CN107473666A - The production method of unburned quincunx tourmaline lightweight through hole haydite - Google Patents
The production method of unburned quincunx tourmaline lightweight through hole haydite Download PDFInfo
- Publication number
- CN107473666A CN107473666A CN201710872638.8A CN201710872638A CN107473666A CN 107473666 A CN107473666 A CN 107473666A CN 201710872638 A CN201710872638 A CN 201710872638A CN 107473666 A CN107473666 A CN 107473666A
- Authority
- CN
- China
- Prior art keywords
- lightweight
- tourmaline
- unburned quincunx
- hole haydite
- hole
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of production method of unburned quincunx tourmaline lightweight through hole haydite, the main points of its technical scheme are the production methods of unburned quincunx tourmaline lightweight through hole haydite:The dispensing of unburned quincunx tourmaline lightweight through hole haydite is stirred after mixing, extruder grain, steam curing, steam drying, polishing, screening and is packaged as unburned quincunx tourmaline lightweight through hole haydite, dispensing is made up of the Concave-convex clay rod after schorl, black portland cement, acidifying, powdery attapulgite foaming agent, light magnesium oxide, alumina silicate fibre, hollow glass micropearl.The baking-free lightweight through hole haydite produced using the production method of the present invention, with it is black and shinny, appearance and modeling is attractive in appearance, lightweight intensity is good, specific surface area is big, bulk density is low, permeability is superior, micropore and the characteristics of through hole is integrated, porosity and water absorption rate are high, it can ensure that growth and development of plants is good, survival rate is high and the life-span is longer, and can greatly reduce the number of moisturizing.
Description
Technical field
The present invention relates to haydite, and in particular to a kind of production method of unburned quincunx tourmaline lightweight through hole haydite.
Background technology
Colored haydite on the market, it is to be granulated to be made after mixing using cement, fine sand and dyestuff, proportion and heap
Product density is all very big, and water absorption rate is smaller, it is impossible to the normal growth and development of plant is ensured, also without the work(for adsorbing and purifying air
Energy.
Tested through multiple sampling:Colored haydite average bulk density >=1200kg/m3 on the market, mean water absorption rate
≤ 20%.
The content of the invention
The purpose of the present invention is to overcome weak point in the prior art, there is provided a kind of unburned quincunx tourmaline lightweight through hole
The production method of haydite.
The production method of unburned quincunx tourmaline lightweight through hole haydite:By unburned quincunx tourmaline lightweight through hole haydite
Dispensing be stirred after mixing, extruder grain, steam curing, steam drying, polishing, screening be packaged as it is unburned it is quincunx electrically
Stone lightweight through hole haydite.
After the dispensing of unburned quincunx tourmaline lightweight through hole haydite is by schorl, black portland cement, acidifying
Concave-convex clay rod, powdery attapulgite foaming agent, light magnesium oxide, alumina silicate fibre, hollow glass micropearl composition.
Tourmaline is the natural minerals of multielement, and tourmaline main component has more than 10 kinds of magnesium, aluminium, iron, boron etc. to have human body
The trace element of profit, because it is a kind of special polarity crystalline solid of structure, itself can produce electron ion for a long time, and forever discharge
Negative aeroion and far infrared, the peculiar smell that the adsorbable paint of tourmaline, colloid, coating are sent, moreover it is possible to smoke is absorbed for a long time,
Schorl color is different and different with composition:Tourmaline rich in Fe is in black, the present invention from schorl granularity≤
0.42 millimeter.
Black portland cement is one kind in colored portland cement, and colored portland cement quality needs to meet " JC/
The standard of T 870-2012 colored portland cements ".
Attapulgite also known as palygorskite or Palygorskite, it is the clay mineral of zeopan containing Shuifu County of a kind of layer of chain structure,
Concave-convex clay rod has unique layer chain structure feature, and crystal is in needle-like, threadiness or fiber collection shape.Attapulgite glues
Soil has good colloidal nature and the higher adsorption capacities such as unique scattered, high temperature resistant, salt resistance alkali.
Concave-convex clay rod after acidifying is made in the absorption property, percent of decolourization, catalysis for increasing substantially Concave-convex clay rod
With, specific surface area, porosity while, can increase acidifying after Concave-convex clay rod colloid viscosity and adjustment acidifying after it is recessed
Convex rod stone clay pH value.
Powdery attapulgite foaming agent has that foaming capacity is strong, coefficient of foaming is high, unit volume bubble production volume is big, foam outer membrane is tough
Property it is good non-breakable, foam stability is good, can not defoam for a long time, foam is fine and smooth, the hole size that is generated in medium uniformly,
The advantages that bleeding quantity is low and good using the compatibility of medium.
Precipitated calcium carbonate is a kind of white powder, and odorlessness is tasteless, and precipitated calcium carbonate fine particles, surface are rougher, than
Surface area is big, and the present invention selects granularity≤0.074 millimeter of precipitated calcium carbonate.
Light magnesium oxide is the loose unformed powder of white lightweight, and odorless, tasteless is nontoxic, and volume shared by light magnesium oxide is about
Three times for heavy-burned magnesia or so, there is extremely fireproof heat-insulating property, reinforcing agent, adhesive, and the present invention selects light magnesium oxide
Granularity≤0.074 millimeter.
Hollow glass micropearl(Hollow glass microbead)It is a kind of small, hollow ball sprills, particle diameter can be as needed
Arbitrarily selected between 30-100 microns, have lightweight is big, thermal conductivity factor is low, compression strength is high, dispersiveness, flowing
Property, the advantages of stability is good, the present invention selects particle diameter≤0.1 millimeter of hollow glass micropearl.
The technical scheme is that:
1st, the production method of unburned quincunx tourmaline lightweight through hole haydite:(1) by unburned quincunx tourmaline lightweight through hole haydite
The stirring mixer that has operated of dispensing input in, be stirred as the mixing of unburned quincunx tourmaline lightweight through hole haydite
Thing;(2) the mixture of unburned quincunx tourmaline lightweight through hole haydite is transported in Squeezinggranulator, extruder grain is unburned
Quincunx tourmaline lightweight through hole semi-finished product, the external diameter control of the semi-finished product of unburned quincunx tourmaline lightweight through hole haydite
At 5~60 millimeters, length is controlled at 5~60 millimeters, the semi-finished product center of unburned quincunx colored tourmaline lightweight through hole haydite
1~6 through hole is designed with, through-hole diameter is controlled at 1~10 millimeter;By unburned quincunx tourmaline lightweight through hole haydite half into
Product are transported to steam-curing chamber and carry out steam curing, and at 55~75 DEG C, curing time controls 7 temperature control in steam curing room
~15 days;(4), by the unburned quincunx tourmaline lightweight through hole semi-finished product after steam curing, steam rotary drying is transported to
Processing is dried in machine, at 60~100 DEG C, drying time was controlled at 1~5 hour for drying temperature control;(5) by drying process
Unburned quincunx tourmaline lightweight through hole semi-finished product afterwards, which is transported in polishing machine, to be polished, after grinding off extruder grain
Flash caused by unburned quincunx tourmaline lightweight through hole semi-finished product surface;(6) by the unburned quincunx tourmaline after polishing
Lightweight through hole semi-finished product, which is transported in vibratory sieve, is sieved, and screens out the unburned quincunx tourmaline lightweight through hole after polishing
Caused chip in semi-finished product, it is packaged as the finished product of unburned quincunx tourmaline lightweight through hole haydite.
2nd, the dispensing of unburned quincunx tourmaline lightweight through hole haydite is made up of following component by weight percentage:Black appliances gas
Concave-convex clay rod 5~20%, powdery attapulgite foaming after stone 15~45%, black portland cement 15~30%, acidifying
Agent 2~15%, light magnesium oxide 1~10%, alumina silicate fibre 1~8%, hollow glass micropearl 1~8% and water 5~40%.
3rd, the Concave-convex clay rod dispensing after being acidified is made up of following component by weight percentage:Attapulgite after acidifying
Clay semi-finished product 90~98%, quick dissolved sodium silicate 0.1~5%, polyvinyl alcohol 0.1~5%, hydroxypropyl methyl cellulose 0.01~
3% and sodium carbonate 0~3%;The production method of Concave-convex clay rod after acidifying:Concave-convex clay rod dispensing after acidifying is defeated
Enter in grinding machine and be milled, grain fineness≤0.074 millimeter, the powder after milling is the Concave-convex clay rod after acidifying;
The production method of Concave-convex clay rod semi-finished product after acidifying:(1) first the Concave-convex clay rod after weathering is inputted
In mixer through operating, then dilute sulfuric acid is slowly added to carry out acidification in the Concave-convex clay rod after weathering;⑵
By the Concave-convex clay rod after acidification, it is Concave-convex clay rod tablet to be extruded by twin rollers, Concave-convex clay rod piece
Thickness≤3 millimeter of shape thing;(3) Concave-convex clay rod tablet is transported in swinging drying oven and be calcined, roasting time 1
~3 hours, sintering temperature was controlled at 250~350 DEG C, Concave-convex clay rod tablet water content≤5% after roasting, after roasting
Concave-convex clay rod tablet for acidifying after Concave-convex clay rod semi-finished product;
The dispensing of Concave-convex clay rod tablet is made up of following component by weight percentage:Attapulgite after weathering glues
Soil 55~75% and dilute sulfuric acid 25~45%;The dispensing of dilute sulfuric acid is made up of following component by weight percentage:The ﹪'s of concentration 98
Sulfuric acid 1~5%, water 95~99%;Concave-convex clay rod raw ore is needed by two time weatherings more than winter, from big
The fine and close raw ore disintegration of block is the Concave-convex clay rod after the weathering of fine particle, picks and is evident that barren rock block, plants
Fibres and other soil impurity, Concave-convex clay rod grain fineness≤5 millimeter after weathering.
Concave-convex clay rod after acidifying is " recessed after acidifying using being applied by the present inventor on 06 01st, 2014
Convex rod stone clay ", Chinese patent Authorization Notice No. is:CN 104016366B, authorized announcement date:On December 02nd, 2015.
4th, powdery attapulgite foaming agent dispensing is made up of following component by weight percentage:Activated attapulgite 45~
95%th, lauryl sodium sulfate 1~35%, SODIUM PERCARBONATE 1~25%, Sodium Polyacrylate 0.01~5%, sodium pyrophosphate 0.01~
5% and poly- naphthalene formaldehyde sulfonate salt 0.01~5%;The production method of powdery attapulgite foaming agent:By powdery attapulgite foaming agent
It is stirred in dispensing input mixer, inputs in grinding machine and be milled after stirring, grain fineness≤0.074 millimeter.
Powdery attapulgite foaming agent using applied by the present inventor on 05 26th, 2013 " powdery attapulgite foam
Agent ", Chinese patent Authorization Notice No. are:The B of CN 103265213, authorized announcement date:On 09 24th, 2014.
5th, the production method of unburned quincunx tourmaline lightweight through hole haydite of the invention, the principal ingredients of selection are not limited to
Concave-convex clay rod after acidifying, zeolite, flyash after acidifying, kaolin, diatomite, sepiolite clay, activated carbon, volcano
Ash, Rectorite, green illiteracy mixed-layer clay, chlorite, medical stone, gangue, bentonite, graphite, illite clay, she is green mixed
Layer clay and illite/smectite mixed layer clay are equally applicable to produce unburned quincunx color light through hole haydite.
6th, the production method of unburned quincunx colored tourmaline lightweight through hole haydite of the invention, it is also applied for producing unburned
Cylindrical color tourmaline lightweight through hole haydite and unburned spheroidal colour tourmaline lightweight through hole haydite.
Tourmaline itself can produce electron ion for a long time, and forever discharge negative aeroion and far infrared, improve unburned plum
The adsorption effect of flower-shape tourmaline lightweight through hole haydite.
Black portland cement can ensure that unburned quincunx tourmaline lightweight through hole haydite is black and shinny, increase unburned plum blossom
The intensity of shape tourmaline lightweight through hole haydite.
Concave-convex clay rod after acidifying can increase substantially unburned quincunx tourmaline lightweight through hole haydite absorption and
Purify the function of air.
Powdery attapulgite foaming agent be stirred for unburned quincunx tourmaline lightweight through hole haydite mixture when, it will
A certain amount of bubble is produced, is advantageous to increase unburned quincunx tourmaline lightweight through hole haydite surface and internal porosity.
Light magnesium oxide, hollow glass micropearl and titanium white are used in unburned quincunx tourmaline lightweight through hole haydite dispensing
Powder, it is ensured that unburned quincunx tourmaline lightweight through hole haydite color is more bright-coloured, increase haydite surface and internal porosity, drop
The bulk density of low unburned quincunx tourmaline lightweight through hole haydite, improve the ratio of unburned quincunx tourmaline lightweight through hole haydite
Surface area and intensity.
Unburned quincunx tourmaline lightweight through hole haydite is advantageous to increase unburned quincunx tourmaline lightweight through hole haydite phase
The bulk density of voidage and the unburned quincunx tourmaline lightweight through hole haydite of reduction between mutually.
There is largely interconnected micropore unburned quincunx colored tourmaline lightweight through hole haydite surface and inside, are a kind of
Open pore, open pore are not only penetrated and also communicated with the external world each other, unburned quincunx colored tourmaline lightweight through hole haydite center
Hole is a kind of through hole, is advantageous to increase the effective ratio area and intensity of unburned quincunx colored tourmaline lightweight through hole haydite,
Improve the adsorption capacity of unburned quincunx colored tourmaline lightweight through hole haydite and reduce bulk density.
Unburned quincunx tourmaline lightweight through hole haydite is put into water, unburned quincunx tourmaline lightweight through hole haydite meeting
Sink under water rapidly, can be by unburned quincunx tourmaline lightweight through hole haydite internal capillary while large quantity of moisture is sucked
Air cement out.
When unburned quincunx tourmaline lightweight through hole haydite water absorption rate >=25%, unburned quincunx tourmaline lightweight through hole
The appearance of haydite is a kind of state of moistening, and not obvious water leaks out, and unburned quincunx tourmaline lightweight is led to
Hole haydite is packed together, and forms numerous spaces between each other, will not be bonded together, and permeability is good, unburned quincunx
Tourmaline lightweight through hole haydite does not have dust in the dry state, and disintegration will not also be produced by being immersed in all the year round in water.
Using the present invention production method produce baking-free lightweight through hole haydite, have it is black and shinny, appearance and modeling is attractive in appearance,
Lightweight intensity is good, specific surface area is big, bulk density is low, permeability is superior, micropore and through hole are integrated, porosity and water absorption rate
The characteristics of high.
In order to ensure the normal growth and development of plant, water, the organic fertilizer of liquid or inorganic fertilizer are sprayed at unburned quincunx
In tourmaline lightweight through hole haydite, or unburned quincunx tourmaline lightweight through hole haydite is immersed in water, organic fertilizer or inorganic fertilizer
Solution in, unburned quincunx tourmaline lightweight through hole haydite absorbs store a certain amount of water or liquid fertilizer after take out, for training
When educating or planting various nursery stocks, flowers and plants and vegetables, the root of plant will be in unburned quincunx tourmaline lightweight through hole haydite
Absorb the nutritional ingredient of water or liquid fertilizer, it is ensured that growth and development of plants is good, and survival rate is high and the life-span is longer, and can greatly reduce benefit
The number of water.
Unburned quincunx tourmaline lightweight through hole haydite is applied to garden landscape engineering, home gardening and prepares soilless culture
Matrix.
Brief description of the drawings
Fig. 1 is unburned quincunx colored tourmaline lightweight through hole haydite schematic diagram, and Fig. 2 is unburned quincunx colored tourmaline
Lightweight through hole haydite A-A sections.
As shown in the figure:1 is unburned quincunx colored tourmaline lightweight through hole haydite, and 2 be unburned quincunx colored tourmaline
The external diameter of lightweight through hole haydite, 3 be the length of unburned quincunx colored tourmaline lightweight through hole haydite, and 4 be unburned quincunx coloured silk
The through hole at color tourmaline lightweight through hole haydite center.
Embodiment
With reference to embodiment, the invention will be further described:
1st, the production method of unburned quincunx tourmaline lightweight through hole haydite:(1) by unburned quincunx tourmaline lightweight through hole haydite
The stirring mixer that has operated of dispensing input in, be stirred as the mixing of unburned quincunx tourmaline lightweight through hole haydite
Thing;(2) the mixture of unburned quincunx tourmaline lightweight through hole haydite is transported in Squeezinggranulator, extruder grain is unburned
The quincunx semi-finished product of tourmaline lightweight through hole haydite 1, the external diameter 2 of the semi-finished product of unburned quincunx tourmaline lightweight through hole haydite 1
Control is at 10 millimeters, and length 3 is controlled at 10 millimeters, and the semi-finished product center of unburned quincunx colored tourmaline lightweight through hole haydite is set
In respect of 1 through hole 4, the diameter control of through hole 4 is at 2 millimeters;(3) the unburned quincunx semi-finished product of tourmaline lightweight through hole haydite 1 are conveyed
Steam curing is carried out to steam-curing chamber, at 65~75 DEG C, curing time controlled at 12 days temperature control in steam curing room;⑷
By the unburned quincunx semi-finished product of tourmaline lightweight through hole haydite 1 after steam curing, it is transported in steam rotary dryer and carries out
Drying process, at 80~90 DEG C, drying time was controlled at 2 hours for drying temperature control;(5) by the unburned plum blossom after drying process
The semi-finished product of shape tourmaline lightweight through hole haydite 1, which are transported in polishing machine, to be polished, and is ground off unburned quincunx after extruder grain
Flash caused by the surface of semi-finished of tourmaline lightweight through hole haydite 1;(6) by the unburned quincunx tourmaline lightweight through hole after polishing
The semi-finished product of haydite 1, which are transported in vibratory sieve, to be sieved, and screens out the unburned quincunx tourmaline lightweight through hole haydite 1 half after polishing
Caused chip in finished product, it is packaged as the finished product of unburned quincunx tourmaline lightweight through hole haydite.
2nd, the dispensing of unburned quincunx tourmaline lightweight through hole haydite is made up of following component by weight percentage:Black appliances gas
Concave-convex clay rod 12%, powdery attapulgite foaming agent 8%, lightweight oxygen after stone 30%, black portland cement 25%, acidifying
Change magnesium 4%, alumina silicate fibre 3%, hollow glass micropearl 2% and water 16%.
3rd, it is 842kg/m3 to survey unburned quincunx tourmaline lightweight through hole haydite average bulk density, and water absorption rate is
56%.
Claims (4)
- A kind of 1. production method of unburned quincunx tourmaline lightweight through hole haydite, it is characterised in that unburned quincunx tourmaline The production method of lightweight through hole haydite:(1) stirred what the dispensing input of unburned quincunx tourmaline lightweight through hole haydite had operated Mix in mixer, be stirred as the mixture of unburned quincunx tourmaline lightweight through hole haydite;(2) will be unburned quincunx electric The mixture of stone lightweight through hole haydite is transported in Squeezinggranulator, and extruder grain is unburned quincunx tourmaline lightweight through hole pottery Grain semi-finished product, at 5~60 millimeters, length control exists for the external diameter control of the semi-finished product of unburned quincunx tourmaline lightweight through hole haydite 5~60 millimeters, the semi-finished product Center of unburned quincunx colored tourmaline lightweight through hole haydite has 1~6 through hole, and through hole is straight Footpath is controlled at 1~10 millimeter;(3) unburned quincunx tourmaline lightweight through hole semi-finished product is transported into steam-curing chamber to carry out Steam curing, at 55~75 DEG C, curing time controlled at 7~15 days temperature control in steam curing room;(4) by after steam curing Unburned quincunx tourmaline lightweight through hole semi-finished product, be transported in steam rotary dryer and processing be dried, dry At 60~100 DEG C, drying time controlled at 1~5 hour temperature control;(5) it is the unburned quincunx tourmaline after drying process is light Matter through hole semi-finished product, which is transported in polishing machine, to be polished, and is ground off the unburned quincunx tourmaline lightweight after extruder grain and is led to Flash caused by the semi-finished product surface of hole;(6) the unburned quincunx tourmaline lightweight through hole semi-finished product after polishing is conveyed Sieved, screened out caused broken in the unburned quincunx tourmaline lightweight through hole semi-finished product after polishing into vibratory sieve Bits, it is packaged as the finished product of unburned quincunx tourmaline lightweight through hole haydite.
- 2. the production method of unburned quincunx colored tourmaline lightweight through hole haydite according to claim 1, its feature exist In the dispensing of unburned quincunx tourmaline lightweight through hole haydite is made up of following component by weight percentage:Schorl 15~ 45%th, black portland cement 15~30%, acidifying after Concave-convex clay rod 5~20%, powdery attapulgite foaming agent 2~ 15%th, light magnesium oxide 1~10%, alumina silicate fibre 1~8%, hollow glass micropearl 1~8% and water 5~40%.
- 3. the production method of unburned quincunx colored tourmaline lightweight through hole haydite according to claim 1, its feature exist In, the production method of unburned quincunx tourmaline lightweight through hole haydite of the invention, after the principal ingredients of selection are not limited to acidifying Concave-convex clay rod, it is zeolite, flyash, kaolin, diatomite, sepiolite clay, activated carbon, volcanic ash after acidifying, tired Support stone clay, green illiteracy mixed-layer clay, chlorite, medical stone, gangue, bentonite, graphite, illite clay, her green mixed layer glue Soil and illite/smectite mixed layer clay are equally applicable to produce unburned quincunx color light through hole haydite.
- 4. the production method of unburned quincunx colored tourmaline lightweight through hole haydite according to claim 1, its feature exist In, the production method of unburned quincunx colored tourmaline lightweight through hole haydite of the invention, it is also applied for producing cylindrical sintering-free Colored tourmaline lightweight through hole haydite and unburned spheroidal colour tourmaline lightweight through hole haydite.