CN107841184A - A kind of scratch resistance hardening agent for powdery paints - Google Patents
A kind of scratch resistance hardening agent for powdery paints Download PDFInfo
- Publication number
- CN107841184A CN107841184A CN201711041828.1A CN201711041828A CN107841184A CN 107841184 A CN107841184 A CN 107841184A CN 201711041828 A CN201711041828 A CN 201711041828A CN 107841184 A CN107841184 A CN 107841184A
- Authority
- CN
- China
- Prior art keywords
- powdery paints
- scratch resistance
- hardening agent
- resistance hardening
- graphene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to improve powdery paints wearability technical field, and in particular to a kind of scratch resistance hardening agent for powdery paints, include the preparation of graphene processing material, then obtained with Tissuemat E, vanadium diboride, graphene processing material mixing and ball milling.The present invention has advantages below compared with prior art:Scratch resistance hardening agent preparation method is simple in the present invention, condition is easily controlled, less addition can increase the surface slip of powdery paints, mitigate frictional force, and then play scratch resistant effect, powder coating product hardness can be improved to 20 25%, while excessively the situation of lustrous surface decline will not occur because of the addition of scratch resistance hardening agent, ensure the product quality of powdery paints.
Description
Technical field
The invention belongs to improve powdery paints wearability technical field, and in particular to a kind of scratch resistance for powdery paints
Hardening agent.
Background technology
For powdery paints because it is free of organic solvent, the feature of environmental protection is good, storage, convenient transportation the advantages that be widely used in each neck
Domain, in some special occasions, higher requirement is proposed to the wearability of powdery paints, but be limited to plexiglas temperature and
Limited without solvent operation viscosity, prior art does not have the powdery paints supply market of high-wear resistance also, and prior art passes through
Film thickness is reduced to improve coating abrasion performance, while the protecting function and appearance requirement of coating can be reduced, is led in the prior art
Cross and high-hardness inorganic compound is added in resin body material to improve wearability, but in preparation process, abrasion-proof particle is same
Sample can scratch equipment in process, cause equipment consumption rate high, and equipment is more easily damaged, and causes production cost higher, should
With greatly being limited, therefore, it is necessary to the wearability of powdery paints is improved by other means, and can meets powder coating
Protective value and appearance design requirement.
The content of the invention
The purpose of the present invention is to be directed to the problem of existing, there is provided a kind of scratch resistance hardening agent for powdery paints.
The present invention is achieved by the following technical solutions:A kind of scratch resistance hardening agent for powdery paints, it is a kind of
Tissuemat E modified materials, its preparation method comprise the following steps:
(1)In magnetic field intensity it is 600-800Gs by graphene, while the ultrasonic disperse 1-2 hours under ultrasound condition, obtain graphite
Alkene processing material is standby;
(2)It will add in sealable ball mill after Tissuemat E, vanadium diboride, graphene processing material mixing, lead to after vacuumizing
Enter temperature for 75-85 DEG C, the ball milling 4-6 hours under conditions of quality of the ball mill ratio is 6-8, rotating speed is 200-400 revs/min, i.e.,
.
As further improvement of these options, the graphene is that 5-8 layers are periodically tight with benzene ring structure by the number of plies
Closely packed carbon atom is formed with different way of stacking stackings.
As further improvement of these options, the step(1)Middle ultrasound condition is that ultrasonic frequency is 86-96W.
As further improvement of these options, usage amount of the scratch resistance hardening agent in powdery paints is total for its
The 1.2-1.8% of weight.
As further improvement of these options, the application method of the scratch resistance hardening agent is directly and powdery paints
The mixing of other raw materials, common extrusion after melting.
The present invention has advantages below compared with prior art:Scratch resistance hardening agent preparation method is simple in the present invention, condition
It is easily controlled, less addition can increase the surface slip of powdery paints, mitigate frictional force, and then play scratch resistant
Powder coating product hardness, can be obviously improved by effect, while will not excessively occur because of the addition of scratch resistance hardening agent
The situation that lustrous surface declines, ensure the product quality of powdery paints.
Embodiment
Embodiment 1
A kind of scratch resistance hardening agent for powdery paints, is a kind of Tissuemat E modified materials, and its preparation method includes following step
Suddenly:
(1)In magnetic field intensity it is 700Gs by graphene, while ultrasonic disperse 1.5 hours under ultrasound condition, obtain at graphene
Reason material is standby;
(2)It will add in sealable ball mill after Tissuemat E, vanadium diboride, graphene processing material mixing, lead to after vacuumizing
Enter temperature for 80 DEG C, ball milling 5 hours, is produced under conditions of quality of the ball mill ratio is 7, rotating speed is 300 revs/min.
Wherein, the graphene by the number of plies be 5-8 layers with benzene ring structure periodically closelypacked carbon atom with different heaps
Pile mode stacking is formed;The step(1)Middle ultrasound condition is that ultrasonic frequency is 91W;The scratch resistance hardening agent is in powder
Usage amount in coating is the 1.5% of its gross weight;The application method of the scratch resistance hardening agent for directly with powdery paints its
He mixes raw material, common extrusion after melting.
Embodiment 2
A kind of scratch resistance hardening agent for powdery paints, is a kind of Tissuemat E modified materials, and its preparation method includes following step
Suddenly:
(1)In magnetic field intensity it is 600Gs by graphene, while ultrasonic disperse 2 hours under ultrasound condition, obtain graphene processing
Expect standby;
(2)It will add in sealable ball mill after Tissuemat E, vanadium diboride, graphene processing material mixing, lead to after vacuumizing
Enter temperature for 75 DEG C, ball milling 6 hours, is produced under conditions of quality of the ball mill ratio is 6, rotating speed is 400 revs/min.
Wherein, the graphene by the number of plies be 5-8 layers with benzene ring structure periodically closelypacked carbon atom with different heaps
Pile mode stacking is formed;The step(1)Middle ultrasound condition is that ultrasonic frequency is 96W;The scratch resistance hardening agent is in powder
Usage amount in coating is the 1.2% of its gross weight;The application method of the scratch resistance hardening agent for directly with powdery paints its
He mixes raw material, common extrusion after melting.
Embodiment 3
A kind of scratch resistance hardening agent for powdery paints, is a kind of Tissuemat E modified materials, and its preparation method includes following step
Suddenly:
(1)In magnetic field intensity it is 800Gs by graphene, while ultrasonic disperse 1 hour under ultrasound condition, obtain graphene processing
Expect standby;
(2)It will add in sealable ball mill after Tissuemat E, vanadium diboride, graphene processing material mixing, lead to after vacuumizing
Enter temperature for 85 DEG C, ball milling 4 hours, is produced under conditions of quality of the ball mill ratio is 8, rotating speed is 200 revs/min.
Wherein, the graphene by the number of plies be 5-8 layers with benzene ring structure periodically closelypacked carbon atom with different heaps
Pile mode stacking is formed;The step(1)Middle ultrasound condition is that ultrasonic frequency is 86W;The scratch resistance hardening agent is in powder
Usage amount in coating is the 1.8% of its gross weight;The application method of the scratch resistance hardening agent for directly with powdery paints its
He mixes raw material, common extrusion after melting.
Control group 1 is set, by step in embodiment 1(1)Remove, i.e., directly add graphene, remaining content and embodiment 1
In it is identical;Control group 2 is set, vanadium diboride in embodiment 1 removed, remaining content is constant;Control group 3 is set, by embodiment 1
Middle graphene processing material removes, and remaining content is constant;Blank group is not add hardening agent;
Wherein powdery paints is mixed by 50 parts of polyester, 10 parts of talcum powder, 10 parts of pigment, 4 parts of curing agent by weight, respectively
Detection performance after addition above each group scratch resistance hardening agent, obtains following result:
Tensile strength performance testing standard is GB/T1040.2-2006;
Bending property testing standard is GB/T9341-2008;
Impact property testing standard is GB/T1843-2008;
Surface pencil hardness test standard is GB/T6739-1996;
Table 1
Group | Tensile strength(MPa) | Bending strength(MPa) | Impact strength(KJ/㎡) | Surface pencil hardness(1Kg) |
Embodiment 1 | 69.2 | 90.5 | 43.2 | 3H |
Embodiment 2 | 68.8 | 89.4 | 43.5 | 3H |
Embodiment 3 | 68.7 | 89.7 | 43.4 | 3H |
Control group 1 | 57.4 | 82.5 | 52.8 | 3H |
Control group 2 | 62.8 | 85.3 | 49.2 | 2H |
Control group 3 | 63.7 | 85.6 | 48.5 | 3H |
Blank group | 52.8 | 80.4 | 58.2 | 1H |
Can be seen that by data in table 1 can strengthen the hardness of powder-coating in the present invention, while strengthen its mechanical property, resistance to
Scuffing ability is stronger, can effectively avoid scratching equipment in process of production.
Claims (5)
- A kind of 1. scratch resistance hardening agent for powdery paints, it is characterised in that it is a kind of Tissuemat E modified materials, its preparation side Method comprises the following steps:(1)In magnetic field intensity it is 600-800Gs by graphene, while the ultrasonic disperse 1-2 hours under ultrasound condition, obtain graphite Alkene processing material is standby;(2)It will add in sealable ball mill after Tissuemat E, vanadium diboride, graphene processing material mixing, lead to after vacuumizing Enter temperature for 75-85 DEG C, the ball milling 4-6 hours under conditions of quality of the ball mill ratio is 6-8, rotating speed is 200-400 revs/min, i.e., .
- 2. a kind of scratch resistance hardening agent for powdery paints as claimed in claim 1, it is characterised in that the graphene is by layer Number is formed for 5-8 layers with the periodically closelypacked carbon atom of benzene ring structure with different way of stacking stackings.
- A kind of 3. scratch resistance hardening agent for powdery paints as claimed in claim 1, it is characterised in that the step(1)In Ultrasound condition is that ultrasonic frequency is 86-96W.
- A kind of 4. scratch resistance hardening agent for powdery paints as claimed in claim 1, it is characterised in that the scratch resistance hardening Usage amount of the agent in powdery paints is the 1.2-1.8% of its gross weight.
- A kind of 5. scratch resistance hardening agent for powdery paints as claimed in claim 1, it is characterised in that the scratch resistance hardening The application method of agent is directly mixes with other raw materials of powdery paints, common extrusion after melting.