CN107722818A - A kind of special luminous paint of painting advertisement and preparation method thereof - Google Patents
A kind of special luminous paint of painting advertisement and preparation method thereof Download PDFInfo
- Publication number
- CN107722818A CN107722818A CN201710929434.3A CN201710929434A CN107722818A CN 107722818 A CN107722818 A CN 107722818A CN 201710929434 A CN201710929434 A CN 201710929434A CN 107722818 A CN107722818 A CN 107722818A
- Authority
- CN
- China
- Prior art keywords
- parts
- polyurethane
- luminous paint
- painting advertisement
- special luminous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses special luminous paint of a kind of painting advertisement and preparation method thereof, the special luminous paint of painting advertisement is made up of the raw material components of following parts by weight：15 25 parts of unsaturated polyester resin, 8 15 parts of toluene di-isocyanate(TDI), 20 30 parts of polyurethane, 10 18 parts of methyl acrylate, 5 12 parts of glycerine, 6 10 parts of ethyl acetate, 26 parts of zeolite powder, 15 parts of luminescent powder, 13 parts of titanium dioxide, 58 parts of sodium silicoaluminate, 0.8 1.8 parts of zinc naphthenate, 13 parts of barium chromate, 13 parts of zinc oxide, 38 parts of graphite, 7 13 parts of borax, 13 parts of adhesive for polyurethane, 49 parts of diethylenetriamine.The water resistance and corrosion resistance of the special luminous paint of painting advertisement in the present invention are strong, are provided simultaneously with good photism, good with its painting advertisement, the effect of publicity.
Description
Technical field
The invention belongs to painting advertisement technical field, the special luminous paint of more particularly to a kind of painting advertisement and its preparation side
Method.
Background technology
Luminous paint refers to that fluorescence, phosphorescence or reflective paint can be sent.It is divided into three kinds of reflective, phosphorescence, fluorescent paint.Reflectorised paint by
Glass bead is fitted in varnish, is brushed and is formed on aluminium primer；Phosphorescent paint adds paint vehicle to be made by phosphorescent pigment；Fluorescent paint be by
Fluorescent pigment adds paint vehicle to be made.It is usually used in road sign, safety signal, billboard, guideboard and Luminous Timekeeper etc..Painting advertisement,
Its original picture and word give visual enjoyment, turn into one of beautiful scenery.But existing advertisement
The water resistance and corrosion resistance of air brushing paint are bad, and do not have photism, are unfavorable for being observed by people.
The content of the invention
It is an object of the invention to provide special luminous paint of a kind of painting advertisement and preparation method thereof, the painting advertisement is special
Luminous paint possesses good photism, good with its painting advertisement, the effect of publicity.
To achieve the above object, the present invention provides following technical scheme：
A kind of special luminous paint of painting advertisement, it is made up of the raw material components of following parts by weight：Unsaturated polyester resin
15-25 parts, toluene di-isocyanate(TDI) 8-15 parts, polyurethane 20-30 parts, methyl acrylate 10-18 parts, glycerine 5-12 parts, second
Acetoacetic ester 6-10 parts, zeolite powder 2-6 parts, luminescent powder 1-5 parts, titanium dioxide 1-3 parts, sodium silicoaluminate 5-8 parts, zinc naphthenate 0.8-
1.8 parts, barium chromate 1-3 parts, zinc oxide 1-3 parts, graphite 3-8 parts, borax 7-13 parts, adhesive for polyurethane 1-3 parts, divinyl three
Amine 4-9 parts.
Preferably, the special luminous paint of described painting advertisement is made up of the raw material components of following parts by weight：Unsaturation is poly-
22 parts of ester resin, 12 parts of toluene di-isocyanate(TDI), 28 parts of polyurethane, 13 parts of methyl acrylate, 8 parts of glycerine, ethyl acetate 8
Part, 3 parts of zeolite powder, 2 parts of luminescent powder, 1.5 parts of titanium dioxide, 6 parts of sodium silicoaluminate, 1.2 parts of zinc naphthenate, 1 part of barium chromate, zinc oxide
2 parts, 5 parts of graphite, 8 parts of borax, 1 part of adhesive for polyurethane, 5 parts of diethylenetriamine.
Preferably, the special luminous paint of described painting advertisement is made up of the raw material components of following parts by weight：Unsaturation is poly-
24 parts of ester resin, 11 parts of toluene di-isocyanate(TDI), 30 parts of polyurethane, 14 parts of methyl acrylate, 7 parts of glycerine, ethyl acetate 7
Part, 6 parts of zeolite powder, 5 parts of luminescent powder, 3 parts of titanium dioxide, 7 parts of sodium silicoaluminate, 1 part of zinc naphthenate, 2 parts of barium chromate, 2 parts of zinc oxide,
6 parts of graphite, 9 parts of borax, 2 parts of adhesive for polyurethane, 8 parts of diethylenetriamine.
Preferably, the special luminous paint of described painting advertisement is made up of the raw material components of following parts by weight：Unsaturation is poly-
23 parts of ester resin, 13 parts of toluene di-isocyanate(TDI), 25 parts of polyurethane, 10 parts of methyl acrylate, 10 parts of glycerine, ethyl acetate 8
Part, 3 parts of zeolite powder, 3 parts of luminescent powder, 1 part of titanium dioxide, 7 parts of sodium silicoaluminate, 1.3 parts of zinc naphthenate, 2.5 parts of barium chromate, zinc oxide
2 parts, 5 parts of graphite, 11 parts of borax, 3 parts of adhesive for polyurethane, 6 parts of diethylenetriamine.
The preparation method of the special luminous paint of described painting advertisement, it comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) by unsaturated polyester resin, toluene di-isocyanate(TDI), polyurethane, methyl acrylate, glycerine, ethyl acetate
And diethylenetriamine is placed in agitating device, 78-85 DEG C is heated to, stirs 25-32 minutes, stops stirring, naturally cools to
24-28℃A；
(3) then add zeolite powder, luminescent powder, titanium dioxide, sodium silicoaluminate, zinc naphthenate, barium chromate, zinc oxide, graphite,
Borax and adhesive for polyurethane, stir 18-23 minutes, you can it is of the invention in the special luminous paint of painting advertisement.
Compared with prior art, the beneficial effects of the invention are as follows：
The special luminous paint of painting advertisement in the present invention using unsaturated polyester resin, toluene di-isocyanate(TDI) and polyurethane as
Primary raw material, while the auxiliary materials such as zeolite powder, luminescent powder, titanium dioxide, sodium silicoaluminate, zinc naphthenate and barium chromate are added, make its tool
Standby good photism is good with its painting advertisement, the effect of publicity.
Embodiment
Technical scheme is described in detail with reference to embodiment, but protection domain is not limited thereto.
Embodiment one：
A kind of special luminous paint of painting advertisement, it is made up of the raw material components of following parts by weight：Unsaturated polyester resin
22 parts, 12 parts of toluene di-isocyanate(TDI), 25 parts of polyurethane, 14 parts of methyl acrylate, 8 parts of glycerine, 9 parts of ethyl acetate, zeolite
5 parts of powder, 4 parts of luminescent powder, 2 parts of titanium dioxide, 6 parts of sodium silicoaluminate, 1.3 parts of zinc naphthenate, 1.5 parts of barium chromate, 2.5 parts of zinc oxide,
6 parts of graphite, 12 parts of borax, 2 parts of adhesive for polyurethane, 4 parts of diethylenetriamine.
The preparation method of the special luminous paint of described painting advertisement, it comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) by unsaturated polyester resin, toluene di-isocyanate(TDI), polyurethane, methyl acrylate, glycerine, ethyl acetate
And diethylenetriamine is placed in agitating device, 78-85 DEG C is heated to, stirs 25-32 minutes, stops stirring, naturally cools to
24-28℃A；
(3) then add zeolite powder, luminescent powder, titanium dioxide, sodium silicoaluminate, zinc naphthenate, barium chromate, zinc oxide, graphite,
Borax and adhesive for polyurethane, stir 18-23 minutes, you can it is of the invention in painting advertisement it is special luminous.
Embodiment two：
A kind of special luminous paint of painting advertisement, it is made up of the raw material components of following parts by weight：Unsaturated polyester resin
22 parts, 12 parts of toluene di-isocyanate(TDI), 28 parts of polyurethane, 13 parts of methyl acrylate, 8 parts of glycerine, 8 parts of ethyl acetate, zeolite
3 parts of powder, 2 parts of luminescent powder, 1.5 parts of titanium dioxide, 6 parts of sodium silicoaluminate, 1.2 parts of zinc naphthenate, 1 part of barium chromate, 2 parts of zinc oxide, stone
5 parts of ink, 8 parts of borax, 1 part of adhesive for polyurethane, 5 parts of diethylenetriamine.
The preparation method of the special luminous paint of described painting advertisement, it comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) by unsaturated polyester resin, toluene di-isocyanate(TDI), polyurethane, methyl acrylate, glycerine, ethyl acetate
And diethylenetriamine is placed in agitating device, 78-85 DEG C is heated to, stirs 25-32 minutes, stops stirring, naturally cools to
24-28℃A；
(3) then add zeolite powder, luminescent powder, titanium dioxide, sodium silicoaluminate, zinc naphthenate, barium chromate, zinc oxide, graphite,
Borax and adhesive for polyurethane, stir 18-23 minutes, you can it is of the invention in painting advertisement it is special luminous.
Embodiment three：
A kind of special luminous paint of painting advertisement, it is made up of the raw material components of following parts by weight：Unsaturated polyester resin
24 parts, 11 parts of toluene di-isocyanate(TDI), 30 parts of polyurethane, 14 parts of methyl acrylate, 7 parts of glycerine, 7 parts of ethyl acetate, zeolite
6 parts of powder, 5 parts of luminescent powder, 3 parts of titanium dioxide, 7 parts of sodium silicoaluminate, 1 part of zinc naphthenate, 2 parts of barium chromate, 2 parts of zinc oxide, graphite 6
Part, 9 parts of borax, 2 parts of adhesive for polyurethane, 8 parts of diethylenetriamine.
The preparation method of the special luminous paint of described painting advertisement, it comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) by unsaturated polyester resin, toluene di-isocyanate(TDI), polyurethane, methyl acrylate, glycerine, ethyl acetate
And diethylenetriamine is placed in agitating device, 78-85 DEG C is heated to, stirs 25-32 minutes, stops stirring, naturally cools to
24-28℃A；
(3) then add zeolite powder, luminescent powder, titanium dioxide, sodium silicoaluminate, zinc naphthenate, barium chromate, zinc oxide, graphite,
Borax and adhesive for polyurethane, stir 18-23 minutes, you can it is of the invention in painting advertisement it is special luminous.
Example IV：
A kind of special luminous paint of painting advertisement, it is made up of the raw material components of following parts by weight：Unsaturated polyester resin
23 parts, 13 parts of toluene di-isocyanate(TDI), 25 parts of polyurethane, 10 parts of methyl acrylate, 10 parts of glycerine, 8 parts of ethyl acetate, zeolite
3 parts of powder, 3 parts of luminescent powder, 1 part of titanium dioxide, 7 parts of sodium silicoaluminate, 1.3 parts of zinc naphthenate, 2.5 parts of barium chromate, 2 parts of zinc oxide, stone
5 parts of ink, 11 parts of borax, 3 parts of adhesive for polyurethane, 6 parts of diethylenetriamine.
The preparation method of the special luminous paint of described painting advertisement, it comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) by unsaturated polyester resin, toluene di-isocyanate(TDI), polyurethane, methyl acrylate, glycerine, ethyl acetate
And diethylenetriamine is placed in agitating device, 78-85 DEG C is heated to, stirs 25-32 minutes, stops stirring, naturally cools to
24-28℃A；
(3) then add zeolite powder, luminescent powder, titanium dioxide, sodium silicoaluminate, zinc naphthenate, barium chromate, zinc oxide, graphite,
Borax and adhesive for polyurethane, stir 18-23 minutes, you can it is of the invention in painting advertisement it is special luminous.
Embodiment five：
A kind of special luminous paint of painting advertisement, it is made up of the raw material components of following parts by weight：Unsaturated polyester resin
15 parts, 8 parts of toluene di-isocyanate(TDI), 20 parts of polyurethane, 10 parts of methyl acrylate, 5 parts of glycerine, 6 parts of ethyl acetate, zeolite powder
2 parts, 1 part of luminescent powder, 1 part of titanium dioxide, 5 parts of sodium silicoaluminate, 0.8 part of zinc naphthenate, 1 part of barium chromate, 1 part of zinc oxide, graphite 3
Part, 7 parts of borax, 1 part of adhesive for polyurethane, 4 parts of diethylenetriamine.
The preparation method of the special luminous paint of described painting advertisement, it comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) by unsaturated polyester resin, toluene di-isocyanate(TDI), polyurethane, methyl acrylate, glycerine, ethyl acetate
And diethylenetriamine is placed in agitating device, 78-85 DEG C is heated to, stirs 25-32 minutes, stops stirring, naturally cools to
24-28℃A；
(3) then add zeolite powder, luminescent powder, titanium dioxide, sodium silicoaluminate, zinc naphthenate, barium chromate, zinc oxide, graphite,
Borax and adhesive for polyurethane, stir 18-23 minutes, you can it is of the invention in painting advertisement it is special luminous.
Embodiment six：
A kind of special luminous paint of painting advertisement, it is made up of the raw material components of following parts by weight：Unsaturated polyester resin
25 parts, 15 parts of toluene di-isocyanate(TDI), 30 parts of polyurethane, 18 parts of methyl acrylate, 12 parts of glycerine, 10 parts of ethyl acetate, boiling
6 parts of stone flour, 5 parts of luminescent powder, 3 parts of titanium dioxide, 8 parts of sodium silicoaluminate, 1.8 parts of zinc naphthenate, 3 parts of barium chromate, 3 parts of zinc oxide, stone
8 parts of ink, 13 parts of borax, 3 parts of adhesive for polyurethane, 9 parts of diethylenetriamine.
The preparation method of the special luminous paint of described painting advertisement, it comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) by unsaturated polyester resin, toluene di-isocyanate(TDI), polyurethane, methyl acrylate, glycerine, ethyl acetate
And diethylenetriamine is placed in agitating device, 78-85 DEG C is heated to, stirs 25-32 minutes, stops stirring, naturally cools to
24-28℃A；
(3) then add zeolite powder, luminescent powder, titanium dioxide, sodium silicoaluminate, zinc naphthenate, barium chromate, zinc oxide, graphite,
Borax and adhesive for polyurethane, stir 18-23 minutes, you can it is of the invention in painting advertisement it is special luminous.
Finally illustrate, the above embodiments are merely illustrative of the technical solutions of the present invention and it is unrestricted, although with reference to compared with
The present invention is described in detail good embodiment, it will be understood by those within the art that, can be to the skill of the present invention
Art scheme is modified or equivalent substitution, and without departing from the objective and scope of the technical program, it all should cover in the present invention
Right among.
Claims (5)
1. a kind of special luminous paint of painting advertisement, it is characterised in that be made up of the raw material components of following parts by weight：Unsaturation is poly-
Ester resin 15-25 parts, toluene di-isocyanate(TDI) 8-15 parts, polyurethane 20-30 parts, methyl acrylate 10-18 parts, glycerine 5-12
Part, ethyl acetate 6-10 parts, zeolite powder 2-6 parts, luminescent powder 1-5 parts, titanium dioxide 1-3 parts, sodium silicoaluminate 5-8 parts, zinc naphthenate
0.8-1.8 parts, barium chromate 1-3 parts, zinc oxide 1-3 parts, graphite 3-8 parts, borax 7-13 parts, adhesive for polyurethane 1-3 parts, diethyl
Alkene triamine 4-9 parts.
2. the special luminous paint of a kind of painting advertisement according to claim 1, it is characterised in that by the original of following parts by weight
Material component is made：22 parts of unsaturated polyester resin, 12 parts of toluene di-isocyanate(TDI), 28 parts of polyurethane, 13 parts of methyl acrylate, third
8 parts of triol, 8 parts of ethyl acetate, 3 parts of zeolite powder, 2 parts of luminescent powder, 1.5 parts of titanium dioxide, 6 parts of sodium silicoaluminate, zinc naphthenate 1.2
Part, 1 part of barium chromate, 2 parts of zinc oxide, 5 parts of graphite, 8 parts of borax, 1 part of adhesive for polyurethane, 5 parts of diethylenetriamine.
3. the special luminous paint of a kind of painting advertisement according to claim 1, it is characterised in that by the original of following parts by weight
Material component is made：24 parts of unsaturated polyester resin, 11 parts of toluene di-isocyanate(TDI), 30 parts of polyurethane, 14 parts of methyl acrylate, third
7 parts of triol, 7 parts of ethyl acetate, 6 parts of zeolite powder, 5 parts of luminescent powder, 3 parts of titanium dioxide, 7 parts of sodium silicoaluminate, 1 part of zinc naphthenate, chromium
Sour 2 parts of barium, 2 parts of zinc oxide, 6 parts of graphite, 9 parts of borax, 2 parts of adhesive for polyurethane, 8 parts of diethylenetriamine.
4. the special luminous paint of a kind of painting advertisement according to claim 1, it is characterised in that by the original of following parts by weight
Material component is made：23 parts of unsaturated polyester resin, 13 parts of toluene di-isocyanate(TDI), 25 parts of polyurethane, 10 parts of methyl acrylate, third
10 parts of triol, 8 parts of ethyl acetate, 3 parts of zeolite powder, 3 parts of luminescent powder, 1 part of titanium dioxide, 7 parts of sodium silicoaluminate, 1.3 parts of zinc naphthenate,
2.5 parts of barium chromate, 2 parts of zinc oxide, 5 parts of graphite, 11 parts of borax, 3 parts of adhesive for polyurethane, 6 parts of diethylenetriamine.
5. a kind of preparation method of the special luminous paint of painting advertisement according to any one of claim 1-4, its feature exist
In comprising the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) by unsaturated polyester resin, toluene di-isocyanate(TDI), polyurethane, methyl acrylate, glycerine, ethyl acetate and
Diethylenetriamine is placed in agitating device, is heated to 78-85 DEG C, stirs 25-32 minutes, is stopped stirring, is naturally cooled to 24-28
℃；
(3) then add zeolite powder, luminescent powder, titanium dioxide, sodium silicoaluminate, zinc naphthenate, barium chromate, zinc oxide, graphite, borax
And adhesive for polyurethane, stir 18-23 minutes, you can it is of the invention in the special luminous paint of painting advertisement.