CN107459846A - 抗剥离耐磨陶瓷涂料及其制备方法 - Google Patents
抗剥离耐磨陶瓷涂料及其制备方法 Download PDFInfo
- Publication number
- CN107459846A CN107459846A CN201710619890.8A CN201710619890A CN107459846A CN 107459846 A CN107459846 A CN 107459846A CN 201710619890 A CN201710619890 A CN 201710619890A CN 107459846 A CN107459846 A CN 107459846A
- Authority
- CN
- China
- Prior art keywords
- parts
- ceramic coat
- antistripping
- wearable ceramic
- rosin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开一种抗剥离耐磨陶瓷涂料及其制备方法,采用以下原料:白刚玉、碳化硅、氧化铝、水泥、聚丙烯酸酯、钢纤维、滑石粉、聚羧酸酯、苯乙烯‑丙烯腈‑压克力橡胶共聚物、异丁基三乙氧基硅、水云母、明胶、牛皮膏、松香以及水;将固体物质粉碎至粒度为0.01mm~1mm;在100℃~150℃、200rpm~250 rpm下,将与上述原料剩余的原料密封、保温搅拌1h~3h;在1200℃~1250℃下,将搅拌后得到的物质煅烧10min~20min。本发明主要通过在硅藻泥原有材料的基础上加入苯乙烯‑丙烯腈‑压克力橡胶共聚物、异丁基三乙氧基硅、水云母、明胶、牛皮膏、松香,从而有效的提高耐磨陶瓷涂料的抗剥离性能。
Description
技术领域
本发明涉及耐磨材料技术领域,尤其是一种耐磨陶瓷涂料。
背景技术
耐磨陶瓷涂料是一种非金属胶凝材料,它是采用耐酸和耐碱的人工合成原料经严格的工艺配比和先进的无机聚合技术制成的一种粉状陶瓷材料。在施工现场,将特制液体无机胶水加入这种材料,采用人工或机械方式涂抹在设备内衬或表面,经过一系列的化学反应,在常温下3d后达到陶瓷的结合强度和硬度,故名耐磨陶瓷涂料。然而,尽管耐磨陶瓷涂料具备上述功能,但是其也存在着一些缺点,例如,将其涂抹在设备内衬或表面后,容易出现剥落的现象,其强度和硬度也大打折扣。
发明内容
本发明提供一种抗剥离耐磨陶瓷涂料及其制备方法,它可以解决现有的耐磨陶瓷涂料在涂抹后容易出现剥落的问题。
为了解决上述技术问题,本发明所采用的技术方案是:
它采用以下重量份数的原料:
白刚玉30份~45份、碳化硅10份~20份、氧化铝5份~10份、水泥5份~10份、聚丙烯酸酯1份~5份、钢纤维1份~5份、滑石粉1份~5份、聚羧酸酯10份~20份、苯乙烯-丙烯腈-压克力橡胶共聚物5份~10份、异丁基三乙氧基硅1份~5份、水云母1份~2份、明胶5份~10份、牛皮膏5份~10份、松香5份~10份以及水10份~20份;
包括以下制备步骤:
A.按比例,先将上述原料中的固体物质粉碎至粒度为0.01mm~1mm;
B.在温度为100℃~150℃、转速为200rpm~250 rpm的搅拌条件下,将A步骤粉碎得到的物质与上述原料剩余的原料密封、保温搅拌1h~3h;
C.在温度为1200℃~1250℃的条件下,将B步骤搅拌后得到的物质煅烧10min~20min。
由于采用上述技术方案,本发明得到的有益效果是:
本发明主要通过在原有材料的基础上加入苯乙烯-丙烯腈-压克力橡胶共聚物、异丁基三乙氧基硅、水云母、明胶、牛皮膏、松香,从而有效的提高耐磨陶瓷涂料的抗剥离性能。
具体实施方式
以下结合具体实施例对本发明作进一步详述,而本发明的保护范围并非仅仅局限于以下实施例。
实施例1——抗剥离耐磨陶瓷涂料
它采用以下重量kg数的原料:
白刚玉38kg、碳化硅17kg、氧化铝6kg、水泥9kg、聚丙烯酸酯4kg、钢纤维3kg、滑石粉2kg、聚羧酸酯18kg、苯乙烯-丙烯腈-压克力橡胶共聚物9kg、异丁基三乙氧基硅4kg、水云母1kg、明胶7kg、牛皮膏6kg、松香7kg以及水19kg;
包括以下制备步骤:
A.按比例,先将上述原料中的固体物质粉碎至粒度为0.6mm;
B.在温度为120℃、转速为220rpm的搅拌条件下,将A步骤粉碎得到的物质与上述原料剩余的原料密封、保温搅拌2h;
C.在温度为1200℃的条件下,将B步骤搅拌后得到的物质煅烧15min。
经检测,本实施例耐磨陶瓷涂料的附着力为0级。
实施例2——抗剥离耐磨陶瓷涂料
它采用以下重量kg数的原料:
白刚玉45kg、碳化硅20kg、氧化铝10kg、水泥10kg、聚丙烯酸酯5kg、钢纤维5kg、滑石粉5kg、聚羧酸酯20kg、苯乙烯-丙烯腈-压克力橡胶共聚物10kg、异丁基三乙氧基硅5kg、水云母2kg、明胶10kg、牛皮膏10kg、松香10kg以及水20kg;
包括以下制备步骤:
A.按比例,先将上述原料中的固体物质粉碎至粒度为1mm;
B.在温度为150℃、转速为250rpm的搅拌条件下,将A步骤粉碎得到的物质与上述原料剩余的原料密封、保温搅拌3h;
C.在温度为1250℃的条件下,将B步骤搅拌后得到的物质煅烧10min~20min。
经检测,本实施例耐磨陶瓷涂料的附着力为0级。
实施例3——抗剥离耐磨陶瓷涂料
它采用以下重量kg数的原料:
白刚玉30kg、碳化硅10kg、氧化铝5kg、水泥5kg、聚丙烯酸酯1kg、钢纤维1kg、滑石粉1kg、聚羧酸酯10kg、苯乙烯-丙烯腈-压克力橡胶共聚物5kg、异丁基三乙氧基硅1kg、水云母1kg、明胶5kg、牛皮膏5kg、松香5kg以及水10kg;
包括以下制备步骤:
A.按比例,先将上述原料中的固体物质粉碎至粒度为0.01mm;
B.在温度为100℃、转速为200rpm的搅拌条件下,将A步骤粉碎得到的物质与上述原料剩余的原料密封、保温搅拌1h~3h;
C.在温度为1200℃的条件下,将B步骤搅拌后得到的物质煅烧10min。
经检测,本实施例耐磨陶瓷涂料的附着力为0级。
Claims (2)
1.一种抗剥离耐磨陶瓷涂料,其特征在于由以下重量份数的原料制成:
白刚玉30份~45份、碳化硅10份~20份、氧化铝5份~10份、水泥5份~10份、聚丙烯酸酯1份~5份、钢纤维1份~5份、滑石粉1份~5份、聚羧酸酯10份~20份、苯乙烯-丙烯腈-压克力橡胶共聚物5份~10份、异丁基三乙氧基硅1份~5份、水云母1份~2份、明胶5份~10份、牛皮膏5份~10份、松香5份~10份以及水10份~20份。
2.一种抗剥离耐磨陶瓷涂料的制备方法,其特征在于:
采用以下重量份数的原料:
白刚玉30份~45份、碳化硅10份~20份、氧化铝5份~10份、水泥5份~10份、聚丙烯酸酯1份~5份、钢纤维1份~5份、滑石粉1份~5份、聚羧酸酯10份~20份、苯乙烯-丙烯腈-压克力橡胶共聚物5份~10份、异丁基三乙氧基硅1份~5份、水云母1份~2份、明胶5份~10份、牛皮膏5份~10份、松香5份~10份以及水10份~20份;
包括以下制备步骤:
A.按比例,先将上述原料中的固体物质粉碎至粒度为0.01mm~1mm;
B.在温度为100℃~150℃、转速为200rpm~250 rpm的搅拌条件下,将A步骤粉碎得到的物质与上述原料剩余的原料密封、保温搅拌1h~3h;
C.在温度为1200℃~1250℃的条件下,将B步骤搅拌后得到的物质煅烧10min~20min。