CN101844930A - 冶金耐火砖交接口密封胶泥 - Google Patents
冶金耐火砖交接口密封胶泥 Download PDFInfo
- Publication number
- CN101844930A CN101844930A CN201010173010A CN201010173010A CN101844930A CN 101844930 A CN101844930 A CN 101844930A CN 201010173010 A CN201010173010 A CN 201010173010A CN 201010173010 A CN201010173010 A CN 201010173010A CN 101844930 A CN101844930 A CN 101844930A
- Authority
- CN
- China
- Prior art keywords
- parts
- metallurgic
- refractory brick
- gum type
- raw materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种冶金耐火砖交接口密封胶泥，是由下列重量份的原料组成：铝矾土熟料粉40-50份；结合剂(软质黏土)30-40份；高温粘结剂30-40份；纤维素1-2份；漂浮剂1-2份；纸浆粉1-2份；其余成分为水。所述原料规格均为80-200目细粉；其制备方法是：称取上述重量份的原料加水充分混合，呈泥浆状混合物包装即可。经应用发现，本发明选取的原料规格为80-200目之间的细粉，可以满足不同冶金耐火砖对接口和砌缝密封的需要。选取的原料重量组分搭配，均能实现低温粘接效果好、高温强度高、耐火性能好的目的。其粘结时间为2-5小时；不仅粘结时间适当，而且流动性粘结度均较为理想。
Description
技术领域
本发明涉及冶金耐火材料领域，应用于冶金耐火砖对接处交接口的密封，特别是针对带有子母扣冶金耐火砖的对接密封。
背景技术
现有技术中，用作冶金耐火砖砌体砌缝密封的材料，主要是黏土质、高铝质、硅质和镁质耐火泥。由耐火粉料、结合剂和外加剂组成。所存在的技术缺陷在于：常温强度较低，高温下形成陶瓷结合才具有较高强度；以水质性、气硬性或热硬性结合材料作为结合剂而成的化学结合耐火泥，在低于形成陶瓷结合温度之前即产生一定的化学反应而硬化。
中国专利公开号为CN101429039A的“高铝质精细耐火泥”是由高铝矾土孰料粉46-22％，羧甲基纤维素钠3-5％，其余为水组成。所要解决的问题是“火泥流动性差，煅烧后容易收缩的问题。”
发明内容
本发明的目的在于提供一种冶金耐火砖交接口密封胶泥，具有低温粘结效果好，高温强度高，耐火性能好的优势。
本发明是由以下的技术方案实现的：所述冶金耐火砖交接口密封胶泥是由下列重量份的原料组成：
铝矾土熟料粉40-50份；结合剂(软质黏土)30-40份；高温粘结剂30-40份；纤维素1-2份；漂浮剂1-2份；纸浆粉1-2份；其余成分为水。
所述原料规格均为80-200目细粉；其制备方法是：称取上述重量份的原料加水充分混合，呈泥浆状混合物包装即可。
本发明所述的冶金耐火砖交接口密封胶泥已在国内大中型钢铁企业推广使用，如安钢、舞钢、酒钢等。
经应用发现，本发明选取的原料规格为80-200目之间的细粉，可以满足不同冶金耐火砖对接口和砌缝密封的需要。选取的原料重量组分搭配，均能实现低温粘接效果好、高温强度高、耐火性能好的目的。其粘结时间为2-5小时；不仅粘结时间适当，而且流动性粘结度均较为理想。
具体实施方式
所述冶金耐火砖交接口密封胶泥是由下列重量份的原料组成：
铝矾土熟料粉40-50份
结合剂(软质黏土)30-40份
高温粘结剂30-40份
纤维素1-2份
漂浮剂1-2份
纸浆粉1-2份
其余成分为水。
所述原料规格均为80-200目细粉；其制备方法是：称取上述重量份的原料加水充分混合，呈泥浆状混合物包装即可。
Claims (2)
1.一种冶金耐火砖交接口密封胶泥，其特征在于：所述冶金耐火砖交接口密封胶泥是由下列重量份的原料组成：
铝矾土熟料粉 40-50份
结合剂(软质黏土) 30-40份
高温粘结剂 30-40份
纤维素 1-2份
漂浮剂 1-2份
纸浆粉 1-2份
其余成分为水。
2.根据权利要求1所述的冶金耐火砖交接口密封胶泥，其特征在于：选取的所有原料规格均为80-200目细粉；其制备方法是：称取所述重量份的原料加水充分混合，呈泥浆状混合物包装即可。