CN107573884A - 一种耐沸水双组份水性拼板胶 - Google Patents

一种耐沸水双组份水性拼板胶 Download PDF

Info

Publication number
CN107573884A
CN107573884A CN201710880811.9A CN201710880811A CN107573884A CN 107573884 A CN107573884 A CN 107573884A CN 201710880811 A CN201710880811 A CN 201710880811A CN 107573884 A CN107573884 A CN 107573884A
Authority
CN
China
Prior art keywords
parts
double
resistance
splicing adhesive
boiling water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710880811.9A
Other languages
English (en)
Inventor
邓卫
刘露
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kang Fei Adhesive Technology (guangdong) Co Ltd
Original Assignee
Kang Fei Adhesive Technology (guangdong) Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kang Fei Adhesive Technology (guangdong) Co Ltd filed Critical Kang Fei Adhesive Technology (guangdong) Co Ltd
Priority to CN201710880811.9A priority Critical patent/CN107573884A/zh
Publication of CN107573884A publication Critical patent/CN107573884A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐沸水双组份水性拼板胶。该拼板胶包括主剂和固化剂，其中主剂由以下质量份的原料组成：100～110份苯丙乳液，200～210份环氧树脂乳液，300～310份碳酸钙，235～245份聚乙烯醇水溶液，0.5～1.5份分散剂，0.5～1.5份润湿剂，0.2～1份消泡剂，0.2～1份防腐剂，130～150份水；固化剂为异氰酸酯固化剂。本发明的拼板胶加入了水性环氧树脂乳液，剪切强度更大，增加了15％，耐水较传统更好。

Description

一种耐沸水双组份水性拼板胶
技术领域
本发明涉及一种耐沸水双组份水性拼板胶。
背景技术
拼板胶是指用于拼接集成材等木制品的粘合剂，适合用于非结构材及结构材用集成材等的拼板粘合。双组份拼板胶是针对木材材质特性，吸、失水变形大的特点研发而成，能良好渗透入木质，胶水成膜极佳，内聚力强，特别是能与木材纤维所具有的特征反应基团形成良好的化学键，解决木材拼板易开裂的难题。
目前传统的拼板胶配方都是由约50％的丙烯酸乳液、聚乙烯醇水溶液和碳酸钙粉等制备而成。拼板胶的剪切强度以及耐水性能仍有待进一步的提高，从而满足市场的需求。
发明内容
本发明的目的在于提供一种耐沸水双组份水性拼板胶。
本发明所采取的技术方案是：
一种耐沸水双组份水性拼板胶，包括主剂和固化剂，其中主剂由以下质量份的原料组成：100～110份苯丙乳液，200～210份环氧树脂乳液，300～310份碳酸钙，235～245份聚乙烯醇水溶液，0.5～1.5份分散剂，0.5～1.5份润湿剂，0.2～1份消泡剂，0.2～1份防腐剂，130～150份水；固化剂为异氰酸酯固化剂。
优选的，一种耐沸水双组份水性拼板胶，包括主剂和固化剂，其中主剂由以下质量份的原料组成：106份苯丙乳液，205份环氧树脂乳液，305份碳酸钙，240份聚乙烯醇水溶液，1份分散剂，1份润湿剂，0.5份消泡剂，0.5份防腐剂，141份水；固化剂为异氰酸酯固化剂。
苯丙乳液的固含量为 55wt％～65wt％。
环氧树脂乳液的固含量为 40wt％～55wt％。
聚乙烯醇水溶液中聚乙烯醇的质量浓度为 20～30％。
分散剂为丙烯酸均聚物钠盐分散剂。
润湿剂为琥珀酸酯磺酸盐润湿剂。
消泡剂为有机硅消泡剂。
防腐剂为异噻唑啉酮类防腐剂。
拼板胶的主剂和固化剂的质量比为100：(10～15)。
本发明的有益效果是：
本发明的拼板胶加入了水性环氧树脂乳液，剪切强度更大，增加了15％，耐水较传统更好。
具体实施方式
一种耐沸水双组份水性拼板胶，包括主剂和固化剂，其中主剂由以下质量份的原料组成：100～110份苯丙乳液，200～210份环氧树脂乳液，300～310份碳酸钙，235～245份聚乙烯醇水溶液，0.5～1.5份分散剂，0.5～1.5份润湿剂，0.2～1份消泡剂，0.2～1份防腐剂，130～150份水；固化剂为异氰酸酯固化剂。
优选的，一种耐沸水双组份水性拼板胶，包括主剂和固化剂，其中主剂由以下质量份的原料组成：106份苯丙乳液，205份环氧树脂乳液，305份碳酸钙，240份聚乙烯醇水溶液，1份分散剂，1份润湿剂，0.5份消泡剂，0.5份防腐剂，141份水；固化剂为异氰酸酯固化剂。
优选的，苯丙乳液的固含量为55wt％～65wt％；进一步优选的，苯丙乳液为上海必荣化学的ENCOR 446。
优选的，环氧树脂乳液的固含量为40wt％～55wt％；进一步优选的，环氧树脂乳液为广州东风化工的水性环氧乳液WE44。
优选的，碳酸钙为轻质碳酸钙。
优选的，聚乙烯醇水溶液中聚乙烯醇的质量浓度为20～30％；进一步优选的，聚乙烯醇水溶液中聚乙烯醇的质量浓度为25％。
优选的，分散剂为丙烯酸均聚物钠盐分散剂；进一步优选的，分散剂为汽巴的分散剂N-40。
优选的，润湿剂为琥珀酸酯磺酸盐润湿剂；进一步优选的，润湿剂为二辛基磺基琥珀磺酸钠盐润湿剂；再进一步优选的，润湿剂为亨斯迈的Surfonic DOS 75。
优选的，消泡剂为有机硅消泡剂；进一步优选的，消泡剂为毕克化学的消泡剂BYK-024。
优选的，防腐剂为异噻唑啉酮类防腐剂；进一步优选的，防腐剂为陶氏LXE防腐剂。
优选的，拼板胶主剂和固化剂的质量比为100：(10～15)；进一步优选的，拼板胶主剂和固化剂的质量比为100:12。
所述双组份水性拼板胶中主剂和固化剂的应用方法为本领域的常规方法。
以下通过具体的实施例对本发明的内容作进一步详细的说明。
实施例1：
实施例1的拼板胶主剂各原料组成如表1所示。
表1实施例1拼板胶主剂
原料 质量份
苯丙乳液 106
环氧树脂乳液 205
分散剂 1
润湿剂 1
消泡剂 0.5
碳酸钙 305
聚乙烯醇水溶液 240
防腐剂 0.5
水 141
实施例1中，苯丙乳液为上海必荣化学的ENCOR 446；环氧树脂乳液为广州东风化工的水性环氧乳液WE44；聚乙烯醇水溶液为25wt％的聚乙烯醇水溶液；分散剂为汽巴的分散剂N-40；润湿剂为亨斯迈的Surfonic DOS 75；消泡剂为毕克化学的消泡剂BYK-024，碳酸钙为轻质碳酸钙；防腐剂为陶氏LXE防腐剂。
本发明的拼板胶主剂的制备方法为按比例称取各种原料，混合搅拌后即可。使用时，将主剂和异氰酸酯固化剂混合使用，主剂与异氰酸酯固化剂的配比为100：(10～15)。异氰酸酯固化剂为本领域的常见原料，双组份的混合使用方法为本领域的常规方法。
将实施例1的主剂与异氰酸酯固化剂按质量比100:12使用，制成的拼板胶进行耐沸水测试(100℃，4h)，其拉伸剪切强度为2.3Mpa，而同等条件下市售产品为2Mpa，本发明的拼板胶其剪切强度比现有的增加了15％。

Claims (10)

1.一种耐沸水双组份水性拼板胶，其特征在于：包括主剂和固化剂，其中主剂由以下质量份的原料组成：100～110份苯丙乳液，200～210份环氧树脂乳液，300～310份碳酸钙，235～245份聚乙烯醇水溶液，0.5～1.5份分散剂，0.5～1.5份润湿剂，0.2～1份消泡剂，0.2～1份防腐剂，130～150份水；固化剂为异氰酸酯固化剂。
2.根据权利要求1所述的一种耐沸水双组份水性拼板胶，其特征在于：包括主剂和固化剂，其中主剂由以下质量份的原料组成：106份苯丙乳液，205份环氧树脂乳液，305份碳酸钙，240份聚乙烯醇水溶液，1份分散剂，1份润湿剂，0.5份消泡剂，0.5份防腐剂，141份水；固化剂为异氰酸酯固化剂。
3.根据权利要求1或2所述的一种耐沸水双组份水性拼板胶，其特征在于：苯丙乳液的固含量为55wt％～65wt％。
4.根据权利要求1或2所述的一种耐沸水双组份水性拼板胶，其特征在于：环氧树脂乳液的固含量为40wt％～55wt％。
5.根据权利要求1或2所述的一种耐沸水双组份水性拼板胶，其特征在于：聚乙烯醇水溶液中聚乙烯醇的质量浓度为20～30％。
6.根据权利要求1或2所述的一种耐沸水双组份水性拼板胶，其特征在于：分散剂为丙烯酸均聚物钠盐分散剂。
7.根据权利要求1或2所述的一种耐沸水双组份水性拼板胶，其特征在于：润湿剂为琥珀酸酯磺酸盐润湿剂。
8.根据权利要求1或2所述的一种耐沸水双组份水性拼板胶，其特征在于：消泡剂为有机硅消泡剂。
9.根据权利要求1或2所述的一种耐沸水双组份水性拼板胶，其特征在于：防腐剂为异噻唑啉酮类防腐剂。
10.根据权利要求1或2所述的一种耐沸水双组份水性拼板胶，其特征在于：拼板胶的主剂和固化剂的质量比为100：(10～15)。
CN201710880811.9A 2017-09-26 2017-09-26 一种耐沸水双组份水性拼板胶 Pending CN107573884A (zh)