CN107540477A - Nanometer organic fertilizer and preparation method thereof - Google Patents
Nanometer organic fertilizer and preparation method thereof Download PDFInfo
- Publication number
- CN107540477A CN107540477A CN201710898446.4A CN201710898446A CN107540477A CN 107540477 A CN107540477 A CN 107540477A CN 201710898446 A CN201710898446 A CN 201710898446A CN 107540477 A CN107540477 A CN 107540477A
- Authority
- CN
- China
- Prior art keywords
- parts
- nano
- fertilizer
- mixed fertilizer
- organic fertilizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses nanometer organic fertilizer and preparation method thereof.Nanometer organic fertilizer, by weight, is prepared by following component is fermented：70 120 parts of corn flour, 75 90 parts of complex micro organism fungicide, 40 50 parts of water, Nano-meter CaCO3310 15 parts, nano-TiO210 15 parts, 4 10 parts of nano-sized carbon, 12 20 parts of bean cake powder, 9 15 parts of peanut press pulp, 14 18 parts of mushroom residue, 22 29 parts of coffee grounds.Nanometer organic fertilizer of the present invention, cost is low, good absorbing, can increase the aeration of soil, makes plant be more easy to absorb, and improves utilization rate to 80 90%, reduces organic fertilizer loss；Growth and development of plants can also be helped, promotes the growth and development of the flower and fruit of plant；Can activating soil, beneficial microorganism quantity is multiplied, vigor enhancing, effectively make increasing crop yield.
Description
Technical field
The present invention relates to organic fertilizer, more particularly to nanometer organic fertilizer.
Background technology
It is well known that chronic administration chemical fertilizer can bring destruction to soil texture, cause under water pollution and utilization rate of fertilizer
The negative issue such as drop and quality of agricultural product reduction.The species of fertilizer is various at present, but its utilization rate is generally relatively low, only 30%-
40%, which results in the massive losses of fertilizer, and therefore, how to improve utilization rate of fertilizer is urgently solved in China's agricultural production process
Certainly the problem of.
The content of the invention
It is an object of the invention to overcome the above-mentioned deficiency in the presence of prior art, there is provided nanometer organic fertilizer.
Nanometer organic fertilizer, by weight, is prepared by following component is fermented：
Corn flour 70-120 parts, complex micro organism fungicide 75-90 parts, water 40-50 parts, Nano-meter CaCO3310-15 parts, nanometer
TiO210-15 parts, nano-sized carbon 4-10 parts, bean cake powder 12-20 parts, peanut press pulp 9-15 parts, mushroom residue 14-18 parts, coffee grounds 22-
29 parts.
Actinomyces, saccharomycete, lactic acid bacteria and a variety of microbial inoculums of mould are included in above-mentioned complex micro organism fungicide.
Preferably, above-mentioned nanometer organic fertilizer, by weight, it is prepared by following component is fermented：
Corn flour 90-110 parts, complex micro organism fungicide 78-85 parts, water 40-45 parts, Nano-meter CaCO3311-14 parts, nanometer
TiO211-14 parts, nano-sized carbon 4-8 parts, bean cake powder 12-18 parts, peanut press pulp 9-15 parts, mushroom residue 14-18 parts, coffee grounds 22-29
Part.
Preferably, above-mentioned nanometer organic fertilizer, by weight, it is prepared by following component is fermented：
100 parts of corn flour, 80 parts of complex micro organism fungicide, 39 parts of water, Nano-meter CaCO3311 parts, nano-TiO211 parts, receive
5 parts of carbon of rice, 16 parts of bean cake powder, 11 parts of peanut press pulp, 17 parts of mushroom residue, 28 parts of coffee grounds.
Preferably, above-mentioned mushroom residue is fresh mushroom residue.Mushroom residue is remaining mushroom bacterium bag after cultivation mushroom.
Preferably, by crushing, granularity is 10-40 mesh for above-mentioned bean cake powder, peanut press pulp, mushroom residue and coffee grounds.
The preparation method of above-mentioned nanometer organic fertilizer, comprises the following steps：
(1) mixed fertilizer A is prepared：Corn flour is mixed with complex micro organism fungicide, obtains mixed fertilizer A；Mixed fertilizer A is placed in
Fermented in open fermentation vat 45-50 hours, interval 2-3 hours are stirred；
(2) mixed fertilizer A is air-dried, makes its water content≤2%；
(3) mixed fertilizer B is prepared：Air-dried mixed fertilizer A is ground into the powdery that particle diameter is 120 μm~170 μm, by powdery
Mixed fertilizer A mixes with water, obtains mixed fertilizer B：
(4) mixed fertilizer C is prepared：Under the conditions of ultrasonic vibration Nano-meter CaCO3 is added into mixed fertilizer B3, nano-TiO2And nanometer
Carbon, obtain mixed fertilizer C；
(5) mixed fertilizer D is prepared：Mixed fertilizer C, bean cake powder, peanut press pulp, mushroom residue and coffee grounds are mixed, are prepared into mixing
Fertile D, water content≤3%；
(6) mixed fertilizer D is placed in the environment that temperature is 30~35 DEG C and relative humidity is 55-68% 46~48 hours.
Compared with prior art, beneficial effects of the present invention：
Nanometer organic fertilizer of the present invention, solves the pollution problem of mushroom residue, coffee grounds, turns waste into wealth, and has cost low, inhales
Keep well, the aeration of soil can be increased, make plant be more easy to absorb, improve utilization rate to 80-90%, reduce organic fertilizer damage
Lose；Growth and development of plants can also be helped, promotes the growth and development of the flower and fruit of plant；Simultaneously containing the organic of abundant activity
Composition and middle and trace element, can activating soil, beneficial microorganism quantity is multiplied, vigor enhancing, after being manured into soil,
Available nutrient needed for plant growth both can be immediately provided, soil can again improved, soil fertility enhancing, effectively increase crops
Production.Nanometer preparation method of organic fertilizer of the present invention, not only increase the fermentation efficiency of complex micro organism fungicide；Also so that corn flour with
Nano-meter CaCO33, nano-TiO2With nano-sized carbon mixing evenly；Nanometer corn flour fertilizer in the present invention can effectively make crops
Volume increase, is adapted to promote the use of.
Embodiment
With reference to test example and embodiment, the present invention is described in further detail.But this should not be understood
Following embodiment is only limitted to for the scope of the above-mentioned theme of the present invention, it is all that this is belonged to based on the technology that present invention is realized
The scope of invention.
1 nanometer of organic fertilizer of embodiment and preparation method thereof
Nanometer organic fertilizer, by weight, is prepared by following component is fermented：
100 parts of corn flour, 80 parts of complex micro organism fungicide, 39 parts of water, Nano-meter CaCO3311 parts, nano-TiO211 parts, receive
5 parts of carbon of rice, 16 parts of bean cake powder, 11 parts of peanut press pulp, 17 parts of mushroom residue, 28 parts of coffee grounds；Water content 58-70%；Mushroom residue is new
Fresh mushroom slag；By crushing, granularity is 20 mesh for bean cake powder, peanut press pulp, mushroom residue and coffee grounds.
The preparation method of this example nanometer organic fertilizer, comprises the following steps：
(1) mixed fertilizer A is prepared：Corn flour is mixed with complex micro organism fungicide, obtains mixed fertilizer A；Mixed fertilizer A is placed in
Fermented 45 hours in open fermentation vat, interval is stirred for 2.2 hours；
(2) mixed fertilizer A is air-dried, makes its water content≤2%；
(3) mixed fertilizer B is prepared：Air-dried mixed fertilizer A is ground into the powdery that particle diameter is 120 μm~140 μm, by powdery
Mixed fertilizer A mixes with water, obtains mixed fertilizer B：
(4) mixed fertilizer C is prepared：Under the conditions of ultrasonic vibration Nano-meter CaCO3 is added into mixed fertilizer B3, nano-TiO2And nanometer
Carbon, obtain mixed fertilizer C；
(5) mixed fertilizer D is prepared：Mixed fertilizer C, bean cake powder, peanut press pulp, mushroom residue and coffee grounds are mixed, are prepared into mixing
Fertile D, water content≤3%；
(6) mixed fertilizer D is placed in the environment that temperature is 30~35 DEG C and relative humidity is 55-68% 46 hours.
2 nanometers of organic fertilizers of embodiment and preparation method thereof
Nanometer organic fertilizer, by weight, is prepared by following component is fermented：
112 parts of corn flour, 81 parts of complex micro organism fungicide, 40 parts of water, Nano-meter CaCO3312 parts, nano-TiO212 parts, receive
6 parts of carbon of rice, 17 parts of bean cake powder, 13 parts of peanut press pulp, 16 parts of mushroom residue, 25 parts of coffee grounds；Water content 58-70%；Mushroom residue is new
Fresh mushroom slag；By crushing, granularity is 10 mesh for bean cake powder, peanut press pulp, mushroom residue and coffee grounds.
The preparation method of this example nanometer organic fertilizer, comprises the following steps：
(1) mixed fertilizer A is prepared：Corn flour is mixed with complex micro organism fungicide, obtains mixed fertilizer A；Mixed fertilizer A is placed in
Fermented 46 hours in open fermentation vat, interval is stirred for 3 hours；
(2) mixed fertilizer A is air-dried, makes its water content≤2%；
(3) mixed fertilizer B is prepared：Air-dried mixed fertilizer A is ground into the powdery that particle diameter is 130 μm~170 μm, by powdery
Mixed fertilizer A mixes with water, obtains mixed fertilizer B：
(4) mixed fertilizer C is prepared：Under the conditions of ultrasonic vibration Nano-meter CaCO3 is added into mixed fertilizer B3, nano-TiO2And nanometer
Carbon, obtain mixed fertilizer C；
(5) mixed fertilizer D is prepared：Mixed fertilizer C, bean cake powder, peanut press pulp, mushroom residue and coffee grounds are mixed, are prepared into mixing
Fertile D, water content≤3%；
(6) mixed fertilizer D is placed in the environment that temperature is 30~35 DEG C and relative humidity is 55-68% 48 hours.
3 nanometers of organic fertilizers of embodiment and preparation method thereof
Nanometer organic fertilizer, by weight, is prepared by following component is fermented：
90 parts of corn flour, 78 parts of complex micro organism fungicide, 45 parts of water, Nano-meter CaCO3314 parts, nano-TiO214 parts, nanometer
8 parts of carbon, 18 parts of bean cake powder, 15 parts of peanut press pulp, 18 parts of mushroom residue, 29 parts of coffee grounds；Water content 58-70%；Mushroom residue is fresh
Mushroom residue；By crushing, granularity is 40 mesh for bean cake powder, peanut press pulp, mushroom residue and coffee grounds.
The preparation method of this example nanometer organic fertilizer, comprises the following steps：
(1) mixed fertilizer A is prepared：Corn flour is mixed with complex micro organism fungicide, obtains mixed fertilizer A；Mixed fertilizer A is placed in
Fermented 50 hours in open fermentation vat, interval is stirred for 2 hours；
(2) mixed fertilizer A is air-dried, makes its water content≤2%；
(3) mixed fertilizer B is prepared：Air-dried mixed fertilizer A is ground into the powdery that particle diameter is 130 μm~150 μm, by powdery
Mixed fertilizer A mixes with water, obtains mixed fertilizer B：
(4) mixed fertilizer C is prepared：Under the conditions of ultrasonic vibration Nano-meter CaCO3 is added into mixed fertilizer B3, nano-TiO2And nanometer
Carbon, obtain mixed fertilizer C；
(5) mixed fertilizer D is prepared：Mixed fertilizer C, bean cake powder, peanut press pulp, mushroom residue and coffee grounds are mixed, are prepared into mixing
Fertile D, water content≤3%；
(6) mixed fertilizer D is placed in the environment that temperature is 30~35 DEG C and relative humidity is 55-68% 47 hours.
The embodiment 1-3 nanometers organic fertilizer of test example 1 contrasts with common fertilizer using effect
By taking cole crop as an example, embodiment 1-3 nanometers organic fertilizer and the contrast of common fertilizer using effect refer to table 1.
The Fertilizer application effect of table 1
Brief summary：Embodiment 1-3 nanometer organic fertilizers, cost is low, good absorbing, can increase the aeration of soil, be more easy to plant
Absorb, improve utilization rate to 80-90%, reduce organic fertilizer loss；Growth and development of plants can also be helped, promotes the flower of plant
With the growth and development of fruit；Simultaneously containing enrich activity organic principle and middle and trace element, can activating soil, make beneficial
The quantity of microorganism is multiplied, and vigor enhancing, after being manured into soil, can both provide available nutrient needed for plant growth immediately, again
It can be improved soil, soil fertility enhancing, effectively make increasing crop yield.
Claims (7)
1. nanometer organic fertilizer, it is characterised in that by weight, be prepared by following component is fermented：
Corn flour 70-120 parts, complex micro organism fungicide 75-90 parts, water 40-50 parts, Nano-meter CaCO3310-15 parts, nano-TiO2
10-15 parts, nano-sized carbon 4-10 parts, bean cake powder 12-20 parts, peanut press pulp 9-15 parts, mushroom residue 14-18 parts, coffee grounds 22-29 parts.
2. according to claim 1 nanometer of organic fertilizer, it is characterised in that by weight, by the fermented preparation of following component
Form：
Corn flour 90-110 parts, complex micro organism fungicide 78-85 parts, water 40-45 parts, Nano-meter CaCO3311-14 parts, nano-TiO2
11-14 parts, nano-sized carbon 4-8 parts, bean cake powder 12-18 parts, peanut press pulp 9-15 parts, mushroom residue 14-18 parts, coffee grounds 22-29 parts.
3. according to claim 2 nanometer of organic fertilizer, it is characterised in that by weight, by the fermented preparation of following component
Form：
100 parts of corn flour, 80 parts of complex micro organism fungicide, 39 parts of water, Nano-meter CaCO3311 parts, nano-TiO211 parts, nano-sized carbon 5
Part, 16 parts of bean cake powder, 11 parts of peanut press pulp, 17 parts of mushroom residue, 28 parts of coffee grounds.
4. according to the nanometer organic fertilizer described in any one of claim 1-3, it is characterised in that the mushroom residue is new fresh mushroom
Slag.
5. according to the nanometer organic fertilizer described in any one of claim 1-3, it is characterised in that the bean cake powder, peanut press pulp, mushroom
By crushing, granularity is 10-40 mesh for mushroom slag and coffee grounds.
6. according to claim 4 nanometer of organic fertilizer, it is characterised in that the bean cake powder, peanut press pulp, mushroom residue and coffee
For slag by crushing, granularity is 10-40 mesh.
7. the preparation method of the nanometer organic fertilizer described in any one of claim 1-6, it is characterised in that comprise the following steps：
(1) mixed fertilizer A is prepared：Corn flour is mixed with complex micro organism fungicide, obtains mixed fertilizer A；Mixed fertilizer A is placed in opening
Fermentation vat in ferment 45-50 hours, interval 2-3 hours be stirred；
(2) mixed fertilizer A is air-dried, makes its water content≤2%；
(3) mixed fertilizer B is prepared：Air-dried mixed fertilizer A is ground into the powdery that particle diameter is 120 μm~170 μm, by the mixing of powdery
Fertile A mixes with water, obtains mixed fertilizer B：
(4) mixed fertilizer C is prepared：Under the conditions of ultrasonic vibration Nano-meter CaCO3 is added into mixed fertilizer B3, nano-TiO2And nano-sized carbon,
Obtain mixed fertilizer C；
(5) mixed fertilizer D is prepared：Mixed fertilizer C, bean cake powder, peanut press pulp, mushroom residue and coffee grounds are mixed, are prepared into mixed fertilizer D,
Water content≤3%；
(6) mixed fertilizer D is placed in the environment that temperature is 30~35 DEG C and relative humidity is 55-68% 46~48 hours.