CN107572989A - A kind of environment-friendly type revetment brick composition of raw materials - Google Patents
A kind of environment-friendly type revetment brick composition of raw materials Download PDFInfo
- Publication number
- CN107572989A CN107572989A CN201710719032.0A CN201710719032A CN107572989A CN 107572989 A CN107572989 A CN 107572989A CN 201710719032 A CN201710719032 A CN 201710719032A CN 107572989 A CN107572989 A CN 107572989A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw materials
- slag
- environment
- revetment brick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of environment-friendly type revetment brick composition of raw materials, is made from the following raw materials in parts by weight：100~150 parts of calcium oxide particle, 500~600 parts of sand, 60~70 parts of Portland clinker, 15~25 parts of carbide slag, 40~50 parts of gypsum, 5~15 parts of fine sand, 6~8 parts of slag, 10~20 parts of cellulose ether, 10~20 parts of magnesium chloride, 10~30 parts of lime-ash, 10~30 parts of bath stone, 12~15 parts of manganese slag.Instant invention overcomes the deficiencies in the prior art, and scientific formulation is reasonable, effectively improve the stability of revetment brick, reduce revetment brick manufacturing cost, while manufacture cement using discarded object, improve the ecological environment, no pollution, and the scope of application is wide.
Description
Technical field
The present invention relates to revetment brick technical field, particularly belongs to a kind of environment-friendly type revetment brick composition of raw materials.
Background technology
The mankind cause different degrees of destruction to natural environment while nature remodeling carries out infrastructure construction, special
It is not the implementation with the development continuously and healthily of China's economy and the strategy of sustainable development over nearly more than 20 years, country is special to various regions
It is the input that west area increases the builds to foundation engineering such as water conservancy, highway, railway, the implementation of these builds to foundation engineering, companion
With there is substantial amounts of construction and excavation, substantial amounts of exposed soil-slope and rock slope are caused, original landforms is changed and answers
Power state so that the stability of some side slopes is changed, and original ecosystem is destroyed, and result in serious water and soil
It is lost in and environmental ecology unbalance.In order to ensure the stabilization of side slope and protecting ecology bad border, people employ various
Method, generally speaking, side slope protection experienced the process from pure project post-evaluation to ecological revetment.
The sustainable development of ecological environmental protection relation economic society, the development of relation people's lives and descendants, close
Based environment protects the development of cause.During the nearly last ten years, ecological environmental protection causes the extensive concern of people, the Party Central Committee, state affairs
Institute takes a series of vital measures, constantly strengthens ecological protection.
The content of the invention
It is an object of the invention to provide a kind of environment-friendly type revetment brick composition of raw materials, the deficiencies in the prior art are overcome, are matched somebody with somebody
Side is scientific and reasonable, effectively improves the stability of revetment brick, reduces revetment brick manufacturing cost, while utilize discarded object manufacture water
Mud, improve the ecological environment, no pollution, the scope of application is wide.
To solve the above problems, the technical solution used in the present invention is as follows：
A kind of environment-friendly type revetment brick composition of raw materials, is made from the following raw materials in parts by weight：100~150 parts of calcium oxide particle, sand
500~600 parts, 60~70 parts of Portland clinker, 15~25 parts of carbide slag, 40~50 parts of gypsum, 5~15 parts of fine sand, ore deposit
6~8 parts of slag, 10~20 parts of cellulose ether, 10~20 parts of magnesium chloride, 10~30 parts of lime-ash, 10~30 parts of bath stone, manganese slag 12~15
Part.
Further, described environment-friendly type revetment brick composition of raw materials is made from the following raw materials in parts by weight：Calcium oxide particle 123
Part, 550 parts of sand, 65 parts of Portland clinker, 20 parts of carbide slag, 45 parts of gypsum, 10 parts of fine sand, 7 parts of slag, cellulose ether
17 parts, 14 parts of magnesium chloride, 19 parts of lime-ash, 22 parts of bath stone, 13 parts of manganese slag.
Further, described environment-friendly type revetment brick composition of raw materials is made from the following raw materials in parts by weight：Calcium oxide particle 118
Part, 560 parts of sand, 68 parts of Portland clinker, 20 parts of carbide slag, 44 parts of gypsum, 10 parts of fine sand, 7 parts of slag, cellulose ether
14 parts, 14 parts of magnesium chloride, 20 parts of lime-ash, 20 parts of bath stone, 14 parts of manganese slag.
Compared with prior art, implementation result of the invention is as follows by the present invention：
A kind of environment-friendly type revetment brick composition of raw materials of the present invention, scientific formulation is reasonable, effectively improves the stability of revetment brick, drop
Low revetment brick manufacturing cost, while using discarded object manufacture cement, improve the ecological environment, no pollution, the scope of application are wide.
Embodiment
With reference to embodiment, the invention will be further described, but the present invention is not limited only to these examples, to be de-
On the premise of from present inventive concept, carried out by it is any improvement be within the scope of the present invention.
Embodiment 1
A kind of environment-friendly type revetment brick composition of raw materials of the present invention, is made from the following raw materials in parts by weight：Calcium oxide particle 100
~150 parts, 500~600 parts of sand, 60~70 parts of Portland clinker, 15~25 parts of carbide slag is 40~50 parts of gypsum, thin
Husky 5~15 parts, 6~8 parts of slag, 10~20 parts of cellulose ether, 10~20 parts of magnesium chloride, 10~30 parts of lime-ash, bath stone 10~30
Part, 12~15 parts of manganese slag.
Embodiment 2
A kind of environment-friendly type revetment brick composition of raw materials of the present invention, is made from the following raw materials in parts by weight：Calcium oxide particle 123
Part, 550 parts of sand, 65 parts of Portland clinker, 20 parts of carbide slag, 45 parts of gypsum, 10 parts of fine sand, 7 parts of slag, cellulose ether
17 parts, 14 parts of magnesium chloride, 19 parts of lime-ash, 22 parts of bath stone, 13 parts of manganese slag.
Embodiment 3
A kind of environment-friendly type revetment brick composition of raw materials of the present invention, is made from the following raw materials in parts by weight：Calcium oxide particle 118
Part, 560 parts of sand, 68 parts of Portland clinker, 20 parts of carbide slag, 44 parts of gypsum, 10 parts of fine sand, 7 parts of slag, cellulose ether
14 parts, 14 parts of magnesium chloride, 20 parts of lime-ash, 20 parts of bath stone, 14 parts of manganese slag.
Claims (3)
- A kind of 1. environment-friendly type revetment brick composition of raw materials, it is characterised in that：It is made from the following raw materials in parts by weight：Calcium oxide particle 100~150 parts, 500~600 parts of sand, 60~70 parts of Portland clinker, 15~25 parts of carbide slag, 40~50 parts of gypsum, 5~15 parts of fine sand, 6~8 parts of slag, 10~20 parts of cellulose ether, 10~20 parts of magnesium chloride, 10~30 parts of lime-ash, bath stone 10~ 30 parts, 12~15 parts of manganese slag.
- A kind of 2. environment-friendly type revetment brick composition of raw materials according to claim 1, it is characterised in that：Described environment-friendly type bank protection Brick composition of raw materials is made from the following raw materials in parts by weight：123 parts of calcium oxide particle, 550 parts of sand, Portland clinker 65 Part, 20 parts of carbide slag, 45 parts of gypsum, 10 parts of fine sand, 7 parts of slag, 17 parts of cellulose ether, 14 parts of magnesium chloride, 19 parts of lime-ash, bath stone 22 parts, 13 parts of manganese slag.
- A kind of 3. environment-friendly type revetment brick composition of raw materials according to claim 1, it is characterised in that：Described environment-friendly type bank protection Brick composition of raw materials is made from the following raw materials in parts by weight：118 parts of calcium oxide particle, 560 parts of sand, Portland clinker 68 Part, 20 parts of carbide slag, 44 parts of gypsum, 10 parts of fine sand, 7 parts of slag, 14 parts of cellulose ether, 14 parts of magnesium chloride, 20 parts of lime-ash, bath stone 20 parts, 14 parts of manganese slag.