CN107629844A - A kind of aluminum alloy plate materials water-soluble flush force feed - Google Patents
A kind of aluminum alloy plate materials water-soluble flush force feed Download PDFInfo
- Publication number
- CN107629844A CN107629844A CN201610575408.0A CN201610575408A CN107629844A CN 107629844 A CN107629844 A CN 107629844A CN 201610575408 A CN201610575408 A CN 201610575408A CN 107629844 A CN107629844 A CN 107629844A
- Authority
- CN
- China
- Prior art keywords
- alloy plate
- aluminum alloy
- plate materials
- force feed
- materials water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of aluminum alloy plate materials water-soluble flush force feed, its raw material components and its percentage by weight are respectively：Pentaerythritol monooleate 3-8%；Extreme pressure agent 2-5%；Petroleum sodium sulfonate 5-12%；Emulsifying agent 4-10%；Antirust agent 0.5-4%；Nonionic surfactant 0.5-2.0%；AEO 1-5%；Amine neutralising phosphoric acid ester aluminium corrosion inhibiter 0.2-1.5%；Defoamer 0.03-0.1%；Preservative MBM 0.5-1.5%；It is oily based on surplus.Aluminum alloy plate materials water-soluble flush force feed provided by the invention is formed by highly refined paraffin base oil and the additive allotments meticulously such as emulsifying agent, extreme pressure agent, synthetic ester oiliness improver, surfactant, defoamer, bactericide and antirust agent.Low smell, there is excellent extreme pressure property, anticorrosive property and lubricity, suitable for processing technologys such as the punching presses, stretching, punching of aluminum alloy plate materials.
Description
Technical field
The invention belongs to chemical products field, more particularly to a kind of aluminum alloy plate materials water-soluble flush force feed.
Background technology
As the contradiction between energy supply and social demand is increasingly sharpened, the major automobile manufacturing company in the whole world increases pair
The dynamics of energy-conservation, consumption reduction Chemical Agent Research and Development.Aluminium alloy plate light weight, specific strength are high, have become automobile panel favor
Object, the lightness of automobile panel, which turns into, solves one of most direct measure of this contradiction.But aluminium alloy plate plasticity is poor, into
The active strong, mould of easily adhering of new metal surface generated during shape, is easily oxidized to hard, brittle wearing layer.This and aluminium
Friction, lubrication state of the alloy plate in shaping has substantial connection.It is therefore desirable to punching oil should possess excellent corrosion resistance
Energy, rustless property, greasy property, resistance to hard water, cleaning performance and cooling performance.
Water miscible aluminium alloy plate punching oil is seldom on domestic market, and workpiece surface is perishable after the completion of punching press being present
Alteration color, the problems such as being a bit darkish in color.Product of the present invention has excellent aluminium corrosion inhibition, excellent greasy property, hard water resistance property
Energy and emulsion stability.The workpiece surface that punching press is completed is bright, is deposited in inter process in one week without discoloration and corrosion.
The content of the invention
It is an object of the invention in place of overcome the deficiencies in the prior art, there is provided a kind of environmental protection with good slow-release function
Type aluminum alloy plate materials water-soluble flush presses oil.
The technical solution adopted for the present invention to solve the technical problems is：
A kind of aluminum alloy plate materials water-soluble flush force feed, its raw material components and its percentage by weight are respectively：
Moreover, the base oil is naphthenic base oils.
Moreover, the emulsifying agent is triethanolamine oleate.
Moreover, the aluminium corrosion inhibiter is amine neutralising phosphoric acid ester.
Moreover, the antirust agent is the NEUF 486 of Nuo Tai companies production.
Moreover, it is described it is non-from surface-active be OP-10.
Moreover, the extreme pressure agent is phosphate.
The preparation method of above-mentioned aluminum alloy plate materials water-soluble flush force feed is：
All raw materials are mixed by proportioning, is stirred, is stood 20 minutes, get product.
The advantages and positive effects of the present invention are：
Aluminum alloy plate materials water-soluble flush force feed provided by the invention is by highly refined paraffin base oil and emulsifying agent, chlorine
Change the additives such as fatty extreme pressure agent, synthetic ester oiliness improver, surfactant, defoamer, bactericide and antirust agent meticulously allotment and
Into.Low smell, there is excellent extreme pressure property and lubricity, work is processed suitable for punching press, stretching, punching of aluminum alloy plate materials etc.
Skill.
Embodiment
Below by specific embodiment, the invention will be further described, and following examples are descriptive, is not limit
Qualitatively, it is impossible to which protection scope of the present invention is limited with this.
Embodiment 1：
A kind of aluminum alloy plate materials water-soluble flush force feed, its raw material components and its weight are respectively：
The preparation method of above-mentioned aluminum alloy plate materials water-soluble flush force feed is：
All raw materials are mixed by proportioning, is stirred, is stood 20 minutes, get product.Embodiment 2：
A kind of aluminum alloy plate materials water-soluble flush force feed, its raw material components and its weight are respectively：
The preparation method of above-mentioned aluminum alloy plate materials water-soluble flush force feed is the same as embodiment 1.
Embodiment 3：
A kind of aluminum alloy plate materials water-soluble flush force feed, its raw material components and its weight are respectively：
The preparation method of above-mentioned aluminum alloy plate materials water-soluble flush force feed is the same as embodiment 1.
Claims (8)
- A kind of 1. aluminum alloy plate materials water-soluble flush force feed, it is characterised in that：Its raw material components and its percentage by weight are respectively：
- 2. aluminum alloy plate materials water-soluble flush force feed according to claim 1, it is characterised in that：The base oil is cycloalkyl Base oil.
- 3. aluminum alloy plate materials water-soluble flush force feed according to claim 1, it is characterised in that：The emulsifying agent is oleic acid three Ethanolamine soap.
- 4. aluminum alloy plate materials water-soluble flush force feed according to claim 1, it is characterised in that：The aluminium corrosion inhibiter is in amine And phosphate.
- 5. aluminum alloy plate materials water-soluble flush force feed according to claim 1, it is characterised in that：The antirust agent is that promise is safe public Take charge of the NEUF 486 of production.
- 6. aluminum alloy plate materials water-soluble flush force feed according to claim 1, it is characterised in that：The non-ionic surface active Agent is OP-10.
- 7. aluminum alloy plate materials water-soluble flush force feed according to claim 1, it is characterised in that：The extreme pressure agent is phosphoric acid Ester.
- A kind of 8. method for preparing aluminum alloy plate materials water-soluble flush force feed as claimed in claim 1, it is characterised in that：By proportioning All raw materials are mixed, stirred, 20 minutes is stood, gets product.