CN105400261A - Antistatic emulsion paint - Google Patents
Antistatic emulsion paint Download PDFInfo
- Publication number
- CN105400261A CN105400261A CN201511028680.9A CN201511028680A CN105400261A CN 105400261 A CN105400261 A CN 105400261A CN 201511028680 A CN201511028680 A CN 201511028680A CN 105400261 A CN105400261 A CN 105400261A
- Authority
- CN
- China
- Prior art keywords
- parts
- emulsion paint
- antistatic
- deionized water
- polyvinyl alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of emulsion paint, especially to an antistatic emulsion paint. The antistatic emulsion paint is prepared from the following raw materials by weight: 8 to 15 parts of sodium propionate, 17 to 35 parts of manganous naphthenate, 20 to 40 parts of silica micropowder, 20 to 35 parts of polyvinyl alcohol, 3 to 5 parts of isooctyl acrylate, 26 to 30 parts of titanium dioxide, 15 to 21 parts of zinc oxide, 25 to 31 parts of vinyl acetate/acrylic emulsion and 80 to 150 parts of deionized water. The antistatic emulsion paint has the advantages of low triboelectrification voltage, good antistatic effect, long-lasting antistatic performance, strong covering power, good levelability of a paint film, good washing resistance and high cleanliness.
Description
Technical field
The present invention relates to emulsion paint field, especially an Anti-static emulsion paint.
Background technology
So-called electrostatic, a kind of exactly electric charge remained static is immobilising electric charge (electric charge of flowing just defines electric current) in other words.When accumulation just defines electrostatic on certain object or time surperficial, all Charger transfer can occur when static electrification object contact zero potential object (ground connection object) or when having the object of potential difference with it, being exactly that we are daily sees Spark Discharges.Such as northern wintry weather is dry, and human body easily brings electrostatic, will Discharge Phenomena when contacting other people or metallic conductor.People has the prickling sensation of electric shock, and night can see spark, and this is that chemical fibre clothes and human body rub the reason of positive electrostatic on human body band.
Along with improving constantly of people's living standard, the rate of utilization of household electrical appliance increases day by day, because household electrical appliance are by the restriction of putting the many factors such as place, volume, make household electrical appliance that the anti-static device of fine anti-static effect cannot be installed, but contact that is frequent because of people and household electrical appliance, make in household electrical appliance often with electrostatic, electron device in household electrical appliance can puncture by electrostatic inadvertently, cause short circuit or the open circuit of household electrical appliance, not only cause the infringement of household electrical appliance, also very easily cause the electric shock of personnel.
Summary of the invention
The object of the invention is to solve the above-mentioned defect that prior art exists, propose a kind of Anti-static emulsion paint, its triboelectrification voltage is low, anti-static effect good, antistatic performance is lasting, strong covering power, paint film good leveling property, abrasion resistance is strong, cleanliness factor is high.
Technical scheme of the present invention is: a kind of Anti-static emulsion paint, is made up of the raw material of following parts by weight: Sodium Propionate 8-15 part, manganese naphthenate 17-35 part, silicon dioxide ultrafine powder 20-40 part, polyvinyl alcohol 20-35 part, vinylformic acid isooctyl 3-5 part, titanium dioxide 26-30 part, zinc oxide 15-21 part, vinegar third 25-31 part, deionized water 80-150 part.
In the present invention, described Anti-static emulsion paint is made up of the raw material of following parts by weight: Sodium Propionate 9-14 part, manganese naphthenate 21-33 part, silicon dioxide ultrafine powder 26-34 part, polyvinyl alcohol 24-33 part, vinylformic acid isooctyl 4-5 part, titanium dioxide 27-29 part, zinc oxide 16-19 part, vinegar third 26-30 part, deionized water 100-140 part.
Preferably, described Anti-static emulsion paint is made up of the raw material of following parts by weight: Sodium Propionate 12 parts, manganese naphthenate 31 parts, silicon dioxide ultrafine powder 32 parts, polyvinyl alcohol 30 parts, vinylformic acid isooctyl 5 parts, titanium dioxide 28 parts, 18 parts, zinc oxide, vinegar the third 27 parts, deionized water 130 parts.
Beneficial effect of the present invention: have that gas defence is antibacterial, the feature such as purify air, is the environment-friendly type aqueous coating of a kind of desirable anti-electrostatic, can be completely achieved biological degradation.
Embodiment
Below in conjunction with embodiment, the present invention is further illustrated.
Embodiment 1
In the present embodiment, Anti-static emulsion paint is made up of the raw material of following parts by weight: Sodium Propionate 8 parts, manganese naphthenate 17 parts, silicon dioxide ultrafine powder 20 parts, polyvinyl alcohol 20 parts, vinylformic acid isooctyl 3 parts, titanium dioxide 26 parts, 15 parts, zinc oxide, vinegar the third 25 parts, deionized water 80 parts.
Embodiment 2
In the present embodiment, described Anti-static emulsion paint is made up of the raw material of following parts by weight: Sodium Propionate 9 parts, manganese naphthenate 21 parts, silicon dioxide ultrafine powder 26 parts, polyvinyl alcohol 24-part, vinylformic acid isooctyl 4 parts, titanium dioxide 27-part, 16 parts, zinc oxide, vinegar the third 26 parts, deionized water 100 parts.
Embodiment 3
In the present embodiment, described Anti-static emulsion paint is made up of the raw material of following parts by weight: Sodium Propionate 12 parts, manganese naphthenate 31 parts, silicon dioxide ultrafine powder 32 parts, polyvinyl alcohol 30 parts, vinylformic acid isooctyl 5 parts, titanium dioxide 28 parts, 18 parts, zinc oxide, vinegar the third 27 parts, deionized water 130 parts.
Embodiment 4
In the present embodiment, described Anti-static emulsion paint is made up of the raw material of following parts by weight: Sodium Propionate 15 parts, manganese naphthenate 35 parts, silicon dioxide ultrafine powder 40 parts, polyvinyl alcohol 35 parts, vinylformic acid isooctyl 5 parts, titanium dioxide 30 parts, 21 parts, zinc oxide, vinegar the third 31 parts, deionized water 150 parts.
Claims (3)
1. an Anti-static emulsion paint, is characterized in that being made up of the raw material of following parts by weight: Sodium Propionate 8-15 part, manganese naphthenate 17-35 part, silicon dioxide ultrafine powder 20-40 part, polyvinyl alcohol 20-35 part, vinylformic acid isooctyl 3-5 part, titanium dioxide 26-30 part, zinc oxide 15-21 part, vinegar third 25-31 part, deionized water 80-150 part.
2. Anti-static emulsion paint according to claim 1, is characterized in that being made up of the raw material of following parts by weight: Sodium Propionate 9-14 part, manganese naphthenate 21-33 part, silicon dioxide ultrafine powder 26-34 part, polyvinyl alcohol 24-33 part, vinylformic acid isooctyl 4-5 part, titanium dioxide 27-29 part, zinc oxide 16-19 part, vinegar third 26-30 part, deionized water 100-140 part.
3. Anti-static emulsion paint according to claim 1, is characterized in that being made up of the raw material of following parts by weight: Sodium Propionate 12 parts, manganese naphthenate 31 parts, silicon dioxide ultrafine powder 32 parts, polyvinyl alcohol 30 parts, vinylformic acid isooctyl 5 parts, titanium dioxide 28 parts, 18 parts, zinc oxide, vinegar the third 27 parts, deionized water 130 parts.