CN107629494A - A kind of preparation method of high molecular water-proof paint - Google Patents
A kind of preparation method of high molecular water-proof paint Download PDFInfo
- Publication number
- CN107629494A CN107629494A CN201710868705.9A CN201710868705A CN107629494A CN 107629494 A CN107629494 A CN 107629494A CN 201710868705 A CN201710868705 A CN 201710868705A CN 107629494 A CN107629494 A CN 107629494A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- polyvinyl alcohol
- high molecular
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of high molecular water-proof paint, it is made up of the component of following mass parts：30 40 parts of 30 40 parts of titanium dioxide, 0.5 3 parts of bactericide, 10 20 parts of polyvinyl alcohol, 0.1 0.8 parts of thickener, 10 15 parts of polyvinyl acetate emulsion, 20 30 parts of heavy carbon soda acid, 10 15 parts of methyl-silicone oil, 8 12 parts of mill base, 15 parts of polysiloxane compound, 3 10 parts of polyvinyl alcohol, 10 20 parts of sodium pyrophosphate and water.Using titanium dioxide as major ingredient in the present invention, addition polyvinyl acetate emulsion has anticorrosive, high temperature-proof, a variety of excellent properties such as low temperature resistant, ductility is good, water proofing property is strong, and cost is low, and human body and environment are not polluted；Meanwhile bactericide is added, add the performance of its sterilization.
Description
Technical field
The present invention relates to building materials technology field, and in particular to a kind of preparation method of high molecular water-proof paint.
Background technology
Water-repellent paint it is cured after formed waterproofing membrane have certain extensibility, elastoplasticity, crack resistance, impermeability and
Weatherability, waterproof can be played, prevent blending protective effect.Water-repellent paint has good thermal adaptability, easy to operate, for ease of maintenaince
With maintenance.The waterproof material of in the market has two major classes：First, polyurethanes water-repellent paint.This kind of material be usually by polyurethane with
Coal tar is made as raw material.The tar gas toxicity that it is volatilized is big, and does not allow easy-clear, therefore in 2000 in Chinese quilt
Prohibit the use of.It is to be used as raw material instead of coal tar by the use of pitch still in the polyurethane waterproofing coating of sale.But using this coating
When, it is general to be diluted using the organic solvents such as toluene, dimethylbenzene are contained, thus also containing toxic；Another kind of is polymer cement
Base waterproof coating.It by the emulsion that a variety of waterborne polymerics synthesize with being formed mixed with the high grade cement of various additives, polymer
The flexibility of (resin) and the rigidity of cement became one so that it is excellent with being showed in terms of stability in impermeability.Its advantages of
It is easy for construction, comprehensive cost low, short time limit, and asepsis environment-protecting.Therefore, polyalcohol cement basis has become water-repellent paint market
Leading role.
At present, the conventional waterproof material of building trade is low, attached in the prevalence of high temperature trickling, low-temperature embrittleness, tensile strength
The problems such as putting forth effort difference.Also constructional difficulties be present, seepage takes place frequently, can not effectively protect the problems such as wall.On the other hand, conventional painting
Expect that formaldehyde and organic compound content are high, and conditioning agent is added during use, environmental pollution is very big.
The content of the invention
In view of the defects and deficiencies of the prior art, the present invention intends to provide a kind of preparation of high molecular water-proof paint
Method, to solve the problems, such as proposed in background technology.
To achieve the above object, the technical solution adopted by the present invention is：A kind of preparation method of high molecular water-proof paint, its
Innovative point is：The high molecular water-proof paint is made up of the component of following mass parts：Titanium dioxide 30-40 parts, bactericide 0.5-3
Part, polyvinyl alcohol 10-20 parts, thickener 0.1-0.8 parts, polyvinyl acetate emulsion 10-15 parts, heavy carbon soda acid 20-30 parts, first
Base silicone oil 10-15 parts, mill base 8-12 parts, polysiloxane compound 1-5 parts, polyvinyl alcohol 3-10 parts, sodium pyrophosphate 10-20 parts
With water 30-40 parts；The preparation method comprises the following steps：
(1) first each component is put into dispersion cylinder according to the ratio in formula, under 600-800rpm speed
Scattered 30-50min is carried out under high-speed stirred；
(2) liquid material is put into dispersion cylinder according to the ratio in formula again, under 150-250rpm speed
Even stirring 2-4 hours, it is cooled to room temperature and produces.
Further, a kind of high molecular water-proof paint, it is made up of the component of following mass parts：Titanium dioxide 32-38 parts, kill
Microbial inoculum 1-2 parts, polyvinyl alcohol 12-18 parts, thickener 0.3-0.6 parts, polyvinyl acetate emulsion 11-14 parts, heavy carbon soda acid 22-
28 parts, methyl-silicone oil 11-14 parts, mill base 9-11 parts, polysiloxane compound 2-4 parts, polyvinyl alcohol 5-8 parts, sodium pyrophosphate 12-
18 parts and water 32-38 parts.
Further, a kind of high molecular water-proof paint, it is made up of the component of following mass parts：35 parts of titanium dioxide, bactericide
1.5 parts, 15 parts of polyvinyl alcohol, 0.5 part of thickener, 12 parts of polyvinyl acetate emulsion, 25 parts of heavy carbon soda acid, methyl-silicone oil 12
Part, 10 parts of mill base, 3 parts of polysiloxane compound, 6 parts of polyvinyl alcohol, 15 parts of sodium pyrophosphate and 35 parts of water.
The present invention has the beneficial effect that：Using titanium dioxide as major ingredient in the present invention, addition polyvinyl acetate emulsion have it is anticorrosive,
High temperature-proof, a variety of excellent properties such as low temperature resistant, ductility is good, water proofing property is strong, and cost is low, to human body and environment without dirt
Dye；Meanwhile bactericide is added, add the performance of its sterilization.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, it is right below in conjunction with embodiment
The present invention is further elaborated.It should be appreciated that embodiment described herein is only to explain the present invention, and
It is not used in the restriction present invention.
Embodiment 1
A kind of preparation method of high molecular water-proof paint, the high molecular water-proof paint by following mass parts component group
Into：30 parts of titanium dioxide, 0.5 part of bactericide, 10 parts of polyvinyl alcohol, 0.1 part of thickener, 10 parts of polyvinyl acetate emulsion, heavy carbon
20 parts of soda acid, 10 parts of methyl-silicone oil, 8 parts of mill base, 1 part of polysiloxane compound, 3 parts of polyvinyl alcohol, 10 parts of sodium pyrophosphate and water
30 parts；The preparation method comprises the following steps：
(1) first each component is put into dispersion cylinder according to the ratio in formula, under 600-800rpm speed
Scattered 30-50min is carried out under high-speed stirred；
(2) liquid material is put into dispersion cylinder according to the ratio in formula again, under 150-250rpm speed
Even stirring 2-4 hours, it is cooled to room temperature and produces.
Embodiment 2
A kind of preparation method of high molecular water-proof paint, the high molecular water-proof paint by following mass parts component group
Into：40 parts of titanium dioxide, 3 parts of bactericide, 20 parts of polyvinyl alcohol, 0.8 part of thickener, 15 parts of polyvinyl acetate emulsion, heavy carbonic acid
30 parts of alkali, 15 parts of methyl-silicone oil, 12 parts of mill base, 5 parts of polysiloxane compound, 10 parts of polyvinyl alcohol, 20 parts of sodium pyrophosphate and water
40 parts；The preparation method comprises the following steps：
(1) first each component is put into dispersion cylinder according to the ratio in formula, under 600-800rpm speed
Scattered 30-50min is carried out under high-speed stirred；
(2) liquid material is put into dispersion cylinder according to the ratio in formula again, under 150-250rpm speed
Even stirring 2-4 hours, it is cooled to room temperature and produces.
Embodiment 3
A kind of preparation method of high molecular water-proof paint, the high molecular water-proof paint by following mass parts component group
Into：35 parts of titanium dioxide, 1.5 parts of bactericide, 15 parts of polyvinyl alcohol, 0.5 part of thickener, 12 parts of polyvinyl acetate emulsion, heavy carbon
25 parts of soda acid, 12 parts of methyl-silicone oil, 10 parts of mill base, 3 parts of polysiloxane compound, 6 parts of polyvinyl alcohol, 15 parts of sodium pyrophosphate and water
35 parts；The preparation method comprises the following steps：
(1) first each component is put into dispersion cylinder according to the ratio in formula, under 600-800rpm speed
Scattered 30-50min is carried out under high-speed stirred；
(2) liquid material is put into dispersion cylinder according to the ratio in formula again, under 150-250rpm speed
Even stirring 2-4 hours, it is cooled to room temperature and produces.
Using titanium dioxide as major ingredient in the present invention, addition polyvinyl acetate emulsion have it is anticorrosive, high temperature-proof, it is low temperature resistant, prolong
A variety of excellent properties such as malleability is good, water proofing property is strong, and cost is low, and human body and environment are not polluted；Meanwhile add sterilization
Agent, add the performance of its sterilization.
It is described above, it is merely illustrative of the technical solution of the present invention and unrestricted, those of ordinary skill in the art are to this hair
The other modifications or equivalent substitution that bright technical scheme is made, without departing from the spirit and scope of technical solution of the present invention,
It all should cover among scope of the presently claimed invention.
Claims (3)
- A kind of 1. preparation method of high molecular water-proof paint, it is characterised in that：The high molecular water-proof paint is by following mass parts Component composition：Titanium dioxide 30-40 parts, bactericide 0.5-3 parts, polyvinyl alcohol 10-20 parts, thickener 0.1-0.8 parts, poly-vinegar acid Vac emulsion 10-15 parts, heavy carbon soda acid 20-30 parts, methyl-silicone oil 10-15 parts, mill base 8-12 parts, polysiloxane compound 1- 5 parts, polyvinyl alcohol 3-10 parts, sodium pyrophosphate 10-20 parts and water 30-40 parts；The preparation method comprises the following steps：（1）First each component is put into dispersion cylinder according to the ratio in formula, under 600-800rpm speed at a high speed Scattered 30-50min is carried out under stirring；（2）The liquid material is put into dispersion cylinder according to the ratio in formula again, uniformly stirred under 150-250rpm speed 2-4 hours are mixed, room temperature is cooled to and produces.
- A kind of 2. preparation method of high molecular water-proof paint according to claim 1, it is characterised in that：The macromolecule is prevented Water paint is made up of the component of following mass parts：Titanium dioxide 32-38 parts, bactericide 1-2 parts, polyvinyl alcohol 12-18 parts, thickener 0.3-0.6 parts, polyvinyl acetate emulsion 11-14 parts, heavy carbon soda acid 22-28 parts, methyl-silicone oil 11-14 parts, mill base 9-11 parts, Polysiloxane compound 2-4 parts, polyvinyl alcohol 5-8 parts, sodium pyrophosphate 12-18 parts and water 32-38 parts.
- A kind of 3. preparation method of high molecular water-proof paint according to claim 1, it is characterised in that：The macromolecule is prevented Water paint is made up of the component of following mass parts：35 parts of titanium dioxide, 1.5 parts of bactericide, 15 parts of polyvinyl alcohol, 0.5 part of thickener, It is 12 parts of polyvinyl acetate emulsion, 25 parts of heavy carbon soda acid, 12 parts of methyl-silicone oil, 10 parts of mill base, 3 parts of polysiloxane compound, poly- 35 parts of 6 parts of vinyl alcohol, 15 parts of sodium pyrophosphate and water.