CN107446433A - A kind of emulsion paint and its manufacture craft - Google Patents
A kind of emulsion paint and its manufacture craft Download PDFInfo
- Publication number
- CN107446433A CN107446433A CN201710615984.8A CN201710615984A CN107446433A CN 107446433 A CN107446433 A CN 107446433A CN 201710615984 A CN201710615984 A CN 201710615984A CN 107446433 A CN107446433 A CN 107446433A
- Authority
- CN
- China
- Prior art keywords
- emulsion
- emulsion paint
- preservative
- light stabilizer
- stirring
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of emulsion paint, including following raw material：Acrylate and vinyl acetate emulsion, acrylic emulsion, sodium propionate, titanium dioxide, silica flour, expanded graphite, glass fibre, solvent, preservative, methanal trapping agent and light stabilizer.The invention also discloses a kind of preparation method of emulsion paint, it comprises the following steps, S1, and acrylic emulsion is added in solvent, stirs, obtains emulsion a；S2, titanium dioxide will be stated and be added in acrylate and vinyl acetate emulsion, silica flour, expanded graphite and glass fibre and solvent is stirring evenly and then adding into, is dispersed with stirring, obtain emulsion b；S3, the emulsion a after above-mentioned processing and emulsion b is mixed, and add preservative, methanal trapping agent and light stabilizer, be dispersed with stirring, produce emulsion paint.Not only fire retardant performance is greatly improved the present invention, and water resistance is excellent, extends the service life of emulsion paint；In addition, preservative, methanal trapping agent and the light stabilizer of addition, further increase the durability of emulsion paint.
Description
Technical field
The present invention relates to technical field of coatings, more particularly to a kind of emulsion paint and its manufacture craft.
Background technology
Paint finishing can very well bond with matrix material in body surface and form the material of complete and tough and tensile diaphragm, claim
For coating.Coating and paint are identical concepts.Paint is people's custom title used for a long time, just sharp always after introducing China
Used in building trade.The effect of coating may be summarized to be three aspects：Protective effect, decoration function, specific function effect.Coating
General composition：Include film forming matter, color stuffing, solvent, auxiliary agent.Building coating has decoration functions, defencive function and inhabitation
Property improve function.Proportion shared by various functions is not quite similar because application target is different.Decoration functions are by building
Beautify to improve the function of its appearance value.Main design design and solid including in terms of plane color, pattern and gloss
The design design of decorative pattern., could be sufficiently but size and shape in itself that will be with the moulding of building in itself and base material is engaged
Bring into play.Defencive function refers to the function of protecting building not protected from environmental and destroy.It is different types of by protective
It is also different to the content of defencive function requirement.As it is indoor with index difference that is reaching required by outdoor application if it is very big.Have
Building have particular/special requirement to mould proof, fire prevention, insulation, corrosion-resistant etc..
Emulsion paint is being commonly called as latex paint, is born in the next period in nineteen seventies, is with acrylic ester copolymer
Emulsion is a major class synthetic resin emulsion coating of representative.Emulsion paint is water-dispersible paint, it be using synthetic resin emulsion as
Base-material, filler add the refined coating formed of various auxiliary agents after grinding distribution.Emulsion paint possesses and traditional metope coating
Different many merits, such as it is easy to brush, dries that rapid, paint film is water-fast, scrub resistance is good.In China, people traditionally
Synthetic resin emulsion is base-material, using water as decentralized medium, adds pigment, filler and auxiliary agent, through painting made of certain technical process
Material, is called emulsion paint, is also latex paint.
However, existing latex paint formulation is complicated, cost is high, has portioned product fire protecting performance bad, holds after long-time illumination
It is easily dry and cracked, finally come off from substrate surface, influence the normal protective action of emulsion paint.In addition, Chinese with a vast territory, the four corners of the world
The temperature height and light irradiation time of weather are differed greatly, and coastal area is influenceed seriously by salt fog, therefore market urgently researches and develops one
Kind high temperature resistant, waterproof, uvioresistant, the strong and full-featured emulsion paint of anti-corrosive properties.
The content of the invention
Based on technical problem existing for background technology, the present invention proposes a kind of emulsion paint and its manufacture craft.
A kind of emulsion paint proposed by the present invention, the percentage by weight of each raw material are：
The product raw material acrylate and vinyl acetate emulsion, acrylic emulsion, sodium propionate, titanium dioxide, silica flour, expanded graphite, glass fibre
It is 100% with solvent gross weight；
Comprise additionally in：(percentage by weight is using above-mentioned raw material weight as radix)
Preservative 2%-4% (additional)
Methanal trapping agent 0.8%-1.2% (additional)
Light stabilizer 0.1%-0.5% (additional).
Preferably, the percentage by weight of each raw material is：Acrylate and vinyl acetate emulsion 30%, acrylic emulsion 15%, sodium propionate 15%, titanium
White powder 12%, silica flour 7%, expanded graphite 5%, glass fibre 2%, solvent 14%.
Preferably, deionized water and acetone or alcohol and acetone.
Preferably, the silica flour uses silicon dioxide ultrafine powder.
Preferably, the preservative is Nordes C15 sterilization antiseptics, Nordes EPW, Dao Weixier -75,1,2- benzene
And the compounding intermixture that the one or more in isothiazoline -3- ketone combine.
Preferably, the methanal trapping agent is 1- methyl isophthalic acid H- imidazoles -5- formylhydrazines, 2- (the chloro- 1H- miaows of bromo- 4, the 5- bis- of 2-
Azoles -1- bases) acethydrazide, mixture one or more in 1- (1H- indoles -3- carbonyls) -1H- imidazoles.
Preferably, it is just pungent to be selected from 2- BTAs, 2,4-DihydroxyBenzophenone, 2- hydroxyls -4- for the light stabilizer
One or more combination in epoxide benzophenone or 2,5- chlorination BTA.
The invention also provides a kind of preparation method of emulsion paint, comprise the following steps：
S1, acrylic emulsion is added in solvent, stirs, obtains emulsion a；
S2, titanium dioxide will be stated and be added in acrylate and vinyl acetate emulsion, be stirring evenly and then adding into silica flour, expanded graphite and glass fibre and
Solvent, 300-400 revs/min is dispersed with stirring 15-25 minutes, obtains emulsion b；
S3, the emulsion a after above-mentioned processing and emulsion b is mixed, and adds preservative, methanal trapping agent and light stabilizer,
1200-1800 revs/min is dispersed with stirring 25-35 minutes, produces the emulsion paint.
The present invention is used as fire retardant, the fire prevention of the emulsion paint of effective raising by adding expanded graphite in emulsion paint
Performance, the glass fibre of addition improve its elasticity and ductility while can not only improving emulsion paint intensity, can after its film forming
So that emulsion paint is bright-colored beautiful, and in elevated temperature melts, the nature of glass mix-froth thermal insulation layer of formation, it can effectively completely cut off heat
The transmission of amount, fire-retardant effect, while the silica flour added are further improved, can be played while flame retardant effect is strengthened anti-
The impervious effect of water, the service life of emulsion paint can be extended, improve its chemical stability；In addition, the preservative of addition can be effective
Suppress to cause rotten microorganism, improve the anti-corrosive properties of emulsion paint, the absorbable capture formaldehyde of methanal trapping agent of addition so that emulsion paint is more
The environmental protection added, the light stabilizer of addition, intense light can be weakened and inject the influence to caused by emulsion paint on metope behind interior.
Embodiment
With reference to specific embodiment, the invention will be further described.
Embodiment 1
A kind of emulsion paint proposed by the present invention, the percentage by weight of each raw material is acrylate and vinyl acetate emulsion 28%, acrylic emulsion
20%th, sodium propionate 10%, titanium dioxide 7%, silicon dioxide ultrafine powder 5%, expanded graphite 3%, glass fibre 1%, remaining is to go
Ionized water and acetone；Comprise additionally in：Preservative 2%, methanal trapping agent 0.8% and light stabilizer 0.1% are (more than percentage by weight
It is radix to state raw material weight).
Wherein, the preservative is Nordes C15 sterilization antiseptics.
Wherein, it is 1- methyl isophthalic acid H- imidazoles -5- formylhydrazines to state methanal trapping agent.
Wherein, the light stabilizer is selected from 2- BTAs.
The invention also provides a kind of preparation method of emulsion paint, comprise the following steps：
S1, acrylic emulsion is added in acetone, stirs, obtains emulsion a；
S2, titanium dioxide will be stated and be added in acrylate and vinyl acetate emulsion, be stirring evenly and then adding into silica flour, expanded graphite and glass fibre and
Ethanol, 300 revs/min are dispersed with stirring 15 minutes, obtain emulsion b；
S3, the emulsion a after above-mentioned processing and emulsion b is mixed, and adds preservative, methanal trapping agent and light stabilizer,
1200 revs/min are dispersed with stirring 25 minutes, produce the emulsion paint.
Embodiment 2
A kind of emulsion paint proposed by the present invention, the percentage by weight of each raw material is acrylate and vinyl acetate emulsion 29%, acrylic emulsion
18%th, sodium propionate 12%, titanium dioxide 10%, silicon dioxide ultrafine powder 6%, expanded graphite 4%, glass fibre 2%, remaining is to go
Ionized water and acetone；Comprise additionally in：Preservative 2.5%, methanal trapping agent 0.9% and light stabilizer 0.2% (percentage by weight with
Above-mentioned raw materials weight is radix).
Wherein, the preservative is Nordes EPW.
Wherein, it is 1- methyl isophthalic acid H- imidazoles -5- formylhydrazines to state methanal trapping agent.
Wherein, the light stabilizer is 2,4-DihydroxyBenzophenone.
The invention also provides a kind of preparation method of emulsion paint, comprise the following steps：
S1, acrylic emulsion is added in acetone, stirs, obtains emulsion a；
S2, titanium dioxide will be stated and be added in acrylate and vinyl acetate emulsion, be stirring evenly and then adding into silica flour, expanded graphite and glass fibre and
Ethanol, 320 revs/min are dispersed with stirring 20 minutes, obtain emulsion b；
S3, the emulsion a after above-mentioned processing and emulsion b is mixed, and adds preservative, methanal trapping agent and light stabilizer,
1300 revs/min are dispersed with stirring 30 minutes, produce the emulsion paint.
Embodiment 3
A kind of emulsion paint proposed by the present invention, the percentage by weight of each raw material is acrylate and vinyl acetate emulsion 30%, acrylic emulsion
16%th, sodium propionate 14%, titanium dioxide 13%, silicon dioxide ultrafine powder 7%, expanded graphite 5%, glass fibre 3%, remaining is to go
Ionized water and acetone；Comprise additionally in：Comprise additionally in：Preservative 3%, methanal trapping agent 1% and the (weight hundred of light stabilizer 0.3%
Divide than using above-mentioned raw material weight as radix).
Wherein, the preservative is Nordes C15 sterilization antiseptics, Nordes EPW, Dao Weixier -75,1,2- benzos
Compounding intermixture in isothiazoline -3- ketone.
Wherein, state methanal trapping agent for 1- methyl isophthalic acid H- imidazoles -5- formylhydrazines, 2- (the chloro- 1H- imidazoles of bromo- 4, the 5- bis- of 2- -
1- yls) acethydrazide and 1- (1H- indoles -3- carbonyls) -1H- imidazoles mixture.
Wherein, the light stabilizer is selected from 2- BTAs, 2,4-DihydroxyBenzophenone, the just pungent oxygen of 2- hydroxyls -4-
The mixture of base benzophenone and 2,5- chlorination BTA.
The invention also provides a kind of preparation method of emulsion paint, comprise the following steps：
S1, acrylic emulsion is added in acetone, stirs, obtains emulsion a；
S2, titanium dioxide will be stated and be added in acrylate and vinyl acetate emulsion, be stirring evenly and then adding into silica flour, expanded graphite and glass fibre and
Deionized water, 350 revs/min are dispersed with stirring 20 minutes, obtain emulsion b；
S3, the emulsion a after above-mentioned processing and emulsion b is mixed, and adds preservative, methanal trapping agent and light stabilizer,
1500 revs/min are dispersed with stirring 30 minutes, produce the emulsion paint.
Embodiment 4
A kind of emulsion paint proposed by the present invention, the percentage by weight of each raw material is acrylate and vinyl acetate emulsion 31%, acrylic emulsion
14%th, sodium propionate 16%, titanium dioxide 16%, silicon dioxide ultrafine powder 8%, expanded graphite 6%, glass fibre 4%, remaining is second
Alcohol and acetone；Comprise additionally in：(percentage by weight is with above-mentioned for preservative 3.5%, methanal trapping agent 1.1% and light stabilizer 0.4%
Raw material weight is radix).
Wherein, the preservative is Dao Weixier -75.
Wherein, it is 2- (the chloro- 1H- imidazoles -1- bases of bromo- 4, the 5- bis- of 2-) acethydrazide to state methanal trapping agent.
Wherein, the light stabilizer is 2-hydroxy-4-n-octoxybenzophenone.
The invention also provides a kind of preparation method of emulsion paint, comprise the following steps：
S1, acrylic emulsion is added in acetone, stirs, obtains emulsion a；
S2, titanium dioxide will be stated and be added in acrylate and vinyl acetate emulsion, be stirring evenly and then adding into silica flour, expanded graphite and glass fibre and
Deionized water, 350 revs/min are dispersed with stirring 20 minutes, obtain emulsion b；
S3, the emulsion a after above-mentioned processing and emulsion b is mixed, and adds preservative, methanal trapping agent and light stabilizer,
1600 revs/min are dispersed with stirring 30 minutes, produce the emulsion paint.
Embodiment 5
A kind of emulsion paint proposed by the present invention, the percentage by weight of each raw material is acrylate and vinyl acetate emulsion 32%, acrylic emulsion
10%th, sodium propionate 20%, titanium dioxide 20%, silicon dioxide ultrafine powder 10%, expanded graphite 7%, glass fibre 5%, remaining is
Solvent；Comprise additionally in：(percentage by weight is with above-mentioned raw materials weight for preservative 4%, methanal trapping agent 1.2% and light stabilizer 0.5%
Measure as radix).
Wherein, the preservative is BIT.
Wherein, it is 1- (1H- indoles -3- carbonyls) -1H- imidazoles to state methanal trapping agent.
Wherein, the light stabilizer is 2,5- chlorination BTAs.
The invention also provides a kind of preparation method of emulsion paint, comprise the following steps：
S1, acrylic emulsion is added in acetone, stirs, obtains emulsion a；
S2, titanium dioxide will be stated and be added in acrylate and vinyl acetate emulsion, be stirring evenly and then adding into silica flour, expanded graphite and glass fibre and
Deionized water, 400 revs/min are dispersed with stirring 25 minutes, obtain emulsion b；
S3, the emulsion a after above-mentioned processing and emulsion b is mixed, and adds preservative, methanal trapping agent and light stabilizer,
1800 revs/min are dispersed with stirring 35 minutes, produce the emulsion paint.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art the invention discloses technical scope in, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should all be included within the scope of the present invention.
Claims (8)
1. a kind of emulsion paint, it is characterised in that the percentage by weight of each raw material is：
The product raw material acrylate and vinyl acetate emulsion, acrylic emulsion, sodium propionate, titanium dioxide, silica flour, expanded graphite, glass fibre and molten
Agent gross weight is 100%；
Comprise additionally in：(percentage by weight is using above-mentioned raw material weight as radix)
Preservative 2%-4% (additional)
Methanal trapping agent 0.8%-1.2% (additional)
Light stabilizer 0.1%-0.5% (additional).
2. a kind of emulsion paint according to claim 1, it is characterised in that the percentage by weight of each raw material is：Acrylate and vinyl acetate emulsion
30%th, acrylic emulsion 15%, sodium propionate 15%, titanium dioxide 12%, silica flour 7%, expanded graphite 5%, glass fibre 2%, molten
Agent 14%.
3. a kind of emulsion paint according to claim 2, it is characterised in that the solvent selects deionized water and acetone or second
Alcohol and acetone.
4. a kind of emulsion paint according to claim 2, it is characterised in that the silica flour uses silicon dioxide ultrafine powder.
5. a kind of emulsion paint according to claim 1, it is characterised in that the preservative is Nordes C15 sterilization and anticorrosions
The compounding that one or more in agent, Nordes EPW, Dao Weixier -75, BIT combine is mixed
Mixture.
6. a kind of emulsion paint according to claim 1, it is characterised in that the methanal trapping agent is 1- methyl isophthalic acid H- miaows
In azoles -5- formylhydrazines, 2- (the chloro- 1H- imidazoles -1- bases of the bromo- 4,5- bis- of 2-) acethydrazide, 1- (1H- indoles -3- carbonyls) -1H- imidazoles
One or more mixtures.
A kind of 7. emulsion paint according to claim 1, it is characterised in that the light stabilizer be selected from 2- BTAs,
One or more of groups in 2,4-DihydroxyBenzophenone, 2-hydroxy-4-n-octoxybenzophenone or 2,5- chlorination BTA
Close.
8. a kind of preparation method of emulsion paint, it is characterised in that comprise the following steps：
S1, acrylic emulsion is added in solvent, stirs, obtains emulsion a；
S2, titanium dioxide will be stated and be added in acrylate and vinyl acetate emulsion, be stirring evenly and then adding into silica flour, expanded graphite and glass fibre and molten
Agent, 300-400 revs/min is dispersed with stirring 15-25 minutes, obtains emulsion b；
S3, the emulsion a after above-mentioned processing and emulsion b is mixed, and adds preservative, methanal trapping agent and light stabilizer,
1200-1800 revs/min is dispersed with stirring 25-35 minutes, produces the emulsion paint.