CN107641363A - A kind of crack resistance poster paint and preparation method thereof - Google Patents
A kind of crack resistance poster paint and preparation method thereof Download PDFInfo
- Publication number
- CN107641363A CN107641363A CN201710929142.XA CN201710929142A CN107641363A CN 107641363 A CN107641363 A CN 107641363A CN 201710929142 A CN201710929142 A CN 201710929142A CN 107641363 A CN107641363 A CN 107641363A
- Authority
- CN
- China
- Prior art keywords
- parts
- crack resistance
- poster paint
- xanthans
- dimethicone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of crack resistance poster paint and preparation method thereof, the crack resistance poster paint is made up of the raw material components of following parts by weight：10 18 parts of xanthans, 10 20 parts of peach gum, 16 23 parts of titanium dioxide, 6 11 parts of citric acid, 5 12 parts of glycerine, 48 parts of ethylene glycol, 8 15 parts of clay, 10 20 parts of kaolin, 5 10 parts of white carbon, 13 parts of propylparaben, 15 parts of benzoic acid, 0.5 1.2 parts of dimethicone, 0.6 1.5 parts of Bronopol, 0.8 1.6 parts of TTA, 0.3 0.8 parts of dispersant, 13 parts of castor oil, 13 parts of benzoyl peroxide, 25 35 parts of water.Crack resistance poster paint in the present invention has the advantages that crack resistance is good, glossiness is full and rheological characteristic is good.
Description
Technical field
The invention belongs to pigment technology field, more particularly to a kind of crack resistance poster paint and preparation method thereof.
Background technology
Poster paint is mainly used in drawing advertising design, artistic design and environment arrangement, and it is by gummy silty aqueous pigment
Develop, with the fast development of advertising, the usage amount of poster paint is increasing, requirement more and more higher.However,
At present, the advertisement paint crack resistance of in the market is poor, and glossiness and rheological characteristic are also difficult to meet to require.
The content of the invention
It is an object of the invention to provide a kind of crack resistance poster paint and preparation method thereof, the crack resistance poster paint tool
Have the advantages that crack resistance is good, glossiness is full and rheological characteristic is good.
To achieve the above object, the present invention provides following technical scheme：
A kind of crack resistance poster paint is made up of the raw material components of following parts by weight：Xanthans 10-18 parts, peach gum 10-
20 parts, titanium dioxide 16-23 parts, citric acid 6-11 parts, glycerine 5-12 parts, ethylene glycol 4-8 parts, clay 8-15 parts, kaolin 10-20
Part, white carbon 5-10 parts, propylparaben 1-3 parts, benzoic acid 1-5 parts, dimethicone 0.5-1.2 parts, Bu Luobo
That 0.6-1.5 parts, TTA 0.8-1.6 parts, dispersant 0.3-0.8 parts, castor oil 1-3 parts, benzoyl peroxide
1-3 parts, water 25-35 parts.
Preferably, described crack resistance poster paint is made up of the raw material components of following parts by weight：16 parts of xanthans, peach
12 parts of glue, 20 parts of titanium dioxide, 8 parts of citric acid, 8 parts of glycerine, 5 parts of ethylene glycol, 12 parts of clay, 15 parts of kaolin, 8 parts of white carbon,
2 parts of propylparaben, 2 parts of benzoic acid, 0.8 part of dimethicone, 1 part of Bronopol, TTA 1.2
Part, 0.3 part of dispersant, 1 part of castor oil, 1.5 parts of benzoyl peroxide, 30 parts of water.
Preferably, described crack resistance poster paint is made up of the raw material components of following parts by weight：14 parts of xanthans, peach
20 parts of glue, 18 parts of titanium dioxide, 9 parts of citric acid, 7 parts of glycerine, 6 parts of ethylene glycol, 10 parts of clay, 16 parts of kaolin, 6 parts of white carbon,
3 parts of propylparaben, 2 parts of benzoic acid, 0.8 part of dimethicone, 1.2 parts of Bronopol, TTA 1.5
Part, 0.5 part of dispersant, 2 parts of castor oil, 3 parts of benzoyl peroxide, 32 parts of water.
The preparation method of described crack resistance poster paint, it comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) by xanthans, peach gum, titanium dioxide, citric acid, glycerine, ethylene glycol, clay, kaolin, white carbon, to hydroxyl
Propyl benzoate, benzoic acid, dimethicone, Bronopol, TTA, dispersant, castor oil, benzoyl peroxide first
Acyl and water are put into sealing container, are well mixed；
(3) temperature in sealing container is heated to 105 DEG C -115 DEG C, protected under the pressurized state of 1.5-1.8 atmospheric pressure
Warm 6-8 hours, natural cooling obtain the crack resistance poster paint of the present invention.
Compared with prior art, the beneficial effects of the invention are as follows：
The present invention adds titanium dioxide, citric acid, P-hydroxybenzoic acid third using xanthans and peach gum as primary raw material
The auxiliary materials such as ester, benzoic acid, dimethicone and TTA, make it have with crack resistance is good, glossiness is full, system
Make the advantages that technique is simple and rheological characteristic is good.
Embodiment
Technical scheme is described in detail with reference to embodiment, but protection domain is not limited thereto.
Embodiment one：
A kind of crack resistance poster paint is made up of the raw material components of following parts by weight：13 parts of xanthans, 18 parts of peach gum, titanium
21 parts of white powder, 8 parts of citric acid, 9 parts of glycerine, 7 parts of ethylene glycol, 12 parts of clay, 15 parts of kaolin, 8 parts of white carbon, para hydroxybenzene first
2 parts of propyl propionate, 3 parts of benzoic acid, 1.2 parts of dimethicone, 1.3 parts of Bronopol, 1.4 parts of TTA, dispersant
1.7 parts, 3 parts of castor oil, 2 parts of benzoyl peroxide, 35 parts of water.
The preparation method of described crack resistance poster paint, it comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) by xanthans, peach gum, titanium dioxide, citric acid, glycerine, ethylene glycol, clay, kaolin, white carbon, to hydroxyl
Propyl benzoate, benzoic acid, dimethicone, Bronopol, TTA, dispersant, castor oil, benzoyl peroxide first
Acyl and water are put into sealing container, are well mixed；
(3) temperature in sealing container is heated to 105 DEG C -115 DEG C, protected under the pressurized state of 1.5-1.8 atmospheric pressure
Warm 6-8 hours, natural cooling obtain the crack resistance poster paint of the present invention.
Embodiment two：
A kind of crack resistance poster paint is made up of the raw material components of following parts by weight：18 parts of xanthans, 16 parts of peach gum, titanium
21 parts of white powder, 11 parts of citric acid, 10 parts of glycerine, 6 parts of ethylene glycol, 15 parts of clay, 11 parts of kaolin, 6 parts of white carbon, para hydroxybenzene
1 part of propyl formate, 1 part of benzoic acid, 0.8 part of dimethicone, 1.2 parts of Bronopol, 1.5 parts of TTA, disperse
1.6 parts of agent, 2 parts of castor oil, 3 parts of benzoyl peroxide, 28 parts of water.
The preparation method of described crack resistance poster paint, it comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) by xanthans, peach gum, titanium dioxide, citric acid, glycerine, ethylene glycol, clay, kaolin, white carbon, to hydroxyl
Propyl benzoate, benzoic acid, dimethicone, Bronopol, TTA, dispersant, castor oil, benzoyl peroxide first
Acyl and water are put into sealing container, are well mixed；
(3) temperature in sealing container is heated to 105 DEG C -115 DEG C, protected under the pressurized state of 1.5-1.8 atmospheric pressure
Warm 6-8 hours, natural cooling obtain the crack resistance poster paint of the present invention.
Embodiment three：
A kind of crack resistance poster paint is made up of the raw material components of following parts by weight：16 parts of xanthans, 12 parts of peach gum, titanium
20 parts of white powder, 8 parts of citric acid, 8 parts of glycerine, 5 parts of ethylene glycol, 12 parts of clay, 15 parts of kaolin, 8 parts of white carbon, para hydroxybenzene first
2 parts of propyl propionate, 2 parts of benzoic acid, 0.8 part of dimethicone, 1 part of Bronopol, 1.2 parts of TTA, dispersant 0.3
Part, 1 part of castor oil, 1.5 parts of benzoyl peroxide, 30 parts of water.
The preparation method of described crack resistance poster paint, it comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) by xanthans, peach gum, titanium dioxide, citric acid, glycerine, ethylene glycol, clay, kaolin, white carbon, to hydroxyl
Propyl benzoate, benzoic acid, dimethicone, Bronopol, TTA, dispersant, castor oil, benzoyl peroxide first
Acyl and water are put into sealing container, are well mixed；
(3) temperature in sealing container is heated to 105 DEG C -115 DEG C, protected under the pressurized state of 1.5-1.8 atmospheric pressure
Warm 6-8 hours, natural cooling obtain the crack resistance poster paint of the present invention.
Example IV：
A kind of crack resistance poster paint is made up of the raw material components of following parts by weight：14 parts of xanthans, 20 parts of peach gum, titanium
18 parts of white powder, 9 parts of citric acid, 7 parts of glycerine, 6 parts of ethylene glycol, 10 parts of clay, 16 parts of kaolin, 6 parts of white carbon, para hydroxybenzene first
3 parts of propyl propionate, 2 parts of benzoic acid, 0.8 part of dimethicone, 1.2 parts of Bronopol, 1.5 parts of TTA, dispersant
0.5 part, 2 parts of castor oil, 3 parts of benzoyl peroxide, 32 parts of water.
The preparation method of described crack resistance poster paint, it comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) by xanthans, peach gum, titanium dioxide, citric acid, glycerine, ethylene glycol, clay, kaolin, white carbon, to hydroxyl
Propyl benzoate, benzoic acid, dimethicone, Bronopol, TTA, dispersant, castor oil, benzoyl peroxide first
Acyl and water are put into sealing container, are well mixed；
(3) temperature in sealing container is heated to 105 DEG C -115 DEG C, protected under the pressurized state of 1.5-1.8 atmospheric pressure
Warm 6-8 hours, natural cooling obtain the crack resistance poster paint of the present invention.
Embodiment five：
A kind of crack resistance poster paint is made up of the raw material components of following parts by weight：10 parts of xanthans, 10 parts of peach gum, titanium
16 parts of white powder, 6 parts of citric acid, 5 parts of glycerine, 4 parts of ethylene glycol, 8 parts of clay, 10 parts of kaolin, 5 parts of white carbon, para hydroxybenzene first
1 part of propyl propionate, 1 part of benzoic acid, 0.5 part of dimethicone, 0.6 part of Bronopol, 0.8 part of TTA, dispersant
0.3 part, 1 part of castor oil, 1 part of benzoyl peroxide, 25 parts of water.
The preparation method of described crack resistance poster paint, it comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) by xanthans, peach gum, titanium dioxide, citric acid, glycerine, ethylene glycol, clay, kaolin, white carbon, to hydroxyl
Propyl benzoate, benzoic acid, dimethicone, Bronopol, TTA, dispersant, castor oil, benzoyl peroxide first
Acyl and water are put into sealing container, are well mixed；
(3) temperature in sealing container is heated to 105 DEG C -115 DEG C, protected under the pressurized state of 1.5-1.8 atmospheric pressure
Warm 6-8 hours, natural cooling obtain the crack resistance poster paint of the present invention.
Embodiment six：
A kind of crack resistance poster paint is made up of the raw material components of following parts by weight：18 parts of xanthans, 20 parts of peach gum, titanium
23 parts of white powder, 11 parts of citric acid, 12 parts of glycerine, 8 parts of ethylene glycol, 15 parts of clay, 20 parts of kaolin, 10 parts of white carbon, to hydroxyl
3 parts of propyl benzoate, 5 parts of benzoic acid, 1.2 parts of dimethicone, 1.5 parts of Bronopol, 1.6 parts of TTA, point
0.8 part of powder, 3 parts of castor oil, 3 parts of benzoyl peroxide, 35 parts of water.
The preparation method of described crack resistance poster paint, it comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) by xanthans, peach gum, titanium dioxide, citric acid, glycerine, ethylene glycol, clay, kaolin, white carbon, to hydroxyl
Propyl benzoate, benzoic acid, dimethicone, Bronopol, TTA, dispersant, castor oil, benzoyl peroxide first
Acyl and water are put into sealing container, are well mixed；
(3) temperature in sealing container is heated to 105 DEG C -115 DEG C, protected under the pressurized state of 1.5-1.8 atmospheric pressure
Warm 6-8 hours, natural cooling obtain the crack resistance poster paint of the present invention.
Finally illustrate, the above embodiments are merely illustrative of the technical solutions of the present invention and it is unrestricted, although with reference to compared with
The present invention is described in detail good embodiment, it will be understood by those within the art that, can be to the skill of the present invention
Art scheme is modified or equivalent substitution, and without departing from the objective and scope of the technical program, it all should cover in the present invention
Right among.
Claims (4)
1. a kind of crack resistance poster paint, it is characterised in that be made up of the raw material components of following parts by weight：Xanthans 10-18
Part, peach gum 10-20 parts, titanium dioxide 16-23 parts, citric acid 6-11 parts, glycerine 5-12 parts, ethylene glycol 4-8 parts, clay 8-15 parts,
Kaolin 10-20 parts, white carbon 5-10 parts, propylparaben 1-3 parts, benzoic acid 1-5 parts, dimethicone 0.5-
1.2 parts, Bronopol 0.6-1.5 parts, TTA 0.8-1.6 parts, dispersant 0.3-0.8 parts, castor oil 1-3 parts,
Benzoyl peroxide 1-3 parts, water 25-35 parts.
2. crack resistance poster paint according to claim 1, it is characterised in that by the raw material components system of following parts by weight
Into：16 parts of xanthans, 12 parts of peach gum, 20 parts of titanium dioxide, 8 parts of citric acid, 8 parts of glycerine, 5 parts of ethylene glycol, 12 parts of clay, kaolin
15 parts, 8 parts of white carbon, 2 parts of propylparaben, 2 parts of benzoic acid, 0.8 part of dimethicone, 1 part of Bronopol, methyl
1.2 parts of benzotriazole, 0.3 part of dispersant, 1 part of castor oil, 1.5 parts of benzoyl peroxide, 30 parts of water.
3. crack resistance poster paint according to claim 1, it is characterised in that by the raw material components system of following parts by weight
Into：14 parts of xanthans, 20 parts of peach gum, 18 parts of titanium dioxide, 9 parts of citric acid, 7 parts of glycerine, 6 parts of ethylene glycol, 10 parts of clay, kaolin
16 parts, 6 parts of white carbon, 3 parts of propylparaben, 2 parts of benzoic acid, 0.8 part of dimethicone, 1.2 parts of Bronopol, first
1.5 parts of base benzotriazole, 0.5 part of dispersant, 2 parts of castor oil, 3 parts of benzoyl peroxide, 32 parts of water.
4. the preparation method of the crack resistance poster paint according to any one of claim 1-3, it is characterised in that including with
Lower step：
(1) each raw material components are weighed according to ratio of weight and number；
(2) by xanthans, peach gum, titanium dioxide, citric acid, glycerine, ethylene glycol, clay, kaolin, white carbon, para hydroxybenzene first
Propyl propionate, benzoic acid, dimethicone, Bronopol, TTA, dispersant, castor oil, benzoyl peroxide and
Water is put into sealing container, is well mixed；
(3) temperature in sealing container is heated to 105 DEG C -115 DEG C, 6-8 is incubated under the pressurized state of 1.5-1.8 atmospheric pressure
Hour, natural cooling obtains the crack resistance poster paint of the present invention.