CN104403529A - High-performance anti-cracking unsaturated polyester white primer for woodware - Google Patents
High-performance anti-cracking unsaturated polyester white primer for woodware Download PDFInfo
- Publication number
- CN104403529A CN104403529A CN201410826134.9A CN201410826134A CN104403529A CN 104403529 A CN104403529 A CN 104403529A CN 201410826134 A CN201410826134 A CN 201410826134A CN 104403529 A CN104403529 A CN 104403529A
- Authority
- CN
- China
- Prior art keywords
- selects
- parts
- unsaturated polyester
- mineral filler
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-solid-content high-fullness environment-friendly varnish white finish paint for woodware, which is prepared from the following raw materials in parts by weight: 30-45 parts of unsaturated polyester resin A, 5-8 parts of unsaturated polyester resin B, 1.5-5 parts of toughener A, 3-6 parts of toughener B, 0.5-1 part of dispersing agent, 0.1-0.5 part of defoaming agent, 0.2-0.5 part of leveling agent, 0.3-0.5 part of antisettling assistant A, 0.5-1 part of antisettling assistant B, 0.01-0.1 part of polymerization inhibitor, 2-3 parts of sanding assistant, 5-10 parts of titanium white, 5-6 parts of inorganic filler A, 10-18 parts of inorganic filler B, 6-10 parts of inorganic filler C, 8-15 parts of inorganic filler D and 3-6 parts of solvent. The novel toughener and reactive toughener are compounded to perform synergic toughening, the anti-sagging agent is compounded to reduce the thickness of the oil accumulation layer, and different types of pigments and fillers with different particle sizes and different hardnesses are matched to enhance the compactness and cohesive force of the coated film.
Description
Technical field
The invention belongs to paint field, be specifically related to a kind of woodenware high-performance crack resistence unsaturated polyester based white primer.
Background technology
All the time, on furniture market, unsaturated polyester based white primer with its large arch dam and excellence fillibility in occupation of many market shares, due to construction wrong, disposable thick painting in woodwork coating process, or employ non-supporting solvent or diluent, amass the place that oil is thicker at some groove place or carving place, easily there is the risk of the cracking of certain probability, even if the product that resin content is relatively high is also difficult to escape by luck, causes and do over again, affect production efficiency.And very easily produce relevant dispute in Furniture Factory to Paint Factory.Trace it to its cause, being mainly unsaturated polyester varnish is cross-linking reaction type coating, and cross-linking density is large, and fragility is strong, and the stress that thick painting itself produces accumulation is comparatively large, and in addition, due to market competition, solvent or diluent does not often use auxiliary products, increases the risk of cracking.Research and develop a construction tolerance good, high-performance resists the unsaturated polyester based white primer of thick painting cracking imperative.
Summary of the invention
The object of the invention is to provide a kind of woodenware high-performance crack resistence unsaturated polyester based white primer, solves unsaturated polyester based white primer common on the market and constructs in carving or groove place due to construction wrong once thick painting or use non-supporting solvent or diluent easily to produce the problem of the risk of cracking.
Technical scheme of the present invention is: the high plentiful environment-friendly luminous white finish paint of a kind of woodenware large arch dam, and its raw material weight consists of,
Unsaturated polyester resin A:30 ~ 45 part
Unsaturated polyester resin B:5 ~ 8 part
Toughner A:1.5 ~ 5 part
Toughner B:3 ~ 6 part
Dispersion agent: 0.5 ~ 1 part
Defoamer: 0.1 ~ 0.5 part
Flow agent: 0.2 ~ 0.5 part
Anti-settling auxiliary agent A: 0.3 ~ 0.5 part
Anti-settling auxiliary agent B: 0.5 ~ 1 part
Stopper: 0.01 ~ 0.1 part
Grinding auxiliary agent: 2 ~ 3 parts
Titanium dioxide: 5 ~ 10 parts
Mineral filler A:5 ~ 6 part
Mineral filler B:10 ~ 18 part
Mineral filler C:6 ~ 10 part
Mineral filler D:8 ~ 15 part
Solvent: 3 ~ 6 parts.
Further, described unsaturated polyester resin A is air drying type dicyclic pentylene modified unsaturated polyester resin, is preferably the 3308A of the sub-nation in Changzhou.
Further, described unsaturated polyester resin B is air drying type allyl ethers modified unsaturated polyester resin, is preferably state and refines learn 8734.
Further, described toughner A is novel non-reactive toughner, is preferably the GF-MV10 of Guang Fu synthetic materials factory of Suzhou City.
Further, described toughner B is response type toughner, is preferably the maleic anhydride grafted polyethylene of Guangzhou Hao Su Chemical Co., Ltd..
Further, described dispersion agent is the high molecular silane copolymer containing close pigment group, is preferably Tag polymkeric substance TECH6300.
Further, described defoamer is acryl-based antifoaming agent, is preferably 052 of BYK chemistry.
Further, described flow agent is modification acrylic acid class flow agent, is preferably the LP-5800 of Guangzhou Heng Yu trade Co., Ltd.
Further, described anti-settling sag prevention auxiliary agent A is aerosil, is preferably watt N-20 digesting.
Further, described anti-settling auxiliary agent B is organic bentonite, is preferably this SD-1 of hamming.
Further, described stopper is Resorcinol.
Further, described grinding auxiliary agent is Zinc Stearate.
Further, described titanium dioxide is rutile titanium-type titanium dioxide, preferably climbs the R-229 of steel.
Further, described mineral filler A is 2000 order silicon powders, is preferably 2000 order silicon powders of the rich Mining Limited Company of Wuzhou grain husk.
Further, described mineral filler B is 1250 order talcum powder, is preferably wide sweet osmanthus board 1250 talcum powder of Guangxi dragon.
Further, described mineral filler C is 800 order talcum powder, is preferably wide sweet osmanthus board 800 talcum powder of Guangxi dragon.
Further, described mineral filler D is 2000 order coarse whitings, is preferably Zhongshan County, Guangxi Yi Feng powder company limited 2000 order coarse whiting.
Further, described solvent is vinylbenzene.
The present invention compared with prior art tool has the following advantages:
The present invention considers the reason of market orientation and cost performance, adopt new type of toughening agent and the toughness reinforcing composite coordination plasticizing of response type, sag prevention additive compound reduces long-pending core intersection, and passes through the color stuffing of collocation different sorts, different-grain diameter, different hardness, increases compactness and the force of cohesion of film.By a large amount of experiments, determine optimum proportion.Obtained unsaturated polyester based white primer construction tolerance is high, and thick painting cracking resistance effect is fine.
Unsaturated polyester based white primer of the present invention, compared with unsaturated polyester based white primer common on market plane, solves the thick risk being applied to groove or carving cracking, good to the non-supporting solvent or diluent tolerance on market.
Embodiment
In following embodiment, unsaturated polyester A selects the 3308A of the sub-nation in Changzhou, unsaturated polyester B selects state to refine learn 8734, toughner A selects the GF-MV10 of Guang Fu synthetic materials factory of Suzhou City, toughner B selects the maleic anhydride grafted polyethylene of Guangzhou Hao Su Chemical Co., Ltd., dispersion agent selects Tag polymkeric substance TECH6300, defoamer selects 052 of BYK chemistry, flow agent selects the LP-5800 of Guangzhou Heng Yu trade Co., Ltd, anti-settling agent A selects watt N-20 digesting, anti-settling agent B selects this SD-1 of hamming, the Resorcinol of Tianjin great Mao chemical reagent factory selected by stopper, the BT-1819 that grinding auxiliary agent selects hundred profits to close, titanium dioxide selects the R-229 climbing steel, mineral filler A selects 2000 order silicon powders of the rich Mining Limited Company of Wuzhou grain husk, mineral filler B selects wide sweet osmanthus board 1250 talcum powder of Guangxi dragon, mineral filler C selects wide sweet osmanthus board 800 talcum powder of Guangxi dragon, mineral filler D selects Zhongshan County, Guangxi Yi Feng powder company limited 2000 order coarse whiting, the vinylbenzene of Chengdu Wan Ming Chemical Co., Ltd. selected by solvent.
Embodiment 1 dumb light fine flour cracking resistant type unsaturated polyester priming paint
Unsaturated polyester resin A:30 part
Unsaturated polyester resin B:5 part
Toughner A:3.5 part
Toughner B:3 part
Dispersion agent: 0.8 part
Defoamer: 0.5 part
Flow agent: 0.4 part
Anti-settling auxiliary agent A: 0.5 part
Anti-settling auxiliary agent B: 0.7 part
Stopper: 0.03 part
Grinding auxiliary agent: 2 parts
Titanium dioxide 6 parts
Mineral filler A:5 part
Mineral filler B:15 part
Mineral filler C:9 part
Mineral filler D:15 part
Solvent 3.57 parts.
Making processes: resin, toughner, dispersion agent, flow agent, defoamer and partial solvent are added → high-speed stirring 10 minutes to evenly → add anti-settling auxiliary agent → high-speed stirring successively 5 minutes → add successively titanium dioxide, mineral filler and grinding auxiliary agent → high speed dispersion 15 minutes to fineness≤55 micron → to add residual solvent moderate-speed mixer even
The white paint outward appearance of gained is: white viscous liquid, surface drying time≤60 minute of paint film after normal spraying application; Do solid work time 24h for 25 DEG C, hardness >=H; Sticking power: one-level.Surface good leveling property.Coated matte fine flour, ply adhesion is 0 grade
Spray 8 rifles there being the plate of groove (degree of depth is about 8mm circular groove) and do limit test, observation overnight, without cracking phenomena in groove, cold cycling (-20 DEG C ~ 50 DEG C) five, plate face is without exception, does not occur coming off, cracking phenomena.
Embodiment 2 light fine flour unsaturated polyester based white primer
Unsaturated polyester resin A:40 part
Unsaturated polyester resin B:5 part
Toughner A:1.5 part
Toughner B:4 part
Dispersion agent: 0.6 part
Defoamer: 0.3 part
Flow agent: 0.3 part
Anti-settling auxiliary agent A: 0.3 part
Anti-settling auxiliary agent B: 0.5 part
Stopper: 0.01 part
Grinding auxiliary agent: 2.5 parts
Titanium dioxide 8 parts
Mineral filler A:6 part
Mineral filler B:10 part
Mineral filler C:6 part
Mineral filler D:10 part
Strong solvent 5 parts.
Making processes: resin ester, toughner, dispersion agent, flow agent, defoamer and partial solvent are added → high-speed stirring 10 minutes to evenly → add anti-settling auxiliary agent → high-speed stirring successively 5 minutes → add successively titanium dioxide, mineral filler and grinding auxiliary agent → high speed dispersion 15 minutes to fineness≤55 micron → to add residual solvent moderate-speed mixer even
The white paint outward appearance of gained is: white viscous liquid, surface drying time≤60 minute of paint film after normal spraying application; Do solid work time 24h for 25 DEG C, hardness >=H; Sticking power: one-level.Surface spraying Brilliant white paint, surface effect is good, without wrinkling.Ply adhesion is 0 grade
Spray 8 rifles there being the plate of groove (degree of depth is about 8mm circular groove) and do limit test, observation overnight, without cracking phenomena in groove, cold cycling (-20 DEG C ~ 50 DEG C) five, plate face is without exception, does not occur coming off, cracking phenomena.
The above embodiment only have expressed the embodiment of the application, and it describes comparatively concrete and detailed, but therefore can not be interpreted as the restriction to the application's protection domain.It should be pointed out that for the person of ordinary skill of the art, under the prerequisite not departing from technical scheme design, can also make some distortion and improvement, these all belong to the protection domain of the application.
Claims (4)
1. the high plentiful environment-friendly luminous white finish paint of woodenware large arch dam, it is characterized in that, its raw material weight consists of,
Unsaturated polyester resin A:30 ~ 45 part
Unsaturated polyester resin B:5 ~ 8 part
Toughner A:1.5 ~ 5 part
Toughner B:3 ~ 6 part
Dispersion agent: 0.5 ~ 1 part
Defoamer: 0.1 ~ 0.5 part
Flow agent: 0.2 ~ 0.5 part
Anti-settling auxiliary agent A: 0.3 ~ 0.5 part
Anti-settling auxiliary agent B: 0.5 ~ 1 part
Stopper: 0.01 ~ 0.1 part
Grinding auxiliary agent: 2 ~ 3 parts
Titanium dioxide: 5 ~ 10 parts
Mineral filler A:5 ~ 6 part
Mineral filler B:10 ~ 18 part
Mineral filler C:6 ~ 10 part
Mineral filler D:8 ~ 15 part
Solvent: 3 ~ 6 parts.
2. the high plentiful environment-friendly luminous white finish paint of a kind of woodenware large arch dam according to claim 1, it is characterized in that, described unsaturated polyester resin A is air drying type dicyclic pentylene modified unsaturated polyester resin, described unsaturated polyester resin B is air drying type allyl ethers modified unsaturated polyester resin, described toughner A is novel non-reactive toughner, described toughner B is response type toughner, described dispersion agent is the high molecular silane copolymer containing close pigment group, described defoamer is acryl-based antifoaming agent, described flow agent is modification acrylic acid class flow agent, described anti-settling sag prevention auxiliary agent A is aerosil, described anti-settling auxiliary agent B is organic bentonite, described stopper is Resorcinol, described grinding auxiliary agent is Zinc Stearate, described titanium dioxide is rutile titanium-type titanium dioxide, described mineral filler A is 2000 order silicon powders, described mineral filler B is 1250 order talcum powder, described mineral filler C is 800 order talcum powder, described mineral filler D is 2000 order coarse whitings, described solvent is vinylbenzene.
3. the high plentiful environment-friendly luminous white finish paint of a kind of woodenware large arch dam according to claim 1 and 2, it is characterized in that, unsaturated polyester A selects the 3308A of the sub-nation in Changzhou, unsaturated polyester B selects state to refine learn 8734, toughner A selects the GF-MV10 of Guang Fu synthetic materials factory of Suzhou City, toughner B selects the maleic anhydride grafted polyethylene of Guangzhou Hao Su Chemical Co., Ltd., dispersion agent selects Tag polymkeric substance TECH6300, defoamer selects 052 of BYK chemistry, flow agent selects the LP-5800 of Guangzhou Heng Yu trade Co., Ltd, anti-settling agent A selects watt N-20 digesting, anti-settling agent B selects this SD-1 of hamming, titanium dioxide selects the R-229 climbing steel.
4. the high plentiful environment-friendly luminous white finish paint of a kind of woodenware large arch dam according to claim 3, it is characterized in that, the Resorcinol of Tianjin great Mao chemical reagent factory selected by stopper, the BT-1819 that grinding auxiliary agent selects hundred profits to close, mineral filler A selects 2000 order silicon powders of the rich Mining Limited Company of Wuzhou grain husk, mineral filler B selects wide sweet osmanthus board 1250 talcum powder of Guangxi dragon, mineral filler C selects wide sweet osmanthus board 800 talcum powder of Guangxi dragon, mineral filler D selects Zhongshan County, Guangxi Yi Feng powder company limited 2000 order coarse whiting, the vinylbenzene of Chengdu Wan Ming Chemical Co., Ltd. selected by solvent.