CN107722801A - A kind of water-based heavy antisepsis finish paint and preparation method thereof - Google Patents
A kind of water-based heavy antisepsis finish paint and preparation method thereof Download PDFInfo
- Publication number
- CN107722801A CN107722801A CN201710929152.3A CN201710929152A CN107722801A CN 107722801 A CN107722801 A CN 107722801A CN 201710929152 A CN201710929152 A CN 201710929152A CN 107722801 A CN107722801 A CN 107722801A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- finish paint
- based heavy
- heavy antisepsis
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to paint field, discloses a kind of water-based heavy antisepsis finish paint, is made up of following raw material：15 20 parts of waterborne polyester acrylic resin；10 20 parts of filling material；0.1 0.5 parts of wetting dispersing agent；40 60 parts of deionized water；0.1 0.5 parts of adhesion promoter；5 10 parts of coalescents；15 parts of thickener.The heavy-duty antiseptic paint has good workability, strong to metal adhesive power, and excitant is extremely low, VOC free discharge, environmentally friendly.
Description
Technical field
The present invention relates to anticorrosive paint field, and in particular to a kind of water-based heavy antisepsis finish paint and preparation method thereof.
Background technology
With the development of modern society, the raising of human living standard, the progressively awakening of energy conservation and environmental awareness, and high score
Requirement of the high speed development of scarabaeidae for environmental protection is also more and more stricter.
With Guangdong Province's provincial standard《Container manufacture Volatile organic emissions standard》Formulation, and the national tax
Department imposes the consumption tax to the painting of high VOC content；Comprehensive Water-borne modification of coating container is more and more urgent.
It is contemplated that in following very long-term, development environment friendly water paint will turn into China's coating research field
Emphasis, focus, to comply with research, realizing that I takes charge of comprehensive update of coating container and green mesh
Mark, therefore intend carrying out the research and development of water-based heavy antisepsis finish paint.
Under the conditions of big variation is not done in container plant requirement in production line rhythm of production, production technology, the construction that can have
Performance, while it is not less than the performance of oiliness acrylic acid top-coat again.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of water-based heavy antisepsis finish paint.The anticorrosive paint has excellent
Workability, suitable viscosity, sagging performance, rapid draing ability.Paint film mechanical performance；Outstanding adhesive force, pliability,
Impact resistance and good decay resistance.Solve is early stage water resistance under the conditions of case factory production line, long-term water-fast
Xie Xing, initial hardness, drying varniss performance and various film defects.The dosage of coalescents is reduced, VOC content is reduced, reaches
In the case of suitable gloss and hardness, film-forming temperature is reduced, ensures the workability under the conditions of winter low temperature.
The technical problems to be solved by the invention are achieved by the following technical programs：
A kind of water-based heavy antisepsis finish paint, is made up of following parts by weight raw material：
Waterborne polyester acrylic resin 15-20 parts；
Filling material 10-20 parts；
Wetting dispersing agent 0.1-0.5 parts；
Deionized water 40-60 parts；
Adhesion promoter 0.1-0.5 parts；
Coalescents 5-10 parts；
Thickener 1-5 parts.
Further, described filling material includes titanium dioxide, micaceous iron oxide, at least one of superfine talcum powder.
Further, described coalescents include propandiol butyl ether, at least one of propylene glycol methyl ether acetate.
Further, described adhesion promoter is organosilan.Further, described organosilan is road health
Peaceful Z6040.
Further, described wetting dispersing agent is sodium dioctyl sulfosuccinate.
A kind of preparation method of described water-based heavy antisepsis finish paint：
（1）Corresponding raw material is weighed by the formula；
（2）Waterborne polyester acrylic resin is added in agitator, wetting dispersing agent is added and stirs 10 ~ 20min；
（3）Color stuffing is added in agitator, quickly stirs 30 ~ 50min, is ensured well mixed；
（4）Thickener, coalescents, adhesion promoter are added in filtrate, stirring 20min obtains finished product.
Beneficial effect：
The anticorrosive paint has excellent workability, suitable viscosity, sagging performance, rapid draing ability.Paint film machinery
Performance；Outstanding adhesive force, pliability, impact resistance and good decay resistance.What is solved is case factory production lines
Early stage water resistance, long-term hydrolytic resistance, initial hardness, drying varniss performance and various film defects under part.Film forming is reduced to help
The dosage of agent, VOC content is reduced, in the case of reaching suitable gloss and hardness, film-forming temperature is reduced, in the winter time under cryogenic conditions
Also preferable workability is possessed.
Embodiment
With reference to embodiment, the present invention will be described in detail, and embodiment is only the preferred embodiment of the present invention,
It is not limitation of the invention.
Organosilan uses DOW CORNING Z6040, and remaining component is conventional commercial product.
Embodiment 1
A kind of water-based heavy antisepsis finish paint, is made up of following parts by weight raw material：
15 parts of waterborne polyester acrylic resin；
10 parts of titanium dioxide, 10 parts of micaceous iron oxide；
0.2 part of sodium dioctyl sulfosuccinate；
50 parts of deionized water；
0.2 part of organosilan；
5 parts of propandiol butyl ether, 5 parts of propylene glycol methyl ether acetate；
1 part of thickener.
The preparation method of described water-based heavy antisepsis finish paint：
（1）Corresponding raw material is weighed by the formula；
（2）Waterborne polyester acrylic resin is added in agitator, wetting dispersing agent is added and stirs 10 ~ 20min；
（3）Color stuffing is added in agitator, quickly stirs 30 ~ 50min, is ensured well mixed；
（4）Thickener, coalescents, adhesion promoter are added in filtrate, stirring 20min obtains finished product.
Embodiment 2
A kind of water-based heavy antisepsis finish paint, is made up of following parts by weight raw material：
20 parts of waterborne polyester acrylic resin；
10 parts of titanium dioxide, 5 parts of superfine talcum powder；
0.5 part of sodium dioctyl sulfosuccinate；
60 parts of deionized water；
0.1 part of organosilan；
5 parts of propylene glycol methyl ether acetate；
5 parts of thickener.
The preparation method of described water-based heavy antisepsis finish paint：
（1）Corresponding raw material is weighed by the formula；
（2）Waterborne polyester acrylic resin is added in agitator, wetting dispersing agent is added and stirs 10 ~ 20min；
（3）Color stuffing is added in agitator, quickly stirs 30 ~ 50min, is ensured well mixed；
（4）Thickener, coalescents, adhesion promoter are added in filtrate, stirring 20min obtains finished product.
Embodiment 3
A kind of water-based heavy antisepsis finish paint, is made up of following parts by weight raw material：
18 parts of waterborne polyester acrylic resin；
4 parts of titanium dioxide, 3 parts of micaceous iron oxide, 3 parts of superfine talcum powder；
0.1 part of sodium dioctyl sulfosuccinate；
40 parts of deionized water；
0.2 part of organosilan；
10 parts of propandiol butyl ether；
3 parts of thickener.
The preparation method of described water-based heavy antisepsis finish paint：
（1）Corresponding raw material is weighed by the formula；
（2）Waterborne polyester acrylic resin is added in agitator, wetting dispersing agent is added and stirs 10 ~ 20min；
（3）Color stuffing is added in agitator, quickly stirs 30 ~ 50min, is ensured well mixed；
（4）Thickener, coalescents, adhesion promoter are added in filtrate, stirring 20min obtains finished product.
Claims (6)
1. a kind of water-based heavy antisepsis finish paint, it is characterised in that described water-based heavy antisepsis finish paint is by following parts by weight raw material group
Into：
Waterborne polyester acrylic emulsion 15-20 parts；
Filling material 10-20 parts；
Wetting dispersing agent 0.1-0.5 parts；
Deionized water 40-60 parts；
Adhesion promoter 0.1-0.5 parts；
Coalescents 5-10 parts；
Thickener 1-5 parts.
2. water-based heavy antisepsis finish paint according to claim 1, it is characterised in that described filling material includes titanium dioxide, cloud
At least one of female iron oxide, superfine talcum powder.
3. water-based heavy antisepsis finish paint according to claim 1, it is characterised in that described coalescents include propane diols fourth
At least one of ether, propylene glycol methyl ether acetate.
4. water-based heavy antisepsis finish paint according to claim 1, it is characterised in that described adhesion promoter is organosilicon
Alkane.
5. water-based heavy antisepsis finish paint according to claim 1, it is characterised in that described wetting dispersing agent is dioctyl sulphur
Change sodium succinate.
6. the preparation method of the water-based heavy antisepsis finish paint described in a kind of claim 1-5 any one, it is characterised in that described
Preparation method is：
（1）Corresponding raw material is weighed by the formula；
（2）Waterborne polyester acrylic resin is added in agitator, wetting dispersing agent is added and stirs 10 ~ 20min；
（3）Color stuffing is added in agitator, quickly stirs 30 ~ 50min, is ensured well mixed；
（4）Thickener, coalescents, adhesion promoter are added in filtrate, stirring 20min obtains finished product.