CN107611631A - The copper aluminium connection sheet and its production technology drawn for battery module both positive and negative polarity - Google Patents
The copper aluminium connection sheet and its production technology drawn for battery module both positive and negative polarity Download PDFInfo
- Publication number
- CN107611631A CN107611631A CN201710779070.5A CN201710779070A CN107611631A CN 107611631 A CN107611631 A CN 107611631A CN 201710779070 A CN201710779070 A CN 201710779070A CN 107611631 A CN107611631 A CN 107611631A
- Authority
- CN
- China
- Prior art keywords
- connection sheet
- aluminium
- red copper
- copper
- temeperature chemistry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of copper aluminium connection sheet drawn for battery module both positive and negative polarity, including red copper connection sheet and aluminium connection sheet, the surface of the red copper connection sheet is coated with a high temeperature chemistry nickel dam, the thickness of the high temeperature chemistry nickel dam is 9~15um, the aluminium connection sheet is fixedly connected on high temeperature chemistry nickel surface by high-frequency induction welder, the width of the red copper connection sheet and aluminium lead-out tablet is 40~50mm, and the bonding area of the red copper connection sheet and aluminium connection sheet is 450~900mm2;A floor height temperature electroless nickel layer is plated on the surface of red copper connection sheet, and aluminium connection sheet and high temeperature chemistry nickel dam are bonded together by high-frequency induction welder, its tightness degree being bonded greatly promotes, the temperature rise of connection substantially reduces, and processes obtained workpiece stretch-proof by this technique and anti-seismic performance is greatly improved.
Description
Technical field
The present invention relates to new energy car battery accessories field, the copper aluminium more particularly to drawn for battery module both positive and negative polarity
Connection sheet and its production technology.
Background technology
Automobile batteries is the indispensable visual plant of automobile, and it can provide electric energy to automobile, such as during startup engine, give
Starter (equipment that the electric energy of automobile batteries is converted into mechanical energy startup engine) provides powerful starting current, and association
Generator is helped to each power supply for electrical equipment of in-car etc..Automobile batteries be fixedly installed in automobile and by lead-out tablet with
Start mechatronics, existing connection sheet includes red copper connection sheet and aluminium connection sheet, red copper connection sheet and aluminium connection sheet it
Between be to be fixedly connected by way of lead welding, because of situations such as automobile can run into the process of moving jolt in addition collide, even
Contact pin must have excellent tension intensity and anti-seismic performance, and the tension intensity and anti-seismic performance of existing lead welding technique need
Mention;The electric current by 250~300A is needed at other connection sheet, and the connection sheet being fabricated by lead welding technique it is easy because
For bonding area out-of-flatness, when being powered, temperature rise is very big, and the interface of red copper connection sheet and aluminium connection sheet easily fuses.
The content of the invention
It is used for electricity it is an object of the invention to provide a kind of tensile property and anti-seismic performance be splendid, interface temperature rise is small
The copper aluminium connection sheet that pond module both positive and negative polarity is drawn, to solve the problems mentioned in the above background technology.
To achieve these goals, the present invention provides following technical scheme:
Electricity is used for the copper aluminium connection sheet that battery module both positive and negative polarity is drawn, including red copper connection sheet and aluminium connection sheet, the red copper
The surface of connection sheet is coated with a high temeperature chemistry nickel dam, and the thickness of the high temeperature chemistry nickel dam is 9~15um, the aluminium connection sheet
High temeperature chemistry nickel surface is fixedly connected on by high-frequency induction welder, the width of the red copper connection sheet and aluminium connection sheet for 40~
50mm, the bonding area of the red copper connection sheet and aluminium connection sheet is 450~900mm2.
As further describing for the present invention:The thickness H of the high temeperature chemistry nickel is 10um, the red copper connection sheet and aluminium
The width W of material connection sheet is 45mm, and the bonding area S of the red copper connection sheet and aluminium connection sheet is 450;The red copper connection
The material of piece is T2 copper, and the material of the aluminium connection sheet is 1060 aluminium.
To achieve the above object, the present invention provides following technical scheme:
The production technology for the copper aluminium connection sheet drawn for battery module both positive and negative polarity, comprises the following steps:(1)Pass through chemical nickel plating
Method plates high temeperature chemistry nickel dam on the surface of red copper connection sheet, and the thickness of high temeperature chemistry nickel dam is 9~15um, will after the completion of plating
The oil stain on red copper connection sheet surface cleans up, and obtains nickel plating red copper connection sheet;
(2)By step(1)In nickel plating after red copper connection sheet and aluminium connection sheet be placed on high-frequency induction welder carry out hot pressing at
Reason, specific heat pressing process process are as follows:The hot pressing die of high-frequency induction welder is used into graphite hot pressing pressing mold first, by the purple after nickel plating
Copper connection sheet and aluminium connection sheet, which are placed in the die cavity of hot pressing pressing mold, carries out Primary Location, and then high-frequency induction welder is in die cavity
Workpiece is heated, and between temperature rises to 650 DEG C~700 DEG C, aluminium connection sheet can be in molten condition, aluminium connection sheet
A part can penetrate into high temeperature chemistry nickel dam, therewith fusion be bonded together;It is removed from the molds, obtains into after workpiece cooling
Product.
Formula and process advantage:
1st, the uniform covering power of thickness evenness thickness is well a big feature of chemical nickel plating, and the reason for be widely used it
One, chemical nickel plating avoids electrodeposited coating because CURRENT DISTRIBUTION is uneven and brought in uneven thickness;During chemical plating, as long as part
Surface and plating solution are contacted, and the composition consumed in plating solution can be supplemented in time, and the thickness of coating at plating piece position is substantially the same, i.e.,
It is also such to make groove, gap, blind hole;Really be because chemical nickel plating after red copper connection sheet surface it is still smooth, with aluminium
Its solder side is smooth during connection sheet progress hot pressing connects, significantly reduces the temperature rise in galvanization.
2nd, plating piece will not ooze hydrogen, without hydrogen embrittlement, dehydrogenation not needed after chemical nickel plating, while be also prevented from material and opened because of hydrogen embrittlement
Split.
3rd, function for example anti-corrosion, the high temperature oxidation resistance grade ratio electronickelling of many materials and parts is good.
4th, can be deposited on the surface of various materials, such as:Steel nickel-base alloy, zinc-containing alloy, copper alloy, aluminium, glass,
On the surface of the materials such as ceramics, plastics, semiconductor, so as to create condition to improve the performance of these materials.
5th, required direct current generator or control device need not typically be electroplated.
Compared with prior art, beneficial effects of the present invention are:One layer of high temeperature chemistry is plated on the surface of red copper connection sheet
Nickel dam, and aluminium connection sheet and high temeperature chemistry nickel dam are bonded together by high-frequency induction welder, the tightness degree that it is bonded is big
Big lifting, the temperature rise of connection substantially reduce, and process obtained workpiece stretch-proof by this technique and anti-seismic performance is able to greatly
Raising.
Brief description of the drawings
Fig. 1 is the overall structure diagram of the present invention;
Fig. 2 is the top perspective view at A in Fig. 1;
Fig. 3 is the schematic cross-section at A-A in Fig. 2.
Embodiment
Embodiment 1
The copper aluminium connection sheet for being used for battery module both positive and negative polarity and drawing as shown in Figure 1 to Figure 3, including red copper connection sheet 1 and aluminium
Connection sheet 2, the surface of the red copper connection sheet 1 are coated with a high temeperature chemistry nickel dam 3, and high temeperature chemistry nickel dam 3 is resistant to 850 DEG C of height
Temperature, the thickness H of the high temeperature chemistry nickel dam 3 is 10um, and the aluminium connection sheet 2 is fixedly connected on high temperature by high-frequency induction welder
The surface of nickel dam 3 is learned, the width W of the red copper connection sheet 1 and aluminium connection sheet 2 is 45mm, and the aluminium connection sheet 2 passes through high frequency
Welding machine is fixedly connected on the surface of high temeperature chemistry nickel dam 3, and the bonding area S of the red copper connection sheet 1 and aluminium connection sheet 2 is
450mm²;The material of the red copper connection sheet 1 is T2 copper, and the material of the aluminium connection sheet 2 is 1060 aluminium.
Red copper connection sheet 1 is followed the steps below with aluminium connection sheet 2 and is fixedly connected:
(1)High temeperature chemistry nickel dam 3, the thickness H of high temeperature chemistry nickel dam are plated on the surface of red copper connection sheet by chemically coated nickel method
For 10um, the oil stain on red copper connection sheet surface is cleaned up after the completion of plating, obtains nickel plating red copper connection sheet;
(2)By step(1)In nickel plating after red copper connection sheet 1 and aluminium connection sheet 2 be placed on high-frequency induction welder and carry out hot pressing
Processing, specific heat pressing process process are as follows:The hot pressing die of high-frequency induction welder uses graphite hot pressing pressing mold, and the red copper after nickel plating is connected
Contact pin 1 and aluminium connection sheet 2, which are placed in the die cavity of hot pressing pressing mold, carries out Primary Location, and then high-frequency induction welder is to the work in die cavity
Part is heated, and between temperature rises to 650 DEG C~700 DEG C, aluminium connection sheet can be in molten condition, aluminium connection sheet
A part can penetrate into high temeperature chemistry nickel dam 3, and fusion therewith is bonded together;It is removed from the molds after workpiece cooling, obtains finished product.
In the prior art by way of lead welding made from product, although its tensile resistance and anti seismic efficiency can be inadequate
Meet standard, the limiting value of tensile resistance and its antidetonation can not break through always, think although those skilled in the art have
Cross by the way of friction welding and ultra-sonic welded and go to replace lead welding;The tensile strength and shock strength of friction welding can dash forward
Broken limiting value, but plugging between pipe fitting can only be realized by suffering from friction welding, for its process difficulty of the workpiece of sheet
Greatly;Although quick using ultra-sonic welded, the workpiece processed its excessively stream effect, tensile resistance and anti seismic efficiency are equal
Cloth is preferable;Inventor can break through industry stretch-proof and resist by finding that this technique can be produced in low cost after kinds of experiments
The technique of pinking energy limit, and the finished product obtained in the present embodiment 1 is tested, pulling force survey is carried out on tensile testing machine
Examination, can bear 1500~2000N pulling force, and its tensile resistance improves 1/3rd than the mode of original lead welding;
Antidetonation test is carried out under conditions of national standard 73, the seismic behavior of its X-axis, Y-axis and Z axis reaches eight grades;In high and low temperature impact test
In, -40 DEG C~80 DEG C of environmental change, long run test 72 hours can be born;, can be wet 85% in high temperature and humidity test
Long run test 1000 hours in degree, 85 DEG C of environment.
Described above to be not intended to limit the scope of the present invention, all foundation the technology of the present invention are substantially to the above
Any modification, equivalent variations and the modification that embodiment is made, in the range of still falling within technical scheme.
Claims (4)
1. the copper aluminium connection sheet drawn for battery module both positive and negative polarity, including red copper connection sheet and aluminium connection sheet, its feature exist
In:The surface of the red copper connection sheet is coated with a high temeperature chemistry nickel dam, and the thickness of the high temeperature chemistry nickel dam is 9~15um, institute
State aluminium connection sheet and high temeperature chemistry nickel surface is fixedly connected on by high-frequency induction welder, the red copper connection sheet and aluminium connection sheet
Width is 40~50mm, and the bonding area of the red copper connection sheet and aluminium connection sheet is 400~1000mm2.
2. the copper aluminium connection sheet according to claim 1 drawn for battery module both positive and negative polarity, it is characterised in that:The aluminium
Material connection sheet includes the aluminium foil of some stackings.
3. the copper aluminium connection sheet according to claim 1 drawn for battery module both positive and negative polarity, it is characterised in that:The height
The thickness H of warm chemical nickel is 10um, and the width W of the red copper connection sheet and aluminium connection sheet is 45mm, the red copper connection sheet
Bonding area S with aluminium connection sheet is 450;The material of the red copper connection sheet is T2 copper, the material of the aluminium connection sheet
For 1060 aluminium.
4. the production technology for the copper aluminium connection sheet drawn as claimed in claim 1 for battery module both positive and negative polarity, its feature exist
In:Comprise the following steps:(1)High temeperature chemistry nickel dam, high temeperature chemistry are plated on the surface of red copper connection sheet by chemically coated nickel method
The thickness of nickel dam is 9~15um, cleans up the oil stain on red copper connection sheet surface after the completion of plating, obtains the connection of nickel plating red copper
Piece;
By step(1)In nickel plating after red copper connection sheet and aluminium connection sheet be placed on high-frequency induction welder and carry out hot-pressing processing,
Specific heat pressing process process is as follows:The hot pressing die of high-frequency induction welder is used into graphite hot pressing pressing mold first, by the red copper after nickel plating
Connection sheet and aluminium connection sheet, which are placed in the die cavity of hot pressing pressing mold, carries out Primary Location, and then high-frequency induction welder is to the work in die cavity
Part is heated, and between temperature rises to 650 DEG C~700 DEG C, aluminium connection sheet can be in molten condition, aluminium connection sheet
A part can penetrate into high temeperature chemistry nickel dam, and fusion therewith is bonded together;It is removed from the molds after workpiece cooling, obtains finished product.