CN108505347A - Breathable fabric - Google Patents
Breathable fabric Download PDFInfo
- Publication number
- CN108505347A CN108505347A CN201810378224.4A CN201810378224A CN108505347A CN 108505347 A CN108505347 A CN 108505347A CN 201810378224 A CN201810378224 A CN 201810378224A CN 108505347 A CN108505347 A CN 108505347A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- fabric
- breathable fabric
- titanate esters
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of breathable fabrics, are prepared using following methods:5 15 parts by weight fluorine carbon emulsions, 0.5 1.5 parts by weight of glycerin phosphates, 13 parts by weight trifluoro propyl methyl cyclotrisiloxane, 24 parts by weight titanate coupling agents, 10 20 parts by weight glycol dimercaptosuccinates, 10 20 parts by weight ethoxylated dodecyl alcohols, 0.3 0.9 parts by weight amido silicon oils are added to be uniformly mixed in 100 120 parts by weight water and obtain dressing liquid;Fabric is impregnated to 10 30min in dressing liquid, the fabric after dipping is subjected to mangle, pick-up is 60 80%, and drying obtains the breathable fabric.The breathable fabric of the present invention has good permeability, comfortable and easy to wear, and the surface modeling of the smooth smoothness of fabric, and can be properly bonded with human body, and good comfort effect is visually generated to people.
Description
Technical field
The present invention relates to a kind of fabrics, and in particular to a kind of breathable fabric.
Background technology
China is that maximum fabric clothing producing country, exported country and country of consumption, export amount account for world export trade in the world
It is more than easy a quarter.Textile fabric is related to the every aspect of people's life, and existing fabric cannot be satisfied the people increasingly
The material and cultural needs of growth.In particular, fabric permeability and bad in the prior art.Therefore, in terms of fabric, need into
The research and discovery of one step.
Invention content
For deficiencies of the prior art, the present invention adopts the following technical scheme that:
A kind of breathable fabric, is prepared using following methods:
S1, by 5-15 parts by weight fluorine carbon emulsion, 0.5-1.5 parts by weight of glycerin phosphate, 1-3 parts by weight trifluoro propyl methyl
Cyclotrisiloxane, 2-4 parts by weight titanate coupling agent, 10-20 parts by weight glycol dimercaptosuccinate, the 10-20 parts by weight moons
Cinnamic alcohol polyoxyethylene ether, 0.3-0.9 parts by weight amido silicon oils, which are added to be uniformly mixed in 100-120 parts by weight water, obtains dressing liquid;
S2, fabric in dressing liquid is impregnated into 10-30min, the fabric after dipping is subjected to mangle, pick-up 60-
80%, drying obtains breathable fabric.
The temperature of the dipping is 30-50 DEG C, and the mass ratio of the fabric and dressing liquid is 1:(5-15).
The temperature of the drying is 65-85 DEG C, time 3-9h.
The fabric is weaved by one or more in terylene, mulberry silk, spandex.The fabric grammes per square metre is 20-
120g/m2。
The titanate coupling agent is isopropyl three (dioctylphyrophosphoric acid acyloxy) titanate esters.
Further, the titanate coupling agent is three (dioctylphyrophosphoric acid acyloxy) titanate esters of modified isopropyl.
The preparation method of the modified isopropyl three (dioctylphyrophosphoric acid acyloxy) titanate esters is:By 120-130g isopropyls
Base three (dioctylphyrophosphoric acid acyloxy) titanate esters are warming up to 55-75 DEG C, and 0.05-0.2g p-hydroxyanisole, 0.003- is added
0.009g dibutyl tin laurates, it is 55-75 DEG C to keep temperature, and 5-15g methyl is added dropwise in the case where rotating speed is 200-500r/min
Temperature after being added dropwise, is risen to 95-105 DEG C, is with rotating speed by hydroxy-ethyl acrylate and 20-30g hydroxy propyl methacrylates
2-5h is reacted under 100-300r/min to get modified three (dioctylphyrophosphoric acid acyloxy) titanate esters of isopropyl.
Further, the preparation method of the modified isopropyl three (dioctylphyrophosphoric acid acyloxy) titanate esters is:It will
120-130g isopropyls three (dioctylphyrophosphoric acid acyloxy) titanate esters are warming up to 55-75 DEG C, and 0.05-0.2g para hydroxybenzenes are added
Methyl ether, 0.003-0.009g dibutyl tin laurates, it is 55-75 DEG C to keep temperature, is dripped in the case where rotating speed is 200-500r/min
Add 5-15g hydroxyethyl methacrylates and 20-30g hydroxy propyl methacrylates, after being added dropwise, 5-15g cerias be added,
Temperature is risen to 95-105 DEG C, is to react 2-5h under 100-300r/min to get modified three (dioctyl coke phosphorus of isopropyl with rotating speed
Sour acyloxy) titanate esters.
The rate of addition of the hydroxyethyl methacrylate is 0.01-0.05g/s.
The rate of addition of the hydroxy propyl methacrylate is 0.01-0.05g/s.
Still further preferably, to improve the anti-microbial property of fabric, the present invention also provides following technical proposals:
A kind of breathable fabric, is prepared using following methods:
S1, by 5-15 parts by weight fluorine carbon emulsion, 0.5-1.5 parts by weight of glycerin phosphate, 1-3 parts by weight trifluoro propyl methyl
Cyclotrisiloxane, 2-4 parts by weight titanate coupling agent, 10-20 parts by weight glycol dimercaptosuccinate, 1-3 parts by weight are antibacterial
Agent, 10-20 parts by weight ethoxylated dodecyl alcohol, 0.3-0.9 parts by weight amido silicon oils are added in 100-120 parts by weight water and mix
Uniformly obtain dressing liquid;
S2, fabric in dressing liquid is impregnated into 10-30min, the fabric after dipping is subjected to mangle, pick-up 60-
80%, drying obtains breathable fabric.
The temperature of the dipping is 30-50 DEG C, and the mass ratio of the fabric and dressing liquid is 1:(5-15).
The temperature of the drying is 65-85 DEG C, time 3-9h.
The bacteriostatic agent is oleic imidazolinone quaternary ammonium salt and/or 1- benzyl -1- aminoethyl -2- alkyl imidazoline in heptan quaternary ammoniums
Salt.Preferably, the bacteriostatic agent is by 60-70wt% oleic imidazolinones quaternary ammonium salt and 30-40wt%1- benzyl -1- aminoethyls -
2- alkyl imidazoline quaternary ammonium salts in heptan form.
The fabric is weaved by one or more in terylene, mulberry silk, spandex.The fabric grammes per square metre is 20-
120g/m2。
The titanate coupling agent is isopropyl three (dioctylphyrophosphoric acid acyloxy) titanate esters.
Further, the titanate coupling agent is three (dioctylphyrophosphoric acid acyloxy) titanate esters of modified isopropyl.
The preparation method of the modified isopropyl three (dioctylphyrophosphoric acid acyloxy) titanate esters is:By 120-130g isopropyls
Base three (dioctylphyrophosphoric acid acyloxy) titanate esters are warming up to 55-75 DEG C, and 0.05-0.2g p-hydroxyanisole, 0.003- is added
0.009g dibutyl tin laurates, it is 55-75 DEG C to keep temperature, and 5-15g methyl is added dropwise in the case where rotating speed is 200-500r/min
Hydroxy-ethyl acrylate and 20-30g hydroxy propyl methacrylates after being added dropwise, are added 5-15g cerias, temperature are risen to
95-105 DEG C, be that 2-5h is reacted under 100-300r/min to get modified isopropyl three (dioctylphyrophosphoric acid acyloxy) with rotating speed
Titanate esters.
The rate of addition of the hydroxyethyl methacrylate is 0.01-0.05g/s.
The rate of addition of the hydroxy propyl methacrylate is 0.01-0.05g/s.
The breathable fabric of the present invention has good permeability, comfortable and easy to wear, and the curved surface of the smooth smoothness of fabric is made
Type, and can be properly bonded with human body, good comfort effect is visually generated to people.
Specific implementation mode
Drapability is tested:It is carried out with reference to FZ/T 01045-1996, test equipment is carried using measuring appratus Co., Ltd of Wuhan state
The fabric Drape analyzer of the model YG811E of confession;Experiment before by antibacterial moisture-permeable shell fabric temperature be 20 DEG C, it is relatively wet
Damping 24 hours under conditions of degree is 65%.The drapability of fabric is an important indicator of wearability of fabric, is had good
The clothes of drapability can form the surface modeling of smooth smoothness, and can be properly bonded with human body, visual comfortable to people
Property.
Permeability detects:By standard GB/T/T5453-1997《The measurement of textile fabric gas permeability》It carries out,
Under the conditions of 1.3kPa in the analytical unit time (second) the penetrated air of every square metre of area amount (L/m2·s)。
Bacteriostasis property is tested:Reference《National Standard of the People's Republic of China GB15979-1995, disposable health are used
Product sanitary standard》, detect bacteriostasis property of the breathable fabric obtained to following microorganisms.The microorganism tested:Candida albicans
Bacterium (ATCC10231), Friedlander's bacillus (ATCC4352).By breathable fabric obtained, (every area is 70cm2) respectively
It is 253.7nm through wavelength, exposure intensity is 200 μ W/cm2After ultraviolet light 1.5min sterilizations, on every breathable fabric
Even coating Candida albicans 1.0 × 105CFU/ pieces, Friedlander's bacillus 1.0 × 105CFU/ pieces, effect are tested every after 30 minutes
Piece breathable fabric bacterial content.
Raw material introduction in embodiment:
Fluorine carbon emulsion is according to application No. is method systems shown in embodiment 1 in the Chinese patent of application number 201410771906.3
It is standby.
Glycerophosphate, No. CAS:57-03-4.
Trifluoro propyl methyl cyclotrisiloxane, No. CAS:2374-14-3.
Glycol dimercaptosuccinate, No. CAS:123-81-9.
The paper that oleic imidazolinone quaternary ammonium salt is delivered according to Wu Xiaonan《The synthesis of oleic imidazolinone quaternary ammonium salt and corrosion inhibition
Research》It is prepared by determining optimum process condition and method.
1- benzyl -1- aminoethyl -2- alkyl imidazoline quaternary ammonium salts in heptan are according to application No. is 200910305443.0 China
In patent prepared by method shown in specific implementation mode two.
Ethoxylated dodecyl alcohol is provided by Jiangsu Hai'an Petrochemical Plant, product specification L-3.
Isopropyl three (dioctylphyrophosphoric acid acyloxy) titanate esters, No. CAS:67691-13-8.
P-hydroxyanisole, No. CAS:150-76-5.
Dibutyl tin laurate, No. CAS:77-58-7.
Hydroxyethyl methacrylate, No. CAS:868-77-9.
Hydroxy propyl methacrylate, No. CAS:27813-02-1.
Ceria, No. CAS:1306-38-3, grain size 200nm.
The fabric is provided by Huzhou Yong Rui Textile Co., Ltd., and color is white, and ingredient is 100% mulberry silk, grammes per square metre
For 34g/m2。
Amido silicon oil is the amido silicon oil for the model JF-8060 that Jiashan Jiangnan textile material Co., Ltd provides.
Embodiment 1
A kind of preparation method of breathable fabric, includes the following steps:
S1, by 10 parts by weight fluorine carbon emulsions, 1 parts by weight of glycerin phosphate, 1.5 parts by weight trifluoro propyl methyl ring, three silica
Alkane, 3 parts by weight isopropyl three (dioctylphyrophosphoric acid acyloxy) titanate esters, 12 parts by weight glycol dimercaptosuccinates, 2 weight
Part oleic imidazolinone quaternary ammonium salt, 12 parts by weight ethoxylated dodecyl alcohols, 0.5 parts by weight amido silicon oil are added 110 parts by weight and go
It is uniformly mixed for 300r/min stirrings 20min with rotating speed in ionized water and obtains dressing liquid;
S2, fabric impregnates to 20min in dressing liquid, the temperature of the dipping is 40 DEG C, the fabric and dressing liquid
Mass ratio is 1:10, the fabric after dipping is subjected to mangle, pick-up 70wt% is dried 7h at being 70 DEG C in temperature, obtained
Breathable fabric.
Embodiment 2
A kind of preparation method of breathable fabric, includes the following steps:
S1, by 10 parts by weight fluorine carbon emulsions, 1 parts by weight of glycerin phosphate, 1.5 parts by weight trifluoro propyl methyl ring, three silica
Alkane, 3 part by weight modified isopropyl three (dioctylphyrophosphoric acid acyloxy) titanate esters, 12 parts by weight glycol dimercaptosuccinates, 2
110 weight are added in parts by weight oleic imidazolinone quaternary ammonium salt, 12 parts by weight ethoxylated dodecyl alcohols, 0.5 parts by weight amido silicon oil
It is uniformly mixed for 300r/min stirrings 20min with rotating speed in part deionized water and obtains dressing liquid;
S2, fabric impregnates to 20min in dressing liquid, the temperature of the dipping is 40 DEG C, the fabric and dressing liquid
Mass ratio is 1:10, the fabric after dipping is subjected to mangle, pick-up 70wt% is dried 7h at being 70 DEG C in temperature, obtained
Breathable fabric.
The preparation method of the modified isopropyl three (dioctylphyrophosphoric acid acyloxy) titanate esters is:By 125g isopropyls three
(dioctylphyrophosphoric acid acyloxy) titanate esters are warming up to 65 DEG C, and 0.1g p-hydroxyanisole, two fourth of 0.005g tin dilaurates is added
Ji Xi, it is 65 DEG C to keep temperature, and 10g hydroxyethyl methacrylates and 25g methacrylic acids is added dropwise in the case where rotating speed is 300r/min
The rate of addition of hydroxypropyl acrylate, the hydroxyethyl methacrylate is 0.02g/s, the rate of addition of the hydroxy propyl methacrylate
10g cerias are added after hydroxyethyl methacrylate and hydroxy propyl methacrylate are all added dropwise for 0.02g/s, it will
Temperature rises to 95 DEG C, is that 4h is reacted under 150r/min to get modified three (dioctylphyrophosphoric acid acyloxy) titanium of isopropyl with rotating speed
Acid esters.
Embodiment 3
A kind of preparation method of breathable fabric, includes the following steps:
S1, by 10 parts by weight fluorine carbon emulsions, 1 parts by weight of glycerin phosphate, 1.5 parts by weight trifluoro propyl methyl ring, three silica
Alkane, 3 part by weight modified isopropyl three (dioctylphyrophosphoric acid acyloxy) titanate esters, 12 parts by weight glycol dimercaptosuccinates, 2
110 weight are added in parts by weight oleic imidazolinone quaternary ammonium salt, 12 parts by weight ethoxylated dodecyl alcohols, 0.5 parts by weight amido silicon oil
It is uniformly mixed for 300r/min stirrings 20min with rotating speed in part deionized water and obtains dressing liquid;
S2, fabric impregnates to 20min in dressing liquid, the temperature of the dipping is 40 DEG C, the fabric and dressing liquid
Mass ratio is 1:10, the fabric after dipping is subjected to mangle, pick-up 70wt% is dried 7h at being 70 DEG C in temperature, obtained
Breathable fabric.
The preparation method of the modified isopropyl three (dioctylphyrophosphoric acid acyloxy) titanate esters is:By 125g isopropyls three
(dioctylphyrophosphoric acid acyloxy) titanate esters are warming up to 65 DEG C, and 0.1g p-hydroxyanisole, two fourth of 0.005g tin dilaurates is added
Ji Xi, it is 65 DEG C to keep temperature, and 10g hydroxyethyl methacrylates and 25g methacrylic acids is added dropwise in the case where rotating speed is 300r/min
The rate of addition of hydroxypropyl acrylate, the hydroxyethyl methacrylate is 0.02g/s, the rate of addition of the hydroxy propyl methacrylate
Temperature is risen to 95 DEG C after hydroxyethyl methacrylate and hydroxy propyl methacrylate are all added dropwise for 0.02g/s, with
Rotating speed is that 4h is reacted under 150r/min to get modified three (dioctylphyrophosphoric acid acyloxy) titanate esters of isopropyl.
Embodiment 4
A kind of preparation method of breathable fabric, includes the following steps:
S1, by 10 parts by weight fluorine carbon emulsions, 1 parts by weight of glycerin phosphate, 1.5 parts by weight trifluoro propyl methyl ring, three silica
Alkane, 3 part by weight modified isopropyl three (dioctylphyrophosphoric acid acyloxy) titanate esters, 12 parts by weight glycol dimercaptosuccinates, 2
Parts by weight 1- benzyl -1- aminoethyl -2- alkyl imidazoline quaternary ammonium salts in heptan, 12 parts by weight ethoxylated dodecyl alcohols, 0.5 parts by weight
Amido silicon oil, which is added in 110 parts by weight of deionized water to be uniformly mixed for 300r/min stirrings 20min with rotating speed, obtains dressing liquid;
S2, fabric impregnates to 20min in dressing liquid, the temperature of the dipping is 40 DEG C, the fabric and dressing liquid
Mass ratio is 1:10, the fabric after dipping is subjected to mangle, pick-up 70wt% is dried 7h at being 70 DEG C in temperature, obtained
Breathable fabric.
The preparation method of the modified isopropyl three (dioctylphyrophosphoric acid acyloxy) titanate esters is:By 125g isopropyls three
(dioctylphyrophosphoric acid acyloxy) titanate esters are warming up to 65 DEG C, and 0.1g p-hydroxyanisole, two fourth of 0.005g tin dilaurates is added
Ji Xi, it is 65 DEG C to keep temperature, and 10g hydroxyethyl methacrylates and 25g methacrylic acids is added dropwise in the case where rotating speed is 300r/min
The rate of addition of hydroxypropyl acrylate, the hydroxyethyl methacrylate is 0.02g/s, the rate of addition of the hydroxy propyl methacrylate
10g cerias are added after hydroxyethyl methacrylate and hydroxy propyl methacrylate are all added dropwise for 0.02g/s, it will
Temperature rises to 95 DEG C, is that 4h is reacted under 150r/min to get modified three (dioctylphyrophosphoric acid acyloxy) titanium of isopropyl with rotating speed
Acid esters.
Embodiment 5
A kind of preparation method of breathable fabric, includes the following steps:
S1, by 10 parts by weight fluorine carbon emulsions, 1 parts by weight of glycerin phosphate, 1.5 parts by weight trifluoro propyl methyl ring, three silica
Alkane, 3 parts by weight isopropyl three (dioctylphyrophosphoric acid acyloxy) titanate esters, 12 parts by weight glycol dimercaptosuccinates, 12 weights
It is 300r/min that amount part ethoxylated dodecyl alcohol, 0.5 parts by weight amido silicon oil, which are added in 110 parts by weight of deionized water with rotating speed,
Stirring 20min, which is uniformly mixed, obtains dressing liquid;
S2, fabric impregnates to 20min in dressing liquid, the temperature of the dipping is 40 DEG C, the fabric and dressing liquid
Mass ratio is 1:10, the fabric after dipping is subjected to mangle, pick-up 70wt% is dried 7h at being 70 DEG C in temperature, obtained
Breathable fabric.
Embodiment 6
A kind of preparation method of breathable fabric, includes the following steps:
S1, by 10 parts by weight fluorine carbon emulsions, 1 parts by weight of glycerin phosphate, 1.5 parts by weight trifluoro propyl methyl ring, three silica
Alkane, 3 part by weight modified isopropyl three (dioctylphyrophosphoric acid acyloxy) titanate esters, 12 parts by weight glycol dimercaptosuccinates,
12 parts by weight ethoxylated dodecyl alcohols, 0.5 parts by weight amido silicon oil are added in 110 parts by weight of deionized water is with rotating speed
300r/min stirrings 20min, which is uniformly mixed, obtains dressing liquid;
S2, fabric impregnates to 20min in dressing liquid, the temperature of the dipping is 40 DEG C, the fabric and dressing liquid
Mass ratio is 1:10, the fabric after dipping is subjected to mangle, pick-up 70wt% is dried 7h at being 70 DEG C in temperature, obtained
Breathable fabric.
The preparation method of the modified isopropyl three (dioctylphyrophosphoric acid acyloxy) titanate esters is:By 125g isopropyls three
(dioctylphyrophosphoric acid acyloxy) titanate esters are warming up to 65 DEG C, and 0.1g p-hydroxyanisole, two fourth of 0.005g tin dilaurates is added
Ji Xi, it is 65 DEG C to keep temperature, and 10g hydroxyethyl methacrylates and 25g methacrylic acids is added dropwise in the case where rotating speed is 300r/min
The rate of addition of hydroxypropyl acrylate, the hydroxyethyl methacrylate is 0.02g/s, the rate of addition of the hydroxy propyl methacrylate
Temperature is risen to 95 DEG C after hydroxyethyl methacrylate and hydroxy propyl methacrylate are all added dropwise for 0.02g/s, with
Rotating speed is that 4h is reacted under 150r/min to get modified three (dioctylphyrophosphoric acid acyloxy) titanate esters of isopropyl.
Embodiment 7
A kind of preparation method of breathable fabric, includes the following steps:
S1, by 10 parts by weight fluorine carbon emulsions, 1 parts by weight of glycerin phosphate, 1.5 parts by weight trifluoro propyl methyl ring, three silica
Alkane, 3 part by weight modified isopropyl three (dioctylphyrophosphoric acid acyloxy) titanate esters, 12 parts by weight glycol dimercaptosuccinates,
12 parts by weight ethoxylated dodecyl alcohols, 0.5 parts by weight amido silicon oil are added in 110 parts by weight of deionized water is with rotating speed
300r/min stirrings 20min, which is uniformly mixed, obtains dressing liquid;
S2, fabric impregnates to 20min in dressing liquid, the temperature of the dipping is 40 DEG C, the fabric and dressing liquid
Mass ratio is 1:10, the fabric after dipping is subjected to mangle, pick-up 70wt% is dried 7h at being 70 DEG C in temperature, obtained
Breathable fabric.
The preparation method of the modified isopropyl three (dioctylphyrophosphoric acid acyloxy) titanate esters is:By 125g isopropyls three
(dioctylphyrophosphoric acid acyloxy) titanate esters are warming up to 65 DEG C, and 0.1g p-hydroxyanisole, two fourth of 0.005g tin dilaurates is added
Ji Xi, it is 65 DEG C to keep temperature, and 10g hydroxyethyl methacrylates and 25g methacrylic acids is added dropwise in the case where rotating speed is 300r/min
The rate of addition of hydroxypropyl acrylate, the hydroxyethyl methacrylate is 0.02g/s, the rate of addition of the hydroxy propyl methacrylate
10g cerias are added after hydroxyethyl methacrylate and hydroxy propyl methacrylate are all added dropwise for 0.02g/s, it will
Temperature rises to 95 DEG C, is that 4h is reacted under 150r/min to get modified three (dioctylphyrophosphoric acid acyloxy) titanium of isopropyl with rotating speed
Acid esters.
Test case 1
Breathable fabric bacteriostasis property prepared by embodiment 1-4, permeability, draping property are tested.Specific test
It the results are shown in Table 1.
Table 1:Test result table
Breathable fabric permeability prepared by embodiment 5-7, draping property are tested.Specific test result is shown in Table 2.
Table 2:Test result table
Permeability (L/m2·s) | Suspended coefficient (%) | |
Embodiment 5 | 348 | 7.08 |
Embodiment 6 | 374 | 6.71 |
Embodiment 7 | 391 | 6.52 |
The breathable fabric of the present invention has good permeability, comfortable and easy to wear, and the curved surface of the smooth smoothness of fabric is made
Type, and can be properly bonded with human body, good comfort effect is visually generated to people.
Claims (4)
1. a kind of breathable fabric, is prepared using following methods:
S1, by 5-15 parts by weight fluorine carbon emulsion, 0.5-1.5 parts by weight of glycerin phosphate, 1-3 parts by weight trifluoro propyl methyl ring three
Siloxanes, 2-4 parts by weight titanate coupling agent, 10-20 parts by weight glycol dimercaptosuccinate, 10-20 parts by weight laruyl alcohols
Polyoxyethylene ether, 0.3-0.9 parts by weight amido silicon oils, which are added to be uniformly mixed in 100-120 parts by weight water, obtains dressing liquid;
S2, fabric in dressing liquid is impregnated into 10-30min, the fabric after dipping is subjected to mangle, pick-up 60-80% dries
It is dry, obtain the breathable fabric.
2. breathable fabric as described in claim 1, which is characterized in that the titanate coupling agent is three (dioctyl of isopropyl
Pyrophosphoric acid acyloxy) titanate esters.
3. breathable fabric as claimed in claim 2, which is characterized in that the titanate coupling agent is modified isopropyl three (two
Octyl pyrophosphoric acid acyloxy) titanate esters.
4. breathable fabric as claimed in claim 3, which is characterized in that three (dioctylphyrophosphoric acid acyl-oxygen of the modified isopropyl
Base) titanate esters are prepared using following methods:By 120-130g isopropyls three (dioctylphyrophosphoric acid acyloxy) titanate esters liter
0.05-0.2g p-hydroxyanisole, 0.003-0.009g dibutyl tin laurates is added to 55-75 DEG C in temperature, and holding temperature is
55-75 DEG C, 5-15g hydroxyethyl methacrylates and 20-30g methacrylic acid hydroxypropyls is added dropwise in the case where rotating speed is 200-500r/min
Temperature after being added dropwise, is risen to 95-105 DEG C by ester, is that 2-5h is reacted under 100-300r/min to get modified isopropyl with rotating speed
Base three (dioctylphyrophosphoric acid acyloxy) titanate esters.