CN107722470A - 一种电缆用防水耐磨阻燃护套及其制备方法 - Google Patents
一种电缆用防水耐磨阻燃护套及其制备方法 Download PDFInfo
- Publication number
- CN107722470A CN107722470A CN201710987759.7A CN201710987759A CN107722470A CN 107722470 A CN107722470 A CN 107722470A CN 201710987759 A CN201710987759 A CN 201710987759A CN 107722470 A CN107722470 A CN 107722470A
- Authority
- CN
- China
- Prior art keywords
- parts
- fine powder
- fire retardant
- preparation
- retardant jacket
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及电缆材料领域,具体是一种电缆用防水耐磨阻燃护套及其制备方法,其具体成分如下:三元乙丙橡胶20‑25份、涤纶纤维20‑22份、沥青防水料10‑12份、炭黑8‑10份、陶瓷细粉6‑8份、碳化硅细粉6‑8份、聚氨酯防水密封涂料5‑7份、增稠剂3‑5份、抗氧化剂3‑5份,一种电缆用防水耐磨阻燃护套的制备方法,其具体步骤如下:(1)混杂;(2)加料;(3)增稠;(4)纤维;(5)挤出,本发明相对于传统的橡胶护套,本发明加入炭黑、陶瓷细粉和涤纶纤维,不但耐摩擦和耐高温,还使得护套质地紧密,不易断裂;最后再涂抹聚氨酯防水密封涂料,防水不易燃烧掉落,做双层防护。
Description
技术领域
本发明涉及电缆材料领域,具体是一种电缆用防水耐磨阻燃护套及其制备方法。
背景技术
电缆的护套大多使用橡胶,耐磨且防水性能好,但是容易燃烧,而后在橡胶中加入金属阻燃成分,加入后护套的弯曲性能和耐磨性能变差,因此,在阻燃的选择上需要加以重视。
发明内容
为了解决上述问题,本发明提出一种电缆用防水耐磨阻燃护套及其制备方法。
一种电缆用防水耐磨阻燃护套,其具体成分如下:
三元乙丙橡胶20-25份、涤纶纤维20-22份、沥青防水料10-12份、炭黑8-10份、陶瓷细粉6-8份、碳化硅细粉6-8份、聚氨酯防水密封涂料5-7份、增稠剂3-5份、抗氧化剂3-5份。
一种电缆用防水耐磨阻燃护套的制备方法,其具体步骤如下:
(1)混杂:将三元乙丙橡胶、沥青防水料、炭黑、增稠剂均放置在高热炉中热熔;
(2)加料:在热熔过程中加入陶瓷细粉和碳化硅细粉并搅拌均匀;
(3)增稠:继续加入增稠剂和抗氧化剂搅拌成为混合物;
(4)纤维:加入涤纶纤维后迅速降温待混合物冷却;
(5)挤出:使用挤出造粒机进行挤出,然后手工或机器均匀涂上聚氨酯防水密封涂料干透即可。
所述的步骤(5)的涂抹厚度为0.5毫米。
本发明的有益效果是:本发明相对于传统的橡胶护套,本发明加入炭黑、陶瓷细粉和涤纶纤维,不但耐摩擦和耐高温,还使得护套质地紧密,不易断裂;最后再涂抹聚氨酯防水密封涂料,防水不易燃烧掉落,做双层防护。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面对本发明进一步阐述。
实施例一:
一种电缆用防水耐磨阻燃护套,其具体成分如下:
三元乙丙橡胶25份、涤纶纤维21份、沥青防水料10份、炭黑10份、陶瓷细粉7份、碳化硅细粉6份、聚氨酯防水密封涂料7份、增稠剂4份、抗氧化剂3份。
一种电缆用防水耐磨阻燃护套的制备方法,其具体步骤如下:
(1)混杂:将三元乙丙橡胶、沥青防水料、炭黑、增稠剂均放置在高热炉中热熔;
(2)加料:在热熔过程中加入陶瓷细粉和碳化硅细粉并搅拌均匀;
(3)增稠:继续加入增稠剂和抗氧化剂搅拌成为混合物;
(4)纤维:加入涤纶纤维后迅速降温待混合物冷却;
(5)挤出:使用挤出造粒机进行挤出,然后手工或机器均匀涂上聚氨酯防水密封涂料干透即可。
所述的步骤(5)的涂抹厚度为0.5毫米。
实施例二:
一种电缆用防水耐磨阻燃护套,其具体成分如下:
三元乙丙橡胶23份、涤纶纤维20份、沥青防水料12份、炭黑9份、陶瓷细粉6份、碳化硅细粉8份、聚氨酯防水密封涂料6份、增稠剂3份、抗氧化剂5份。
一种电缆用防水耐磨阻燃护套的制备方法,其具体步骤如下:
(1)混杂:将三元乙丙橡胶、沥青防水料、炭黑、增稠剂均放置在高热炉中热熔;
(2)加料:在热熔过程中加入陶瓷细粉和碳化硅细粉并搅拌均匀;
(3)增稠:继续加入增稠剂和抗氧化剂搅拌成为混合物;
(4)纤维:加入涤纶纤维后迅速降温待混合物冷却;
(5)挤出:使用挤出造粒机进行挤出,然后手工或机器均匀涂上聚氨酯防水密封涂料干透即可。
所述的步骤(5)的涂抹厚度为0.5毫米。
实施例三:
一种电缆用防水耐磨阻燃护套,其具体成分如下:
三元乙丙橡胶20份、涤纶纤维22份、沥青防水料11份、炭黑8份、陶瓷细粉8份、碳化硅细粉7份、聚氨酯防水密封涂料5份、增稠剂5份、抗氧化剂4份。
一种电缆用防水耐磨阻燃护套的制备方法,其具体步骤如下:
(1)混杂:将三元乙丙橡胶、沥青防水料、炭黑、增稠剂均放置在高热炉中热熔;
(2)加料:在热熔过程中加入陶瓷细粉和碳化硅细粉并搅拌均匀;
(3)增稠:继续加入增稠剂和抗氧化剂搅拌成为混合物;
(4)纤维:加入涤纶纤维后迅速降温待混合物冷却;
(5)挤出:使用挤出造粒机进行挤出,然后手工或机器均匀涂上聚氨酯防水密封涂料干透即可。
所述的步骤(5)的涂抹厚度为0.5毫米。
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (3)
1.一种电缆用防水耐磨阻燃护套,其特征在于:其具体成分如下:三元乙丙橡胶20-25份、涤纶纤维20-22份、沥青防水料10-12份、炭黑8-10份、陶瓷细粉6-8份、碳化硅细粉6-8份、聚氨酯防水密封涂料5-7份、增稠剂3-5份、抗氧化剂3-5份。
2.根据权利要求1所述的一种电缆用防水耐磨阻燃护套的制备方法,其特征在于:其具体步骤如下:
(1)混杂:将三元乙丙橡胶、沥青防水料、炭黑、增稠剂均放置在高热炉中热熔;
(2)加料:在热熔过程中加入陶瓷细粉和碳化硅细粉并搅拌均匀;
(3)增稠:继续加入增稠剂和抗氧化剂搅拌成为混合物;
(4)纤维:加入涤纶纤维后迅速降温待混合物冷却;
(5)挤出:使用挤出造粒机进行挤出,然后手工或机器均匀涂上聚氨酯防水密封涂料干透即可。
3.根据权利要求2所述的一种电缆用防水耐磨阻燃护套的制备方法,其特征在于:所述的步骤(5)的涂抹厚度为0.5毫米。