CN106348687A - Environment-friendly masonry cement - Google Patents
Environment-friendly masonry cement Download PDFInfo
- Publication number
- CN106348687A CN106348687A CN201610721979.0A CN201610721979A CN106348687A CN 106348687 A CN106348687 A CN 106348687A CN 201610721979 A CN201610721979 A CN 201610721979A CN 106348687 A CN106348687 A CN 106348687A
- Authority
- CN
- China
- Prior art keywords
- parts
- slag
- cement
- environment
- clinker
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environment-friendly masonry cement which is prepared from the following raw materials in parts by weight: 50-80 parts of Portland cement clinker, 10-30 parts of carbide slag, 10-30 parts of gypsum, 5-15 parts of fine sand, 5-15 parts of polypropylene fiber, 5-10 parts of mine slag, 10-20 parts of cellulose ether, 1-10 parts of 27.5% oxydol, 10-20 parts of magnesium chloride, 10-30 parts of clinker, 10-30 parts of smectite and 12-15 parts of manganese slag. The cement prepared by using industrial wastes has scientific and reasonable formula, effectively enhances the stability of the cement clinker, and has lower manufacturing cost. The wastes are utilized to prepare the cement, thereby improving the ecological environment and conforming to the environmental protection concept.
Description
Technical field
The present invention relates to building material technical field, particularly to a kind of environment-friendly type masonry cement formula.
Background technology
Cement, powdery hydraulicity inorganic coagulation material.Add water and become slurry after stirring, can harden in atmosphere or in water
Preferably harden, and can be cemented together securely for the materials such as sand, stone.Before the history of cement can trace back to 5000 earliest
Chinese Qin'an the earth people from gulf, they laid similar modern times cement ground.The stone that roman uses under construction later
Ash and the mixture of volcanic ash, this mixture is much like with modern lime pozzolanic cement.Made with its cementing rubble
Concrete, after hardening, not only intensity is higher, and can also resist the erosion of fresh water or brackish water.For a long time, it is as one kind
Important Binder Materials, are widely used in the engineerings such as civil construction, water conservancy, national defence.
The accelerated development in city brings white elephant to environment, and the consumption of cement is increasing, and factory is a lot,
For energy saving, develop a kind of there is good stability there is the cement gesture of premium properties must using what waste produced
OK.
Content of the invention
For solving problems of the prior art, the invention provides a kind of environment-friendly type by the use of waste as raw material is built
Build cement formula.
The purpose of the present invention to implement by the following technical programs:
A kind of environment-friendly type masonry cement formula, is made up of the raw material of following weight portion: Portland clinker 50-80 part, carbide
Slag 10-30 part, Gypsum Fibrosum 10-30 part, fine sand 5-15 part, polypropylene fibre 5-15 part, slag 5-10 part, cellulose ether 10-20 part,
27.5% hydrogen peroxide 1-10 part, magnesium chloride 10-20 part, lime-ash 10-30 part, bath stone 10-30 part, manganese slag 12-15 part.
Further, it is made up of the raw material of following weight portion: 60 parts of Portland clinker, 20 parts of carbide slag, Gypsum Fibrosum 20
Part, 10 parts of fine sand, 10 parts of polypropylene fibre, 8 parts of slag, 15 parts of cellulose ether, 27.5% 5 parts of hydrogen peroxide, 15 parts of magnesium chloride,
20 parts of lime-ash, 20 parts of bath stone, 13 parts of manganese slag.
Beneficial effect:
The invention provides the cement that a kind of utilization industrial waste material manufactures, scientific formulation rationally, effectively improves clinker
Stability, reduce cement manufacturing cost, simultaneously utilize garbage manufacture cement, improve the ecological environment, meet environmental protection concept.
Specific embodiment
Embodiment 1:
A kind of environment-friendly type masonry cement formula, is made up of the raw material of following weight portion: 50 parts of Portland clinker, carbide slag 10
Part, 10 parts of Gypsum Fibrosum, 5 parts of fine sand, 5 parts of polypropylene fibre, 5 parts of slag, 10 parts of cellulose ether, 27.5% 1 part of hydrogen peroxide, chlorination
10 parts of magnesium, 10 parts of lime-ash, 10 parts of bath stone, 12 parts of manganese slag.
Embodiment 2:
A kind of environment-friendly type masonry cement formula, is made up of the raw material of following weight portion: 80 parts of Portland clinker, carbide slag 30
Part, 30 parts of Gypsum Fibrosum, 15 parts of fine sand, 15 parts of polypropylene fibre, 10 parts of slag, 20 parts of cellulose ether, 27.5% 10 parts of hydrogen peroxide,
20 parts of magnesium chloride, 30 parts of lime-ash, 30 parts of bath stone, 15 parts of manganese slag.
Embodiment 3:
A kind of environment-friendly type masonry cement formula, is made up of the raw material of following weight portion: 60 parts of Portland clinker, carbide slag 20
Part, 20 parts of Gypsum Fibrosum, 10 parts of fine sand, 10 parts of polypropylene fibre, 8 parts of slag, 15 parts of cellulose ether, 27.5% 5 parts of hydrogen peroxide, chlorine
Change 15 parts of magnesium, 20 parts of lime-ash, 20 parts of bath stone, 13 parts of manganese slag.
Finally it is noted that the foregoing is only the preferred embodiments of the present invention, it is not limited to the present invention,
Although being described in detail to the present invention with reference to the foregoing embodiments, for a person skilled in the art, it still may be used
To modify to the technical scheme described in foregoing embodiments, or equivalent is carried out to wherein some technical characteristics.
All any modification, equivalent substitution and improvement within the spirit and principles in the present invention, made etc., should be included in the present invention's
Within protection domain.
Claims (2)
1. a kind of environment-friendly type masonry cement formula it is characterised in that: be made up of the raw material of following weight portion: Portland clinker
50-80 part, carbide slag 10-30 part, Gypsum Fibrosum 10-30 part, fine sand 5-15 part, polypropylene fibre 5-15 part, slag 5-10 part, fiber
Plain ether 10-20 part, 27.5% hydrogen peroxide 1-10 part, magnesium chloride 10-20 part, lime-ash 10-30 part, bath stone 10-30 part, manganese slag 12-
15 parts.
2. a kind of environment-friendly type masonry cement formula according to claim 1 it is characterised in that: by the raw material of following weight portion
Composition: 60 parts of Portland clinker, 20 parts of carbide slag, 20 parts of Gypsum Fibrosum, 10 parts of fine sand, 10 parts of polypropylene fibre, 8 parts of slag,
15 parts of cellulose ether, 27.5% 5 parts of hydrogen peroxide, 15 parts of magnesium chloride, 20 parts of lime-ash, 20 parts of bath stone, 13 parts of manganese slag.