CN107722829A - A kind of wood furniture is painted with flame-proof antibiotic - Google Patents
A kind of wood furniture is painted with flame-proof antibiotic Download PDFInfo
- Publication number
- CN107722829A CN107722829A CN201711007200.XA CN201711007200A CN107722829A CN 107722829 A CN107722829 A CN 107722829A CN 201711007200 A CN201711007200 A CN 201711007200A CN 107722829 A CN107722829 A CN 107722829A
- Authority
- CN
- China
- Prior art keywords
- flame
- parts
- retardant
- proof antibiotic
- painted
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of wood furniture to be painted with flame-proof antibiotic, and being calculated according to mass parts mainly includes following component：Silicone alkyd：10 15 parts；Acrylonitrile：58 parts；Organic epoxy resin：35 parts；Oil：20‑25；Pigment：1.5 3 parts；Composite flame-retardant agent：5 12.5 parts；Modified antiseptic：25 parts.The present invention effectively prevents wood furniture from burning by adding composite flame-retardant agent in paint, and the composite flame-retardant agent shows good flame retardant synergistic effect；The bactericidal property of resistance to bacterium of paint, Ag are effectively improved by adding modified antiseptic+TiO can be expanded2Photocatalysis excitation wavelength, while embedded TiO2Ag in crystal defect+It can be realized in sterilization process and slowly discharge and prevent from being oxidized, reach the effect of double sterilization.
Description
Technical field
The invention belongs to the technical field of furniture paint, and in particular to a kind of wood furniture is painted with flame-proof antibiotic.
Background technology
Paint is that one kind can firmly be covered in body surface, and the chemistry for playing protection, decoration, mark and other specific uses mixes
Compound coating.Paint is decorating and protect the coating of article made of the raw materials such as iron oxide or resin.It is toughening oil
Property pigment, it is inflammable in the case of not dry, insoluble in fire, fat is slightly soluble in, dissolves in alcohol, aldehyde, ether, benzene, alkane, is soluble in gasoline, coal
Oil, diesel oil.
In place of the paint Shortcomings of existing market：Such as without flameproof effect, the loss such as cause to be difficult to make up running into fire etc.,
And paint making cost of material is higher, can not meet user's economic benefit.Becoming increasingly conspicuous with environmental protection problem simultaneously
And pursuit of the people to health environment, antibacterium paint as a kind of environment-friendly new function material, be social development and
The inevitable outcome of scientific and technological progress.
The content of the invention
It is an object of the invention to provide a kind of wood furniture to be painted with flame-proof antibiotic, and being calculated according to mass parts mainly includes
Following component：Silicone alkyd：10-15 parts；Acrylonitrile：5-8 parts；Organic epoxy resin：3-5 parts；Oil：
20-25；Pigment：1.5-3 part；Composite flame-retardant agent：5-12.5 part；Modified antiseptic：2-5 parts；The present invention in paint by adding
Add composite flame-retardant agent effectively to prevent wood furniture from burning, the resistance to bacterium bactericidal properties of paint are effectively improved by adding modified antiseptic
Energy, reduce the occurrence index of wood furniture.
The present invention is achieved through the following technical solutions：A kind of wood furniture is painted with flame-proof antibiotic, according to mass parts
Calculating mainly includes following component：Silicone alkyd：10-15 parts；Acrylonitrile：5-8 parts；Organic epoxy resin：
3-5 parts；Oil：20-25；Pigment：1.5-3 part；Composite flame-retardant agent：5-12.5 part；Modified antiseptic：2-5 parts.
Organic siliconresin is using silicon oxygen bond as its molecular backbone, and Si-O keys are than C-C keys in common organic high molecular compound
Bond energy and polarity are bigger, can play shielding action to connected alkyl, can improve the oxidation stability of naval stores.And work as Si
After the alkyl connected on atom is oxidized, generation is more stable Si-O-Si keys, can prevent backbone breaking from degrading；Separately
Outside, the stabilized protection course rich in Si-O-Si chains of Organosilicon Polymers Surface Creation, can mitigate external environment to high polymer inside
Influence, organic siliconresin has excellent weatherability, water resistance, heat resistance and resistance to acids and bases.
Alkyd resin mainly using vegetable oil as raw material, have wide material sources, it is cheap, do not influenceed by oil price,
And it is easy to the advantages such as application, paint film be plentiful.But contain more hydroxyl and ester group in alkyd resin molecular structure so that its
There is clearly disadvantageous for film performance.Silicone alkyd refers to be copolymerized with organosilicon and alkyd resin, increases
The strong chemical stability of alkyd resin, and its weatherability, water resistance, heat resistance and resistance to acids and bases can be improved.
Titanium dioxide carrying silver antimicrobials have good antibiotic property, TiO2Series antibacterial agent has very high photocatalytic activity,
With acid and alkali-resistance and the advantages of low and nontoxic photochemical corrosion, cost；Ag series antibacterial agent bactericidal properties are extremely strong, consumed energy pole
Few, good endurance is difficult to assemble in human body, is referred to as permanent bactericide in chemistry；Therefore TiO is utilized2Series antibacterial agent
With the mutual supplement with each other's advantages of Ag series antibacterial agents, Novel Titanium dioxide carrying silver antimicrobials are developed.
Titanium dioxide carrying silver antimicrobials in use, Ag+TiO can be prevented2Compound, the promotion of middle electron-hole pair
The separation of electron-hole pair, expand TiO2Photocatalysis excitation wavelength, exciting light is expanded to visible-range, such antibacterial
Performance can be remarkably reinforced；Embedded TiO simultaneously2Ag in crystal defect+Can be realized in sterilization process slowly discharge and prevent by
Oxidation, so as to solve the nigrescence of antiseptic silver and sustained release sex chromosome mosaicism, ensure there are enough Ag in antiseptic+In the presence of reaching dual
The effect of sterilization.
In order to preferably realize the present invention, further, the composite flame-retardant agent is by flame-retardant direction and APP according to quality
Than 3:1-4:1 forms with mesoporous silicon oxide compounding.
In order to preferably realize the present invention, further, the flame-retardant direction and APP are with mesoporous silicon oxide according to matter
Measure ratio 0.5:1-0.8:1 compounding forms.
WOOD FIRE RETARDANT FRW is a kind of New Phosphorus-nitrogen-boron-based flame retardant of east Forestry University development, its anti-corrosion, insect prevention
Excellent effect, and environmental protection, flame retarding efficiency height, can be applicable to the flame retardant treatment of the materials such as solid wood, wood-based plate.Fire retardant APP is low
Degree of polymerization APP, because having excellent water solubility and fire resistance, also it is widely used in fire-retarding of wood processing；It is situated between
Hole silica has high specific surface area and pore capacities, orderly pore passage structure and good heat endurance, meso-porous titanium dioxide
Silicon not only has absorption and loading functional, and can keep skeleton stable in combustion, plays a part of protecting layer of charcoal；
There are some researches show two kinds of ignition-proof elements of Si and P can show good flame retardant synergistic effect, P can promote the life of charcoal under hot conditions
Into, Si can increase the heat endurance of layer of charcoal, and this contributes to the protection layer of charcoal of flame-retardant system formation Si-O-C keys and Si-C keys, from
And produce more preferable flame retardant effect.
In order to preferably realize the present invention, further, the modified antiseptic is the dioxy of titanate coupling agent modified
Change titanium silver base inorganic antibacterial agent.Because inorganic nanometer powder is easily reunited, therefore using titanate coupling agent to TiO 2 carrying
Silver antibacterial agent carries out surface modification, so as to improve dispersive property of the titanium dioxide carrying silver antimicrobials in paint, so as to improve oil
The stability of paint.
In order to preferably realize the present invention, further, the composite flame-retardant agent is by flame-retardant direction and APP according to quality
Than 4:1 compounding composition；The flame-proof antibiotic paint calculates according to mass parts mainly includes 12 parts of silicone alkyds, 6
Part acrylonitrile, 3 organic epoxy resins, 20 parts of oil, 8 parts of composite flame-retardant agents, 4 parts of modified antiseptics.
In order to preferably realize the present invention, further, the composite flame-retardant agent is by flame-retardant direction and APP according to quality
Than 4:1 compounding composition；The flame-proof antibiotic paint calculates according to mass parts mainly includes 15 parts of silicone alkyds, 8
Part acrylonitrile, 3 organic epoxy resins, 25 parts of oil, 10.8 parts of composite flame-retardant agents, 4.5 parts of modified antiseptics.
Beneficial effects of the present invention:
（1）The present invention use silicone alkyd, contain silicon oxygen bond in the silicone alkyd, with compared with
Weatherability well, water resistance, at the same it is more environmentally friendly；
（2）The present invention uses titanium dioxide carrying silver antimicrobials, and the titanium dioxide produces antibacterial synergy, antibacterial effect with silver
Preferably；
（3）The present invention uses composite flame-retardant agent, with reference to the advantages of flame-retardant direction and APP, effectively reduces cost, improves fire-retardant effect
Fruit；The present invention has preferable stability, while generate fire-retardant association using mesoporous silicon oxide load flame-retardant direction and APP
Same-action, flame retardant effect is more preferably.
Brief description of the drawings
Nothing.
Embodiment
Embodiment 1：
A kind of wood furniture is painted with flame-proof antibiotic, and being calculated according to mass parts mainly includes 12 parts of silicone alkyds, 6
Part acrylonitrile, 3 organic epoxy resins, 20 parts of oil, 8 parts of composite flame-retardant agents, 4 parts of modified antiseptics；The modified antiseptic
For the titanium dioxide carrying silver antimicrobials of HC-114 titanate coupling agent modifieds；The composite flame-retardant agent is pressed by flame-retardant direction and APP
According to mass ratio 4:1 compounding composition；The flame-retardant direction and APP are with mesoporous silicon oxide according to mass ratio 0.7:1 compounding forms.
Test the anti-microbial property of paint：By flame-proof antibiotic paint application on print, paint is detected with film adherence method
Anti-microbial property；In order to embody the spectrum antimicrobial properties of nano antibacterial paint, three kinds of representative Staphylococcus aureus are have selected
Bacterium, big field bacillus and Candida albicans；The bacterium solution of preparation is uniformly applied to the surface of print, covered with sterile plastic sheet
Print, it is then placed within 37 DEG C, cultivates 24h in the insulating box that relative humidity is 90%；Then with PBS by the bacterium solution on each print
Elution is got off, and by de- washing lotion inoculated and cultured 24h, is observed result and is calculated antibiotic rate.
Found after test, flame-proof antibiotic paint is after 24h 99.9% to the antibiotic rate of Escherichia coli, to golden yellow grape ball
The antibiotic rate of bacterium is 99.9%, and the antibiotic rate to Candida albicans is 99.7%；Antiseptic manufactured in the present embodiment has higher
Anti-microbial property.
The timber coated compared to the antibacterium paint for being not added with fire retardant, flame-proof antibiotic paint application manufactured in the present embodiment
The average HRR of timber have dropped 62%, illustrate composite flame-retardant agent addition effectively reduce timber thermal degradation generation can
The speed of combustion property volatility product, fire intensity reduce；Show that flame-proof antibiotic paint manufactured in the present embodiment has preferable fire-retardant effect
Fruit.
The present invention carries out surface modification using titanate coupling agent to titanium dioxide carrying silver antimicrobials, improves titanium dioxide
Dispersive property of the carrying silver antimicrobials in paint；Effectively prevent wood furniture from burning by adding composite flame-retardant agent in paint,
The composite flame-retardant agent shows good flame retardant synergistic effect；The resistance to bacterium for effectively improving paint by adding modified antiseptic kills
Bacterium performance, Ag+TiO can be expanded2Photocatalysis excitation wavelength, while embedded TiO2Ag in crystal defect+In sterilization process
It can realize and slowly discharge and prevent from being oxidized, reach the effect of double sterilization；Flame-proof antibiotic prepared by present invention paint can be with
Effectively reduce the occurrence index of wood furniture.
Embodiment 2：
A kind of wood furniture is painted with flame-proof antibiotic, and being calculated according to mass parts mainly includes 15 parts of silicone alkyds, 8
Part acrylonitrile, 3 organic epoxy resins, 25 parts of oil, 10.8 parts of composite flame-retardant agents, 4.5 parts of modified antiseptics；The modification resists
Microbial inoculum is the titanium dioxide carrying silver antimicrobials of HC-114 titanate coupling agent modifieds；The composite flame-retardant agent by flame-retardant direction with
APP is according to mass ratio 4:1 compounding composition；The flame-retardant direction and APP are with mesoporous silicon oxide according to mass ratio 0.8:1 compounding
Form.
Test the anti-microbial property of paint：By flame-proof antibiotic paint application on print, paint is detected with film adherence method
Anti-microbial property；In order to embody the spectrum antimicrobial properties of nano antibacterial paint, three kinds of representative Staphylococcus aureus are have selected
Bacterium, big field bacillus and Candida albicans；The bacterium solution of preparation is uniformly applied to the surface of print, covered with sterile plastic sheet
Print, it is then placed within 37 DEG C, cultivates 24h in the insulating box that relative humidity is 90%；Then with PBS by the bacterium solution on each print
Elution is got off, and by de- washing lotion inoculated and cultured 24h, is observed result and is calculated antibiotic rate.
Found after test, flame-proof antibiotic paint is after 24h 99.9% to the antibiotic rate of Escherichia coli, to golden yellow grape ball
The antibiotic rate of bacterium is 99.9%, and the antibiotic rate to Candida albicans is 99.9%；Antiseptic manufactured in the present embodiment has higher
Anti-microbial property.
The timber coated compared to the antibacterium paint for being not added with fire retardant, flame-proof antibiotic paint application manufactured in the present embodiment
The average HRR of timber have dropped 56.8%, illustrate that the addition of composite flame-retardant agent effectively reduces timber thermal degradation generation
The speed of flammable volatility product, fire intensity reduce；It is preferably fire-retardant to show that flame-proof antibiotic paint manufactured in the present embodiment has
Effect.
The present invention carries out surface modification using titanate coupling agent to titanium dioxide carrying silver antimicrobials, improves titanium dioxide
Dispersive property of the carrying silver antimicrobials in paint；Effectively prevent wood furniture from burning by adding composite flame-retardant agent in paint,
The composite flame-retardant agent shows good flame retardant synergistic effect；The resistance to bacterium for effectively improving paint by adding modified antiseptic kills
Bacterium performance, Ag+TiO can be expanded2Photocatalysis excitation wavelength, while embedded TiO2Ag in crystal defect+In sterilization process
It can realize and slowly discharge and prevent from being oxidized, reach the effect of double sterilization；Flame-proof antibiotic prepared by present invention paint can be with
Effectively reduce the occurrence index of wood furniture.
It is described above, be only presently preferred embodiments of the present invention, any formal limitation not done to the present invention, it is every according to
Any simply modification, the equivalent variations made according to the technical spirit of the present invention to above example, each fall within the protection of the present invention
Within the scope of.
Claims (6)
1. a kind of wood furniture is painted with flame-proof antibiotic, it is characterised in that being calculated according to mass parts mainly includes following component：
Silicone alkyd：10-15 parts；
Acrylonitrile：5-8 parts；
Organic epoxy resin：3-5 parts；
Oil：20-25；
Pigment：1.5-3 part；
Composite flame-retardant agent：5-12.5 part；
Modified antiseptic：2-5 parts.
2. a kind of wood furniture according to claim 1 is painted with flame-proof antibiotic, it is characterised in that the composite flame-retardant agent
By flame-retardant direction and APP according to mass ratio 3:1-4:1 forms with mesoporous silicon oxide compounding.
3. a kind of wood furniture according to claim 2 is painted with flame-proof antibiotic, it is characterised in that the flame-retardant direction
With APP and mesoporous silicon oxide according to mass ratio 0.5:1-0.8:1 compounding forms.
4. a kind of wood furniture according to claim 1 is painted with flame-proof antibiotic, it is characterised in that the modified antiseptic
For the titanium dioxide silver base inorganic antibacterial agent of titanate coupling agent modified.
5. a kind of wood furniture according to claim 1 is painted with flame-proof antibiotic, it is characterised in that the composite flame-retardant agent
By flame-retardant direction and APP according to mass ratio 4:1 compounding composition；The flame-proof antibiotic paint calculates according to mass parts mainly to be included
12 parts of silicone alkyds, 6 parts of acrylonitrile, 3 organic epoxy resins, 20 parts of oil, 8 parts of composite flame-retardant agents, 4 parts change
Property antiseptic.
6. a kind of wood furniture according to claim 1 is painted with flame-proof antibiotic, it is characterised in that the composite flame-retardant agent
By flame-retardant direction and APP according to mass ratio 4:1 compounding composition；The flame-proof antibiotic paint calculates according to mass parts mainly to be included
15 parts of silicone alkyds, 8 parts of acrylonitrile, 3 organic epoxy resins, 25 parts of oil, 10.8 parts of composite flame-retardant agents,
4.5 parts of modified antiseptics.