CN103773201A - Ageing resistant coating for lamp poles and preparation method thereof - Google Patents
Ageing resistant coating for lamp poles and preparation method thereof Download PDFInfo
- Publication number
- CN103773201A CN103773201A CN201410025995.7A CN201410025995A CN103773201A CN 103773201 A CN103773201 A CN 103773201A CN 201410025995 A CN201410025995 A CN 201410025995A CN 103773201 A CN103773201 A CN 103773201A
- Authority
- CN
- China
- Prior art keywords
- parts
- resistant coating
- lamp stand
- pigment
- calcium carbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention provides ageing resistant coating for lamp poles and a preparation method thereof. The ageing resistant coating comprises the following components in parts by weight: 25-35 parts of acrylic modified alkyd resin, 6-13 parts of pigment, 18-30 parts of calcium carbonate, 6-12 parts of silica powder, 4-10 parts of organic bentonite, 1.3-2.7 parts of dibutyl phthalate, 1-2.2 parts of ultraviolet absorber, 0.5-1.3 parts of aminopropyltriethoxysilane, 2.8-4.2 parts of methylbenzene, 0.3-0.5 parts of polyester organic silicone resin and 2-5 parts of water. The ageing resistant coating provided by the invention has very good adhesive force and ageing resistance, the characteristics of light maintenance, weather fastness and alkali resistance, high definition, strong stereoscopic impression and very good protection and decoration effects on the lamp poles.
Description
Technical field
The present invention relates to paint field, relate in particular to a kind of lamp stand aging resistant coating and preparation method thereof.
Background technology
At present the outward appearance of lamp stand is varied, and lamp stand is part and parcel very in Road construction, and part is also absolutely necessary.Generally can scribble coating in lamp stand outside, the effect of playing protection and decorating.Lamp stand is because long-term exposure is outdoor, and its surperficial coating easily peels off and variable color, and therefore coating must have good sticking power and ageing-resistant performance, also needs to have to protect light, weather-proof characteristic.But existing lamp stand is not high by the ageing-resistant performance of coating, and of long duration easily come off.
Summary of the invention
the technical problem solving:for existing lamp stand with coating ageing-resistant performance not high, of long duration hold caducous shortcoming, the invention provides a kind of lamp stand aging resistant coating and preparation method thereof.
technical scheme:a kind of lamp stand aging resistant coating, contain following composition in mass parts: 25～35 parts of acrylic acid modified alkyd resins, 6～13 parts of pigment, 18～30 parts, calcium carbonate, 6～12 parts of silicon powders, 4～10 parts of organobentonites, 1.3～2.7 parts of dibutyl phthalates, 1～2.2 part of UV light absorber, 0.5～1.3 part of aminopropyl triethoxysilane, 2.8～4.2 parts of toluene, 0.3～0.5 part of polyester silicone resin, 2～5 parts, water.
A kind of lamp stand aging resistant coating described above, contain following composition in mass parts: 30 parts of acrylic acid modified alkyd resins, 9.5 parts of pigment, 24 parts, calcium carbonate, 9 parts of silicon powders, 7 parts of organobentonites, 2 parts of dibutyl phthalates, 1.6 parts of UV light absorber, 0.9 part of aminopropyl triethoxysilane, 3.6 parts of toluene, 0.4 part of polyester silicone resin, 3.5 parts, water.
A kind of lamp stand described above is as follows by the preparation process of aging resistant coating: after acrylic acid modified alkyd resin, pigment, calcium carbonate, silicon powder, organobentonite and toluene are mixed, be ground to fineness≤20 μ m, then mix with dibutyl phthalate, aminopropyl triethoxysilane, UV light absorber, polyester silicone resin and water, filtration gets product again.
beneficial effect:aging resistant coating and preparation method thereof for a kind of lamp stand provided by the invention; this coating has good sticking power and ageing-resistant performance, also have the light of guarantor, weather-proof, alkaline-resisting characteristic, and sharpness is high; stereoscopic sensation is strong, and lamp stand is had to good protection and decorative effect.
Embodiment
embodiment 1
The present embodiment provides a kind of lamp stand aging resistant coating, contain following composition in mass parts: 25 parts of acrylic acid modified alkyd resins, 6 parts of pigment, 18 parts, calcium carbonate, 6 parts of silicon powders, 4 parts of organobentonites, 1.3 parts of dibutyl phthalates, 1 part of UV light absorber, 0.5 part of aminopropyl triethoxysilane, 2.8 parts of toluene, 0.3 part of polyester silicone resin, 2 parts, water.
A kind of lamp stand is as follows by the preparation process of aging resistant coating: after acrylic acid modified alkyd resin, pigment, calcium carbonate, silicon powder, organobentonite and toluene are mixed, be ground to fineness≤20 μ m, then mix with dibutyl phthalate, aminopropyl triethoxysilane, UV light absorber, polyester silicone resin and water, filtration gets product again.
embodiment 2
The present embodiment provides a kind of lamp stand aging resistant coating, contain following composition in mass parts: 35 parts of acrylic acid modified alkyd resins, 13 parts of pigment, 30 parts, calcium carbonate, 12 parts of silicon powders, 10 parts of organobentonites, 2.7 parts of dibutyl phthalates, 2.2 parts of UV light absorber, 1.3 parts of aminopropyl triethoxysilanes, 4.2 parts of toluene, 0.5 part of polyester silicone resin, 5 parts, water.
A kind of lamp stand is as follows by the preparation process of aging resistant coating: after acrylic acid modified alkyd resin, pigment, calcium carbonate, silicon powder, organobentonite and toluene are mixed, be ground to fineness≤20 μ m, then mix with dibutyl phthalate, aminopropyl triethoxysilane, UV light absorber, polyester silicone resin and water, filtration gets product again.
embodiment 3
The present embodiment provides a kind of lamp stand aging resistant coating, contain following composition in mass parts: 30 parts of acrylic acid modified alkyd resins, 9.5 parts of pigment, 24 parts, calcium carbonate, 9 parts of silicon powders, 7 parts of organobentonites, 2 parts of dibutyl phthalates, 1.6 parts of UV light absorber, 0.9 part of aminopropyl triethoxysilane, 3.6 parts of toluene, 0.4 part of polyester silicone resin, 3.5 parts, water.
A kind of lamp stand is as follows by the preparation process of aging resistant coating: after acrylic acid modified alkyd resin, pigment, calcium carbonate, silicon powder, organobentonite and toluene are mixed, be ground to fineness≤20 μ m, then mix with dibutyl phthalate, aminopropyl triethoxysilane, UV light absorber, polyester silicone resin and water, filtration gets product again.
The technical performance index of above-mentioned a kind of lamp stand aging resistant coating of stating embodiment 1～embodiment 3, its detected result is as follows:
Detected result
| Test item | Test index | Embodiment 1 | Embodiment 2 | Embodiment 3 |
| Sticking power/MPa | GB/T 5210-2006 | 6.32 | 6.26 | 6.35 |
| Temper(ing) time/h | ? | 1230 | 1250 | 1300 |
| Ultraviolet resistance irradiation time/h | ? | 953 | 951 | 965 |
Above the embodiment of the present invention is described in detail, for one of ordinary skill in the art, according to the thought of the embodiment of the present invention, all will change in specific embodiments and applications, in sum, this description should not be construed as limitation of the present invention.
Claims (3)
1. a lamp stand aging resistant coating, it is characterized in that containing following composition in mass parts: 25～35 parts of acrylic acid modified alkyd resins, 6～13 parts of pigment, 18～30 parts, calcium carbonate, 6～12 parts of silicon powders, 4～10 parts of organobentonites, 1.3～2.7 parts of dibutyl phthalates, 1～2.2 part of UV light absorber, 0.5～1.3 part of aminopropyl triethoxysilane, 2.8～4.2 parts of toluene, 0.3～0.5 part of polyester silicone resin, 2～5 parts, water.
2. a kind of lamp stand aging resistant coating according to claim 1, it is characterized in that containing following composition in mass parts: 30 parts of acrylic acid modified alkyd resins, 9.5 parts of pigment, 24 parts, calcium carbonate, 9 parts of silicon powders, 7 parts of organobentonites, 2 parts of dibutyl phthalates, 1.6 parts of UV light absorber, 0.9 part of aminopropyl triethoxysilane, 3.6 parts of toluene, 0.4 part of polyester silicone resin, 3.5 parts, water.
3. the preparation method of aging resistant coating for a kind of lamp stand as claimed in claim 1, the preparation process that it is characterized in that the method is as follows: after acrylic acid modified alkyd resin, pigment, calcium carbonate, silicon powder, organobentonite and toluene are mixed, be ground to fineness≤20 μ m, then mix with dibutyl phthalate, aminopropyl triethoxysilane, UV light absorber, polyester silicone resin and water, filtration gets product again.