CN105400325A - High-flexibility relievo paint and preparation process thereof - Google Patents
High-flexibility relievo paint and preparation process thereof Download PDFInfo
- Publication number
- CN105400325A CN105400325A CN201510846253.5A CN201510846253A CN105400325A CN 105400325 A CN105400325 A CN 105400325A CN 201510846253 A CN201510846253 A CN 201510846253A CN 105400325 A CN105400325 A CN 105400325A
- Authority
- CN
- China
- Prior art keywords
- aqueous solution
- lignocellulose
- water
- hydroxyethylmethyl
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses high-flexibility relievo paint. The high-flexibility relievo paint is prepared from the following raw materials in parts by weight: 150-200 g of deionized water, 60-70 g of a pure acrylic emulsion, 550-650 g of coarse whiting, 70-90 g of talcum powder, 30-40 g of a hydroxyethyl methyl cellulose water solution, 10-20 g of a lignocellulose water solution, 4-6 g of a film-forming additive, 1.5-2.5 g of an anti-corrosion disinfectant, 1.8-2.2 g of a dispersant, 1.8-2.2 g of a wetting agent, 3.5-4.5 g of a thickening agent and 9-11 g of ethylene glycol, wherein the hydroxyethyl methyl cellulose water solution is prepared by dissolving 2-4% hydroxyethyl methyl cellulose in water; the lignocellulose water solution is prepared by dissolving 1-3% lignocellulose in water. The invention further discloses a process for preparing a high-flexibility relievo paint. The relievo paint is low in drying speed, good in flexibility, free from cracking during construction and excellent in surface vision.
Description
Technical field
The present invention relates to synthetic resins water soluble paint, particularly a kind of textured paint with high-flexibility, also relate to a kind of textured paint preparation technology with high-flexibility.
Background technology
Water soluble paint take water-soluble synthetic resin as main film forming substance, and water is thinner, adds appropriate pigment, filler and auxiliary agent etc., through the coating of grinding.Water-borne coatings is also relative to oil paint, and oil paint is because containing oiliness in coating, and does not have oily matter inside the composition of water-borne coatings, and therefore it be just called as water-borne coatings using water as solvent and dispersion medium.Most water-borne coatings is all do not contain or contained few harmful material, so water-borne coatings environment-protecting asepsis.Water soluble paint development is swift and violent, has formed multi items, multi-functional, multi-usage, huge and rounded system.
Textured paint is a kind of water-borne coatings, adopts snappiness synthetic resins to be base-material, adds filler, auxiliary agent and mill base and make.It is the colored metope coating material that a kind of match volume is true to nature, and the metope after decoration exactly likes three-dimensional perception effect as embossment, so be referred to as textured paint.Textured paint has certain rebound resilience and snappiness, can make up the micro-cracks of buildings base course wall, and construction is simple, so be widely used in inner-outer wall wall decoration.
Now textured paint brand is commercially a lot, fill a prescription similar, generally by 20% water, the fillers such as the coarse whiting of 70%, the emulsion of 6%, the ethylene glycol of 1%, dispersion agent, wetting agent, sterilant, thickening material etc. are mixed with, drop into according to particular order in the paint mixing cylinder of uniform rotation, after toning, be packaged into finished product.
But flatten this procedure in construction process to be easy to cause enamelled coating to ftracture, have a strong impact on the decorative effect of textured paint.The reason causing textured paint to ftracture mainly contains 2 points, namely suppleness not and rate of drying too fast.
Summary of the invention
In view of this, the object of this invention is to provide a kind of textured paint with high-flexibility, rate of drying is slow, and snappiness is good, does not ftracture during construction, and surperficial vision is good; The present invention also provides a kind of technique preparing the textured paint with high-flexibility, and technique is simple, easy to use.
An object of the present invention is achieved through the following technical solutions:
There is a textured paint for high-flexibility, be made up of the raw material of following weight part: deionized water 150-200g; Pure-acrylic emulsion 60-70g; Coarse whiting 550-650g; Talcum powder 70-90g; Hydroxyethylmethyl-cellulose aqueous solution 30-40g; Lignocellulose aqueous solution 10-20g; Film coalescence aid 4-6g; Anticorrosion and bactericidal agent 1.5-2.5g; Dispersion agent 1.8-2.2g; Wetting agent 1.8-2.2g; Thickening material 3.5-4.5g; Ethylene glycol 9-11g;
The described hydroxyethylmethyl-cellulose aqueous solution is made by 2-4% hydroxyethylmethyl-cellulose is water-soluble;
The described lignocellulose aqueous solution is made by 1-3% lignocellulose is water-soluble.
Further, a kind of textured paint with high-flexibility according to claim 1, is characterized in that: be made up of the raw material of following weight part: deionized water 180g; Pure-acrylic emulsion 65g; Coarse whiting 600g; Talcum powder 80g; Hydroxyethylmethyl-cellulose aqueous solution 35g; Lignocellulose aqueous solution 15g; Film coalescence aid 5g; Anticorrosion and bactericidal agent 2g; Dispersion agent 2g; Wetting agent 2g; Thickening material 4g; Ethylene glycol 10g;
The described hydroxyethylmethyl-cellulose aqueous solution is made by 2% hydroxyethylmethyl-cellulose is water-soluble;
The described lignocellulose aqueous solution is made by 2% lignocellulose is water-soluble;
Further, described coarse whiting is 1250 orders, and described talcum powder is 1250 orders.
Two of object of the present invention is achieved through the following technical solutions:
Prepare a technique for the textured paint with high-flexibility, comprise the steps:
(1) raw material is got out according to following weight part: deionized water 150-200g; Pure-acrylic emulsion 60-70g; Coarse whiting 550-650g; Talcum powder 70-90g; Hydroxyethylmethyl-cellulose aqueous solution 30-40g; Lignocellulose aqueous solution 10-20g; Film coalescence aid 4-6g; Anticorrosion and bactericidal agent 1.5-2.5g; Dispersion agent 1.8-2.2g; Wetting agent 1.8-2.2g; Thickening material 3.5-4.5g; Ethylene glycol 9-11g;
The described hydroxyethylmethyl-cellulose aqueous solution: with dispersion machine by 2-4% hydroxyethylmethyl-cellulose and water-dispersion uniformly pasty state;
The described lignocellulose aqueous solution: with dispersion machine by 1-3% lignocellulose and water-dispersion uniformly pasty state;
Dispersing speed is 280-320r/min;
(2) in paint is filled with, add 800-900g water, stir with dispersion machine, dispersing speed is 900-1000r/min, adds anticorrosion and bactericidal agent, defoamer, wetting agent, dispersion agent successively;
(3) in the obtained solution of step (2), add coarse whiting, talcum powder, cellulose aqueous solution, then dispersing speed is adjusted to 380-420r/min, adds ethylene glycol and deionized water, described deionized water is the 9-10g of formula ratio;
(4) by dispersion machine speed governing to 580-620r/min, stir 30-40 minute, measure particles in solution fineness and solution pH value, after touching the mark, slowly add pure-acrylic emulsion, stir 19-22 minute;
(5) in the obtained solution of step (4), add film coalescence aid, defoamer, the deionized water of residue formula ratio and thickening material, adjustment viscosity, until touch the mark;
(6) dispersing speed is adjusted to 280-320r/min to mix colours, after having mixed colours, carries out the examination and test of products, after the assay was approved, filter and package.
Further, described coarse whiting is 1250 orders;
Further, described talcum powder is 1250 orders;
Further again, described step (1) Raw (weight part) is: deionized water 180g; Pure-acrylic emulsion 65g; Coarse whiting 600g; Talcum powder 80g; Hydroxyethylmethyl-cellulose aqueous solution 35g; Lignocellulose aqueous solution 15g; Film coalescence aid 5g; Anticorrosion and bactericidal agent 2g; Dispersion agent 2g; Wetting agent 2g; Thickening material 4g; Ethylene glycol 10g;
The described hydroxyethylmethyl-cellulose aqueous solution is made by 2% hydroxyethylmethyl-cellulose is water-soluble;
The described lignocellulose aqueous solution is made by 2% lignocellulose is water-soluble.
The invention has the beneficial effects as follows:
The textured paint with high-flexibility of the present invention, by adding the hydroxyethylmethyl-cellulose aqueous solution and the lignocellulose aqueous solution in formula, make textured paint rate of drying slightly slow, and there is no crackle with when flattening without hair roller, after textured paint all parches, the product that the surperficial visual impression such as surface flatness, hardness and stereoscopic sensation all obtains than prior art is outstanding.
Embodiment
Below will be described in detail the preferred embodiments of the present invention.
embodiment one
Prepare a technique for the textured paint with high-flexibility, comprise the steps:
(1) raw material is got out according to following weight part: deionized water 180g; Pure-acrylic emulsion 65g; 1250 order coarse whiting 600g; 1250 order talcum powder 80g; Hydroxyethylmethyl-cellulose aqueous solution 35g; Lignocellulose aqueous solution 15g; Film coalescence aid 5g; Anticorrosion and bactericidal agent 2g; Dispersion agent 2g; Wetting agent 2g; Thickening material 4g; Ethylene glycol 10g;
The described hydroxyethylmethyl-cellulose aqueous solution: with dispersion machine by 2% hydroxyethylmethyl-cellulose and water-dispersion uniformly pasty state;
The described lignocellulose aqueous solution: with dispersion machine by 2% lignocellulose and water-dispersion uniformly pasty state;
Dispersing speed is 300r/min;
(2) in paint is filled with, add 850g water, stir with dispersion machine, dispersing speed is 1000r/min, adds anticorrosion and bactericidal agent, defoamer, wetting agent, dispersion agent successively;
(3) in the obtained solution of step (2), add 1250 order coarse whitings, 1250 order talcum powder, cellulose aqueous solution, then dispersing speed is adjusted to 400r/min, adds ethylene glycol and deionized water, described deionized water is the 9g of formula ratio;
(4) by dispersion machine speed governing to 600r/min, stir 35 minutes, measure particles in solution fineness and solution pH value, after touching the mark, slowly add pure-acrylic emulsion, stir 20 minutes;
(5) in the obtained solution of step (4), add film coalescence aid, defoamer, the deionized water of residue formula ratio and thickening material, adjustment viscosity, until touch the mark;
(6) dispersing speed is adjusted to 300r/min to mix colours, after having mixed colours, carries out the examination and test of products, after the assay was approved, filter and package.
embodiment two
Prepare a technique for the textured paint with high-flexibility, comprise the steps:
(1) raw material is got out according to following weight part: deionized water 150g; Pure-acrylic emulsion 70g; Coarse whiting 550g; Talcum powder 90g; Hydroxyethylmethyl-cellulose aqueous solution 30g; Lignocellulose aqueous solution 20g; Film coalescence aid 4g; Anticorrosion and bactericidal agent 2.5g; Dispersion agent 1.8g; Wetting agent 2.2g; Thickening material 3.5g; Ethylene glycol 11g;
The described hydroxyethylmethyl-cellulose aqueous solution: with dispersion machine by 4% hydroxyethylmethyl-cellulose and water-dispersion uniformly pasty state;
The described lignocellulose aqueous solution: with dispersion machine by 1% lignocellulose and water-dispersion uniformly pasty state;
Dispersing speed is 280r/min;
(2) in paint is filled with, add 900g water, stir with dispersion machine, dispersing speed is 900r/min, adds anticorrosion and bactericidal agent, defoamer, wetting agent, dispersion agent successively;
(3) in the obtained solution of step (2), add coarse whiting, talcum powder, cellulose aqueous solution, then dispersing speed is adjusted to 420r/min, adds ethylene glycol and deionized water, described deionized water is the 10g of formula ratio;
(4) by dispersion machine speed governing to 580r/min, stir 30 minutes, measure particles in solution fineness and solution pH value, after touching the mark, slowly add pure-acrylic emulsion, stir 22 minutes;
(5) in the obtained solution of step (4), add film coalescence aid, defoamer, the deionized water of residue formula ratio and thickening material, adjustment viscosity, until touch the mark;
(6) dispersing speed is adjusted to 320r/min to mix colours, after having mixed colours, carries out the examination and test of products, after the assay was approved, filter and package.
embodiment three
Prepare a technique for the textured paint with high-flexibility, comprise the steps:
(1) raw material is got out according to following weight part: deionized water 200g; Pure-acrylic emulsion 60g; Coarse whiting 650g; Talcum powder 70g; Hydroxyethylmethyl-cellulose aqueous solution 40g; Lignocellulose aqueous solution 10g; Film coalescence aid 6g; Anticorrosion and bactericidal agent 1.5g; Dispersion agent 2.2g; Wetting agent 1.8g; Thickening material 4.5g; Ethylene glycol 9g;
The described hydroxyethylmethyl-cellulose aqueous solution: with dispersion machine by 3% hydroxyethylmethyl-cellulose and water-dispersion uniformly pasty state;
The described lignocellulose aqueous solution: with dispersion machine by 3% lignocellulose and water-dispersion uniformly pasty state;
Dispersing speed is 320r/min;
(2) in paint is filled with, add 800g water, stir with dispersion machine, dispersing speed is 950r/min, adds anticorrosion and bactericidal agent, defoamer, wetting agent, dispersion agent successively;
(3) in the obtained solution of step (2), add coarse whiting, talcum powder, cellulose aqueous solution, then dispersing speed is adjusted to 380r/min, adds ethylene glycol and deionized water, described deionized water is the 9g of formula ratio;
(4) by dispersion machine speed governing to 620r/min, stir 40 minutes, measure particles in solution fineness and solution pH value, after touching the mark, slowly add pure-acrylic emulsion, stir 19 minutes;
(5) in the obtained solution of step (4), add film coalescence aid, defoamer, the deionized water of residue formula ratio and thickening material, adjustment viscosity, until touch the mark;
(6) dispersing speed is adjusted to 280r/min to mix colours, after having mixed colours, carries out the examination and test of products, after the assay was approved, filter and package.
Key of the present invention is the improvement of filling a prescription, and adds appropriate hydroxyethylmethyl-cellulose and lignocellulose in formula.The effect of hydroxyethylmethyl-cellulose is the viscosity and the water-retentivity that strengthen textured paint, thus slows down the rate of drying of textured paint.Drying varniss speed is slow, and string stress declines, and the stress of paint film can be avoided to ftracture.Lignocellulose is that natural reproducible timber processes through chemical treatment, mechanical process the organic wadding fibrous material obtained, it has excellent snappiness and dispersiveness, tridimensional network is formed after mixing, enhance anchorage force and the resisting power of system, the stability of system, intensity, degree of compactness and uniformity coefficient can be improved, thus strengthen the effect of prestressed of paint film.
Another key point of the present invention is the formula consumption of hydroxyethylmethyl-cellulose and lignocellulose.The very few textured paint of consumption does not reach effect of prestressed, and consumption is excessive, affects the three-dimensional decorative effect of textured paint.
In preparation technology of the present invention, coarse whiting, talcous amount are comparatively large, in order to make various auxiliary agent mix in water, should first add anticorrosion and bactericidal agent, wetting agent, defoamer and dispersion agent before interpolation filler.
To carry out under stirring at low speed when adding pure-acrylic emulsion, if the too high meeting of rotating speed causes breakdown of emulsion, make to paint Tofu pudding shape.
PH index in step (4) is 8 ~ 9, because body of wall mostly is alkalescence, is conducive to the construction of painting.
In order to embody difference and the improvement of textured paint of the present invention and common textured paint, two kinds of textured paints are carried out to the detection of five indices.
1. routine inspection
(1) abrasion resistance detection is carried out by GB/T9266-88 " mensuration of building coating layer abrasion resistance " standard.
(2) alkali resistance detection is carried out by GB9265-88 " testing method of building coating layer alkali resistance " standard.
(3) mensuration of free formaldehyde adopts volumetry.Take sample 5g, be placed in 250mL iodine flask, add 20mL distilled water to disperse completely to sample, getting 20mL sodium sulfite solution (C=10g/L) with transfer pipet adds in iodine flask, jump a queue, leave standstill 2 hours in dark place, add 50mL distilled water and 1mL starch solution (C=10g/L), it is light blue for being titrated to solution with iodine standard titration solution (C (1/2I2)=0.1mol/L).
Utilize following formulae discovery free formaldehyde content:
X=(V-V0)*C(1/2I2)*30.03/m
In formula: X---the massfraction of water-borne coatings Free-formaldehyde, g/kg;
V0---consume the volume of iodine standard titration solution during blank test, mL;
V---consume the volume of iodine standard titration solution when measuring sample, mL;
C (1/2I2)---the concentration of iodine standard titration solution, mol/L;
The quality of m---sample, kg;
30.03---the molar mass of formaldehyde, g/mol.
After completing above three kinds of leading indicators test, carry out other Indexs measure, result is as shown in table 2.Two kinds of textured paints all meet national standard, and the time of drying of high-flexibility textured paint will be grown.
The detected result of table 2 product
| Test item | Desired value | Common textured paint | High-flexibility textured paint |
| Condition in container | Without lump, uniformly state after stirring | Even without lump | Even without lump |
| Appearance of film | Appearance of film is normal | Flat smooth | Flat smooth |
| Time of drying/h | ≤2 | 1.2 | 1.5 |
| Application property | Spray accessible | Accessible | Accessible |
| Alkali resistance | 24h is without exception | Without exception | Without exception |
| Abrasion resistance/time | ≥200 | ＞400 | ＞400 |
| Free formaldehyde/g/kg | ≤0.1 | 0.008 | 0.008 |
| Low-temperature stability | Never degenerate | Never degenerate | Never degenerate |
2. snappiness and anti-cracking performance detect
(1) the snappiness detection of textured paint is carried out by GB GB/T1731-93 " paint film flexibility assay method ", by QTX paint film flexibility tester test result as table 3.
Table 3 two kinds of textured paint suppleness contrast tables
| Textured paint kind | Common textured paint | High-flexibility textured paint |
| Snappiness/mm | 10 | 4 |
(2) splitting resistance detects and uses dynamic crack resistance testing machine to detect, and detected result is as table 4.
Table 4 two kinds of textured paint dynamic cracking resistance contrast tables
| Textured paint kind | Common textured paint | High-flexibility textured paint |
| Dynamic cracking resistance/mm | 0.22 | 0.08 |
Above two kinds of test results show, the snappiness of high-flexibility textured paint and splitting resistance are obviously better than common textured paint.
Claims (7)
1. there is a textured paint for high-flexibility, it is characterized in that: be made up of the raw material of following weight part: deionized water 150-200g; Pure-acrylic emulsion 60-70g; Coarse whiting 550-650g; Talcum powder 70-90g; Hydroxyethylmethyl-cellulose aqueous solution 30-40g; Lignocellulose aqueous solution 10-20g; Film coalescence aid 4-6g; Anticorrosion and bactericidal agent 1.5-2.5g; Dispersion agent 1.8-2.2g; Wetting agent 1.8-2.2g; Thickening material 3.5-4.5g; Ethylene glycol 9-11g;
The described hydroxyethylmethyl-cellulose aqueous solution is made by 2-4% hydroxyethylmethyl-cellulose is water-soluble;
The described lignocellulose aqueous solution is made by 1-3% lignocellulose is water-soluble.
2. a kind of textured paint with high-flexibility according to claim 1, is characterized in that: be made up of the raw material of following weight part: deionized water 180g; Pure-acrylic emulsion 65g; Coarse whiting 600g; Talcum powder 80g; Hydroxyethylmethyl-cellulose aqueous solution 35g; Lignocellulose aqueous solution 15g; Film coalescence aid 5g; Anticorrosion and bactericidal agent 2g; Defoamer 2g; Dispersion agent 2g; Wetting agent 2g; Thickening material 4g; Ethylene glycol 10g;
The described hydroxyethylmethyl-cellulose aqueous solution is made by 2% hydroxyethylmethyl-cellulose is water-soluble;
The described lignocellulose aqueous solution is made by 2% lignocellulose is water-soluble.
3. a kind of textured paint with high-flexibility according to claim 1, it is characterized in that: described coarse whiting is 1250 orders, described talcum powder is 1250 orders.
4. prepare the technique with the textured paint of high-flexibility described in claim 1 or 2, it is characterized in that: comprise the steps:
(1) raw material is got out according to following weight part: deionized water 150-200g; Pure-acrylic emulsion 60-70g; Coarse whiting 550-650g; Talcum powder 70-90g; Hydroxyethylmethyl-cellulose aqueous solution 30-40g; Lignocellulose aqueous solution 10-20g; Film coalescence aid 4-6g; Anticorrosion and bactericidal agent 1.5-2.5g; Dispersion agent 1.8-2.2g; Wetting agent 1.8-2.2g; Thickening material 3.5-4.5g; Ethylene glycol 9-11g;
The described hydroxyethylmethyl-cellulose aqueous solution: with dispersion machine by 2-4% hydroxyethylmethyl-cellulose and water-dispersion uniformly pasty state;
The described lignocellulose aqueous solution: with dispersion machine by 1-3% lignocellulose and water-dispersion uniformly pasty state;
Dispersing speed is 280-320r/min;
(2) in paint is filled with, add 800-900g water, stir with dispersion machine, dispersing speed is 900-1000r/min, adds anticorrosion and bactericidal agent, defoamer, wetting agent, dispersion agent successively;
(3) in the obtained solution of step (2), add coarse whiting, talcum powder, cellulose aqueous solution, then dispersing speed is adjusted to 380-420r/min, adds ethylene glycol and deionized water, described deionized water is the 9-10g of formula ratio;
(4) by dispersion machine speed governing to 580-620r/min, stir 30-40 minute, measure particles in solution fineness and solution pH value, after touching the mark, slowly add pure-acrylic emulsion, stir 19-22 minute;
(5) in the obtained solution of step (4), add film coalescence aid, defoamer, the deionized water of residue formula ratio and thickening material, adjustment viscosity, until touch the mark;
(6) dispersing speed is adjusted to 280-320r/min to mix colours, after having mixed colours, carries out the examination and test of products, after the assay was approved, filter and package.
5. a kind of technique preparing the textured paint with high-flexibility according to claim 4, is characterized in that: described coarse whiting is 1250 orders.
6. a kind of technique preparing the textured paint with high-flexibility according to claim 4 or 5, is characterized in that: described talcum powder is 1250 orders.
7. a kind of technique preparing the textured paint with high-flexibility according to claim 4, is characterized in that: described step (1) Raw (weight part) is: deionized water 180g; Pure-acrylic emulsion 65g; Coarse whiting 600g; Talcum powder 80g; Hydroxyethylmethyl-cellulose aqueous solution 35g; Lignocellulose aqueous solution 15g; Film coalescence aid 5g; Anticorrosion and bactericidal agent 2g; Dispersion agent 2g; Wetting agent 2g; Thickening material 4g; Ethylene glycol 10g;
The described hydroxyethylmethyl-cellulose aqueous solution is made by 2% hydroxyethylmethyl-cellulose is water-soluble;
The described lignocellulose aqueous solution is made by 2% lignocellulose is water-soluble.