CN107572818A - A kind of glaze - Google Patents
A kind of glaze Download PDFInfo
- Publication number
- CN107572818A CN107572818A CN201711080480.7A CN201711080480A CN107572818A CN 107572818 A CN107572818 A CN 107572818A CN 201711080480 A CN201711080480 A CN 201711080480A CN 107572818 A CN107572818 A CN 107572818A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- frit
- raw material
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention belongs to porcelain field, and in particular to a kind of glaze, be made up of the raw material of following parts by weight：10 15 parts of calcite, 10 15 parts of plant ash, 15 parts of cupric oxide, 5 10 parts of Suzhou soil, 5 10 parts of Copper Ores, 10 15 parts of silica flour, 10 15 parts of frit；The frit is made up of the raw material of following parts by weight：Including 15 parts of quartz sand, 20 25 parts of albite in powder, 10 15 parts of calcium carbonate, 10 15 parts of barium carbonate, 15 parts of zinc oxide, 5 10 parts of boric acid, glaze paint glossiness of the present invention is good, and color dot decorative effect significantly improves, glaze-body bonding is good, and water absorption rate is low, High anti bending strength, and heat endurance is high.
Description
Technical field
The invention belongs to porcelain field, and in particular to a kind of glaze.
Background technology
Glaze is one layer of glassy silicate thin layer of ceramic and enamel tool face, and glaze performance directly affects
The quality of porcelain, therefore how to produce one kind and be combined with base substrate, the glaze of excellent physical properties just seems particularly significant.
The content of the invention
The defects of based on prior art, it is an object of the invention to provide a kind of glaze.
In order to achieve the above object, the present invention uses following technical scheme：A kind of glaze, by the raw material group of following parts by weight
Into：Calcite 10-15 parts, plant ash 10-15 parts, cupric oxide 1-5 parts, Suzhou soil 5-10 parts, Copper Ores 5-10 parts, silica flour
10-15 parts, frit 10-15 parts；
The frit is made up of the raw material of following parts by weight：Including quartz sand 1-5 parts, albite in powder 20-25 parts, calcium carbonate 10-
15 parts, barium carbonate 10-15 parts, zinc oxide 1-5 parts, boric acid 5-10 parts.
Glaze paint glossiness of the present invention is good, and color dot decorative effect significantly improves, and glaze-body bonding is good, and water absorption rate is low, and anti-folding is strong
Degree is high, and heat endurance is high, and albite melting temperature is low in frit, and fluxing capabilities are strong, and the melt transparency formed is good, Suzhou soil
Calcium carbonate can make the suspension that glaze slip has had, and strengthen the adhesive capacity of glaze and base, zinc oxide and can both make fluxing agent, can increase again
Glaze paint gloss, appropriate BaCO3 is added, can significantly improve glaze quality.
Embodiment
The present invention is described in further details below by embodiment, embodiment is only used for illustrating the present invention, and unlimited
The scope of the present invention processed.
Embodiment 1：A kind of glaze, it is made up of the raw material of following parts by weight：10 parts of calcite, 10 parts of plant ash, cupric oxide 1
Part, 5 parts of Suzhou soil, 5 parts of Copper Ores, 10 parts of silica flour, 10 parts of frit；
The frit is made up of the raw material of following parts by weight：Including 1 part of quartz sand, 20 parts of albite in powder, 10 parts of calcium carbonate, carbonic acid
10 parts of barium, 1 part of zinc oxide, 5 parts of boric acid.
The preparation technology flow of frit:The raw material that the above-mentioned parts by weight of frit will be formed mixes by dispensing, mixing
Raw material enters is melt into glass metal in 1500~1550 DEG C in fused block furnace, water quenching, ground 100 mesh sieve after drying, and white is made
Glass frit powder.
The raw material of above-mentioned parts by weight is entered into ball mill and wears into glaze slip wherein, expect: ball: water=1: 1.5: 0.6, in ball milling outside
Add sodium tripolyphosphate 0.3%, CMC0.1%, after formulation material goes out mill, its glaze fineness is 300 mesh screen residue 0.15-0.2%, and glaze slip is close
Spend for 1.48g/ml.
Embodiment 2：A kind of glaze, it is characterised in that be made up of the raw material of following parts by weight：12 parts of calcite, plant ash
11 parts, 3 parts of cupric oxide, 8 parts of Suzhou soil, 8 parts of Copper Ores, 12 parts of silica flour, 12 parts of frit；
The frit is made up of the raw material of following parts by weight：Including 3 parts of quartz sand, 22 parts of albite in powder, 12 parts of calcium carbonate, carbonic acid
12 parts of barium, 3 parts of zinc oxide, 8 parts of boric acid.
The preparation technology flow of frit:The raw material that the above-mentioned parts by weight of frit will be formed mixes by dispensing, mixing
Raw material enters is melt into glass metal in 1500~1550 DEG C in fused block furnace, water quenching, ground 100 mesh sieve after drying, and white is made
Glass frit powder.
The raw material of above-mentioned parts by weight is entered into ball mill and wears into glaze slip wherein, expect: ball: water=1: 1.5: 0.6, in ball milling outside
Add sodium tripolyphosphate 0.3%, CMC0.1%, after formulation material goes out mill, its glaze fineness is 300 mesh screen residue 0.15-0.2%, and glaze slip is close
Spend for 1.48g/ml.
Embodiment 3：A kind of glaze, it is characterised in that be made up of the raw material of following parts by weight：Calcite 10-15 parts, vegetation
15 parts of ash, 5 parts of cupric oxide, 10 parts of Suzhou soil, 10 parts of Copper Ores, 15 parts of silica flour, 15 parts of frit；
The frit is made up of the raw material of following parts by weight：Including 5 parts of quartz sand, 25 parts of albite in powder, 15 parts of calcium carbonate, carbonic acid
15 parts of barium, 5 parts of zinc oxide, 10 parts of boric acid.
The preparation technology flow of frit:The raw material that the above-mentioned parts by weight of frit will be formed mixes by dispensing, mixing
Raw material enters is melt into glass metal in 1500~1550 DEG C in fused block furnace, water quenching, ground 100 mesh sieve after drying, and white is made
Glass frit powder.
The raw material of above-mentioned parts by weight is entered into ball mill and wears into glaze slip wherein, expect: ball: water=1: 1.5: 0.6, in ball milling outside
Add sodium tripolyphosphate 0.3%, CMC0.1%, after formulation material goes out mill, its glaze fineness is 300 mesh screen residue 0.15-0.2%, and glaze slip is close
Spend for 1.48g/ml.
Claims (1)
1. a kind of glaze, it is characterised in that be made up of the raw material of following parts by weight：Calcite 10-15 parts, plant ash 10-15
Part, cupric oxide 1-5 parts, Suzhou soil 5-10 parts, Copper Ores 5-10 parts, silica flour 10-15 parts, frit 10-15 parts；
The frit is made up of the raw material of following parts by weight：Including quartz sand 1-5 parts, albite in powder 20-25 parts, calcium carbonate 10-
15 parts, barium carbonate 10-15 parts, zinc oxide 1-5 parts, boric acid 5-10 parts.