CN107630309A - A kind of spandex one side of washing shakes a method for cloth improvement color fastness - Google Patents
A kind of spandex one side of washing shakes a method for cloth improvement color fastness Download PDFInfo
- Publication number
- CN107630309A CN107630309A CN201710924304.0A CN201710924304A CN107630309A CN 107630309 A CN107630309 A CN 107630309A CN 201710924304 A CN201710924304 A CN 201710924304A CN 107630309 A CN107630309 A CN 107630309A
- Authority
- CN
- China
- Prior art keywords
- spandex
- color fastness
- good
- washing
- shakes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of spandex one side of washing to shake a method for cloth improvement color fastness, including:Pretreatment procedure, dyeing process, matting, adding assistant process, plucking process, middle shaping process, carding process, cropping process, postprocessing working procedures.Whole flow process of the present invention has taken into account fabric stability, higher color fastness ensures, it is more beautiful to make to shake a style, at the same time reduces finishing process, reduces energy consumption, no especial equipment requirements;Fabric style after present invention processing is good, the good, good hand touch of elasticity, fastness is good, anti pilling is good, it is possible to achieve production stability, solves the technical barrier washed in the processing of spandex polar fleece fabric color fastness.
Description
Technical field
The invention belongs to shell-fabric dyeing and finishing field, more particularly to a kind of spandex one side of washing shakes a method for cloth improvement color fastness.
Background technology
The synthesis that spandex face fabric is terylene and spandex is washed, the cloth that two kinds of compositions are combined, feel is soft comfortable,
Excellent elasticity.But this fabric in processing because it lacks polar group, under normal temperature condition be difficult by activity, it is acid,
It is scattered to wait dyestuff coloring, therefore relatively common polyester fabric, wash spandex face fabric dye dosage under same depth conditions and be higher by relatively
Much, and because spandex has similar loose structure to terylene, therefore, when being dyed with polyester fiber simultaneously, to scattered dye
Material has adsorptivity, so during to the dyeing fabric of terylene+spandex, can substantially reduce the color fastness of fabric, therefore limit it and answer
Use prospect.And a style is shaken, it is necessary to be dried by steam injection and hot air ring, more aggravate color fastness difficulty up to standard.
The content of the invention
The technical problems to be solved by the invention, which are to provide to wash spandex one side and shake cloth, improves a method for color fastness, this method
Whole flow process has taken into account fabric stability, higher color fastness ensures, it is more beautiful to make to shake a style, after at the same time reducing
Arranging process, reduce energy consumption, no especial equipment requirements;Fabric style after present invention processing is good, the good, good hand touch of elasticity, fastness
Well, anti pilling is good, it is possible to achieve production stability, it is difficult to solve the technology washed in the processing of spandex polar fleece fabric color fastness
Topic.
The invention provides a kind of spandex one side of washing to shake a method for cloth improvement color fastness, including:
Pretreatment procedure, dyeing process, matting, adding assistant process, plucking process, middle shaping process, carding work
Sequence, cropping process, postprocessing working procedures;Wherein, postprocessing working procedures include 170~180 DEG C of high-temperature shapings, reduction cleaning, 130~
140 DEG C low-temperature shaped.
The technological parameter of the pretreatment procedure is:Using 1.5g/l degreasers, 80 DEG C of processing 20min.
The technological parameter of the dyeing process is:Normal temperature adding assistant, 50 DEG C of addition dyestuffs are warming up to, are warming up to 70 DEG C, 70
130 DEG C DEG C are risen to again, are cooled after 130 DEG C of insulation 30min.
The technological parameter of the reduction cleaning is:Using 3g/l cleaning agents and 0.5g/l formic acid, 90 DEG C of insulations are warming up to
30min is washed, and adds 0.3g/l sodium bicarbonate and 1g/l bleeding agents, and 80 DEG C neutralize washing.
The present invention, which cancels, washs spandex face fabric blank pre-setting process, ensure that fabric has the characteristics of high-elastic.Locate after dyeing
Manage high temperature discharge and reduce cleaning additive and with waterside number, (be used to ensure fabric door using high-temperature shaping in second of adding assistant
The stability of width, grammes per square metre and shrinkage), disperse dyes is discharged at high operating temperatures, then enter cylinder again and do reduction cleaning, make high temperature
The dyestuff residual separated out under state cleans up, and enters cylinder wet cloth state while has completed the style that matte shakes grain, finally going out cylinder takes off
Only needed after water low-temperature shaped, you can.Change of the present invention Jing Guo flow, saves and shakes a process, plucking-carding-cropping-high temperature is fixed
Type-enter cylinder reduction cleaning, you can obtain shaking a style.
Beneficial effect
Whole flow process of the present invention has taken into account fabric stability, higher color fastness ensures, it is more beautiful to make to shake a style,
At the same time finishing process is reduced, reduces energy consumption, no especial equipment requirements;After present invention processing fabric style is good, feel
Well, fastness is good, anti pilling is good, it is possible to achieve production stability, solves and washs in the processing of spandex polar fleece fabric color fastness
Technical barrier.
Embodiment
With reference to specific embodiment, the present invention is expanded on further.It should be understood that these embodiments are merely to illustrate the present invention
Rather than limitation the scope of the present invention.In addition, it is to be understood that after the content of the invention lectured has been read, people in the art
Member can make various changes or modifications to the present invention, and these equivalent form of values equally fall within the application appended claims and limited
Scope.
Embodiment 1
Spandex, which is washed, for dark color shakes a dyeing and finishing technology and flow for cloth raising color fastness:
(1) pre-treatment:
60 DEG C of washings;Degreaser 1.5g/l;80℃*20min.
(2) dye:
Auxiliary agent (normal temperature addition) be warming up to 50 DEG C add dyestuffs (feed time 10min), after be warming up to 70 DEG C (heating speed
2 DEG C/min of rate), 70 DEG C rise to 130 DEG C (this stage heating rate is slow, easy dyeing defect, 0.7 DEG C/min), 130 DEG C of insulations again
Cool (1 DEG C/min of rate of temperature fall) after 30min.
(3) clean:
High temperature discharge:Dye vat directly enters cold water, and one side draining is while water inlet (realizing that cooling and cleaning are synchronous) probably carries out 2
Water emptying cloth outputting after secondary washing, now 3.5 grades or so of color fastness.
(4) dry:
130 DEG C of drying temperature.
(5) shaped after adding assistant:
Groove of shaping adds raising agent, the setting of door width:160 centimetres, temperature:150 DEG C, speed:20 ms/min, air quantity:Up and down
100/100, overfeeding:10%, now 3 grades or so of color fastness.
(6) plucking:
A machine speed:16 ms/min, staight needle 1%, looper 1%, swift rotating speed:155RPM, progressive tension force:14 ms/min, go out
Cloth tension force:1KG, clearer rotating speed:600RPM.
B machine speed:16 ms/min, staight needle 0.5%, looper 0.5%, swift rotating speed:155RPM, cloth feeding tension force:15 meters/
Point, cloth outputting tension force:0KG, clearer rotating speed:600RPM.
(7) shaped among:
Door width:155 centimetres, temperature:163 DEG C, speed:30 ms/min, air quantity:Up/down 30/30, overfeeding:8%, color fastness
2.5 grades or so.
(8) carding:
Speed:18 ms/min, cloth feeding tension force:16.5 ms/min, A rollers:17 ms/min, B rollers:17.5 ms/min, cloth outputting:15.8
M/min, staight needle:68, looper:68, swift rotating speed:130RPM, clearer rotating speed:700RPM.
(9) cropping:
Speed:15 ms/min, the tension force of cloth feeding 1:1.5KG, the tension force of cloth feeding 2:8KG, cloth outputting:1.5KG, knife away from:0.6/0.2, knife
Speed:1100, brush height:5 millimeters, brush rotating speed:50 turns.
(10) high-temperature shaping:
Door width:170 centimetres, temperature:180 DEG C, speed:20 ms/min, air quantity:Up/down 30/30, overfeeding:5% (makes to disperse
Dyestuff is discharged at high operating temperatures, then enters cylinder again and cleans, and the dyestuff for making to separate out under the condition of high temperature is remained and cleaned up), this
When 1.5~2 grades or so of color fastness.
(11) reduction cleaning:
Cleaning agent 3g/l, formic acid 0.5g/l, 90 DEG C of * 30min;
Hot water wash;
Sodium bicarbonate 0.3g/l, bleeding agent 1g/l, 80 DEG C of * 20min;
Washing (adds up to 4 times with water).
Cylinder body washing is completed to shake an effect (uniform particle, while wash away floating hair and improve anti pilling effect) simultaneously, now color
4.5 grades or so of fastness.
(12) it is final low-temperature shaped:
Door width:155 centimetres, temperature:130 DEG C, speed:20 ms/min, air quantity:Up/down 30/30, overfeeding:8%, now color
4~4.5 grades of fastness.
Claims (4)
1. a kind of spandex one side of washing shakes a method for cloth improvement color fastness, including:
Pretreatment procedure, dyeing process, matting, adding assistant process, plucking process, middle shaping process, carding process, cut
Hair process, postprocessing working procedures;Wherein, postprocessing working procedures include 170~180 DEG C of high-temperature shapings, reduction cleaning, 130~140 DEG C it is low
Temperature sizing.
2. a kind of spandex one side of washing according to claim 1 shakes a method for cloth improvement color fastness, it is characterised in that:It is described
The technological parameter of pretreatment procedure is:Using 1.5g/l degreasers, 80 DEG C of processing 20min.
3. a kind of spandex one side of washing according to claim 1 shakes a method for cloth improvement color fastness, it is characterised in that:It is described
The technological parameter of dyeing process is:Normal temperature adding assistant, 50 DEG C of addition dyestuffs are warming up to, are warming up to 70 DEG C, 70 DEG C rise to 130 again
DEG C, cool after 130 DEG C of insulation 30min.
4. a kind of spandex one side of washing according to claim 1 shakes a method for cloth improvement color fastness, it is characterised in that:It is described
The technological parameter of reduction cleaning is:Using 3g/l cleaning agents and 0.5g/l formic acid, 90 DEG C of insulation 30min washings are warming up to, then add
Enter 0.3g/l sodium bicarbonate and 1g/l bleeding agents, 80 DEG C neutralize washing.