizing.
(2) alkali mercerized processing：
Pure cotton woven through pre-treatment is immersed in the alkali lye of 24 Baume degrees and carry out the alkali mercerized processing of mercerising, processing time
For 1min.
(3) the continuous enzyme of open width washes processing：
Under conditions of speed 15m/min, the pure cotton woven after alkali mercerized processing is subjected to the continuous cloth feeding of open width, and
Continuous pad is washed by cellulase mass concentration to carry out continuous enzyme in 0.2g/L enzyme washing lotion, and open width continues through deflector roll simultaneously
Mechanical friction, open width continuous washing, the inactivation of open width continuous drying are carried out with deflector roll.
Wherein, in this step, pad time of the pure cotton woven after alkali mercerized processing in enzyme washing lotion is 7min；Lead
Roller is stainless steel fabric guide roll, and a diameter of 20 ± 1cm, the total number of deflector roll is 261, is continuously sequentially passed through along pure cotton woven
The distance of axis of the adjacent deflector roll of any two be 0.3~1.1m；The temperature of drying inactivation is 110 DEG C.(4) at softness
Reason：
Pure cotton woven after enzyme is washed pads carries out soft treatment, speed in the softening agent of ternary polymerization modified silicon oil
For 80m/min, temperature is 150 DEG C, and drying time is 20~25s.
(5) preshrunk is handled：
To after soft treatment pure cotton woven carry out preshrunk processing, speed 50m/min, obtain pure cotton woven into
Product.
Embodiment 3
A kind of processing method of pure cotton woven is present embodiments provided, the single thread yarn count of used pure cotton woven is
50S, its processing method comprise the following steps：
(1) pre-treatment：
Pre-treatment is carried out by traditional pre-treating technology to pure cotton woven, includes singing successively, desizing.
(2) alkali mercerized processing：
Pure cotton woven through pre-treatment is immersed in the alkali lye of 24 Baume degrees and carry out the alkali mercerized processing of mercerising, processing time
For 1min.
(3) the continuous enzyme of open width washes processing：
Under conditions of speed 25m/min, the pure cotton woven after alkali mercerized processing is subjected to the continuous cloth feeding of open width, and
Continuous pad is washed by cellulase mass concentration to carry out continuous enzyme in 0.3g/L enzyme washing lotion, and open width continues through deflector roll simultaneously
Mechanical friction, open width continuous washing, the inactivation of open width continuous drying are carried out with deflector roll.
Wherein, in step, pad time of the pure cotton woven in enzyme washing lotion after alkali mercerized processing is 7min；Deflector roll
For stainless steel fabric guide roll, a diameter of 20 ± 1cm, the total number of deflector roll is 255, what is continuously sequentially passed through along pure cotton woven
The distance of the axis of the adjacent deflector roll of any two is 0.3~1.1m；The temperature of drying inactivation is 110 DEG C.
(4) soft treatment：
Pure cotton woven after enzyme is washed pads carries out soft treatment, speed in the softening agent of ternary polymerization modified silicon oil
For 80m/min, temperature is 150 DEG C, and drying time is 20~25s.
(5) preshrunk is handled：
To after soft treatment pure cotton woven carry out preshrunk processing, speed 50m/min, obtain pure cotton woven into
Product.
Embodiment 4
A kind of processing method of pure cotton woven is present embodiments provided, the single thread yarn count of used pure cotton woven is
50S, its processing method comprise the following steps：
(1) pre-treatment：
Pre-treatment is carried out by traditional pre-treating technology to pure cotton woven, includes singing successively, desizing.
(2) alkali mercerized processing：
Pure cotton woven through pre-treatment is immersed in the alkali lye of 24 Baume degrees and carry out the alkali mercerized processing of mercerising, processing time
For 1min.
(3) the continuous enzyme of open width washes processing：
Under conditions of speed 25m/min, the pure cotton woven after alkali mercerized processing is subjected to the continuous cloth feeding of open width, and
Continuous pad is washed by carrying out continuous enzyme in enzyme washing lotion that cellulase mass concentration is 1g/L, open width continue through deflector roll and with
Deflector roll carries out mechanical friction, open width continuous washing, the inactivation of open width continuous drying.
Wherein, in step, pad time of the pure cotton woven in enzyme washing lotion after alkali mercerized processing is 7min；Deflector roll
For stainless steel fabric guide roll, a diameter of 20 ± 1cm, the total number of deflector roll is 265, what is continuously sequentially passed through along pure cotton woven
The distance of the axis of the adjacent deflector roll of any two is 0.3~1.1m；The temperature of drying inactivation is 110 DEG C.
(4) soft treatment：
Pure cotton woven after enzyme is washed pads carries out soft treatment, speed in the softening agent of ternary polymerization modified silicon oil
For 80m/min, temperature is 150 DEG C, and drying time is 20~25s.
(5) preshrunk is handled：
To after soft treatment pure cotton woven carry out preshrunk processing, speed 50m/min, obtain pure cotton woven into
Product.
Embodiment 5
A kind of processing method of pure cotton woven is present embodiments provided, the single thread yarn count of used pure cotton woven is
60S, its processing method comprise the following steps：
(1) pre-treatment：
Pre-treatment is carried out by traditional pre-treating technology to pure cotton woven, includes singing successively, desizing.
(2) alkali mercerized processing：
Pure cotton woven through pre-treatment is immersed in the alkali lye of 24 Baume degrees and carry out the alkali mercerized processing of mercerising, processing time
For 1min.
(3) the continuous enzyme of open width washes processing：
Under conditions of speed 19m/min, the pure cotton woven after alkali mercerized processing is subjected to the continuous cloth feeding of open width, and
Continuous pad is washed by cellulase mass concentration to carry out continuous enzyme in 0.5g/L enzyme washing lotion, and open width continues through deflector roll simultaneously
Mechanical friction, open width continuous washing, the inactivation of open width continuous drying are carried out with deflector roll.
Wherein, in step, pad time of the pure cotton woven in enzyme washing lotion after alkali mercerized processing is 7min；Deflector roll
For stainless steel fabric guide roll, a diameter of 20 ± 1cm, the total number of deflector roll is 261, what is continuously sequentially passed through along pure cotton woven
The distance of the axis of the adjacent deflector roll of any two is 0.3~1.1m；The temperature of drying inactivation is 110 DEG C.
(4) soft treatment：
Pure cotton woven after enzyme is washed pads carries out soft treatment, speed in the softening agent of ternary polymerization modified silicon oil
For 80m/min, temperature is 150 DEG C, and drying time is 20~25s.
(5) preshrunk is handled：
To after soft treatment pure cotton woven carry out preshrunk processing, speed 50m/min, obtain pure cotton woven into
Product.
Embodiment 6
A kind of processing method of pure cotton woven is present embodiments provided, the single thread yarn count of used pure cotton woven is
50S, identical the step of the step of its processing method with embodiment 1, difference is：The softening agent used in the step of soft treatment
For traditional silicone oil softener.
Comparative example 1
This comparative example provides a kind of processing method of pure cotton woven, and the single thread yarn count of used pure cotton woven is
50S, identical the step of the step of its processing method with embodiment 1, difference is：Washed in the continuous enzyme of open width in processing, deflector roll
Total number is 50.
Index test
Pliability is tested：Evaluated with hand digital palpation for examination of trauma, using being averaged after more person-times of rank scores, score value is the higher the better,
Otherwise feel is then poor (assessment method is that feasible method of testing is generally acknowledged inside textile industry), "+" represents better (ratio
Such as fabric softness +++ ratio ++ what a grade).
Finish is tested：Using contrast evaluation is visually observed, using (process and the result of being averaged after more people's rank scores
Method for expressing is tested with pliability).
The highest assessment grade of the finish of fabric and the pliability of fabric is " +++ ++ ", and minimum assessment grade is
“+”。
The processing method of embodiment 1 to 6 and the cotton woven of comparative example 1 is processed to the pure cotton woven finished product of acquisition respectively
Fabric defect, pliability, the strength of finish and cloth cover are tested, and statistical result see the table below 1：
The test result of the pure cotton woven finished product of table 1
The pure cotton that the processing method processing of the pure cotton woven of embodiment 1 obtains it can be seen from the test result in table 1
The finish and pliability of woven finished product are optimal, and overall feel is best, and the strength of cloth cover is qualified.
The processing method of the pure cotton woven of the present invention is applied to single thread yarn count more than 50 English branch (S), including 50 English branch,
60 English branch, 80 English branch strands, 120 English branch strands etc..When single thread yarn count is less than 50 English branch, because the feel of yarn itself is coarse,
Feel by its pure cotton woven being made into is not soft enough.In addition, in the processing method, pure cotton woven is continuously given birth in open width
Tensioning state is kept during production.
Each technical characteristic of embodiment described above can be combined arbitrarily, to make description succinct, not to above-mentioned reality
Apply all possible combination of each technical characteristic in example to be all described, as long as however, the combination of these technical characteristics is not deposited
In contradiction, the scope that this specification is recorded all is considered to be.
Embodiment described above only expresses the several embodiments of the present invention, and its description is more specific and detailed, but simultaneously
Can not therefore it be construed as limiting the scope of the patent.It should be pointed out that come for one of ordinary skill in the art
Say, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to the protection of the present invention
Scope.Therefore, the protection domain of patent of the present invention should be determined by the appended claims.
Claims (10)
1. a kind of processing method of pure cotton woven, it is characterised in that comprise the following steps：
Pre-treatment；
Alkali mercerized processing；
The continuous enzyme of open width washes processing：Under conditions of speed 14m/min~26m/min, by the pure cotton shuttle after alkali mercerized processing
Fabric carries out the continuous cloth feeding of open width, and continuously pads in the enzyme washing lotion for being 0.1g/L~0.5g/L by cellulase mass concentration
Carry out continuous enzyme to wash, open width continues through multiple deflector rolls and carries out mechanical friction, open width continuous washing with deflector roll, and open width is continuously dried
Dry inactivation, obtains enzyme and washes pure cotton woven；
Soft treatment；
Preshrunk is handled, and obtains pure cotton woven finished product.
2. the processing method of pure cotton woven according to claim 1, it is characterised in that wash place in the continuous enzyme of the open width
In the step of reason, speed is 14m/min~20m/min, and the mass concentration of enzyme washing lotion cellulase is 0.18g/L~0.5g/
L, it is 6min~8min to pad the time.
3. the processing method of pure cotton woven according to claim 2, it is characterised in that wash place in the continuous enzyme of the open width
In the step of reason, speed is 15 ± 0.5m/min, and the mass concentration of enzyme washing lotion cellulase is 0.28g/L~0.32g/L.
4. the processing method of the pure cotton woven according to any one of claims 1 to 3, it is characterised in that in the open width
In the step of continuous enzyme washes processing, a diameter of 20 ± 1cm of the deflector roll, total number is 250~270, along the pure cotton
The distance of the axis for the adjacent deflector roll of any two that woven continuously sequentially passes through is 0.3m~1.1m.
5. the processing method of the pure cotton woven according to any one of claims 1 to 3, it is characterised in that in the open width
In the step of continuous enzyme is washed, the temperature for drying inactivation is 105 DEG C~115 DEG C.
6. the processing method of the pure cotton woven according to any one of claims 1 to 3, it is characterised in that in the softness
In the step of processing, used softening agent is ternary polymerization modified silicon oil, and speed is 75m/min~85m/min, and temperature is
145 DEG C~155 DEG C, drying time is 18s~27s.
7. the processing method of the pure cotton woven according to any one of claims 1 to 3, it is characterised in that the pre-treatment
The step of include singing and desizing successively.
8. the processing method of the pure cotton woven according to any one of claims 1 to 3, it is characterised in that in the alkali silk
In the step of light processing, the concentration of alkali lye is 22~26 Baume degrees, and processing time is 50~70s.
9. the processing method of the pure cotton woven according to any one of claims 1 to 3, it is characterised in that handled in preshrunk
The step of in, speed is 49m/min~51m/min.
10. the pure cotton woven that the processing method processing of the pure cotton woven any one of claim 1 to 9 obtains.