CN107687010A - 一种五金件电镀液 - Google Patents

一种五金件电镀液 Download PDF

Info

Publication number
CN107687010A
CN107687010A CN201710575791.4A CN201710575791A CN107687010A CN 107687010 A CN107687010 A CN 107687010A CN 201710575791 A CN201710575791 A CN 201710575791A CN 107687010 A CN107687010 A CN 107687010A
Authority
CN
China
Prior art keywords
parts
handware
electroplate liquid
sodium
brightener
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710575791.4A
Other languages
English (en)
Inventor
姚小林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chengdu Lian Lida Hardware Products Co Ltd
Original Assignee
Chengdu Lian Lida Hardware Products Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chengdu Lian Lida Hardware Products Co Ltd filed Critical Chengdu Lian Lida Hardware Products Co Ltd
Priority to CN201710575791.4A priority Critical patent/CN107687010A/zh
Publication of CN107687010A publication Critical patent/CN107687010A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种五金件电镀液，其原料按重量份计包括：硫酸铜50～90份、硫酸镍5～10份、硫酸锰50～100份、酒石酸钾钠10～20份、硝基酚5～30份、氯化铵15～40份、硅酸钠4～12份、稳定剂2～5份、光亮剂3～8份。本发明制得电镀液稳定性好，电镀效率高，原料易得成本低、安全环保，镀层色泽美观亮丽、耐刮、耐腐蚀性好。

Description

一种五金件电镀液
技术领域
本发明涉及电镀液技术领域，具体而言，涉及一种五金件电镀液。
背景技术
五金件是指铁、钢、铝等金属经过锻造、压延、切割等物理加工制造而成的各种金属器件,例如五金工具、五金零部件、日用五金、建筑五金以及安防用品等,五金件在各行各业的生产制造中都得到广泛的应用。五金件的材质都是金属，一般都会经过表面处理工艺，防止五金件在后续的加工和使用过程中出现被氧化和腐蚀的现象。
电镀是一种很常用的表面处理工艺。电镀是利用电解原理在某些金属表面上镀上一薄层其它金属或合金的过程，是利用电解作用使金属或其它材料制件的表面附着一层金属膜的工艺从而起到防止腐蚀，提高耐磨性、导电性、反光性及增进美观等作用。
发明内容
本发明提出了一种五金件电镀液，电镀后外表美观，防腐蚀。
为了实现上述目的，本发明所采用的技术方案为：
一种五金件电镀液，其原料按重量份计包括：硫酸铜50～90份、硫酸镍5～10份、硫酸锰50～100份、酒石酸钾钠10～20份、硝基酚5～30份、氯化铵15～40份、硅酸钠4～12份、稳定剂2～5份、光亮剂3～8份。
进一步的，其原料按重量份计包括：硫酸铜50份、硫酸镍5份、硫酸锰50份、酒石酸钾钠15份、硝基酚22份、氯化铵19份、硅酸钠8份、稳定剂4份、光亮剂5份。
进一步的，其原料按重量份计包括：硫酸铜75份、硫酸镍10份、硫酸锰88份、酒石酸钾钠13份、硝基酚20份、氯化铵34份、硅酸钠5份、稳定剂3份、光亮剂7份。
进一步的，所述稳定剂为柠檬酸钠、葡萄糖酸钙中一种或多种。
进一步的，所述光亮剂为蛋白质、苄叉丙酮、苯甲酸钠质量比为1:1:1的组合物。
一种五金件电镀液的制备方法，包括以下步骤：
(1)将硫酸铜50～90份、硫酸镍5～10份、硫酸锰50～100份、酒石酸钾钠10～20份、硝基酚5～30份、氯化铵15～40份、硅酸钠4～12份、稳定剂2～5份、光亮剂3～8份加水定容至1L，并搅拌溶解制成混合液；
(2)将上述混合液调节pH值至5～6.5即得。
本发明有益效果：
本发明制得电镀液稳定性好，电镀效率高，原料易得成本低、安全环保，镀层色泽美观亮丽、耐刮、耐腐蚀性好。
具体实施方式
下面通过具体的实施例对本发明做进一步的详细描述。
实施例1
一种五金件电镀液的制备方法，包括以下步骤：
(1)将硫酸铜50份、硫酸镍10份、硫酸锰50份、酒石酸钾钠10～20份、硝基酚30份、氯化铵15份、硅酸钠12份、稳定剂2份、光亮剂8份加水定容至1L，并搅拌溶解制成混合液；
(2)将上述混合液调节pH值至5～6.5即得。
实施例2
一种五金件电镀液的制备方法，包括以下步骤：
(1)将硫酸铜50份、硫酸镍5份、硫酸锰50份、酒石酸钾钠15份、硝基酚22份、氯化铵19份、硅酸钠8份、稳定剂4份、光亮剂5份加水定容至1L，并搅拌溶解制成混合液；
(2)将上述混合液调节pH值至5～6.5即得。
实施例3
一种五金件电镀液的制备方法，包括以下步骤：
(1)将硫酸铜75份、硫酸镍10份、硫酸锰88份、酒石酸钾钠13份、硝基酚20份、氯化铵34份、硅酸钠5份、稳定剂3份、光亮剂7份加水定容至1L，并搅拌溶解制成混合液；
(2)将上述混合液调节pH值至5～6.5即得。
以上所述仅为本发明的优选实施例而已，并不用于限制本发明，对于本领域的技术人员来说，在本发明的精神和原则内可以有各种更改和变化，这些等同的变型或替换等，均包含在本发明的保护范围之内。

Claims (6)

1.一种五金件电镀液，其特征在于：其原料按重量份计包括：硫酸铜50～90份、硫酸镍5～10份、硫酸锰50～100份、酒石酸钾钠10～20份、硝基酚5～30份、氯化铵15～40份、硅酸钠4～12份、稳定剂2～5份、光亮剂3～8份。
2.根据权利要求1所述的五金件电镀液，其特征在于：其原料按重量份计包括：硫酸铜50份、硫酸镍5份、硫酸锰50份、酒石酸钾钠15份、硝基酚22份、氯化铵19份、硅酸钠8份、稳定剂4份、光亮剂5份。
3.根据权利要求1所述的五金件电镀液，其特征在于：其原料按重量份计包括：硫酸铜75份、硫酸镍10份、硫酸锰88份、酒石酸钾钠13份、硝基酚20份、氯化铵34份、硅酸钠5份、稳定剂3份、光亮剂7份。
4.根据权利要求1所述的五金件电镀液，其特征在于：所述稳定剂为柠檬酸钠、葡萄糖酸钙中一种或多种。
5.根据权利要求1所述的五金件电镀液，其特征在于：所述光亮剂为蛋白质、苄叉丙酮、苯甲酸钠质量比为1:1:1的组合物。
6.一种五金件电镀液的制备方法，其特征在于：包括以下步骤：
(1)将硫酸铜50～90份、硫酸镍5～10份、硫酸锰50～100份、酒石酸钾钠10～20份、硝基酚5～30份、氯化铵15～40份、硅酸钠4～12份、稳定剂2～5份、光亮剂3～8份加水定容至1L，并搅拌溶解制成混合液；
(2)将上述混合液调节pH值至5～6.5即得。
CN201710575791.4A 2017-07-14 2017-07-14 一种五金件电镀液 Pending CN107687010A (zh)