CN107604510A - One kind is breathed freely and uvioresistant fabrics and its manufacture method - Google Patents
One kind is breathed freely and uvioresistant fabrics and its manufacture method Download PDFInfo
- Publication number
- CN107604510A CN107604510A CN201710950886.XA CN201710950886A CN107604510A CN 107604510 A CN107604510 A CN 107604510A CN 201710950886 A CN201710950886 A CN 201710950886A CN 107604510 A CN107604510 A CN 107604510A
- Authority
- CN
- China
- Prior art keywords
- yarn
- fabric
- uvioresistant
- parts
- ventilative
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Ventilative and uvioresistant fabrics and its manufacture method present invention is disclosed one kind, fabric includes warp thread group and weft yarn group, the warp thread group uses covering yarn, the covering yarn includes heart yarn and surface layer yarn, the heart yarn is with the higher fiber from elongation in water suction, it is more than 10% from elongation, the surface layer yarn is the fiber for having during water suction itself relatively low elongation, it is less than 2% from elongation, weft yarn group uses conventional yarns, the fabric is impregnated in uvioresistant auxiliary agent, and the uvioresistant auxiliary agent is made up of following raw material：12 ~ 15 parts of fluorine carbon emulsion, 2 (aminomethyl phenyl of 2 ' hydroxyl, 3 ' tertiary butyl 5 ') 2 ~ 5 parts of 5 chlorobenzotriazoles, 5 ~ 8 parts of 2 hydroxyl, 4 methoxy benzophenone, 30 ~ 40 parts of ceramic powder, 90 ~ 110 parts of deionized water.Heretofore described fabric has good gas permeability when perspiring or fabric soak, and has good comfort level, and has anti-ultraviolet property.
Description
Technical field
The present invention relates to a kind of fabric and preparation method thereof, belongs to dress materials technical field.
Background technology
Garment material is widely present and applied in everyone life, most clothings uses weaving face fabric.
With the continuous propulsion of social development, human lives enter the fast pace epoch, and the requirement to quality of life improves constantly.Taking
Load onto, in addition to traditional attractive in appearance and fit requirement, even more to ask easily ventilative in perspiring, can be kept at any time when drying
Or easily recover its original form.And current fabric to multi-functional trend development, in addition to requiring ventilative and attractive in appearance, is gone back
Need to have other functions such as uvioresistant, antistatic.
In view of the shortcomings of the prior art, it is deformable ventilative when design one kind is perspired, recover the fabric of original form when drying
And there is anti-ultraviolet function, it appears highly significant.
The content of the invention
The purpose of the present invention is exactly to solve the above-mentioned problems in the prior art, there is provided one kind is breathed freely and uvioresistant
Line fabric and preparation method thereof, fabric has good gas permeability in perspiring, and has anti-ultraviolet function.
The present invention technical solution be：One kind is breathed freely and uvioresistant fabrics, including warp thread group and weft yarn group, described
Warp thread group uses covering yarn, and the covering yarn includes heart yarn and surface layer yarn, and the heart yarn is to have higher elongation certainly in water suction
The fiber of rate, it is more than 10% from elongation, and to have the fiber of itself relatively low elongation during water suction, it stretches the surface layer yarn certainly
Long rate is less than 2%, and the weft yarn group uses conventional yarns；The fabric is impregnated with uvioresistant auxiliary agent, the uvioresistant auxiliary agent
It is made up of following raw material：12 ~ 15 parts of fluorine carbon emulsion, the chloro- benzos three of 2- (2 '-hydroxyl -3 '-tertiary butyl -5 '-aminomethyl phenyl) -5-
2 ~ 5 parts of azoles, 5 ~ 8 parts of ESCALOL 567,30 ~ 40 parts of ceramic powder, 90 ~ 110 parts of deionized water.
Further, above-mentioned ventilative and uvioresistant fabrics, wherein：The weft yarn group is by staple fibre and/or naturally
Fiber is made.
Further, above-mentioned ventilative and uvioresistant fabrics, wherein：The heart yarn is made up of PEE, described
PEE is made up of polyester elastomer, and the polyester elastomer includes the hard of polybutylene terephthalate (PBT) formation
Segment and the soft chain segment formed by polyoxyethylene glycol, the mass ratio of the hard segment and soft chain segment is 30/70 ~ 70/30
In the range of.
Further, above-mentioned ventilative and uvioresistant fabrics, wherein：The polyester elastomer further comprises as copolymerization
The metal salt of the organic sulfonic acid of composition.
Further, above-mentioned ventilative and uvioresistant fabrics, wherein：The surface layer yarn is made up of polyester fiber.
Further, above-mentioned ventilative and uvioresistant fabrics, wherein：Covering yarn SMIS yarn length and the surface layer yarn length
Degree is than being 0.4 ~ 0.7.
This law is bright to also disclose a kind of ventilative and uvioresistant fabrics manufacture method,（1）By for forming hard segment
Polybutylene terephthalate (PBT) and polyoxyethylene glycol for soft chain segment are put into reactor melting, and melting compound is passed through
Melt-blowing head sprays polymer filaments, and monfil is made, and monfil is made into heart yarn,（2）Using polyester fiber as
Surface layer yarn, heart yarn and surface layer yarn are made by covering yarn by twisting process, warp thread group uses the covering yarn, and weft yarn group is using normal
Advise yarn,（3）Warp thread group and weft yarn group are interweaved fabric are made,（4）Fabric is impregnated in uvioresistant auxiliary agent, impregnates work
After the completion of fabric is dried,（5）Fabric is subjected to dyeing processing, dried fabric after the completion of dyeing processing,（6）By fabric again
It is impregnated in uvioresistant auxiliary agent, carries out double-steeping, after the completion of impregnating work, warp thread group and weft yarn group is dried.
Further, above-mentioned ventilative and uvioresistant fabrics manufacture method, wherein：The step（4）Middle drying temperature
Spend for 170 ~ 180 DEG C, the step（5）Middle drying temperature is 180 ~ 190 DEG C, the step（6）Middle drying temperature is 150 ~ 160
℃。
The prominent substantive distinguishing features of the present invention and significant progress are mainly reflected in：People wears heretofore described fabric,
In perspiring, the heart yarn of covering yarn has higher from elongation in water suction in the first yarns, but its top layer yarns exists
Have during water suction relatively low from elongation, obstruction heart yarn extension, so as to cause the covering yarn of warp thread group to deform upon so that covering yarn
Final undulate is bent, the wave portion only protruded and human contact, the contact area of fabric and human body is reduced, improves and relax
Appropriateness, and due to covering yarn undulate, form perforate, strengthen the permeability of fabric, and fabric is impregnated with uvioresistant
Auxiliary agent so that fabric has anti-ultraviolet function.After drying, heart yarn can recover its original state, so as to which covering yarn recovers former
There is form, it is attractive in appearance not interfere with fabric, applied widely.
Embodiment
It is described in further detail with the embodiment to the present invention, so that technical solution of the present invention is more readily understood and slapped
Hold.
One kind is breathed freely and uvioresistant fabrics, is made up of warp thread group and weft yarn group interwoven textile, and the warp thread is covering yarn,
Including heart yarn and surface layer yarn, the surface layer yarn be coated on heart yarn outer peripheral face, heart yarn and surface layer yarn be made up of twisting process it is described
Covering yarn, the heart yarn are that it is more than 10% from elongation, and surface layer yarn is suction in water suction with the higher fiber from elongation
There is the fiber of itself relatively low elongation, it is less than 2% from elongation during water.Specifically, heart yarn is made up of PEE, institute
State PEE to be made up of polyester elastomer, the polyester elastomer includes what polybutylene terephthalate (PBT) was formed
Hard segment and the soft chain segment formed by polyoxyethylene glycol.The mass ratio of hard segment and soft chain segment is preferably 30：70~70：30.
Surface layer yarn is made by polyester fiber.The weft yarn group uses conventional yarns, and conventional yarns can be by natural fiber and/or artificial fibre
Dimension is made, and the warp thread group and weft yarn group are impregnated in uvioresistant auxiliary agent, and the uvioresistant auxiliary agent is made up of following raw material
12 ~ 15 parts of fluorine carbon emulsion, 2 ~ 5 parts of the chloro- BTAs of 2- (2 '-hydroxyl -3 '-tertiary butyl -5 '-aminomethyl phenyl) -5-, 2- hydroxyls -
5 ~ 8 parts of 4- methoxy benzophenones, 30 ~ 40 parts of ceramic powder, 90 ~ 110 parts of deionized water.
Preferably, polyester elastomer is further comprised as between the metal salt of the organic sulfonic acid of copolymer composition, such as 5- sulfo groups
During phthalic acid sodium, can obtain further improved in water suction fiber from elongation.
PEE can be manufactured by Conventional melt spinning head melting extrusion polyester elastomer, with 500 900m/
The coiling speed of minute batches the long filament of extrusion, is wound winding filaments with 1.0 1.2 times of speed with above-mentioned coiling speed,
Preferably 1.0 1.1 times.Made PEE, single fiber thickness are preferably 0.6 100dtex, the gross thickness of heart yarn
Preferably 30 300dtex.
Due to heart yarn have in water suction it is higher from elongation, and surface layer yarn have in water suction it is relatively low from elongation, it is excellent
Selection of land, covering yarn SMIS yarn length and top layer yarn length ratio are between 0.4 ~ 0.7.If heart yarn length and surface layer yarn length ratio are big
When 0.7, the draftability deficiency of gained covering yarn.In addition, if heart yarn length and surface layer yarn length ratio are less than 0.4, gained
The shape that is showed in water suction and wetting of surface layer yarn and cosmetic variation it is too small, be unfavorable for strengthening gas permeability.
Above-mentioned ventilative and uvioresistant fabrics manufacture method comprises the following steps,（1）By for forming the poly- of hard segment
Mutual-phenenyl two acid bromide two alcohol ester and for form the polyoxyethylene glycol of soft chain segment be put into reactor melting, melting compound is led to
Cross melt spinning head and spray polymer filaments, monfil is made, and heart yarn is made in monfil,（2）Polyester fiber is made
For surface layer yarn, heart yarn and surface layer yarn are made by covering yarn by twisting process, warp thread group is made up of covering yarn, and weft yarn group is by routine
Yarn forms,（3）Warp thread group and weft yarn group are interweaved fabric are made,（4）Fabric is impregnated in uvioresistant auxiliary agent, impregnates work
Fabric to be dried after the completion of work, drying temperature is 170 ~ 180 DEG C,（6）Fabric is subjected to dyeing processing, will after the completion of dyeing processing
Fabric is dried, and drying temperature is 180 ~ 190 DEG C,（7）Fabric is impregnated in uvioresistant auxiliary agent again, carries out double-steeping,
After the completion of impregnating work, fabric is dried, drying temperature is 150 ~ 160 DEG C.
Embodiment 1
Warp thread is covering yarn, including heart yarn and surface layer yarn, by the poly terephthalic acid for being used to form hard segment of 50 mass fractions
The polyoxyethylene glycol that the number-average molecular weight for being used to form soft chain segment of butanediol ester and 50 mass fractions is 4000, is placed in
230 DEG C of thermotonus kettle melting, and spinning head is extruded through with the rate of extrusion of 3.05g/ minutes and sprays polymer filaments.Squeeze
The polymer filaments gone out are wound by two godets, and to provide stretchable power, heart yarn has to be inhaled from its long axis direction
Elongation is 10% during water, boiling water shrinkage 8%, elongation at break 816%.The poly- multifilament yarn of routine that surface layer yarn uses
Line, i.e. polyethylene terephthalate multifilament, its own elongation are less than 1%.Then heart yarn and top layer yarn twisting are made
Covering yarn, warp thread group use the covering yarn.Cotton fiber is used in weft yarn group, warp thread group and weft yarn group is interweaved fabric is made,
Fabric is impregnated in uvioresistant auxiliary agent afterwards, the specific composition of uvioresistant auxiliary agent is：12 parts of fluorine carbon emulsion, 2- (2 '-
Hydroxyl -3 '-tertiary butyl -5 '-aminomethyl phenyl) 5 parts of the chloro- BTAs of -5-, 6 parts of ESCALOL 567, coupling
5 parts of agent, 300 parts of ceramic powder, the moisture content of deionization 100.
Then fabric is dried, drying temperature is 170 DEG C；
Fabric is subjected to dyeing processing afterwards, after the completion of dyeing, drying and shaping processing is carried out to fabric, drying qualitative temperature is
190℃；
Fabric is subjected to double-steeping processing afterwards, uvioresistant auxiliary agent impregnates adjuvant used identical, impregnation with first time
After the completion of, dried, drying temperature is 150 DEG C.
By above description as can be seen that heretofore described fabric has very well when perspiring or fabric soak
Gas permeability, and there is good comfort level, it is attractive in appearance not interfere with fabric, can voluntarily recover after the drying as former state, and have
There is anti-ultraviolet function, there is multifunctionality.
People wears heretofore described fabric, and in perspiring, the covering yarn used in warp thread group, its heart yarn is in water suction
With higher from elongation, but its top layer yarn has relatively low from elongation in water suction, hinders heart yarn to extend, so as to cause
Covering yarn deforms upon so that covering yarn bends final undulate, the wave portion only protruded and human contact, reduces face
The contact area of material and human body, comfort level is improved, and due to covering yarn undulate, form perforate, strengthen the gas permeability of fabric
Energy.After drying, heart yarn can recover its original state, so as to which covering yarn recovers original form.If whole fabric is by above-mentioned bag
Heart yarn is formed, and in immersion whole fabric can be caused to wrinkle, extremely unsightly, therefore, covering yarn be used only in warp thread group, because
This does not interfere with fabric overall appearance.And fabric is impregnated by uvioresistant auxiliary agent so that fabric has anti-ultraviolet function.
Certainly, the above is the representative instance of the present invention, and in addition, the present invention can also have other a variety of specific implementations
Mode, all technical schemes formed using equivalent substitution or equivalent transformation, is all fallen within the scope of protection of present invention.
Claims (10)
1. one kind is breathed freely and uvioresistant fabrics, it is characterised in that：Including warp thread group and weft yarn group, the warp thread group uses cored
Yarn, the covering yarn include heart yarn and surface layer yarn, and the heart yarn is that it stretches certainly in water suction with the higher fiber from elongation
Long rate is more than 10%, and for the surface layer yarn to have the fiber of itself relatively low elongation during water suction, it is less than 2% from elongation, described
Weft yarn group uses conventional yarns；The fabric is impregnated with uvioresistant auxiliary agent, and the uvioresistant auxiliary agent is made up of following raw material：
12 ~ 15 parts of fluorine carbon emulsion, 2 ~ 5 parts of the chloro- BTAs of 2- (2 '-hydroxyl -3 '-tertiary butyl -5 '-aminomethyl phenyl) -5-, 2- hydroxyls -
5 ~ 8 parts of 4- methoxy benzophenones, 30 ~ 40 parts of ceramic powder, 90 ~ 110 parts of deionized water.
2. ventilative and uvioresistant fabrics according to claim 1, it is characterised in that：The weft yarn group is by staple fibre
And/or natural fiber is made.
3. ventilative and uvioresistant fabrics according to claim 1, it is characterised in that：The heart yarn is by PEE system
Into the PEE is made up of polyester elastomer, and the polyester elastomer includes polybutylene terephthalate (PBT)
The hard segment of formation and the soft chain segment formed by polyoxyethylene glycol, the mass ratio of the hard segment and soft chain segment is 30：70~
70：30.
4. ventilative and uvioresistant fabrics according to claim 4, it is characterised in that：The polyester elastomer also includes
Metal salt as the organic sulfonic acid of copolymer composition.
5. ventilative and uvioresistant fabrics according to claim 1, it is characterised in that：The surface layer yarn is by polyester fiber system
Into.
6. ventilative and uvioresistant fabrics according to claim 1, it is characterised in that：The covering yarn SMIS yarn length and
Top layer yarn length ratio is 0.4 ~ 0.7.
A kind of 7. ventilative and uvioresistant fabrics manufacture method, it is characterised in that：Comprise the following steps,（1）It will be used to form
The polybutylene terephthalate (PBT) of hard segment and polyoxyethylene glycol for soft chain segment are put into reactor melting, by meltingization
Compound sprays polymer filaments by melt-blowing head, and monfil is made, and monfil is made into heart yarn,（2）By polyester
As surface layer yarn covering yarn is made, warp thread group uses the covering yarn, weft yarn by twisting process in heart yarn and surface layer yarn by fiber
Group uses conventional yarns,（3）Warp thread group and weft yarn group are interweaved fabric are made,（4）Fabric is impregnated in uvioresistant auxiliary agent,
Fabric is dried after the completion of dipping work,（5）Fabric is subjected to dyeing processing, dried fabric after the completion of dyeing processing,（6）Will
Fabric is impregnated in uvioresistant auxiliary agent again, carries out double-steeping, and after the completion of impregnating work, warp thread group and weft yarn group are dried
It is dry.
8. ventilative and uvioresistant fabrics manufacture method according to claim 7, it is characterised in that：The step（4）
Middle drying temperature is 170 ~ 180 DEG C.
9. ventilative and uvioresistant fabrics manufacture method according to claim 7, it is characterised in that：The step（5）
Middle drying temperature is 180 ~ 190 DEG C.
10. ventilative and uvioresistant fabrics manufacture method according to claim 7, it is characterised in that：The step（6）
Middle drying temperature is 150 ~ 160 DEG C.