CN107629521A - A kind of reflective anaglyphy paint - Google Patents
A kind of reflective anaglyphy paint Download PDFInfo
- Publication number
- CN107629521A CN107629521A CN201710859893.9A CN201710859893A CN107629521A CN 107629521 A CN107629521 A CN 107629521A CN 201710859893 A CN201710859893 A CN 201710859893A CN 107629521 A CN107629521 A CN 107629521A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- anaglyphy
- powder
- graceful
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of graceful soft reflective anaglyphy paint, comprising in parts by weight：20 25 parts of deionized water, 30 36 parts of epoxy modified acrylic resin, 59 parts of methacrylic acid R esters, 6 10 parts of acrylic acid hydroxyl R esters, 18 25 parts of talcum powder, 10 12 parts of polyvinyl alcohol, 15 22 parts of cellulose solution, 16 25 parts of oyster shell whiting, 17 22 parts of pearl powder, 2 26 parts of calcite in powder, 2 26 parts of Fluorspar Powder, 25 parts of compound disinfectant, 58 parts of coalescents, 35 parts of dispersant, 23 parts of thickener.The design of the present invention is taken the course of its own, coordinated using soft water paint and building stones skeleton and auxiliary agent, while with good cementability, corrosion-resistant, weatherability, the soft brightness effect of uniqueness can be obtained with the proportioning adjustment of building stones composition, it is formulated design philosophy can be referred to as a kind of art in itself.
Description
Technical field
The present invention relates to a kind of emulsion paint, especially a kind of graceful soft reflective anaglyphy paint.
Background technology
Art coatings, originating from Europe, advanced technique is also come by Europe sprawling, into after domestic market, with it
Novel decorated style, unusual decorative effect, welcomed by the people again and high praise.High-quality art coatings coating can be criticized
Brush, adsorptivity is strong, and color sustains its quality through age.
Textured paint is a series in art coatings, and the metope after decoration exactly likes three-dimensional perception effect as embossment, high-end
Air, there is graceful, luxurious characteristic, there is artistic effect again.However, art coatings are not easy to cement mostly at present, if come off
Following black cement will be exposed, the Color control of textured paint is preferable in addition, but bright control is not fully up to expectations, so as to reduce
The art work, it appears very bright or very dull, the relative soft clearly anaglyphy effect of elegance that obtains also has distance.
So a kind of soft reflective art that develop refined taste, that light is moderately reflected and reflected paints, in technology
Aspect gives world of art support, it appears more lumping weight will.
The content of the invention
Goal of the invention：Of the invention to provide a kind of graceful soft reflective anaglyphy paint, it possesses good cementability and glued
Knotting strength, while reflective elegance is soft, all angles do not lose aesthetic feeling, to solve problems of the prior art.
The content of the invention：A kind of graceful soft reflective anaglyphy paint, it includes the component of following parts by weight：
Preferably, contain lignin, carboxymethyl cellulose, carboxy-propyl cellulose, cellulose in the cellulose solution
Ether, hydroxyethyl ether cellulose.Above cellulose strengthens the component connecting performance of paint system.
Preferably, the compound disinfectant is the compound disinfectant containing Nano Silver or Nanometer Copper.Nano Silver, Nanometer Copper
Compound disinfectant bactericidal effect is significantly efficient.
Preferably, the methacrylic acid R esters are anti-for the saturated monohydroxy alcohol of methacrylic acid and carbon number 1~10
The ester that should be generated.How crosslinkable methacrylic acid R ester species mixed and disorderly and three-dimensional degree be high.
Preferably, the molecular weight ranges of the polyvinyl alcohol are in 15-22 ten thousand.This is the poly- second of high viscosity of middle HMW
Enol, strengthens the adhesive property of system, there is polymeric emulsification effect again.
Preferably, the acrylic acid hydroxyl R esters are in hydroxy-ethyl acrylate, hydroxypropyl acrylate, hy-droxybutyl
A kind of or its combination.Acrylic acid hydroxyl R esters can obtain the effect of similar pure-acrylic emulsion with methacrylic acid R ester mating reactions,
Active hydroxyl can be crosslinked with other components again.
Preferably, the dispersant is silicate.Silicate dispersiveness and it is good with body series matching property.
The beneficial effects of the present invention are：The graceful soft reflective anaglyphy paint of one kind of the present invention, reflective soft, level
It is graceful.The synergy of epoxide modified acrylic resin, methacrylic acid R esters and acrylic acid hydroxyl R esters and under emulsification
Obtain the effect of similar pure-acrylic emulsion and water paint, texture is soft and non-greasy, weather-proof corrosion resistant；Cellulose solution, polyvinyl alcohol
Greatly increase each organic component bridging property；Talcum powder, oyster shell whiting, pearl powder, calcite in powder, Fluorspar Powder form the skeleton of paint,
Wherein oyster shell whiting and pearl powder have soft bright and natural biology matter effect, and calcite has birefringent phenomenon, fluorite tool
There is low dispersion, this two kinds cooperation can obtain the optical effect of uniqueness.The design of the present invention is taken the course of its own, and utilization is soft
Water paint and building stones skeleton and auxiliary agent coordinate, while with good cementability, corrosion-resistant, weatherability, building stones can be used
The proportioning of composition is adjusted to obtain the soft brightness effect of uniqueness, and it is formulated design philosophy in itself can be referred to as a kind of artistic.
Embodiment
In order to illustrate more clearly of the embodiment of the present application or technical scheme of the prior art, letter will be made to embodiment below
Single introduction.A kind of graceful soft reflective anaglyphy paint, including the parts by weight of component involved by embodiment in table 1.
Component (the unit of the embodiment of table 1：Parts by weight)
Wherein, lignin, carboxymethyl cellulose, carboxy-propyl cellulose, cellulose ether, hydroxyl are contained in the cellulose solution
Cellulose ether；The compound disinfectant is the compound disinfectant containing Nano Silver or Nanometer Copper；The methacrylic acid R esters exist
Embodiment 1~5 respectively isopropyl methacrylate, methyl methacrylate, n octyl methacrylate, methacrylic acid are just
Butyl ester, methacrylic acid peopentyl ester；The acrylic acid hydroxyl R esters are in the respectively hydroxy-ethyl acrylate of embodiment 1~5, acrylic acid hydroxyl
Propyl ester+hydroxy-ethyl acrylate, hy-droxybutyl+hydroxypropyl acrylate, hydroxy-ethyl acrylate+hy-droxybutyl, acrylic acid
Hydroxyl ethyl ester+hydroxypropyl acrylate+hy-droxybutyl.
Further, the molecular weight ranges of the polyvinyl alcohol are in 15-22 ten thousand.
Further, the dispersant is silicate.
Test result is shown in Table 2, and artificial ageing resistance experiment is with reference to standard GB/T-T 1865-2009.
The partial properties index of the embodiment of table 2
After the paint of the present invention is sprayed on into the art work, lustrous surface performance：
In embodiment 1, in there is ghost image, brighter sub-dued lustre, a light can be aobvious at one on art work surface
Write plane and obtain more than 2 inverted images, all angles reflection color and luster and intensity are slightly different；
In embodiment 2, art work surface is in the Natural color sub-dued lustre with transparent feel, and light is in any region without
Shadow, all angles reflection color and luster is very weak, intensity is almost identical；
In embodiment 3, art work surface is in aobvious at one almost without ghost image, intermediate light sub-dued lustre, a light
2 inverted images can occasionally be found by writing plane, and all angles reflection color and luster and intensity are almost identical；
In embodiment 4, art work surface is several in a notable plane in even with ghost image, partially dull sub-dued lustre, light
Without inverted image, all angles reflection color and luster and intensity are slightly different；
In embodiment 5, art work surface is without ghost image, dull sub-dued lustre, and light is in any region without inverted image, all angles
It is identical with intensity to reflect color and luster.
Above example is only illustrating the preferred technical solution of the present invention, it is noted that for the general of the art
For logical technical staff, under the premise without departing from the principles of the invention, some improvement made or equivalent substitution, this is accordingly to be regarded as
The protection domain of invention, it should cover in scope of the presently claimed invention.
Claims (7)
1. a kind of graceful soft reflective anaglyphy paint, it is characterised in that it includes the component of following parts by weight：
Deionized water 20-25 parts
Epoxy modified acrylic resin 30-36 parts
Methacrylic acid R ester 5-9 parts
Acrylic acid hydroxyl R ester 6-10 parts
Talcum powder 18-25 parts
Polyvinyl alcohol 10-12 parts
Cellulose solution 15-22 parts
Oyster shell whiting 16-25 parts
Pearl powder 17-22 parts
Calcite in powder 2-26 parts
Fluorspar Powder 2-26 parts
Compound disinfectant 2-5 parts
Coalescents 5-8 parts
Dispersant 3-5 parts
Thickener 2-3 parts.
2. a kind of graceful soft reflective anaglyphy paint as claimed in claim 1, it is characterised in that in the cellulose solution
Contain lignin, carboxymethyl cellulose, carboxy-propyl cellulose, cellulose ether, hydroxyethyl ether cellulose.
3. soft reflective anaglyphy paint as claimed in claim 1 a kind of graceful, it is characterised in that the compound disinfectant is
Compound disinfectant containing Nano Silver or Nanometer Copper.
A kind of 4. graceful soft reflective anaglyphy paint as claimed in claim 1, it is characterised in that the methacrylic acid R
Ester is methacrylic acid and the ester of the saturated monohydroxy alcohol reaction generation of carbon number 1 ~ 10.
A kind of 5. graceful soft reflective anaglyphy paint as claimed in claim 1, it is characterised in that point of the polyvinyl alcohol
Son amount scope is in 15-22 ten thousand.
A kind of 6. graceful soft reflective anaglyphy paint as claimed in claim 1, it is characterised in that the acrylic acid hydroxyl R esters
For one kind in hydroxy-ethyl acrylate, hydroxypropyl acrylate, hy-droxybutyl or its combination.
7. a kind of graceful soft reflective anaglyphy paint as claimed in claim 1, it is characterised in that the dispersant is silicic acid
Salt.