CN107675065B - 一种轻轨车辆用铜基受电弓滑板及其制备方法 - Google Patents
一种轻轨车辆用铜基受电弓滑板及其制备方法 Download PDFInfo
- Publication number
- CN107675065B CN107675065B CN201710918849.0A CN201710918849A CN107675065B CN 107675065 B CN107675065 B CN 107675065B CN 201710918849 A CN201710918849 A CN 201710918849A CN 107675065 B CN107675065 B CN 107675065B
- Authority
- CN
- China
- Prior art keywords
- powder
- copper
- temperature
- slide plate
- rail vehicle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及带电滑动摩擦材料技术领域,特别涉及一种轻轨车辆用铜基受电弓滑板;由以下按质量份计的原料组成:铜粉38~42、铁粉12~18、石墨7~12、碳化钨3~8、锡粉2~4、镍粉1~3、钼粉1~3、二硫化钼1~3、钨粉3~8、钆粉2~5、硅粉8~12、碳酸镁3~6、铬粉1~3;本发明以铜粉为基体组元,通过加入强化组元,从而对基体进行强化;通过加入润滑组元,从而增加受电弓滑板磨损过程中表面的光滑度以及减少使用过程中,受电弓滑板受电流及电弧烧蚀的磨损量,根据实际运用在轻轨车辆上后受电弓滑板磨损量降至3.1mm/万机车公里,导线磨损量降至0.0056mm2/万机车公里,极大的减少了更换频率。
Description
技术领域
本发明涉及带电滑动摩擦材料技术领域,特别涉及一种轻轨车辆用铜基受电弓滑板及其制备方法。
背景技术
受电弓滑板是电力机车获得动力来源的重要集电元件,安装在受电弓的顶部,直接与接触网导线接触。受电弓滑板在静止或滑动状态下从接触网导线上获得电流,为机车供应电力。受电弓滑板的好坏将直接影响轨道运输的效率和效益。如果受电弓滑板质量不好,将使接触网导线产生异常磨损,使用期大大缩短,或者接触网导线将受电弓滑板磨偏后直接接触到受电弓,导致停车事故。接触网导线与受电弓滑板的异常消耗还使得维修费用大大增加。
目前,我国铁路电气化路段中采用的受电弓滑板主要有:纯碳滑板、浸金属碳滑板、粉末冶金滑板。纯碳滑板机械强度低,易脆性折断和破损,引起弓网事故,且电阻大,易引起接触网导线过热氧化,加速导线磨耗;浸金属碳滑板机械强度略高于纯碳滑板,但抗冲击力不足,大部分在没有磨耗到极限前就发生断裂、掉块,使用过程中需要整形,成本高;粉末冶金滑板是以金属铁和铜粉末为基本成分,添加一些润滑成分如炭、铅和二氧化钼等硫化物,通过机械混合使各种成分均匀分布后,利用液压机将混料模压成型,后将毛坯高温烧结,最后浸入润滑油制得,由于粉末冶金材料时金属体,和导线材质相近,而且导线是静态,滑板是动态,所以粉末冶金滑板对导线磨耗较大。而且在使用中易产生电弧。
随着我国铁路的飞速发展,电路电气化的普及,对此过程中运用的电弓滑板的要求越来越高,显然目前传统的电弓滑板于无法满足飞速发展的铁路需求,因此,对现有的电弓滑板进行改进,提高其机械强度、抗冲击性能等综合性能,降低导线磨耗是目前电弓滑板研究的重要方向
发明内容
本发明为解决上述技术问题,提供了一种轻轨车辆用铜基受电弓滑板及其制备方法。
具体是通过以下技术方案来实现的:
一种轻轨车辆用铜基受电弓滑板,由以下按质量份计的原料组成:铜粉38~42、铁粉12~18、石墨7~12、碳化钨3~8、锡粉2~4、镍粉1~3、钼粉1~3、二硫化钼1~3、钨粉3~8、钆粉2~5、硅粉8~12、碳酸镁3~6、铬粉1~3。
由以下按质量份计的原料组成:铜粉40、铁粉15、石墨9、碳化钨5、锡粉3、镍粉2、钼粉2、二硫化钼2、钨粉5、钆粉3、硅粉10、碳酸镁5、铬粉2。
所述铜粉,纯度≥99.5%,粒度为20~75μm,树枝状;所述铁粉,纯度≥98%,粒度为20~75μm,海绵状;所述石墨,纯度≥92%,粒度为20~40μm,颗粒状;所述碳化钨,纯度≥99.5%,灰色粉剂;所述锡粉,纯度≥99.5%,粒度为20~75μm,滴状;所述镍粉,纯度≥99.5%,粒度为20~63μm,球状;所述钼粉,纯度≥99%,粒度为20~40μm,银灰色粉剂;所述二硫化钼,纯度≥97%,粒度为20~45μm,层状粉剂;所述钨粉,纯度≥99%,粒度为38~45μm,深灰色粉剂;所述钆粉,纯度≥99%,粒度为20~50μm,银白色粉剂;所述硅粉,纯度≥95%。
所述的轻轨车辆用铜基受电弓滑板的制备方法,包括以下步骤:
(1)预处理:
a、还原处理:将铜粉和铁粉分别在在氨分解气体中还原处理3h,再冷至室温,过筛即可;
b、烘干:将石墨、碳化钨、锡粉、镍粉、钼粉、二硫化钼、钨粉、钆粉、硅粉、碳酸镁和铬粉分别进行烘干处理,保温3h后随炉冷却即可;
(2)混料:将步骤(1)中处理好的各原料进行混料处理,得混料;
(3)压制成型:将步骤(3)中的混料,倒入压制模具中,在500~800Mpa压力下,压制制得压坯;
(4)预烧结:将压坯置于烧结炉中分层堆放,每层之间用石磨盘隔开,在氨分解气体保护下,以8~15℃/min的升温速度从室温升到500℃;温度升至500℃后保温20~30min;再以5~8℃/min的升温速度从500℃升到900±50℃;接着在900±50℃时保温180~240min;保温结束后随炉冷却到60℃以下,制得毛坯;
(5)复压:将步骤(5)所得的毛坯在500~800MPa的压制压力下进行复压,制得复压坯;
(6)复烧结:将复压坯置于烧结炉中分层堆放,每层之间用石磨盘隔开,在氨分解气体保护下,以8~15℃/min的升温速度从室温升到500℃;温度升至500℃后保温20~30min;再以5~8℃/min的升温速度从500℃升到900±50℃;接着在900±50℃时保温180~240min;保温结束后随炉冷却到60℃以下,制得粗品;
(7)整形:将粗品经整形即制得本发明铜基受电弓滑板。
进一步,石磨在烘干之前,还包括将石磨进行球磨的步骤,球磨时间是1~3h。
进一步,铜粉的还原处理,是在400~450℃下进行,铁粉的还原处理是在600~700℃下进行。
所述的烘干,温度为150~200℃。
所述的混料处理,是将各原料在转速为30~60r/min的条件下,混合6~12h即可。
综上所述,本发明的有益效果在于:以铜粉为基体组元,通过加入铁粉、镍粉、钆粉、硅粉、碳酸镁和铬粉等强化组元,从而对基体进行强化;通过加入石墨、碳化钨、钼粉和二硫化钼等润滑组元,从而增加受电弓滑板磨损过程中表面的光滑度以及减少使用过程中,受电弓滑板受电流及电弧烧蚀的磨损量。使用本技术方案制备的受电弓滑板,使用过程中无需与润滑块配套使用,而且受电弓滑板自身以及接触网导线的磨损量都比较小,增加了受电弓滑板以及接触网导线的寿命,减少更换频率,受电弓滑板磨损量降至3.1mm/万机车公里,导线磨损量降至0.0056mm2/万机车公里。
具体实施方式
下面对本发明的具体实施方式作进一步详细的说明,但本发明并不局限于这些实施方式,任何在本实施例基本精神上的改进或代替,仍属于本发明权利要求所要求保护的范围。
实施例1
一种轻轨车辆用铜基受电弓滑板,由以下按质量份计的原料组成:铜粉38g、铁粉12g、石墨7g、碳化钨3g、锡粉2g、镍粉1g、钼粉1g、二硫化钼1g、钨粉3g、钆粉2g、硅粉8g、碳酸镁3g、铬粉1g。
所述的轻轨车辆用铜基受电弓滑板的制备方法,包括以下步骤:
(1)预处理:
a、还原处理:在氨分解气体中,将铜粉在400℃下进行还原处理3h,将铁粉在600℃下进行还原处理3h;
和铁粉分别在还原处理3h,再冷至室温,过筛即可;
b、烘干:先将石磨球磨1~3h后,再将球磨后的石磨、碳化钨、锡粉、镍粉、钼粉、二硫化钼、钨粉、钆粉、硅粉、碳酸镁和铬粉分别在150℃下进行烘干处理,保温3h后随炉冷却即可;
(2)混料:将步骤(1)中处理好的各原料在转速为30r/min的条件下,进行混料6h,即得混料;
(3)压制成型:将步骤(3)中的混料,倒入压制模具中,在500Mpa压力下,压制制得压坯;
(4)预烧结:将压坯置于烧结炉中分层堆放,每层之间用石磨盘隔开,在氨分解气体保护下,以8℃/min的升温速度从室温升到500℃;温度升至500℃后保温20min;再以5℃/min的升温速度从500℃升到850℃;接着在850℃时保温180min;保温结束后随炉冷却到60℃以下,制得毛坯;
(5)复压:将步骤(5)所得的毛坯在500MPa的压制压力下进行复压,制得复压坯;
(6)复烧结:将复压坯置于烧结炉中分层堆放,每层之间用石磨盘隔开,在氨分解气体保护下,以8℃/min的升温速度从室温升到500℃;温度升至500℃后保温20min;再以5℃/min的升温速度从500℃升到850℃;接着在850℃时保温180min;保温结束后随炉冷却到60℃以下,制得粗品;
(7)整形:将粗品经整形即制得本发明铜基受电弓滑板。
实施例2
一种轻轨车辆用铜基受电弓滑板,由以下按质量份计的原料组成:铜粉42g、铁粉18g、石墨12g、碳化钨8g、锡粉4g、镍粉3g、钼粉3g、二硫化钼3g、钨粉8g、钆粉5g、硅粉12g、碳酸镁6g、铬粉3g。
所述的轻轨车辆用铜基受电弓滑板的制备方法,包括以下步骤:
(1)预处理:
a、还原处理:在氨分解气体中,将铜粉在450℃下进行还原处理3h,将铁粉在700℃下进行还原处理3h;
和铁粉分别在还原处理3h,再冷至室温,过筛即可;
b、烘干:先将石磨球磨1~3h后,再将球磨后的石磨、碳化钨、锡粉、镍粉、钼粉、二硫化钼、钨粉、钆粉、硅粉、碳酸镁和铬粉分别在200℃下进行烘干处理,保温3h后随炉冷却即可;
(2)混料:将步骤(1)中处理好的各原料在转速为60r/min的条件下,进行混料12h,即得混料;
(3)压制成型:将步骤(3)中的混料,倒入压制模具中,在800Mpa压力下,压制制得压坯;
(4)预烧结:将压坯置于烧结炉中分层堆放,每层之间用石磨盘隔开,在氨分解气体保护下,以15℃/min的升温速度从室温升到500℃;温度升至500℃后保温30min;再以8℃/min的升温速度从500℃升到950℃;接着在950℃时保温240min;保温结束后随炉冷却到60℃以下,制得毛坯;
(5)复压:将步骤(5)所得的毛坯在800MPa的压制压力下进行复压,制得复压坯;
(6)复烧结:将复压坯置于烧结炉中分层堆放,每层之间用石磨盘隔开,在氨分解气体保护下,以15℃/min的升温速度从室温升到500℃;温度升至500℃后保温30min;再以8℃/min的升温速度从500℃升到950℃;接着在950℃时保温240min;保温结束后随炉冷却到60℃以下,制得毛坯;
(7)整形:将粗品经整形即制得本发明铜基受电弓滑板。
实施例3
一种轻轨车辆用铜基受电弓滑板,由以下按质量份计的原料组成:铜粉40g、铁粉15g、石墨9g、碳化钨5g、锡粉3g、镍粉2g、钼粉2g、二硫化钼2g、钨粉5g、钆粉3g、硅粉10g、碳酸镁5g、铬粉2g。
所述的轻轨车辆用铜基受电弓滑板的制备方法,包括以下步骤:
(1)预处理:
a、还原处理:在氨分解气体中,将铜粉在430℃下进行还原处理3h,将铁粉在650℃下进行还原处理3h;
和铁粉分别在还原处理3h,再冷至室温,过筛即可;
b、烘干:先将石磨球磨1~3h后,再将球磨后的石磨、碳化钨、锡粉、镍粉、钼粉、二硫化钼、钨粉、钆粉、硅粉、碳酸镁和铬粉分别在180℃下进行烘干处理,保温3h后随炉冷却即可;
(2)混料:将步骤(1)中处理好的各原料在转速为45r/min的条件下,进行混料10h,即得混料;
(3)压制成型:将步骤(3)中的混料,倒入压制模具中,在680Mpa压力下,压制制得压坯;
(4)预烧结:将压坯置于烧结炉中分层堆放,每层之间用石磨盘隔开,在氨分解气体保护下,以10℃/min的升温速度从室温升到500℃;温度升至500℃后保温25min;再以7℃/min的升温速度从500℃升到900℃;接着在900℃时保温200min;保温结束后随炉冷却到60℃以下,制得毛坯;
(5)复压:将步骤(5)所得的毛坯在680MPa的压制压力下进行复压,制得复压坯;
(6)复烧结:将复压坯置于烧结炉中分层堆放,每层之间用石磨盘隔开,在氨分解气体保护下,以10℃/min的升温速度从室温升到500℃;温度升至500℃后保温25min;再以7℃/min的升温速度从500℃升到900℃;接着在900℃时保温200min;保温结束后随炉冷却到60℃以下,制得毛坯;
(7)整形:将粗品经整形即制得本发明铜基受电弓滑板。
实施例4
一种轻轨车辆用铜基受电弓滑板,由以下按质量份计的原料组成:铜粉38g、铁粉18g、石墨7g、碳化钨8g、锡粉2g、镍粉3g、钼粉1g、二硫化钼3g、钨粉3g、钆粉5g、硅粉8g、碳酸镁6g、铬粉1g。
所述的轻轨车辆用铜基受电弓滑板的制备方法,包括以下步骤:
(1)预处理:
a、还原处理:在氨分解气体中,将铜粉在400℃下进行还原处理3h,将铁粉在700℃下进行还原处理3h;
和铁粉分别在还原处理3h,再冷至室温,过筛即可;
b、烘干:先将石磨球磨1~3h后,再将球磨后的石磨、碳化钨、锡粉、镍粉、钼粉、二硫化钼、钨粉、钆粉、硅粉、碳酸镁和铬粉分别在150℃下进行烘干处理,保温3h后随炉冷却即可;
(2)混料:将步骤(1)中处理好的各原料在转速为60r/min的条件下,进行混料6h,即得混料;
(3)压制成型:将步骤(3)中的混料,倒入压制模具中,在800Mpa压力下,压制制得压坯;
(4)预烧结:将压坯置于烧结炉中分层堆放,每层之间用石磨盘隔开,在氨分解气体保护下,以15℃/min的升温速度从室温升到500℃;温度升至500℃后保温20min;再以8℃/min的升温速度从500℃升到900℃;接着在900℃时保温240min;保温结束后随炉冷却到60℃以下,制得毛坯;
(5)复压:将步骤(5)所得的毛坯在800MPa的压制压力下进行复压,制得复压坯;
(6)复烧结:将复压坯置于烧结炉中分层堆放,每层之间用石磨盘隔开,在氨分解气体保护下,以8℃/min的升温速度从室温升到500℃;温度升至500℃后保温30min;再以5℃/min的升温速度从500℃升到950℃;接着在950℃时保温240min;保温结束后随炉冷却到60℃以下,制得粗品;
(7)整形:将粗品经整形即制得本发明铜基受电弓滑板。
实施例5
一种轻轨车辆用铜基受电弓滑板,由以下按质量份计的原料组成:铜粉42g、铁粉12g、石墨12g、碳化钨3g、锡粉4g、镍粉1g、钼粉3g、二硫化钼1g、钨粉8g、钆粉2g、硅粉12g、碳酸镁3g、铬粉3g。
所述的轻轨车辆用铜基受电弓滑板的制备方法,包括以下步骤:
(1)预处理:
a、还原处理:在氨分解气体中,将铜粉在450℃下进行还原处理3h,将铁粉在600℃下进行还原处理3h;
和铁粉分别在还原处理3h,再冷至室温,过筛即可;
b、烘干:先将石磨球磨1~3h后,再将球磨后的石磨、碳化钨、锡粉、镍粉、钼粉、二硫化钼、钨粉、钆粉、硅粉、碳酸镁和铬粉分别在200℃下进行烘干处理,保温3h后随炉冷却即可;
(2)混料:将步骤(1)中处理好的各原料在转速为30~60r/min的条件下,进行混料6~12h,即得混料;
(3)压制成型:将步骤(3)中的混料,倒入压制模具中,在800Mpa压力下,压制制得压坯;
(4)预烧结:将压坯置于烧结炉中分层堆放,每层之间用石磨盘隔开,在氨分解气体保护下,以15℃/min的升温速度从室温升到500℃;温度升至500℃后保温20min;再以8℃/min的升温速度从500℃升到900℃;接着在900℃时保温240min;保温结束后随炉冷却到60℃以下,制得毛坯;
(5)复压:将步骤(5)所得的毛坯在500MPa的压制压力下进行复压,制得复压坯;
(6)复烧结:将复压坯置于烧结炉中分层堆放,每层之间用石磨盘隔开,在氨分解气体保护下,以15℃/min的升温速度从室温升到500℃;温度升至500℃后保温30min;再以5℃/min的升温速度从500℃升到950℃;接着在950℃时保温220min;保温结束后随炉冷却到60℃以下,制得粗品;
(7)整形:将粗品经整形即制得本发明铜基受电弓滑板。
分别对本实施例1~5的铜基受电弓滑板的材料性能进行测定,以申请号201510952423.8《一种铜基受电弓滑板材料及其制备方法》公开的铜基受电弓滑板材料作为对照,将铜基受电弓滑板运用到某型轻轨车上,结果如表1所示:
Claims (7)
1.一种轻轨车辆用铜基受电弓滑板,其特征在于,由以下按质量份计的原料组成:铜粉38~42、铁粉12~18、石墨7~12、碳化钨3~8、锡粉2~4、镍粉1~3、钼粉1~3、二硫化钼1~3、钨粉3~8、钆粉2~5、硅粉8~12、碳酸镁3~6、铬粉1~3;
其制备方法包括以下步骤:
(1)预处理:
a、还原处理:将铜粉和铁粉分别在在氨分解气体中还原处理3h,再冷至室温,过筛;
b、烘干:将石墨、碳化钨、锡粉、镍粉、钼粉、二硫化钼、钨粉、钆粉、硅粉、碳酸镁和铬粉分别进行烘干处理,保温3h后随炉冷却;
(2)混料:将步骤(1)中处理好的各原料进行混料处理,得混料;
(3)压制成型:将步骤(3)中的混料,倒入压制模具中,在500~800Mpa压力下,压制制得压坯;
(4)预烧结:将压坯置于烧结炉中分层堆放,每层之间用石磨盘隔开,在氨分解气体保护下,以8~15℃/min的升温速度从室温升到500℃;温度升至500℃后保温20~30min;再以5~8℃/min的升温速度从500℃升到900±50℃;接着在900±50℃时保温180~240min;保温结束后随炉冷却到60℃以下,制得毛坯;
(5)复压:将步骤(5)所得的毛坯在500~800MPa的压制压力下进行复压,制得复压坯;
(6)复烧结:将复压坯置于烧结炉中分层堆放,每层之间用石磨盘隔开,在氨分解气体保护下,以8~15℃/min的升温速度从室温升到500℃;温度升至500℃后保温20~30min;再以5~8℃/min的升温速度从500℃升到900±50℃;接着在900±50℃时保温180~240min;保温结束后随炉冷却到60℃以下,制得粗品;
(7)整形:将粗品经整形制得铜基受电弓滑板。
2.如权利要求1所述的轻轨车辆用铜基受电弓滑板,其特征在于,由以下按质量份计的原料组成:铜粉40、铁粉15、石墨9、碳化钨5、锡粉3、镍粉2、钼粉2、二硫化钼2、钨粉5、钆粉3、硅粉10、碳酸镁5、铬粉2。
3.如权利要求1或2所述的轻轨车辆用铜基受电弓滑板,其特征在于,所述铜粉,纯度≥99.5%,粒度为20~75μm,树枝状;所述铁粉,纯度≥98%,粒度为20~75μm,海绵状;所述石墨,纯度≥92%,粒度为20~40μm,颗粒状;所述碳化钨,纯度≥99.5%,灰色粉剂;所述锡粉,纯度≥99.5%,粒度为20~75μm,滴状;所述镍粉,纯度≥99.5%,粒度为20~63μm,球状;所述钼粉,纯度≥99%,粒度为20~40μm,银灰色粉剂;所述二硫化钼,纯度≥97%,粒度为20~45μm,层状粉剂;所述钨粉,纯度≥99%,粒度为38~45μm,深灰色粉剂;所述钆粉,纯度≥99%,粒度为20~50μm,银白色粉剂;所述硅粉,纯度≥95%。
4.如权利要求1所述的轻轨车辆用铜基受电弓滑板的制备方法,其特征在于,石墨在烘干之前,还包括将石墨进行球磨的步骤,球磨时间是1~3h。
5.如权利要求1所述的轻轨车辆用铜基受电弓滑板的制备方法,其特征在于,铜粉的还原处理是在400~450℃下进行,铁粉的还原处理是在600~700℃下进行。
6.如权利要求1所述的轻轨车辆用铜基受电弓滑板的制备方法,其特征在于,所述的烘干,温度为150~200℃。
7.如权利要求1所述的轻轨车辆用铜基受电弓滑板的制备方法,其特征在于,所述的混料处理是将各原料在转速为30~60r/min的条件下,混合6~12h。