CN107554975A - 新型农药软塑组合包装材料及其制备方法 - Google Patents
新型农药软塑组合包装材料及其制备方法 Download PDFInfo
- Publication number
- CN107554975A CN107554975A CN201710907534.6A CN201710907534A CN107554975A CN 107554975 A CN107554975 A CN 107554975A CN 201710907534 A CN201710907534 A CN 201710907534A CN 107554975 A CN107554975 A CN 107554975A
- Authority
- CN
- China
- Prior art keywords
- parts
- packaging material
- polypropylene film
- soft modeling
- novel agrochemical
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种新型农药软塑组合包装材料及其制备方法,包括聚丙烯膜层,所述聚丙烯膜层下设有油墨层,所述油墨层下设有复合层,所述复合层由以重量份计的如下材料组成:聚乙烯20‑30份,聚丙烯20‑30份,氯磺化聚乙烯3‑5份,填充剂2‑4份,卵磷脂2‑3份,微晶纤维素0.1‑0.4份,粗硫酸松节油0.5‑1份,且所述聚丙烯膜层为表面氟化聚丙烯膜层。本发明中的新型农药软塑组合包装材料具有高阻隔性能和更强的抗渗透性和密封性并具有优异的抗弯曲疲劳性,化学稳定性很好,强高度的同时使制品不产生可见烟尘;有良好阻燃功能。且耐冻融,耐较高温度、良好的贮存稳定性且干燥速度快。
Description
技术领域
本发明涉及一种包装材料,具体涉及一种农药软塑组合包装材料。
背景技术
为了简化使用步骤,部分农药制剂制成液体剂型,使用时只需加水稀释后即可对农作物进行喷施。传统液体农药制剂采用塑料瓶进行包装,但存在包装成本高的缺点,并且包装剂量较大,未能一次使用完的液体农药制剂需要注意密封保存,否则会影响下次使用效果。为了解决上述问题,目前部分液体农药制剂采用塑料袋进行包装,包装剂量可大可小,方便使用,并且由于大部分农药制剂为化学物质,因此其塑料包装袋不仅需要具有优异的密封性、抗渗透性和抗老化性,还要具有显著的化学稳定性,长期储存时不会与农药制剂中的成分发生任何反应,从而保证农药制剂的使用效果。软塑料一般是指热塑性塑料,用注塑法加工.成型后可以再次加工使用的塑料就叫软塑料。一般来说软塑料是熟塑料,比较耐用。软塑料一般不容易被折断,所以可以用于各种用途。
发明内容
本发明目的是:提供一种新型农药软塑组合包装材料及其制备方法。
本发明的技术方案是:一种新型农药软塑组合包装材料,包括聚丙烯膜层,所述聚丙烯膜层下设有油墨层,所述油墨层下设有复合层,所述复合层由以重量份计的如下材料组成:聚乙烯20-30份,聚丙烯20-30份,氯磺化聚乙烯3-5份,填充剂2-4份,卵磷脂2-3份,微晶纤维素0.1-0.4份,粗硫酸松节油0.5-1份,且所述聚丙烯膜层为表面氟化聚丙烯膜层。
进一步的:所述填充剂由同等份的碳酸钙、滑石粉、二硫化铝、钛酸酯、铝酸酯偶联剂、纯硅铜塑料改性剂制成,制备方法为:先将钛酸脂、铝酸酯偶联剂充分混合后于微波频率2450MHz、功率700W下微波处理5min,冷却至室温后加入碳酸钙、二硫化铝经粉碎机制成粉末,最后加入滑石粉,充分研磨混合均匀。
进一步的:所述复合层是将聚乙烯、聚丙烯、氯磺化聚乙烯、填充剂、卵磷脂、微晶纤维素以及粗硫酸松节油混合后吹塑制成。
进一步的:所述聚丙烯膜层和所述油墨层以及所述复合层之间通过聚氨酯胶剂粘合。
进一步的:所述聚氨酯胶剂由以重量计的如下材料混合组成:聚氨酯胶5份,固化剂1份,醋酸乙酯6-8份。
上述新型农药软塑组合包装材料的制备方法包括如下步骤:
步骤1:在所述聚丙烯膜层的一侧施加聚氨酯胶剂并在50-55℃下加热15min,再压合油墨层;
步骤2:在所述油墨层上施加聚氨酯胶剂并50-55℃下加热15min,再压合复合层并干燥,得到胚模;
步骤3:将所述胚模在25-40摄氏度下固化,固化时间≥48小时,得到新型农药软塑组合包装材料。
本发明的优点是:
1.本发明中的新型农药软塑组合包装材料采用多层高阻隔再进行表面氟化处理,两种阻隔方式并用,具有高阻隔性能和更强的抗渗透性和密封性。
本发明中的新型农药软塑组合包装材料采用聚丙烯膜层,具有优异的抗弯曲疲劳性,其制品在常温下可弯折106次而不损坏。化学稳定性很好,除能被浓硫酸、浓硝酸侵蚀外,对其它各种化学试剂都比较稳定。
本发明中的新型农药软塑组合包装材料的复合层中添加有纯硅铜塑料改性剂,提高制成品的强度的同时使制品不产生可见烟尘;有良好阻燃功能。
本发明中的新型农药软塑组合包装材料通过聚氨酯胶剂粘合,粘接强度高、耐冻融,耐较高温度、良好的贮存稳定性且干燥速度快。
具体实施方式
实施例1:一种新型农药软塑组合包装材料,包括聚丙烯膜层,所述聚丙烯膜层下设有油墨层,所述油墨层下设有复合层, 所述聚丙烯膜层和所述油墨层以及所述复合层之间通过聚氨酯胶剂粘合。
所述复合层由以重量份计的如下材料混合后吹塑组成:聚乙烯30份,聚丙烯30份,氯磺化聚乙烯5份,填充剂3份,卵磷脂3份,微晶纤维素0.4份,粗硫酸松节油1份,且所述聚丙烯膜层为表面氟化聚丙烯膜层。
所述填充剂由1份碳酸钙、1份滑石粉、1份二硫化铝、一份钛酸酯、1份滑石粉、1份铝酸酯偶联剂、1份纯硅铜塑料改性剂制成,制备方法为:先将钛酸脂、铝酸酯偶联剂充分混合后于微波频率2450MHz、功率700W下微波处理5min,冷却至室温后加入碳酸钙、二硫化铝经粉碎机制成粉末,最后加入滑石粉,充分研磨混合均匀。
所述聚氨酯胶剂由以重量计的如下材料混合组成:聚氨酯胶5份,固化剂1份,醋酸乙酯8份。
所述新型农药软塑组合包装材料的制备方法包括如下步骤:
步骤1:在所述聚丙烯膜层的一侧施加聚氨酯胶剂并在55℃下加热15min,再压合油墨层;
步骤2:在所述油墨层上施加聚氨酯胶剂并55℃下加热15min,再压合复合层并干燥,得到胚模;
步骤3:将所述胚模在40摄氏度下固化,固化50小时,得到新型农药软塑组合包装材料。
实施例2:一种新型农药软塑组合包装材料,包括聚丙烯膜层,所述聚丙烯膜层下设有油墨层,所述油墨层下设有复合层,所述复合层由以重量份计的如下材料组成:聚乙烯20份,聚丙烯25份,氯磺化聚乙烯3份,填充剂2份,卵磷脂2份,微晶纤维素0.2份,粗硫酸松节油0.5份,所述复合层是将上述材料混合后吹塑制成。且所述聚丙烯膜层为表面氟化聚丙烯膜层。所述聚丙烯膜层和所述油墨层以及所述复合层之间通过聚氨酯胶剂粘合。
所述填充剂由同等份的碳酸钙、滑石粉、二硫化铝、钛酸酯、铝酸酯偶联剂、纯硅铜塑料改性剂制成,制备方法为:先将太酸脂、铝酸酯偶联剂充分混合后于微波频率2450MHz、功率700W下微波处理5min,冷却至室温后加入碳酸钙、二硫化铝经粉碎机制成粉末,最后加入滑石粉,充分研磨混合均匀。
所述聚氨酯胶剂由以重量计的如下材料混合组成:聚氨酯胶5份,固化剂1份,醋酸乙酯6份。
上述新型农药软塑组合包装材料的制备方法包括如下步骤:
步骤1:在所述聚丙烯膜层的一侧施加聚氨酯胶剂并在50℃下加热15min,再压合油墨层;
步骤2:在所述油墨层上施加聚氨酯胶剂并50℃下加热15min,再压合复合层并干燥,得到胚模;
步骤3:将所述胚模在25摄氏度下固化,固化48小时,得到新型农药软塑组合包装材料。
当然上述实施例只为说明本发明的技术构思及特点,其目的在于让熟悉此项技术的人能够了解本发明的内容并据以实施,并不能以此限制本发明的保护范围。凡根据本发明主要技术方案的精神实质所做的修饰,都应涵盖在本发明的保护范围之内。
Claims (6)
1.一种新型农药软塑组合包装材料,其特征在于:包括聚丙烯膜层,所述聚丙烯膜层下设有油墨层,所述油墨层下设有复合层,所述复合层由以重量份计的如下材料组成:聚乙烯20-30份,聚丙烯20-30份,氯磺化聚乙烯3-5份,填充剂2-4份,卵磷脂2-3份,微晶纤维素0.1-0.4份,粗硫酸松节油0.5-1份,且所述聚丙烯膜层为表面氟化聚丙烯膜层。
2.根据权利要求1所述的新型农药软塑组合包装材料,其特征在于:所述填充剂由同等份的碳酸钙、滑石粉、二硫化铝、钛酸酯、铝酸酯偶联剂、纯硅铜塑料改性剂制成,制备方法为:先将钛酸脂、铝酸酯偶联剂充分混合后于微波频率2450MHz、功率700W下微波处理5min,冷却至室温后加入碳酸钙、二硫化铝经粉碎机制成粉末,最后加入滑石粉,充分研磨混合均匀。
3.根据权利要求1所述的新型农药软塑组合包装材料,其特征在于:所述复合层是将聚乙烯、聚丙烯、氯磺化聚乙烯、填充剂、卵磷脂、微晶纤维素以及粗硫酸松节油混合后吹塑制成。
4.根据权利要求1所述的新型农药软塑组合包装材料,其特征在于:所述聚丙烯膜层和所述油墨层以及所述复合层之间通过聚氨酯胶剂粘合。
5.根据权利要求4所述的新型农药软塑组合包装材料,其特征在于:所述聚氨酯胶剂由以重量计的如下材料混合组成:聚氨酯胶5份,固化剂1份,醋酸乙酯6-8份。
6.权利要求1所述的新型农药软塑组合包装材料的制备方法,其特征在于:包括如下步骤:
步骤1:在所述聚丙烯膜层的一侧施加聚氨酯胶剂并在50-55℃下加热15min,再压合油墨层;
步骤2:在所述油墨层上施加聚氨酯胶剂并50-55℃下加热15min,再压合复合层并干燥,得到胚模;
步骤3:将所述胚模在25-40摄氏度下固化,固化时间≥48小时,得到新型农药软塑组合包装材料。