CN107672228A - A kind of preparation method of degradable packaging bag - Google Patents
A kind of preparation method of degradable packaging bag Download PDFInfo
- Publication number
- CN107672228A CN107672228A CN201710922651.XA CN201710922651A CN107672228A CN 107672228 A CN107672228 A CN 107672228A CN 201710922651 A CN201710922651 A CN 201710922651A CN 107672228 A CN107672228 A CN 107672228A
- Authority
- CN
- China
- Prior art keywords
- packaging bag
- parts
- degradable packaging
- bag preparation
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of degradable packaging bag, comprise the steps of:Raw material preparation, calendering technology, printing and veneer tunic, obtain finished product.Packaging bag prepared by the present invention is degradable, and preparation process is simple, environmental protection, available for product packaging.
Description
Technical field
The present invention relates to packaging bag, more particularly to a kind of preparation method of degradable packaging bag.
Background technology
Packaging bag refers to the sack for packing various articles for use, makes goods convenience in transport in the process of circulation is produced, easily
Storage.It is widely used in daily life and industrial production.Real figure shows there is the polybag after 80% use, finally with one
As rubbish be equally transported to the processing of rubbish heap field area, only 7 percent plastics are recovered recycling.
The content of the invention
Goal of the invention:The present invention provides a kind of preparation method of degradable packaging bag, and solving existing packaging bag can not
The problem of degraded.
Technical scheme:A kind of preparation method of biodegradable bag of the present invention, is comprised the steps of:(1) raw material
Prepare:After each component is stirred together for uniformly, ground repeatedly under normal temperature on three-roll grinder, into slurry viscosity 60PaS or so
It is standby;(2) calendering technology:Above-mentioned composition is overlayed into plastic layer on four-roller machine;(3) print:Carried out on intaglio press,
The surface layer film printed is attached on leather next process is counter;(4) veneer tunic:By printing dried semi-finished product compound
Pad pasting on machine, obtains finished product.
The plastic layer is in 1-1.2mm.
The four-roller linear velocity 5-10m/min.
It is 90-100 DEG C that the compounding machine combined temp, which is controlled in pre- hot-rolling, and heating roller is 150-180 DEG C.
The packaging bag mainly includes following components:By weight, 9-10 parts polyurethane, 10-20 parts starch, 1-8 parts
Crosslinking agent, 5-10 parts cosolvent and 20-25 part celluloses.
The crosslinking agent is selected from di-tert-butyl peroxide or di-isopropylbenzene hydroperoxide.
The cosolvent is selected from polysorbate60, span 80 or this disk 60.
Above-mentioned composition includes following components, by weight, 9-10 parts polyurethane, 10-15 parts starch, the crosslinking of 3-5 parts
Agent, 5-8 parts cosolvent and 23-25 part celluloses.
Further, above-mentioned composition includes following components:By weight, 10 parts of polyurethane, 13 parts of starch, 4 parts of friendships
Join agent, 6 parts of cosolvents and 24 parts of celluloses.
Beneficial effect:Packaging bag prepared by the present invention is degradable, and preparation process is simple, environmental protection, can large-scale industrialization
Production.
Embodiment
First, sample preparation
Embodiment 1:By weight, 9 parts of polyurethane, 10 parts of starch, 1 part of crosslinking agent di-tert-butyl peroxide, 5 parts help
Solvent span 80 and 20 parts of cellulose mixing, after each component is stirred together for uniformly, grind repeatedly on three-roll grinder under normal temperature
Mill, it is standby into slurry viscosity 60PaS or so;Calendering technology:Above-mentioned composition is overlayed into plastic layer, four-roller linear speed on four-roller machine
10m/min is spent, it is in 1mm to make plastic layer;Printing:Carried out on intaglio press, the surface layer film printed is at lower one
Process is counter to be attached on leather;Veneer tunic:By printing dried semi-finished product pad pasting on compounding machine, compounding machine combined temp control
System is 90 DEG C in pre- hot-rolling, and heating roller is 150 DEG C.Obtain finished product.
Embodiment 2:10 parts of polyurethane, 20 parts of starch, 8 parts of crosslinking agent di-isopropylbenzene hydroperoxides, 10 parts of cosolvent this disks
60 and 25 parts of cellulose mixing, remaining is the same as embodiment 1.
Embodiment 3:9 parts of polyurethane, 10 parts of starch, 3 parts of crosslinking agent di-tert-butyl peroxides, 5 parts of cosolvent polysorbate60s
With 23 parts of celluloses.
Embodiment 4:10 parts of polyurethane, 15 parts of starch, 5 parts of crosslinking agent di-isopropylbenzene hydroperoxides, 8 parts of cosolvent span 80s
With 25 parts of celluloses.
Embodiment 5:10 parts of polyurethane, 13 parts of starch, 4 parts of crosslinking agent di-tert-butyl peroxides, 6 parts of cosolvent polysorbate60s
With 24 parts of celluloses.
2nd, detection method
1st, degraded solutions:1.5mol/L hydrochloric acid is molten
2nd, biodegrading process refers to CIPAC MT 176《The rate of dissolution of water-soluble bag》
3rd, testing result
Sample prepared by embodiment 1-5, point three groups of parallel tests, measurement result is shown in Table 1, it can be seen from the result of table 1
Packaging bag prepared by the present invention can degrade under strongly acidic conditions, and packaging bag can focus on, and will not cause environmental pollution.
The sample degradation speed of table 1
Claims (7)
1. a kind of degradable packaging bag preparation method, is comprised the steps of:
(1) raw material prepare:After each component is stirred together for uniformly, ground repeatedly under normal temperature on three-roll grinder, it is viscous into slurry
It is standby to spend 60PaS or so;
(2) calendering technology:Above-mentioned composition is overlayed into plastic layer on four-roller machine;
(3) print:Carried out on intaglio press, the surface layer film printed is attached on leather next process is counter;(4) overlay coating
Film:By printing dried semi-finished product pad pasting on compounding machine, finished product is obtained.
2. degradable packaging bag preparation method according to claim 1, it is characterised in that in step (2), the plastics
Thickness degree is in 1-1.2mm.
3. degradable packaging bag preparation method according to claim 1, it is characterised in that in step (2), the four-roller
Linear velocity is 5-10m/min.
4. degradable packaging bag preparation method according to claim 1, it is characterised in that described compound in step (4)
It is 90-100 DEG C that machine combined temp, which is controlled in pre- hot-rolling, and heating roller is 150-180 DEG C.
5. degradable packaging bag preparation method according to claim 1, it is characterised in that the component is that 9-10 parts are gathered
Urethane, 10-20 parts starch, 1-8 parts crosslinking agent, 5-10 parts cosolvent and 20-25 part celluloses.
6. degradable packaging bag preparation method according to claim 5, it is characterised in that the crosslinking agent is selected from two uncles
Butylperoxide or di-isopropylbenzene hydroperoxide.
7. degradable packaging bag preparation method according to claim 5, it is characterised in that the cosolvent is selected from tween
60th, span 80 or this disk 60.