CN107476596A - 一种现浇rc楼板修复补强施工方法 - Google Patents

一种现浇rc楼板修复补强施工方法 Download PDF

Info

Publication number
CN107476596A
CN107476596A CN201710848860.4A CN201710848860A CN107476596A CN 107476596 A CN107476596 A CN 107476596A CN 201710848860 A CN201710848860 A CN 201710848860A CN 107476596 A CN107476596 A CN 107476596A
Authority
CN
China
Prior art keywords
floor
carbon cloth
crack
cast
place
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710848860.4A
Other languages
English (en)
Inventor
龚良勇
熊信福
邓燕华
张荣平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHONGHENG CONSTRUCTION GROUP Co Ltd
Original Assignee
ZHONGHENG CONSTRUCTION GROUP Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHONGHENG CONSTRUCTION GROUP Co Ltd filed Critical ZHONGHENG CONSTRUCTION GROUP Co Ltd
Priority to CN201710848860.4A priority Critical patent/CN107476596A/zh
Publication of CN107476596A publication Critical patent/CN107476596A/zh
Pending legal-status Critical Current

Abstract

本发明提供的一种现浇RC楼板修复补强施工方法，通过碳纤维布加改性橡胶的方法（简称CFC+MR方法）对其在楼板面上进行修补，充分发挥碳纤维布抗拉强度高和改性橡胶防水能力强的优势，既对开裂楼板进行了补强又进行了防水防渗，对楼板的缺陷彻底根治，永不复发，提高楼板和结构的整体性。传统方法通常是先找到裂缝部位然后戳出V型槽沟，内填柔性防水材料，随着混凝土徐变增长，裂缝卷土重来，而本方法修复时将防水堵漏与结构加固一起考虑，既防水堵漏又提高了结构强度，做到标本兼治。

Description

一种现浇RC楼板修复补强施工方法
技术领域
本发明属于建筑施工技术领域，具体涉及一种现浇RC楼板修复补强施工方法。
背景技术
实际工程中现浇楼板在支座附近常出现开裂现象，主要原因是施工过程中负筋的长度不足、间距过大、钢筋的规格和型号不符合设计、保护层过大等因素造成的，楼板的开裂导致上层住户污水渗入下层已经装修的住户。由于该处为结构性裂缝，采用传统的防水砂浆和沥青等材料修复后，因混凝土的徐变效应导致裂缝在原处重新开裂。
发明内容
本发明所要解决的是现有现浇楼板修复方法仍然会导致裂缝在原处重新开裂的技术问题，提供一种高效、安全的现浇RC楼板修复补强施工方法，通过热熔改性橡胶灌缝处理，将裂缝两侧的楼板重新粘合，有一定变形能力，彻底根治楼板在支座处因施工原因导致的开裂，既实现结构强度加固，又满足防水堵漏要求，提高楼板和结构的整体性。
为了解决本发明的技术问题，本发明是通过以下技术方案实现的：一种现浇RC楼板修复补强施工方法，包括以下步骤：
步骤一：找到楼板裂缝开展部位，沿裂缝两侧扩大50mm，对于裂缝不清晰，难于发现其发展趋势的部位，画出裂缝范围；
步骤二：用角磨机戳掉楼板面混凝土负筋保护层，深度8mm-10mm，保持干燥，并清理干净；
步骤三：在戳打范围内填5mm-8mm厚的热熔改性橡胶；
步骤四：增设两层碳纤维布加固补强，碳纤维布的宽度为100mm；
步骤五：在碳纤维布上抹厚5mm-8mm的水泥砂浆，水泥砂浆比例为1：1，内掺107胶水。
与现有技术相比，本发明获得的有益效果是：
本发明提供的一种现浇RC楼板修复补强施工方法，通过热熔改性橡胶灌缝处理，将裂缝两侧的楼板重新粘合，有一定变形能力，彻底根治楼板在支座处因施工原因导致的开裂，既实现结构强度加固，又满足防水堵漏要求，提高楼板和结构的整体性。传统方法通常是先找到裂缝部位然后戳出V型槽沟，内填柔性防水材料，随着混凝土徐变增长，裂缝卷土重来，而本方法修复时将防水堵漏与结构加固一起考虑，既防水堵漏又提高了结构强度，做到标本兼治、永不复发。
本发明提供的一种现浇RC楼板修复补强施工方法，只需知道裂缝大概位置即可进行修复补强，而传统方法需要对裂缝精确定位，实际中很难做到。传统方法需要戳V型槽沟，对负筋和既有结构造成一定损伤，而本方法只需要用角磨机戳掉楼板表面，施工简单、方便，且不会对既有结构造成损伤。
本发明提供的一种现浇RC楼板修复补强施工方法，修复后颜色与周边一致，不影响外观；在楼板面上修复，不影响下面住户也不对下面住户的装修造成损失。
具体实施方式
下面对实施例进行详细说明。
一种现浇RC楼板修复补强施工方法，包括以下步骤：
步骤一：找到楼板裂缝开展部位，沿裂缝两侧扩大50mm，对于裂缝不清晰，难于发现其发展趋势的部位，画出裂缝范围；只需知道裂缝大概位置即可进行修复补强，而传统方法需要对裂缝精确定位，实际中很难做到。
步骤二：用角磨机戳掉楼板面混凝土负筋保护层，深度8mm-10mm，保持干燥，并清理干净；传统方法需要戳V型槽沟，对负筋和既有结构造成一定损伤，采用角磨机戳掉楼板表面，施工简单、方便，且不会对既有结构造成损伤。
步骤三：在戳打范围内填5mm-8mm厚的热熔改性橡胶，将裂缝两侧的楼板重新粘合，有一定变形能力，彻底根治楼板在支座处因施工原因导致的开裂，既实现结构强度加固，又满足防水堵漏要求，提高楼板和结构的整体性。
步骤四：增设两层碳纤维布加固补强，碳纤维布的宽度为100mm；间距根据设计计算确定，一般为300mm-500mm。
步骤五：在碳纤维布上抹厚5mm-8mm的水泥砂浆，水泥砂浆比例为1：1，内掺107胶水。
一种现浇RC楼板修复补强施工方法，通过碳纤维布加改性橡胶的方法（简称CFC+MR方法）对其在楼板面上进行修补，充分发挥碳纤维布抗拉强度高和改性橡胶防水能力强的优势，既对开裂楼板进行了补强又进行了防水防渗，对楼板的缺陷彻底根治，永不复发。且修复后颜色与周边一致，不影响外观；在楼板面上修复，不影响下面住户也不对下面住户的装修造成损失。
以上列举的仅是本发明的具体实施例之一。显然，本发明不限于以上实施例，还可以有许多类似的改形。本领域的普通技术人员能从本发明公开的内容直接导出或联想到的所有变形，均应认为是本发明所要保护的范围。

Claims (1)

1.一种现浇RC楼板修复补强施工方法，其特征在于：包括以下步骤：
步骤一：找到楼板裂缝开展部位，沿裂缝两侧扩大50mm，对于裂缝不清晰，难于发现其发展趋势的部位，画出裂缝范围；
步骤二：用角磨机戳掉楼板面混凝土负筋保护层，深度8mm-10mm，保持干燥，并清理干净；
步骤三：在戳打范围内填5mm-8mm厚的热熔改性橡胶；
步骤四：增设两层碳纤维布加固补强，碳纤维布的宽度为100mm；
步骤五：在碳纤维布上抹厚5mm-8mm的水泥砂浆，水泥砂浆比例为1：1，内掺107胶水。
CN201710848860.4A 2017-09-20 2017-09-20 一种现浇rc楼板修复补强施工方法 Pending CN107476596A (zh)